Article
The Effect of Artificial Aging on Mechanical Properties of Metal Matrix Composite
تأثير التعتيق الصناعي على الخواص الميكانيكية للمواد المركبة ذات الاساس المعدني

Author: Jenan S. Kashan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 2 Pages: 282-288
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Recently the use of the composite material based on aluminum alloys matrix isincreased because of their good mechanical properties and light weight.In this work the addition of % SiC particle to the aluminum (6063) matrix effect wasconsidered and the solution heat treatment was applied on the produced compositematerial which has optimum properties followed by artificial aging.The work shows that the hardness increased and the wear rate decreased with theaddition of silicon carbide particles (SiC) , where as optimum produced compositematerial which has best properties is ( 15% SiC ) . On the other hand the increasingin temperature and time of artificial aging increases the properties.

يزداد استعمال المواد المركبة ذات الاساس من سبائك الالمنيوم كثيرا في الوقت الحاضر نظرا لما تملكههذه المواد من خواص ميكانيكية جيدة مع خفة الوزن.الى Wt%( تم في هذا البحث دراسة تاثير اضافة نسب مختلفة من دقائق كاربيد السليكون و هي ( 5و 10 و 15ارضية من سبيكة 6063 المنيوم ثم اجراء معاملة حرارية محلولية يتبعها تعتيق صناعي بدرجات حرارية وازمان مختلفة للمادة المركبة الناتجة ذات الخواص الامثل.اظهرت الدراسة ان الصلادة تزداد و معدل البلى يقل عند اضافة الدقائق السيراميكية المقوية و ان نسبة الاضافةالبالغة 15 % تعطي احسن الخواص. كما تبين من خلال النتائج ان زيادة درجة حرارة و زمن التعتيق الصناعييزيد من الخواص.


Article
Corrosion Resistance of Aluminum Alloy 7020-T6 in Sea Water

Author: Mustafa Khaleel Ismael
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 8 Pages: 1482-1490
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The present work is aimed to investigate the effect of heat treatment on corrosion resistance of Al-alloy 7020-T6 in sea water, the specimens which manufactured by (1.5*1.5*0.2) cm, according to ASTM (G31-72) [1] The heat treatment was carried out at 480°C and water quench after that artificial aging are implemented at temperature 150°C for (1, 4) hours. Microstructure and phase properties after heat treatment and corrosion test were investigated by optical microscope; X-ray diffraction andcomputer potentiodynamic polarization technique have been used to study corrosion behavior in 3.5% NaCl. The results of corrosion resistance 7020-T6 decrease by solution heat treatment and, increase the holding time from 1- 4 hour would increase the corrosion rate, Intermetallics compounds containing zinc represent as the sacrificial anode and control pitting corrosion in 7020-T6 alloy also, the artificialageing time increase the precipitation of zinc and decrease pitting corrosion at 1 hour.


Article
تأثير المعالجات الحرارية والميكانيكية على الخواص الميكانيكية لسبائك Al-Zn-Mg-Cu

Authors: فؤاد ضحية --- محمود الأسعد --- محمد يحيى النيفاوي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2019 Volume: 27 Issue: 1 Pages: 119-129
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In this research the effect of various heat treatments on tensile properties and hardness of Aluminum-Zinc-Magnesium-Copper alloy (7075 Aluminum alloy) was studied, with and without mechanical treatment by extrusion process. The 7075 alloy samples were submitted to two type of heat treatments, T6 heat treatment by artificial ageing samples in 120 ºC for 24 h and retrogression and re-ageing (RRA). Where in RRA treatment the first ageing done in 120 ºC for 24 h, then the retrogression done in 180 ºCfor 30 min and re-ageing in 120 ºC for 24 h. We got the best results by apply the RRA treatment with extrusion process, where tensile strength was reached to 380 Mpa without extrusion machining process, while reached to 530 Mpa with extrusion process

يدرس هذا البحث تأثير المعالجات الحرارية المختلفة على خواص الشد والقساوة لسبيكة ألمنيوم-زنك-مغنيزيوم-نحاس 7075 مع وبدون المعالجة الميكانيكية بالتشكيل بالبثق، حيث تم تعريض عينات من السبيكة 7075 لمعالجتين حراريتين مختلفتين هما المعالجة الحرارية (T6) المعروفة،وذلك بتعتيق العينات اصطناعياً Artificial Ageing في درجة الحرارة 120 ºC لمدة 24 h، والمعالجة الحرارية الثانية هي الإرجاع وإعادة التعتيق Retrogression and re-ageing (RRA) حيث تم التعتيق الأول في درجة الحرارة 120 ºC لمدة 24 h ثم الإرجاع في درجة الحرارة 180 ºC لمدة 30 min ثم إعادة التعتيق في درجة الحرارة 120 ºCلمدة 24 h.وقد حصلنا على أفضل النتائج بتطبيق المعالجة RRA مع عملية التشكيل بالبثق حيث بلغت مقاومة الشد 380 Mpa بدون عملية التشكيل بالبثق وبلغت530 Mpa مع عملية التشكيل بالبثق.