Article
Influence of Ceramic Particles Reinforcement on some Mechanical Properties of AA 6061 Aluminium Alloy
تاثیر التقویة بالدقائق السیرامیكیة على بعضالخواصالمیكانیكیة لسبیكة الالمنیوم (AA 6061)

Author: Jameel Habeeb Ghazi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 14 Part (A) Engineering Pages: 2611-2618
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This paper is to investigate the influence of adding 5,10 and 15 weight percentagesilicon carbide particles on some mechanical properties of 6061 Aluminium alloy.The composites Al6061/SiC were prepared by stir casting technique.The results revealed that as the reinforcement content was increased, there weresignificant increases in the ultimate tensile strength, yield strength and hardness ofcomposites accompanied by a reduction in its percentage of elongation.Microstructural studies have been carried out to understand the nature of structure.


Article
Evaluation Microstructure and the Mechanical Properties of Composite Material for Al-Matrix Reinforced by Ceramic Materials (Sic And Al2O3)
تقييم الخواص الميكانيكية لمواد مركبة ذات أساس من الالمنيوم مقواة بمواد سيراميكية (Al2O3 ,SiC)

Author: Lamyaa Kalel لمياء خليل حسن
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2018 Volume: 24 Issue: 8 Pages: 19-28
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this investigation, the mechanical properties and microstructure of Metal Matrix Composites (MMCs) of Al.6061 alloy reinforced by ceramic materials SiC and Al2O3 with different additive percentages 2.5, 5, 7.5, and 10 wt.% for the particle size of 53 µm are studied. Metal matrix composites were prepared by stir casting using vortex technique and then treated thermally by solution heat treatment at 530 0C for 1 hr. and followed by aging at 175 0C with different periods. Mechanical tests were done for the samples before and after heat treatment, such as impact test, hardness test, and tensile test. Also, the microstructure of the metal matrix composites was examined by optical microscopy before and after heat treatment. The results of this work showed that precipitation of Mg2Si as a secondary phase and improvements in mechanical properties with increase in the percentage of SiC and Al2O3. Also, the results of SiC revealed an improvement in mechanical properties more than for Al2O3 such as hardness, impact strength, yield strength, tensile strength, increasing the plasticity constant (k) and decreasing the strain hardening exponent (n).

في هذا البحث تمت دراسة الخواص الميكانيكية والبنية المجهرية لمواد مركبة ذات أساس معدني من سبيكة الألمنيوم نوع 6061­ Α المقواة بمواد سيراميكية (Al2O3 ,SiC) وبنسب أضافات وزنية مختلفة (2.5, 5, 7.5, و 10%) وبحجم حبيبي 53 مايكرون . تم تحضير المادة المركبة بالسباكة بالتحريك بأستخدام التقنية الدوامة, ومن ثم تمت معاملتها حراريا بالمعالجة الحرارية المحلولية عند درجة حرارة (С 0 530) لمدة (.hr 1) والتعتيق عند درجة حرارة (С 0 175) لفترات زمنية مختلفة. أجريت أختبارات ميكانيكية للعينات قبل وبعد أجراء المعاملة الحرارية, مثل اختبار الصدمة, اختبار الصلادة وأختبار الشد. كذلك تم فحص البنية المجهرية للمادة المركبة ذات الارضية المعدنية قبل وبعد المعاملة الحرارية. أظهرت نتائج البحث ترسيب الطور Mg2Si كطور ثانوي و تحسن الخواص الميكانيكية بزيادة نسبة المواد السيراميكية من SiC,Al2O3) ,) . كذلك أظهرت النتائج أن SiC يبدي تحسن في الخواص الميكانيكية أكثر مما هو عليه Al2O3 مثل الصلادة, مقاومة الصدمة, مقاومة الخضوع, مقاومة الشد, ثابت اللدونة k مع نقصان أس الاصلاد الانفعالي (n).


Article
Mechanical Properties of Al 6061/Al2O3 Nanocomposite by Stir Casting

Authors: Hussain J.Alalkawi --- Huda A. Al-Salihi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 3 Part (A) Engineering Pages: 328-332
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Present work deals with the examination of the mechanical properties of Al 6061 composites, which were successfully fabricated by stir casting technique and then reinforced by using different percentages of Al2O3 nanoparticles up to 10 wt%. The required samples were carefully prepared. Evaluation of the mechanical properties such as hardness, yield tensile stress and ultimate tensile stress were effectively obtained at various percentages of Al2O3 nanoparticles .It was found that the mechanical properties of 6061 /Al2O3 nanoparticles are critically influenced by the concentrations of the reinforced Al2O3 nanoparticle, since there was a substantial enhancement in the mechanical properties, as the fractions of Al2O3 nanoparticles increased. This improvement in the mechanical properties was attributed to the uniform distribution of reinforcement nanoparticles as well as the grain refinement of aluminum matrix with minimal porosity.


