Article
A new type of powder denture cleaner

Authors: Amer A TAQA --- Tarik Y QASSAB-BASHI --- Issam K AL-KHAYAT
Journal: Al-Rafidain Dental Journal مجلة الرافدين لطب الأسنان ISSN: 18121217 Year: 2002 Volume: 2 Issue: 3 Pages: 411-413
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

A new type of weak acid (oxalic acid) sodium carbonate of bicarbonate powder mixture denture cleaner was prepared. The powder mixture was examined pre-clinically and clinically to clean partial and complete dentures using immersion technique. It gave us a good cleaning effect through removing calculus and stains, beside its neglectable effect on denture base materials


Article
Extraction of Valuable Metals From Spent Hydrodesulfurization Catalyst By Two Stage Leaching Method

Loading...
Loading...
Abstract

Spent hydrodesulfurization (Co-Mo/γ-Al2O3) catalyst generally contains valuable metals like molybdenum (Mo), cobalt (Co), aluminium (Al) on a supporting material, such as γ-Al2O3. In the present study, a two stages alkali/acid leaching process was conducted to study leaching of cobalt, molybdenum and aluminium from Co-Mo/γ-Al2O3 catalyst. The acid leaching of spent catalyst, previously treated by alkali solution to remove molybdenum, yielded a solution rich in cobalt and aluminium.


Article
Determination of Meloxicam in Pharmaceutical Formulation byAzo-Coupling Reaction with Sulphanilic Acid Using Both Batch and Flow- Injection Technique
تقدير الميلوكسيكام في المستحضرات الصيدلانية بواسطة تفاعل آزو الأزدواجي مع سلفانيليك أسيد بالطريقة الكلاسيكية و تقنية الحقن الجرياني

Authors: Aveen F. Jallal آفين عبد الله جلال --- Shirwan O. Baban شيروان عمر بابان
Journal: Rafidain journal of science مجلة علوم الرافدين ISSN: 16089391 Year: 2011 Volume: 22 Issue: 4E Pages: 121-132
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

Two sensitive and fast spectrophotometric methods were used by batch and flow-injection spectrophotometric techniques for the determination of meloxicam are proposed. The methods were based on azo-coupling reaction of meloxicam with sulphanilic acid in the presence of sodium nitrite in alkaline medium after converted to primary aromatic amine. The calibration curves resulting from measuring the absorbance at 365 nm are linear over the ranges 1.0-20 and 3.0-30µg/ml with detection limits of 0.5 and 1.0µg/ml, respectively. The molar absorptivity and Sandell index were 1.3839×104l/mol.cm and 2.539×10-2µg/cm2 respectively. The methods are applied to the routine analysis of meloxicam in pharmaceutical formulations.

يتناول هذه البحث طريقتين طيفيتين سريعتين و حساستين باستخدام ألطريقه الكلاسيكية وتقنيه الحقن الجريانى لتقدير الميلوكسيكام.هذه الطريقة تعتمد على تفاعل آزو الأزدواجي لميلوكسيكام مع سلفانيليك أسيد بوجود نيتريت الصوديوم في وسط قاعدي بعد تحويل الميلوكسيكام الى أمين أولى أروماتى.تم قياس الامتصاصية عند طول موجى 365 نانوميتر و ان الخط المستقيم ضمن مدى 1.0-20 مايكروغرام مل، 3.0-30 مايكروغرام مل وحد الكشف 0.5 مايكروغرام مل و 1.0 مايكروغرام مل على الترتيب. وكانت قيمة كل من الأمتصاصية المولارية و معامل ساندل كالأتى ×1041.3839 لترمول.سم و ×10-22.539 مايكروغرامسم2 على الترتيب للطريقة الكلاسيكيه. و تم تطبيق هذة الطريقة لتحليل الميلوكسيكام في المستحضرات الصيدلانية.


Article
أستخدام كاربونات الكالسيوم الصوديوم في انتاج مخاريط عالية الحرارة

Authors: سلام احمد حمزة --- محمد حمزة المعموري --- عبد الحميد فاضل البياتي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2014 Volume: 22 Issue: 5 Pages: 1165-1178
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This study included the possibility of using Kaolin Duekhla and sand Ardma as materials in the production of local thermal cones with the addition of other materials such as sodium carbonate and calcium carbonate, red lead oxide, potassium feldspar, borax and fled in different proportions as material help smelting.Chemical analysis was to sand Erdma and Kaolin Duekhla to prove disqualified for work. Models have been formed through the stone cast and after mixing materials in a dry water was added to it to facilitate manual stamping CBS models were then drying models degree oven 120c. Program was burning in the oven at a rate of 300c per hour. Was prepared nine models change ratios of sodium carbonate and calcium carbonate for the difference in the degree of bending.The results of the fusion behavior of calcium carbonate are extrusive nonlinear Unlike Sodium Carbonate, which is in reverse, with the higher percentage of carbonate, sodium told temperature, and vice versa, either (density) rises with increasing temperature extrusive nonlinear unlike (porosity) drops with increasing temperature incineration Lama (hardness) and (compressibility) with a gradual increase in the temperature rise

