Article
The Effect of Rolling and Heat Treatment on Mechanical Behavior of 6061 Aluminum Alloy
تأثير الدرفلة والمعاملة الحرارية على السلوك الميكانيكيلسبائك المنيوم 6061

Author: Ruaaabd al Kaream Salman
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 6 Part (A) Engineering Pages: 1389-1398
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study, the influence of bothheat treatment and cold working (rolling) on the tensile properties andhardness of6061 aluminum alloy sheets was investigated. The solution heat treatment is first performed at about 520°C 1 hr followed by rolling to(40% and 60%). Artificial aging is obtained by heating to about 180 °C for 1/2hr and 2 hr.Theexperimental work has revealed that when two strengthening mechanism(cold work and aging)are combined, the values of the mechanical properties are come up.Increasing the aging time from ½ hrto 2hr with redaction in area was causing increase in the values of the strength and hardness and dropping the elongation. In the other hand, increasing the redaction in area from (40%) to (60%) with aging was rising the value of the strength and hardness and dropping the elongation. The changes in mechanical properties were discussed as a result of increasing the dislocation density(result of rolling) and formation of precipitation(effect of aging) which are interface with the motion of dislocation and causes hindering of dislocation.

في هذاالبحث تم دراسة تأثير كلاً من المعاملة الحرارية و التشكيل على البارد (الدرفله) على الخواص الميكانيكية والصلادة لصفائح من سبيكة المنيوم 6061. تم اجراء معاملة حرارية للصفائح عند 520 م° لمدة ساعة واتبعت المعاملة بالدرفلة بمقدار (40% و60%) بعدها يتم اجراء التعتيق عند درجة حرارة 180 م° لمدة (2/1 و2) ساعة .تبين نتائج الجانب العملي التالي,ان جمع اليتين من اليات التقوية تزيد من الخواص الميكانيكية لسبيكة المنيوم 6061. ان رفع زمن التعتيق من نصف ساعة الى ساعتين مع اختزال المساحة (الدرفلة) يؤدي الى رفع قيم المقاومة والصلادة وخفض المطيلية, ومن ناحية اخرى, فأن زيادة كمية الاختزال من(40%) الى (60%) مع التعتيق يرفع من قيم المقاومة و الصلادة و يخفض المطيلية. ان التغيرات في الخواص الميكانيكية هو نتيجة لزيادة كثافة الانخلاعات(بسبب الدرفلة) و زيادة الترسيب (بسبب التعتيق)و الذي يتداخل مع الانخلاعات مما يسبب اعاقة لحركتها .


Article
The Influence of Quenching Media and Aging Time on Microstructure and Mechanical Behavior of 6061 Aluminum Alloy
تأثير أوساط الاخماد وزمن التعتيق على التركيب المجهري والسلوك الميكانيكي لسبائك المنيوم 6061

Author: Naser Korde Zedin
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 8 Part (A) Engineering Pages: 1757-1770
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Aluminum-magnesium-silicon (Al-Mg-Si) alloys are medium strength, excellent formability, good corrosion resistance and widely used in extruded products and automotive body materials. The influence of quenching media with different aging time on microstructure and mechanical properties of 6061 aluminum alloy was investigated. The results show formation of (Mg2Si) and (CuAl2) phaseswhensolution treatmentwas applied (at 520°C for 2h,followed by quenching in water and oil at room temperature then aging (at 175°C for 2, 4and6h)) which resultimprovingof both the strength, hardness and decreases elongation. It can be noted that, the grains of samples which are quenching in water is finer than the structure of samples which are quenching in oil. The values of yield stress and ultimate tensile strength decrease respectively with increasing aging time to 6h as (258MPa) and (264MPa) for water quenching and (199MPa) and (235MPa) for oil quenching. In this piper were measured and discussedthe variation of the yield stress, ultimate tensile strength and elongation with different solution quenching and aging time.

تمتاز سبائك (Al-Mg-Si) بمقاومتها المتوسطة وقابليتها العالية للتشكيل ومقاومتها الجيده للتاكل مما جعلها واسعة الانتشار في صناعة المبثوقات وهياكل وسائط النقل. في هذا البحث تم دراسة تأثير اختلاف أوساط الاخماد و زمن تعتيق على البنية المجهرية و الخواص الميكانيكية لسبائك المنيوم 6061. بينت النتائج تكون طوري Mg2Si و CuAl2عند اجراء المعالجة المحلولية (بدرجة حرارة 520مͦلمدة(2ساعة) والمتبوعة بالاخماد (مرة بالماء و مرة بالزيت) عند درجة حرارة الغرفة ثم التعتيق عند درجة حرارية 175 مͦلمدة (6,4,2ساعة) مما ينتج تحسين في كلاً من المقاومة و الصلادة وتنخفض المطيلية. كذلك نلاحظ ان البنية المجهرية للعينات التي يتم اخمادها بالماء اصغر من البنية المجهرية للعينات التي يتم اخمادها بالزيت. قيم اجهاد الخضوع ومقاومة الشد القصوى التي تم الحصول عليها تقل بزيادة زمن التعتيق الى 6 ساعة ,القيم بالتتابع (258 ميكا باسكال) و(264 ميكا باسكال) للاخماد بالماء و (199 ميكا باسكال) و(235 ميكا باسكال) للاخماد بالزيت. في هذا البحثتم قياس و دراسة التغيرات التي تحدث على المعادن بواسطة دراسة مقاومة الخضوع ومقاومة الشد والمطيلية مع اختلاف محاليل الاخماد و زمن التعتيق.