Article
EFFECT OF DIFFERENT CADMIUM CONTENT ON MODIFICATION OF SILICON EUTECTIC IN Al-12%Si ALLOYS
تاثير اختلاف محتوى الكادميوم على تحوير سيليكون اليوتكتك في سبيكة Al-12%Si

Author: Waleed T. Rashid وليـــد تركــــــــــي راشــــــد
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2017 Volume: 30 Issue: 1 Pages: E79-E86
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

This work is devoted to examine and quantify the expected change in the mechanical properties and microstructure of an Aluminum-Silicon alloy after adding various percentages of cadmium. Two alloys were prepared with adding cadmium (1.5 and 3%wt) to the Al-12%Si base alloy. The new microstructure shows that the addition of (1.5 and3% Cd) resulted in a modification of eutectic Si phase from needle plate form to almost spherical one. The modification in Si eutectic phase could improve the mechanical properties. In specific, the hardness increased from 59 to 69 kgmm2, the tensile strength increased from 121 to 140Mpa and the yield strength increased from 31 to51 Map, while ductility decreased from 13 to 8 %.

يتناول هذا البحث دراسة تأثير إضافة الكادميوم على البنية المجهرية والخواص الميكانيكية لسبيكة 12%SiAl-.وقد تم تحضير سبيكتين بإضافة عنصر الكادميوم (1.5-3%) بالإضافة إلى السبيكة الأساس. أوضحت نتائج البنية المجهرية إن إضافة الكادميوم بنسبة (1.5-3%) يؤدي إلى تحوير طور السليكون اليوتكتيكي من شكل صفائح أبرية إلى شكل كروي تقريبا. وتتحسن الخواص الميكانيكية بسبب تحوير طور السليكون اليوتكتيكي , حيث ازدادت الصــلادة(من 56إلى69kgmm2) ومقاومة الشد(من121إلى140Mpa) ومقاومة الخضوع(من31إلى 51 Mpa) وانخفضت المطيلية (من 13% إلى 8 %).