تضمنت هذه الدراسة امكانية استخدام كاؤلين دويخلة ورمل ارضمة بوصفها مواد اولية محلية في انتاج مخاريط حرارية مع إضافة مواد أخرى مثل كاربونات الصوديوم وكاربونات الكالسيوم, اوكسيد الرصاص الاحمر,فلسبار بوتاسيوم, والبوراكس فرت بنسب مختلفة كمواد مساعدة على الصهر . تم التحليل الكيميائي لرمل أرضمة و كاؤلين دويخلة لاثبات صلاحيتهما للعمل. تم تشكيل النماذج من خلال قالب جبسي وبعد خلط المواد بشكل جاف تمت إضافة الماء اليها لتسهيل كبس النماذج بالكبس اليدوي ثم تم تجفيف النماذج بالفرن بدرجة 120c . برنامج الحرق في الفرن كان بمعدل 300c لكل ساعة .تم نحضير تسعة نماذج بتغير نسب كاربونات الصوديوم وكاربونات الكالسيوم للحصول على فارق في درجات الانحناء.وبينت نتائج الانصهارية سلوك كاربونات الكالسيوم بشكل طردي لاخطي بعكس كاربونات الصوديوم التي هي بشكل عكسي اذ كلما ارتفعت نسبة كاربونات الصوديوم قلت درجة الحرارة والعكس صحيح,اما (الكثافة) فترتفع مع زيادة درجة الحرارة بشكل طردي لاخطي بعكس (المسامية) فتنخفض مع زيادة درجة حرارة الحرق اما (الصلادة) و(الانضغاطية) فزيادة تدريجية مع ارتفاع درجة الحرارة .


Article
أستخدام كاربونات الصوديوم وفلسبار بوتاسيوم في انتاج مخاريط واطئة الحرارة

Authors: سلام احمد حمزة --- محمد حمزة المعموري --- عبد الحميد فاضل البياتي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2014 Volume: 22 Issue: 6 Pages: 1404-1415
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This study included the possibility of using Kaolin Duekhla and sand Ardma as materials in the production of local thermal cones with the addition of other materials such as sodium carbonate and calcium carbonate, red lead oxide, potassium feldspar, borax and fled in different proportions as material help smelting.Chemical analysis was to sand and Erdma Kaolin Duekhla to prove disqualified for work. Models have been formed through the template created by the researcher and Gypsum After mixing the materials are dry water was added to it to facilitate manual stamping CBS models were then drying models degree oven 120c. Program was burning in the oven at a rate of 300c per hour.Was prepared seven models change ratios of sodium carbonate and potassium feldspar for the difference in the degree of bending. The results showed high temperature with increasing feldspar potassium and is extrusive nonlinear The results (density) an increase with increasing temperature is nonlinear and also results (compressibility) increase with rising temperature Lama (hardness) Increasing the few with a high temperature, unlike (porosity) decrease with increasing temperature.

تضمنت هذه الدراسة امكانية استخدام كاؤلين دويخلة ورمل ارضمة بوصفها مواد محلية في انتاج مخاريط حرارية مع إضافة مواد أخرى مثل كاربونات الصوديوم وكاربونات الكالسيوم,واوكسيد الرصاص الاحمر,وفلسبار بوتاسيوم, والبوراكس فرت بنسب مختلفة كمواد مساعدة على الصهر. تم التحليل الكيميائي لرمل أرضمة و كاؤلين دويخلة لاثبات صلاحيتهما للعمل. تم تشكيل النماذج من خلال قالب جبسي صنعه الباحث وبعد خلط المواد بشكل جاف تمت إضافت الماء اليها لتسهيل كبس النماذج بالكبس اليدوي ثم تم تجفيف النماذج بالفرن بدرجة 120c.برنامج الحرق في الفرن كان بمعدل300c لكل ساعة .تم تحضير سبعة نماذج بتغير نسب كاربونات الصوديوم وفلسبار بوتاسيوم للحصول على فارق في درجات الانحناء.وبينت النتائج ارتفاع درجة الحرارة مع زيادة فلسبار بوتاسيوم وبشكل طردي لاخطي وجاءت نتائج (الكثافة) بارتفاع مع زيادة درجة الحرارة بشكل لاخطي وايضا نتائج (الانضغاطية) زيادة مع ارتفاع درجة الحرارة اما (الصلادة) فزيادة قليلة مع ارتفاع درجة الحرارة بعكس (المسامية) انخفاض مع زيادة درجة الحرارة


