Study On the Flexural and Impact Properties of Short Okra Natural Fiber Reinforced Epoxy Matrix Composites
دراسة خواصالانحناء والصدمة للمادة المركبة ذات الأساس من الایبوكسي المقواة بألیاف نبات البامیة

Authors: Aseel Mahmood Abdullah --- Ahmed Mudhafar Hashim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 10 Pages: 1696-1706
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The okra natural fiber reinforced epoxy matrix composites were prepared byhand-lay-up. The weight fractions of okra fiber are (1, 3, 6, 9, and 12% by weightwt). The flexural properties and impact resistance of composites were determinedby the flexural and impact tests. The maximum modulus of elasticity is (844.93MPa) at the weight fraction of (12 % wt) of okra fiber, comparison with (91.25MPa) for virgin epoxy material. The maximum impact energy is (0.75 J) at theweight fraction of I(12 % wt) of okra fiber, comparison with (0.05 J) for virginepoxy material.

في الدراسة الحالیة تم تحضیر المادة المركبة ذات الأساس من الایبوكسي المق واة بألی اف نب ات1) بطریق ة الص ب الی دوي ، وم ن ث م دراس ة , 3, 6, 9, 12 % wt) البامیة بكسور وزنیة مختلفةخواص الانحناء والصدمة لنماذج المادة المركبة. وقد بین ت النت ائج أن أعظ م ق یم لمعام ل الإنحن اء12 % )من ألیاف نبات البامیة مقارنةً wt) 844.93 ) وذلك للمادة المركبة المقواة ب MPa) كانت91.25 ) للایبوكسي غیر المقوى. أما بالنسبة لنتائج اختبار مقاومة الصدمة فقد كانت أعظم MP) ب12 % ) من ألیاف نبات البامیة wt) 0.75 ) وذلك للمادة المركبة المقواة ب J) قیمة للطاقة الممتصة0.05 ) للایبوكسي غیر المقوى. J) مقارنة بً


Article
Effect of Mid Plane Layer on Flexural Properties of Plies Under Transverse Loading
تاثير الطبقة الوسطية على متانة الانحناء للطبقات تحت الاجهاد المستعرض

Authors: Zainab Raheem Muslem زينب رحيم مسلم --- Harith Ibrahim Jaffer حارث ابراهيم جعفر
Journal: Albahir journal مجلة الباهر ISSN: 23125721 Year: 2015 Volume: 2 Issue: 3,4 Pages: 15-19
Publisher: AL-Abbas Holy Shrine العتبة العباسية المقدسة

Loading...
Loading...
Abstract

Abstract The effect of mid layer on flexural strength and young modulus were studied using Instron testing machine. E-glass/epoxy composites were manufactured using hand lay-up technique. The laminated composites were prepared with dimension (4x10x80) mm, Epoxy composites were reinforced with multidirectional layer of woven glass fiber and random glass fiber of stacking sequence [M]16, [R]16, [M/R//M1/M1//R/M]s, [//M/R//]s, and [R/M//R1/R1//M/R]s. The effect of transverse loading on flexural strength and young modulus was investigated for specimens subjected to Three-point bending test. The results show that the mid layer (M1/M1) which had (homogeneous distribution) has higher flexural strength value and young modulus than mid layer (M1/R1) and (R1/R1).

ﺍﳋﻼﺻﺔ ﺗﻢ ﺩﺭﺍﺳﺔ ﺍﻟﻄﺒﻘﺔ ﺍﻟﻮﺳﻄﻴﺔ ﻋﲆ ﻣﺘﺎﻧﺔ ﺍﻻﻧﺤﻨﺎﺀ ﻭﻣﻌﺎﻣﻞ ﻳﻮﻧﻚ. ﺗﻢ ﲢﻀﲑ ﻣﱰﺍﻛﺒﺎﺕ ﻣﻦ ﺍﻻﻳﺒﻮﻛﴘ- ﺍﻟﻴﺎﻑ ﺯﺟﺎﺟﻴﺔ .ﺳﻠﺤﺖ ﺍﳌﱰﺍﻛﺒﺎﺕ ﺑﻄﺒﻘﺎﺕ ﻣﺘﻌﺪﺩﺓ ﻣﻦ ﺍﻟﻴﺎﻑ ﺯﺟﺎﺟﻴﺔ ﻋﺸﻮﺍﺋﻴﺔ ﻭﺣﺼﲑﺓ.ﺗﻢ ﺩﺭﺍﺳﺔ ﺍﻻﺟﻬﺎﺩ ﺍﳌﺴﺘﻌﺮﺽ ﻋﲆ Eﻧﻮﻉ –ﻣﺘﺎﻧﺔ ﺍﻻﻧﺤﻨﺎﺀ ﻭﻣﻌﺎﻣﻞ ﻳﻮﻧﻚ ﺑﺎﺳﺘﺨﺪﺍﻡ ﻓﺤﺺ ﺍﻻﻧﺤﻨﺎﺀ ﺍﻟﺜﻼﺛﻲ. ﺍﻇﻬﺮﺕ ﺍﻟﻨﺘﺎﺋﺞ ﺍﻥ ﺍﻟﻄﺒﻘﺔ ﺍﻟﻮﺳﻄﻴﺔ ﻧﻮﻉ ﺣﺼﲑﺓ ﺣﺼﲑﺓ ﻭﺍﻟﺘﻲ ﲤﻠﻚ ﺗﻮﺯﻳﻊ ﻣﺘﺠﺎﻧﺲ ﺍﻇﻬﺮﺕ ﻣﺘﺎﻧﺔ ﺍﻻﻧﺤﻨﺎﺀ ﻭﻣﻌﺎﻣﻞ ﻳﻮﻧﻚ ﻋﺎﻟﻴﲔ ﻭﻫﻲ ﺍﻋﲆ ﻣﻦ ﻣﻦ ﺣﺼﲑﺓ -ﻋﺸﻮﺍﺋﻲ ﻋﺸﻮﺍﺋﻲ


Article
Studying The Properties of PP/LDPE polymer blend

Authors: Lina Fadhil Kadhim --- Zainab Fadhil Kadhim
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 1 Pages: 193-201
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research studies some of the mechanical, thermaland physical properties for a polymer blend of polypropylene(PP)&low density polyethylene (LDPE). The blend compositions under studying were(pure PP, 25LDPE/75PP,50LDPE/50PP,75LDPE/25LDPE,pure PP). From the results it can be observed that the addition of LDPE to PP has been declined the tensile strength, flexural strength, flexural modulus and hardness while the density improved . the superior tensile strength was obtained at (25LDPE/75PP) composition while preferable flexural strength was ascribed to (50LDPE/50PP) blend composition.

يدرس هذا البحث مجموعة من الخواص الميكانيكية والحرارية والفيزيائية لخليط بوليمري من البولي بروبلين والبولي اثيلين الواطئ الكثافةوتم دراسة نسب الخلط التالية (25/75، 50/50، 75/25) بالأضافة الى البولي بروبيلين والبولي أثيلين واطئ الكثافة النقيين، اظهرت النتائج ان اضافة البولي اثيلين الواطئ الكثافة الى البولي بروبلين ساهمت في تقليل مقاومة الشد ومقاومة الأنحناء ومعامل الانحناء والصلادة وتحسن الكثافة ، عند النسبة (25/75) من الخليط تم الحصول على أعلى مقاومة شد بينما أفضل مقاومة انحناء تعطيها نسبة الخلط (50/50).

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

English (3)


Year
From To Submit

2017 (1)

2015 (1)

2012 (1)