Article
DEVELOPMENT OF MICRO-HARDNESS AND WEAR PERFORMANCES OF BIOMEDICAL TITANIUM

Author: Mohsin T. Mohammed
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2018 Volume: 9 Issue: 2 Pages: 131-138
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

In the present work, the influence of thermal oxidation (TO) process on the micro-hardness and wear performances of a pure titanium (Ti) was studied. The process has been carried out at various values of temperature for determined time followed by furnace cooling to room temperature. The TO has supported the development of strong surface film on the Ti without spallation. This surface structure improved the results of micro-hardness and wear compared to untreated samples.


Article
Effect of Heat treatment and Phase Change on BFS of Two Hydroxyapatite Ceramic Powders

Authors: M. Y. Shareef --- M. A. Hassen --- K. A. Maher ماهر خالد
Journal: Iraqi National Journal Of Chemistry المجلة العراقية الوطنية لعلوم الكيمياء ISSN: 22236686 Year: 2011 Issue: 44 Pages: 526-538
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Abstract Thermal stability and sintering behaviour of two hydroxyapatite (HAP) powders where designated. AHAP and BHAP have been investigated at fired sintering temperature range from 1100 to 1450 oC for 3 hrs using XRD and IR spectroscopy. The fired compacts have been characterised by measuring their bulk density, firing shrinkage and biaxial flexural strength (BFS).BHAP has been found to transform to oxyhydroxyapatite (OHAP) at T1200oC, and at T1300oC started to decompose to -tricalcium phosphate (-TCP). AHAP has been found to be marginally less stable than BHAP with OHAP forming at T1150oC and -TCP forming at T1200oC. In both materials, -TCP transformed to -TCP at T 1350oC. Maximum densification (95% of theoretical density) occurred at a lower firing temperature for AHAP (1150oC) than for BHAP (1250oC), with AHAP also showing a slightly higher firing shrinkage (23% compared with 20% for BHAP). The BFS of both materials have been found to increase with increasing sintering temperature up to 1300oC, reaching a maximum value of 90-100 MPa. At T1300oC, this is followed by rapid reduction in BFS due to cracks forming as a result of a volume increase associated with the transformation of -TCP into -TCP.It has been concluded that BHAP is marginally more thermally stable than AHAP, while the latter densifies at a lower firing temperature, this is not a disadvantage and comparable properties can be achieved for both powders, although different firing conditions need to be used.

الخلاصة الثبات الحراري وسلوك التلبيد لمسحوقين من هيدروكسيباتيت (PAH ) وبالتحديد (BHAP) و(AHAP ) بحثت بعد تلبيدهما حراريا في مدى درجات حرارة تتراوح ما بين 1450- 1100مº لمدة ثلاث ساعات وباستخدام تقنياتXRD وIRS . تعاقدات النار شخصت بقياس الكثافة الحجمية و الاتكماش الناري وقوة اللانثناء ثنائي المحور لها . لقد لوحظ تحول (BHAP) الى اوكسي هيدروكسيباتيت (OHAP) عند درجة حرارة T ≥ 1200 مº و عند درجة حرارة T ≥ 1300 مº يبدا بالتفكك ليعطي بيتا ثلاثي كالسيوم فوسفات (PCΤ-β). كما لوحظ ان (AHAP) ذات استقرارية حرارية اقل من (BHAP) الذي بدوره يتحول الى (OHAP) عند درجة حرارة T ≥ 1150 مº ومن ثم الى (PCΤ-β) عند درجة حرارة T ≥ 1200 مº . في كلا اللبيديتين يتحول (PCΤ-β) الى (PCΤ-α) عند درجة حرارة T ≥ 1350 مº . كما لوحظ ان فوة الانثناء ثنائي المحورBFS لكلا اللبيدتين ازدادت مع زيادة درجة التلبيد ليصل الى اعلى قيمة لها عند aP M  90 – 100


