Ceramic Filled Polymer Matrix Composite Used For Bio-Medical Application

Authors: Waleed Asim Hanna --- Abbas Khammas Hussei --- Hayder Abbas Sallal
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 9 Pages: 1765-1773
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Synthetic polymers such as polyurethane are used widely in the field ofbiomedical applications such as implants or part of implant systems.This work focuses on the preparation of base polymer matrix compositematerials by (Hand Lay-Up) method ,and studying the effect of selected weightfractions (3 , 6 , 9 , 12 ,15) % wt of Calcium oxide (CaO) , Calcium carbonate(CaCO3), Magnesium oxide (MgO) ,and Magnesium carbonate (MgCO3) particleson some properties of the prepared composite.Some mechanical tests were used to evaluate the prepared system (Tensile,Compression, Impact, and Hardness) tests, and a physical test of (Waterabsorption %), and all tests were accomplished at room temperature.maximum results of tensile strength, compression strength, impact energy,hardness, water absorption were ( (31 MPa),( 51 MPa),( o.265 J), (79.8 Shor (D)),(0.229 %)) at using ( (9% wt (MgCO3)) , ( 9% wt of (MgCO3)) , ( 9% wt of(CaCO3)) , ( 15% wt of (MgO)) , ( 15% wt of (MgCO3)) respectively


Article
Preparation and Characterization of Polymer- Ceramic Composite Bio-material
تحضیر ودراسة مادة حیویة متراكبة ذات أساس بولیمري مقواة بدقائق سیرامیكیة

Authors: Rabab Asim Abdul-Aziz --- Waleed Asim Hanna --- Kahtan Khalaf Al-khazraji
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 13 Pages: 2497-2515
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work focuses on studying the addition effect of the prepared HA powder asa filler material before and after the calcination process with different volumefractions (2.5, 5, 7.5, 10, 12.5, 15) vol% to the unsaturated polyester resin matrix.Many mechanical and physical tests were used to determine the properties of theprepared composite material which involved tensile strength, the modulus ofelasticity, the elongation percentage at break, compression strength, compressionmodulus, bending strength, impact strength, fracture toughness, hardness and waterabsorption percentage. For the prepared HA powder, the Ca/P ratio was increasedafter the calcination process from 2.45 to 2.51. X- ray diffraction patterns for theprepared HA powder before and after the calcination process revealed an increasein the HA peak intensity after the calcination process. Secondary phases alsoappeared after the calcination process like (α- Ca3(PO4)2 ) and (β- Ca2P2O7). For theprepared composite material with both groups of HA filler particles, the results hadshown that the mechanical properties which included: tensile strength, modulus ofelasticity, compression strength, compression modulus, bending strength, fracturetoughness and hardness have been increased with increasing volume fraction ofHA filler particles and reached their maximum value at (7.5 vol%). Furthermore,the increasing in volume fraction revealed a decreasing in the evaluated properties.Both the elongation percentage at the break point and the impact strengthdecreased with increasing volume fraction of HA filler particles. The waterabsorption percentage as a physical property for the prepared composite materialshowed an increase with increasing volume fraction of HA filler particles. Theimprovement of unsaturated polyester resin with calcined HA filler particles hadshown greater values for the fore-mentioned properties than the improvement ofunsaturated polyester resin with uncalcined HA filler particles.

يركز هذا البحث على دراسة تأثير اضافة مسحوق الهيدروكسي اباتايت المحضر وبكلا 2.5, 5, 7.5, الحالتين قبل وبعد عملية الكلسنة كحشوات تقوية بكسور حجمية مختلفة ( , 1012.5 ) الى راتنج البولي استر غير المشبع كمادة اساس. تم أجراء العديد من , 15) vol% الاختبارات الميكانيكية والفيزيائية لغرض تحديد خواص المادة المتراكبة المحضرة, حيث تضمنت تلك الاختبارات: مقاومة الشد, معامل المرونة, النسبة المئوية للاستطالة عند الكسر , مقاومة الانضغاط, معامل الانضغاط, مقاومة الانحناء, مقاومة الص دمة , متان ة الكس ر , الص لادة والنسبة المئوية للامتصاصية. بالنسبة لمسحوق الهيدروكسي اباتايت المحضر بعد عملية الكلسنة, بزيادة مقدارها من 2.45 الى 2.51 . في حين اظهرت مخططات حيود Ca/P ازدادت نسبة β- Ca2P2O7 , α- Ca3(PO4) الاشعة السينية بعد عملية الكلسنة ظهور الطورين الثانويين [ 2]كما اظهرت زيادة في قمة الشدة للهيدروكسي اباتايت المكلسن . بالنسبة للمادة المتراكبةالمحضرة وبكلا المجموعتين من حشوات التقوية (مسحوق الهيدروكسي اباتايت الغير مكلسن والمكلسن), وضحت النتائج بأن الخواص الميكانيكية التي تضمنت: مقاومة الشد, معامل المرونة, مقاومة الانضغاط, معامل الانضغاط, مقاومة الانحناء, متانة الكسر و الصلادة قد ازدادت بزيادة 7.5 ) بعدها Vol% ) الكسر الحجمي لحشوات التقوية وبلغت أقصى قيمة لها عند الكسر الحجمي بدأت تلك الخواص بالانخفاض مع زيادة الكسر الحجمي. اما النسبة المئوية للاستطالة عند الكسر ومقاومة الصدمة فقد قلتا مع زيادة الكسر الحجمي لحشوات التقوية. اما الأختبار الفيزيائي في هذا البحث والمتمثل بالنسبة المئوية للامتصاصية للمادة المتراكبة المحضرة فقد اظهر زيادة نسبة الامتصاصية بزيادة الكسر الحجمي لحشوات التقوية. لقد بينت النتائج العملية لهذا البحث ان تدعيم راتنج البولي استر غير المشبع بحشوات تقوية من مسحوق الهيدروكسي اباتايت المكلسن يعطي قيم اعلى للخواص الموضحة اعلاه من تدعيم الراتنج نفسه بحشوات تقوية من مسحوق الهيدروكسي اباتايت غير المكلسن.