Article
Effects of Chopped Alumina Fibers on Hardness and Impact Strength of Unsaturated Polyester

Authors: Shaker Jahel Eddres --- Ali Hubi Haleem --- Alaa Rasheed Omran --- Newal Muhammad
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 4 Pages: 1005-1014
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Unsaturated polyester resins are widely used in industry by virtue of combinations of favourable characteristics including good mechanical and physical properties, ease of processing and low cost. However, these resins suffer from the disadvantage of brittleness.In this work, polymeric composites were prepared from unsaturated polyester resin reinforced with different weight fractions of chopped alumina fibers (6%, 12%, and 18%).The following properties were studied: hardness, impact strength, and material toughness.Experimental data showed that incorporation of alumina fiber reinforcements in the extremely brittle unsaturated polyester resin resulted in improvement material properties. Hardness, impact strength, and material toughness increased by 151%, 521% and 474% respectively at weight fraction of chopped alumina fibers (18%). The role of fiber reinforcing on the materials properties was discussed in terms of fibers nature and content.

تستخدم راتنجات البولي أستر غير المشبع بصورة واسعة في الصناعة وذلك لامتلاكها العديد من المزايا المرغوبة والتي تشمل الخواص الميكانيكية والفيزيائية الجيدة وسهولة التشكيل وقلة الكلفة. لكن إحدى مساوئ هذه الراتنجات هي صفة التقصف التي تحدد من استعمالها في العديد من الاستخدامات.تم في هذا البحث تحضير مواد مركبة بوليمرية من راتنج البولي أستر غير المشبع مع تقويته بكسور وزنيه مختلفة من ألياف الألومينا المقطعة (6% ,12%,18%) وتم فحص خواص الصلادة, مقاومة الصدم, متانة المادة.لقد بينت النتائج إن تقوية راتنج البولي أستر غير المشبع القصيف بألياف الألومينا يعمل على تحسين خواص المادة. إذ ارتفعت الصلادة , مقاومة الصدم, متانة المادة بنسبة( 151%, 521%, 474%) على التوالي عند التقوية بألياف الألومينا وبكسر وزني(18%). تم مناقشة تأثير ألياف التقوية على خواص المادة المركبة وحسب طبيعة الألياف ومحتواها.الكلمات الرئيسية: المواد المركبة ذات أساس بوليمري, ألياف الألومينا, الخواص الميكانيكية, راتنج البولي أستر غير المشبع, المواد المركبة الليفية.


Article
Study of Some Mechanical Properties for Aluminum Reinforced by Alumina Fibers

Authors: Shaker Jahel Eddres --- Ali Hubi Haleem --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 3 Pages: 607-615
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this research was to study the ability of improving the impact resistance and Vickers microhardness of composite material based on aluminum metal reinforced by 5, 10, and 15wt.% of chopped alumina fibers. Stirring casting method has been used to make composite material by using vortex technique which is used to pull the chopped alumina fibers to inside the melted aluminum and distributed them homogeneously.Regarding the impact test, results shown that the impact resistance of the composite material are more than that in the aluminum metal and these values are increased with increasing of the amount add fibers and they reached maximum values at (10 wt. %). Then they are decreased at (15 wt. %) but these values remain at higher values than that in the aluminum metal. While the Vickers microhardness reached maximum values at (15 wt. %).

يهدف البحث الحالي إلى دراسة تحسين مقاومة الصدمة و صلادة فيكرز المايكروية لمادة مركبة ذات أساس من معدن الألمنيوم مقوى بألياف الألومينا المقطعة وبنسب وزنية (5%, 10%, 15%). وتم استخدام طريقة السباكة بالمزج في تصنيع المادة المتراكبة باستخدام تقنية الدوامة والتي تعمل على سحب ألياف الألومينا ألمقطعه إلى داخل منصهر معدن الألمنيوم وتوزيعها خلاله بشكل متجانس.أظهرت نتائج اختبار الصدم إن مقاومة الصدمة للمادة المركبة أعلى مما هي عليه لمعدن الألمنيوم وتزداد هذه القيم مع زيادة النسب الوزنية لألياف الألومينا والى حد (10%) ثم تسلك سلوكا مغايرا لكنها تبقى محافظة على قيم أعلى مما هي عليه لمعدن الألمنيوم . في حين تصل صلادة فيكرز المايكروية أعلى قيمها عند التقوية بألياف الألومينا المقطعة وبكسر وزني ((15%.