Article
Nanostructural study of Ti-Ni binary alloy prepared by mechanical alloying
دراسة البناء النانوي لسبيكة النظام الثنائي Ti – Ni المحضرة بطريقة التسبيك الميكانيكي

Authors: Kawkab D. Salim كوكب داوود --- Amer Sh. Mahmood عامر شاكر --- Rajaa . S .Najm رجاء سهيل --- Ismael K. Jassim إسماعيل خليل جاسم
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2012 Volume: 10 Issue: 18 Pages: 122-126
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In the present study, a powder mixture of elements Ti and Ni was mechanically alloyed in a high energy ball mill. Microstructure of the nanosized amorphous milled product in different stages of milling has been characterized by X- ray diffraction, scanning electron microscopy and differential thermal analysis. We found that time of mechanical alloying is more significant to convert all crystalline structure to the amorphous phase. Nanocrystalline phase was achieved as a result of the mechanical alloying process. The results also indicates that the phase transformation and the grain size occurs in these alloys are controlled by ball milling time.

في الدراسة الحالية، خلطت عناصر من التيتانيوم مع النيكل بأستخدام طريقة التسبيك الميكانيكي من خلال الطحن بكرات ذات طاقة عالية. تم تشخيص البناء النانوي بمديات زمنية مختلفة من الطحن بواسطة تقنيات حيود الاشعة السينية، المجهر الالكتروني الماسح والتحاليل الحرارية التفاضلية. لقد لوحظ بان زمن الطحن يلعب دورا رئيسياً لتحويل البناء البلوري المنتظم الى الحالة العشوائية. كما اكدت النتائج التجريبية بان التحولات الطورية مع الحجم الحبيبي يمكن السيطرة عليها من خلال زمن الطحن بواسطة الكرات .


Article
Effect of Particle Size on the Physical and Mechanical Properties of Nano HA/HDPE Bio-Composite for Synthetic Bone Substitute
تاثیر الحجم الحبیبي على الخواص الفیزیاویة والمیكنیكیة للمادة المتراكبة نانو ھیدروكسي ابتایت/بولي اثلین

Authors: Jenan Sattar Kashan --- Jafar.T.Al-Haidary --- Amin D.Thamir
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 2 Part (A) Engineering Pages: 286-297
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The effect of using nano particle size of Hydroxyabatite to produce HA/HDPE biocompositeby Hot Pressing technique was studied by investigating the effect of particlesize and production technique on the physical and mechanical properties of the biocompositeat different volume fraction of nano HA powder and different compressionpressures.Nano particle size and Hot Compression technique had great impact on the propertiesby reversing the behavior of the bio composite comparing with that using micro scaleparticle size in some of previous studies .The fracture strength and hardness increasedwith increasing the filler content by more than 200% for strength and 300-400% formicro hardness values , the densities increased with increasing filler contentcompressing pressure where as the porosity decreased.The modification in mechanical properties due to filler particle size and productionprocess enhanced the osteo- conductivity of biomaterial to use in different bone substituteapplications.

تم دراسة تأثيراستخدام حجم حبي بيذومدىنانويل مسحوق الهايدروكسي ابتايت لإنتاج مادة مركبة بيولوجية باستخدام تقنية الكبس على الساخن وتأثير ذلك على الخواص الفيزياوية والميكانيكية للمادة المركبة عند نسب حجمية مختلفة من المادة المضافة النانوية وعند ضغوط كبس مختلفة. كان لاستخدام الحجم الحبيبي النانوي وتقنية الكبس على الساخن تأثر كبير جدا على الخواص بحيث عكس سلوك المادة المركبة مقارنة مع نفس المادة عند حجم حبيبي ذو مد مايكرو والتي تم تناولها في الدراسات السابقة.لوحظ زيادة بمقاومة الكسرتصل الى نسبة 200% من مقاومة الكسر لنفس المادة بالمقاس المايكروي وزيادة في قيم الصلادة تصل الى 300-400% من قيم الصلادة لنفس المادة بالمقاس المايكروي. كما ان قيم الكثافة ازدادت مع زيادة محتوى المادة النانوية المضافة ومع زيادة ضغط الكبس كما قل تقيم المسامية. ان الزيادة الكبيرة في الخواص الميكانيكية وتحسن الخواص الفيزياوية للمادة المركبة جعل من الممكن استخدامها في مختلف تطبيقات الاحلال بدل مادة العظم الطبيعي.