Article
EVALUATION OF WATER QUALITY OF DIYALA RIVER FOR IRRIGATION PURPOSES
تقیم نوعیة میاه نهر دیالى لأغ ا رض الري

Author: Nahida H. Hamza ناهده حمید حمز
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2012 Volume: 5 Issue: 2 Pages: 82-98
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The study comprised suitability evaluation water of quality of Diyala riverfor irrigation uses. Four stations were selected along Diyala river which are Jalawlah station(DI2) before Jalawlah Bridge, Saadiyah station (DI3) before inter to Hamren Dam, Muqdadiastation (DI4) after Diyala Dam, and Baqubah station (DI5) at Iron Bridge, besides wand riverstation in Khanaqin (DIW) Before Dam. Water samples were collected and analyzed for pH,electric conductivity (EC), TDS, Na+, K+, Ca2+, Mg2+, HCO3-, CO32-, SO42-, Cl-, and NO3- onesample monthly were taken from these stations during January to December 2010. Inaddition, to classifying water quality and evaluation its suitability for irrigation purposes,Sodium Adsorption Ratio (SAR), Soluble Sodium Percentage (SSP) and Residual SodiumCarbonate (RSC) were calculated following standard equations and found experimentally as(0.985), (20.027), (-4.404) respectively. According to the EC and SAR plotted on the USsalinity diagram, it is illustrated that water samples of DIW and DI5 fall in the class of C3-S1indicating high salinity with low sodium water, which can be used for irrigation on almost alltypes of soil with only a minimum risk of exchangeable sodium, while water samples of otherstations fall in the class of C2-S1 indicating medium salinity with low sodium water, whichcan be suitable to salt tolerant plants with probability developed permeability problem of soilwhen Lime is not existing. RSC values are negative at all sampling sites, indicating that thereis no complete precipitation of calcium and magnesium. All other parameters were withinstandard levels. The results of the study revealed that the quality of Diyala river water can beclassified as suitable for irrigation with few exceptions.

تضمنت الدراسة تقییم صلاحیة میاه نهر دیالى لأغراض الري، حیث تم أختیار اربع محطات على طول نهرمحطة الرصد في المقدادیة ،(DI محطة الرصد في السعدیة ( 3 ،(DI دیالى وهي محطة الرصد لنهر دیالى في جلولاء ( 2تم جمع .(DIW) بالأضافة الى محطة الرصد على نهر الوند في خانقین ،(DI ومحطة الرصد في بعقوبه ( 5 (DI4)pH, EC, TDS, Na+, K+, Ca2+, Mg2+, HCO عینات المیاه وتحلیل العناصر 3-, CO32-, SO4NO 2- و , Cl- 3-شهریآ لهذه المحطات للفترة من كانون الثاني الى تشرین الثاني ٢٠١٠ . ولتصنیف نوعیة المیاه وتقییم صلاحیتها لأغراضوكاربونات الصودیوم المتبقیه (SSP) نسبة الصودیوم القابل للذوبان ،(SAR) الري تم حساب قیم نسبة أمتزاز الصودیوم٢٠,٠٢٧ ) و(- ٤,٤٠٤ ) على التوالي. ووفقآ لقیم التوصیل ) ،( بأتباع المعادلات القیاسیة ووجدت القیم ( ٠,٩٨٥ (RSC)الكهربائي ونسبة امتزاز الصودیوم ومقارنتها بمخطط تصنیف الملوحة الامریكیة ، أوضحت آن عینات المیاه للمحطاتماء عالي الملوحة-قلیل الصودیوم) والذي ممكن أن یكون صالح للري في ) (C3-S هي ضمن الصنف ( 1 DIw,DI5جمیع انواع الاتربة تقریبآ مع خطر قلیل لتكوین تركیزات خطرة من الصودیوم القابل للتبادل، بینما عینات المیاه لبقیةماء متوسط الملوحة-قلیل الصودیوم)، الماء ملائم للنباتات جیدة التحمل ) (C2-S المحطات هي ضمن الصنف ( 1للأملاح مع احتمال تطور مشكلة النفاذیة للترب الناعمة النسجة عند عدم وجود اللایم. قیم كاربونات الصودیوم المتبقیةسالبة لجمیع قیم العینات وهذا یشیر الى عدم اكتمال ترسیب الصودیوم والمغنیسیوم. أما بالنسبة لبقیة العناصر الأخرىفأنها ضمن الحدود المسموح به، أخی آ ر فإن نوعیة میاه نهر دیالى ممكن أن یصنف بانها مناسبة للري عدا بعضالاستثناءات القلیلة.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (4)

Arabic (2)


Year
From To Submit

2014 (2)

2012 (1)

2011 (2)

2002 (1)