The Effect of Admixing Al2O3 on Some Properties of High Copper Dental Amalgam

Author: Jassim Mohammed Salman
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2014 Volume: 22 Issue: 4 Pages: 875-883
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In recent years, there have been many attempts to improve properties of dental amalgam. The aim of this study is to investigate the effect of additional Al2O3 on properties of high copper dental amalgam. Al2O3 is added in different percentages ( 0.1, 0.2, 0.3, and 0.4wt% ). The specimens were prepared according to A.D.A specification No. 1. The specimens have been stored at 37±1 Cº by using glass chamber prepared for this purpose. The prepared specimens are characterized by different types of tests such as creep,hardness,dimensional change ,microstructure by optical microscopic and corrosion test. The results show that the hardness increase with increasing Al2O3 percentage . Results of creep resistance are within the approved percentage of A.D.A., dimensional change is less than the approved percentage by A.D.A. also. The best corrosion resistance is at 0.2 and 0.4wt% of Al2O3 with improving ( 60 %) and (55 %) respectively.

كانت هنالك محاولات عديدة لتحسين خواص سبائك ملغم الاسنان في السنين الاخيرة ,الهدف من هذه الدراسة هو لبيان تأثير اضافة اوكسيد الالمنيوم على بعض خواص سبيكة ملغم النحاس عالية النحاس. تم اضافة اوكسيد الالمنيوم بنسب مئوية مختلفة (0.1,0.2,0.3,0.4 ). حضرت العينات حسب المواصفة رقم( 1) للجمعية الأمريكية للأسنان. تم حفظ العينات بدرجة حرارة 37 في حجرة زجاجيه معده لهذا الغرض . اعدت العينات المحضرة لأنواع مختلفة من الفحوصات مثل: الزحف, الصلادة , التغير بالأبعاد , البنيه المجهرية بواسطة المجهر الضوئي وفحص التآكل. .اضهرت النتائج زياده في قيم الصلادة بزيادة نسب اوكسيد الالمنيوم المضاف , نتائج مقاومة الزحف ضمن النسب المسموح بها من قبل الجمعية الأمريكية للأسنان وكذلك التغير بالأبعاد. افضل مقاومة تآكل كانت لنسب اوكسيد الالمنيوم 0.2 و0.4 وبتحسن مقداره ( % 60 ) و(% 55 )على التوالي.


Article
Study the Efffect of Adding Cu on Some Mechanical and Structural Properties of the Ag-Sn Alloy
دراسة تأثير إضافة النحاس على بعض الخصائص التركيبية والميكانيكية لسبيكة فضة-قصدير

Authors: Mohammed Obaid Kadhim --- Hassan Juma Abd --- Huda Khailed Hameed
Journal: Iraqi Journal of Science and Technology المجلة العراقية للعلوم والتكنولوجيا ISSN: 18136893 Year: 2013 Volume: 4 Issue: 3 Pages: 134-141
Publisher: Ministry of science and technology وزارة العلوم والتكنولوجيا

Loading...
Loading...
Abstract

In this Research, four high-copper amalgam alloys have been prepared by melting at 1050oC in an inert atmosphere, with copper content ranging from (14 to 26wt. %). Heat treatment processes were carried out to increase phases homogeneity and to reduce residual stresses, then, the alloys were mixed with mercury with a ratio of (1:1.2). Several structural measurements were carried out such as x-ray diffraction and microstructure analysis and some mechanical tests such as micro-hardness and compressive strength. X-ray diffraction results show that the amalgams and amalgams alloys have a variety of phases which depends on the copper content in the alloys. On the other hand, results of micro-hardness and compressive strength show that there is a linear increment in the mechanical properties with increasing copper in the amalgam, the results of D (Cu 26%) amalgam was comparable to those measured for the commercial amalgam of ANA that have high mechanical properties.

حضرت أربع سبائك ملغم عالية النحاس بصهرها عند درجة حرارة 1050oC في أجواء خاملة. وقد تراوحت نسب النحاس في السبائك بين (14~26wt.%) , تم إجراء معالجات حرارية لتحسين التجانس الطوري في السبائك وإزالة الإجهادات، أُجريت عملية الملغمة بخلط السبائك مع الزئبق بنسبة (1:1.2) ,أُجري عدد من القياسات التركيبية مثل تحليلات حيود الأشعة السينية وتحليلات البنية الدقيقة وبعض الخواص الميكانيكية المهمة مثل الصلادة ومقاومة الأنضغاط. وبينت تحليلات حيود الأشعة السينية وجود عدد من الأطوار الرئيسية في السبائك والملاغم تعتمد نسبها وتوزيعها على محتوى النحاس في السبيكة. بينما أظهرت نتائج قياسات الصلادة ومقاومة الانضغاط حصول زيادة خطية في الخصائص الميكانيكية مع زيادة النحاس في الملاغم. وكانت نتائج الملغم D (%26 Cu) مقاربة للقيم المقاسة للملغم التجاري ANA والذي يمتلك خصائص ميكانيكية عالية