Article
Preparation of Titanium dioxide Nano powder and deposits the powder on Titanium slides
تحضير مسحوق اوكسيد التيتانيوم النانومتري وترسيبه على شرائح من التيتانيوم

Author: KhalidahGattaaHasaan خالده كاطع حسن
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2017 Volume: 9 Issue: 2 Pages: 21-26
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

The research aims to prepare titanium dioxide (TiO2) nanoparticle powder in a chemically based method depending on the principle of top-to-bottom construction, and to use the prepared powder to coat titanium strips and study their properties for medical applications. The powder was prepared by the reaction of titanium trichloride with ammonium hydroxide and by appropriate standard conditions of temperature and pressure, and then put the reaction product from the previous process in an ultrasonic device where the solution turns into a colloidal white-colored state. Synthetic tests were performed using X-ray diffraction technique, results showed the presence of titanium dioxide granules with residues of ammonium compounds, we also examined the granular size of this foam liquid and the particle sizes were in micrometers. The prepared compound is placed in a centrifuge machine where we obtain a white powder and then dry it in a 100 ° C. The atomic force microscopy tests showed that the granular volume of the prepared TiO2 was about 80-60 nanometers. A titanium strip was coated with a thin layer of the prepared nonmetric powder. The corrosion tests were performed for the slide. The curves of the open circuit and the tafel show an improvement in the metal behavior after coating with the powder, which increases its resistance to corrosion

يهدف البحث الى تحضير مسحوق جسيمات ثاني اوكسيد التيتانيوم النانويه مختبريا بطريقة كيمياوية اعتمادا على مبدأ البناء من القمة الى القاعدة ، واستخدام المسحوق المحضر لطلاء شرائح من التيتانيوم ودراسة خواصها للتطبيقات الطبيه.تم تحضير المسحوق عن طريق تفاعل ثلاثي كلوريد التيتانيوم مع هيدروكسيد الامونيوم وبظروف قياسية مناسبة من درجة الحرارة والضغط ، ومن ثم وضع ناتج التفاعل من العملية السابقة في جهاز يعمل بالموجات فوق الصوتية حيث تحول المحلول الى حالة غرويه لونه ابيض . تم إجراء الفحوصات التركيبية باستخدام تقنية حيود الاشعه السينيه وأظهرت النتائج عن وجود حبيبات ثاني اوكسيد التيتانيوم مع مخلفات من مركبات الامونيوم وكما أجرينا فحص للحجم الحبيبي لهذا السائل الرغوي وكان أحجام الحبيبات بالميكرومتر .يوضع المركب المحضر من الخطوه السابقه في جهاز للطرد المركزي حيث نحصل على مسحوق ابيض رطب ومن ثم يجفف في فرن بدرجة حراره 100 درجه مئويه, اظهرت فحوصات مجهر القوه الذريه ان الحجم الحبيبي لمادة TiO2 المحضرة كانت بحدود (80–60 ) نانوميتر. طليت شريحة من التيتانيوم بطبقة رقيقة من المسحوق النانومتري المحضر وأجريت فحوصات التآكل للشريحة وتبين من خلال منحنيات الدائرة المفتوحة والتافل وجود تحسن في سلوك المعدن بعد طلاءه بالمسحوق أي زيادة في مقاومته للتآكل.