Article
STUDY THE EFFECT OF SILICA (SIO2) PARTICLES ADDITIONS ON THE WEAR RESISTANCE OF ALUMINUM BIASED ALLOYS (AL-6061, AL-5086)
دراسة تاثير اضافة دقائق السليكا (SiO2) على مقاومة البلى لمواد متراكبة ذات اساس من سبيكة الالمنيوم (Al-6061 وAl-5086).

Author: Yasir Muhi Abdulsahib ياسر محي عبدالصاحب
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2015 Volume: 8 Issue: 3 Pages: 8-19
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Aluminum matrix composite is most important materials used in various industries because of its good properties such as wear resistance, low density, and high resistance to weight ratio. In this paper, Metal matrix composites (MMCs) of the base alloy (Al-6061) and (Al-5086) reinforced by silica particles (SiO2) (1.5, 3, and 4.5 wt%) with particles size (150 µm) was prepared by stir casting using vortex technique, silica particles (SiO2) are added to the molten and then stirred the melt by electrical mixer stir to work the vortex and then pour the mixture molten into cylindrical mold and then was cutting and preparation of samples for examination and testing of wear, hardness, density and study the microstructure of the samples and the comparison between them. Results show from this study that the wear resistance of Al matrix composite its improvement due to addition of silica particles (SiO2) as compared with basis alloys, (Al-5086) matrix composite has higher wear resistance rather than (Al-6061) matrix composite. The higher wear resistance at added the 4.5 wt.% of silica (SiO2). The addition of silica particles in proportions above has contributed to the improvement of hardness which is reflected in improved wear resistance, and that this improvement in properties increases with the proportion of silica particles added to alloys base. As for the properties of density, decreases the density of Al-matrix composites as compared with base alloys with low proportion when added the silica particles (SiO2).

تعد المواد المتراكبة ذات اساس المنيوم من اهم المواد التي تدخل في مختلف الصناعات بسبب ماتملكه من خصائص جيدة مثل مقاومة البلى, الكثافة الواطئة, والمقاومة العالية نسبة الى الوزن. تم في هذا البحث تحضير مواد متراكبة ذات اساس من سبيكة المنيوم (Al-6061) و (Al-5086) مقواة بدقائق السليكا (SiO2) وبنسبة وزنية (1.5%، 3%، 4.5%) وبحجم حبيبي مقداره (150 مايكرون). المواد المتراكبة حضرت بطريقة الدوامة (Vortex method)، حيث تم اضافة دقائق السليكا (SiO2) الى المنصهر ثم الخلط بواسطة خلاط كهربائي لعمل الدوامة ثم صب الخليط المنصهر في قالب معدني اسطواني, بعد ذلك تم تقطيع وتحضير العينات لاجراء فحص واختبار البلى, الصلادة، الكثافة ودراسة التركيب المجهري للنماذج والمقارنة بينهما. تبین من النتائج التي تم الحصول علیها من خلال هذه الدراسة ان مقاومة البلى للمواد المتراكبة قد تحسنت نتیجة إضافة دقائق السليكا (SiO2) مقارنة مع السبیكة الاساس وكانت مقاومة البلى للمواد المتراكبة ذات اساس (Al-5086) اعلى من مقاومة البلى للمواد المتراكبة ذات اساس (Al-6061). وقد تم الحصول على اعلى مقاومة بلى عند نسبة اضافة 4.5% من دقائق السليكا (SiO2). ان اضافة دقائق السليكا بالنسب اعلاه قد ساهم في تحسن قيم الصلادة مما انعكس على تحسن مقاومة البلى، وان هذا التحسن في الخواص یزداد بزیادة نسبة إضافة دقائق السليكا للسبیكة الاساس. اما بالنسبة الى خاصية الكثافة, فقد قلت قيمها للمواد المتراكبة بالنسبة الى السبيكة الاساس وبنسبة قليلة عند اضافة دقائق التقوية السليكا (SiO2).