Article
A Novel Use of Biomaterial Implants For Reconstruction of Orbital Floor Fracture

Authors: Kamal Turki Aftan --- Elham Hazeim Abdulkareem
Journal: Journal of Oral and Dental Research مجلة طب الفم والاسنان ISSN: 23106417 Year: 2017 Volume: 4 Issue: 1 Pages: 25-34
Publisher: Iraqi Association for Oral Research الجمعية العراقية لبحوث طب الفم


Article
STUDY TO DETERMINE THE LONGEST VALIDITY PERIOD FOR ORTHODONTIC WIRES IN A DIFFERENT ENVIRONMENTS
دراسة تحديد أطول فترة صلاحية لأسلاك تقويم الأسنان في أجواء مختلفة

Author: Mohammed Abdulateef Ahmed محمد عبد اللطيف أحمد
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2014 Volume: 7 Issue: 1 Pages: 25-38
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The research summary to knowing longest period of validity for orthodontic wires in four corrosive media ,the first medium approximately similar to human mouth such as corrosive medium (Artificial Saliva), human body temperature, hydrogen power (pH), and aeration ,and compared with orthodontic wires these serve in same corrosive medium but at room temperature and the identical aeration as a second corrosive medium, and compared to orthodontic wires present or attending in sodium chloride solution instead of artificial saliva at room temperature and the like aeration as a third corrosive medium. The final comparison test with orthodontic wires present in sodium chloride solution at human body temperature and the like aeration too. The study done by using device or system was native designed and manufactured according to modified American standard specification (ASTM G31), the orthodontic wires were from type austenitic stainless steel (301). After four mentioned corrosion experiments for serial six months period ,and usage Corrosion Penetration Rate law (CPR) and by traditional mathematical methods addition to the microstructures of samples before and after corrosion experiments ,conclude that ;the longest validity period for orthodontic wires at environment approximately similar to human mouth ,then wires worked in artificial saliva at room temperature, followed by the wires served in sodium chloride solution at room temperature, finally; orthodontic wires were worked in sodium chloride solution at human body temperature had shortest validity period.

يتلخص البحث بتحديد أطول فترة صلاحية لأسلاك تقويم الأسنان في أربع أجواء أكالة ، الأول جو مماثل لفم الأنسان تقريبا" من حيث الوسط الأكال (اللعاب الصناعي) (Artificial Saliva) و درجة الحرارة والحامضية والتهوية، ومقارنتها بالأسلاك العاملة في نفس الوسط الأكال والتهوية ولكن بدرجة حرارة الغرفة كجو أكال ثاني، ثم الأسلاك المتواجدة في محلول كلوريد الصوديوم (3.5%wt NaCl) بدلا" عن اللعاب الصناعي وبدرجة حرارة الغرفة وبنفس التهوية كجو أكال ثالث وأخيرا" المقارنة مع الأسلاك المتواجدة في محلول كلوريد االصوديوم وبدرجة حرارة جسم الأنسان ومعرضة لنفس التهوية أيضا". وتمت الدراسة بأستخدام منظومة مصممة و مصنعة محليا" حسب المواصفة القياسية الأميركية المعدلة (ASTM G31)، وأسلاك تقويم الأسنان المستخدمة من نوع الفولاذ المقاوم للصدأ الأوستنايتي (301)، وبعد إجراء أختبارات التآكل الأربعة أعلاه و لفترة زمنية مقدارها ستة أشهر متتالية وبأستخدام قانون معدل تغلغل أومعدل نفاذ تنقر التآكل (Corrosion Penetration Rate ) وبالطرق الرياضية التقليدية ومن الصور المجهرية للعينات قبل وبعد حالات التآكل نستنتج بأن الأسلاك تكون بفترة صلاحية أطول عند جو مماثل لفم الأنسان وتليها الأسلاك العاملة في اللعاب الصناعي وعند درجة حرارة الغرفة ثم تليها الأسلاك العاملة في كلوريد الصوديوم عند درجة حرارة الغرفة و أقصر فترة صلاحية تكون للأسلاك العاملة في محلول كلوريد الصوديوم عند درجة حرارة جسم الأنسان.


Article
The Effect of Different Thermal Treatments on Corrosion Behavior of the Hydroxyapatite Coated on Ti-6Al-4V Alloy by Electrophoretic Deposition and Dip Coating
تأثير المعاملات الحرارية المختلفة على السلوك التاكلي للهايدروكسي أبتايت المطلي على سبيكة Ti-6Al-4V بطريقة الترسيب بهجرة الدقائق المشحونة وطريقة التغطيس

Loading...
Loading...
Abstract

In this research, the study of thermal treating by laser, plasma glow discharge and tubular furnace on Ti-6Al-4V alloy coated with hydroxyapatite by methods of dip coating and electrophoretic deposition .A group of samples was coated by dip coating and another group was coated by electrophoretic deposition. The first group was treated by pulse laser 10 (mJ) as energy for samples from both coating with uniform distributed pulses on every single sample surface, The second thermal treating was made by plasma glow discharge in a locally made system with argon atmosphere, 600 Volt , and 6 cm distance between the electrodes, The third treating was made by tubular furnace in air atmosphere and 400 °C for 1 hour duration. Then the samples were tested by optical microscope, XRD, SEM, and the corrosion characteristic with open circuit potential (OCP) and polarization curve (Tafel), The results showed that the samples tr eated by tubular furnace were the best where the corrosion rate was reduced to 3.567×10-4 mm/y for the dip coated samples and 7.221×10-4 mm/y for the electrophoretic deposited samples compared with 9.396×10-3mm/y for uncoated sample.

تم في هذا البحث دراسة المعاملات الحرارية باستعمال الليزر، بلازما التفريغ التوهجي و الفرن الحراري الانبوبي على سبيكة Ti-6Al-4V المطلية بالهايدروكسي أبتايت بطريقتي التغطيس والترسيب بهجرة الدقائق المشحونة . اذ تم طلاء مجموعة من العينات باستعمال طريقة التغطيس وطلاء مجموعة أخرى من العينات باستعمال طريقة الترسيب بهجرة الدقائق المشحونة، ومن ثم تمت المعاملة الحرارية الاولى باستخدام الليزر النبضي بطاقة 10 ملي جول لعينات مطلية بالطريقتين وتم توزيع النبضات على سطح العينة الواحدة ، ثم تمت المعاملة الحرارية الثانية باستخدام بلازما التفريغ التوهجي داخل منظومة مصنعة محلياً بجو من غاز الاركون بفولتية مقدارها 600 فولت وبمسافة بين القطبين مقدارها 6 سم ، وتمت المعاملة الثالثة باستعمال الفرن الحراري الأنبوبي بجو من الهواء وبدرجة حرارة 400 °م لمدة ساعة،بعدها تم فحص العينات باستعمال المجهر الضوئي البصري ،XRD،SEM ، وفحص الخصائص التاكلية باستعمال فحص جهد الدائرة المفتوحة (OCP) ومنحنى جهد الاستقطاب (Tafel) ، أظهرت النتائج أن العينات المعاملة بالفرن الحراري الأنبوبي هي الأفضل، إذ تناقص معدل التاكل الى 3.567×10-4 mm/y بالنسبة للعينات المطلية بالتغطيس و 7.221×10-4 mm/y بالنسبة للعينات المطلية بهجرة الدقائق المشحونة مقارنة بمعدل تاكل 9.396×10-3 mm/y للعينة غير المطلية .

Listing 1 - 8 of 8
Sort by
Narrow your search

Resource type

article (8)


Language

English (5)

Arabic and English (2)

Arabic (1)


Year
From To Submit

2018 (1)

2017 (3)

2014 (2)

2012 (1)

2011 (1)