Inhibiting of C --steelL80 Corrosion by Using of Polyacrylamide and Thiophene -2- Carboxaldehyde
تثبيط تآكل C - SteelL80 باستخدام البولي اكريل امايد مع الثايوفين -2- كاربوكسي الديهايد -

Loading...
Loading...
Abstract

In this research Five steady weights (0.5) g. of polyacrylamide were mixed with five different volumes of thiophene-2-carboxildehyde (0.5, 1, 1.5, 2 and 2.5) ml to obtain five concentrations of inhibitor in (50)ml of 15% HCl. (C-Steel L80) bars were immersed in the prepared solution and the lost weights were calculated in different temperatures (40,60, 80 and 90) ℃ at different times (3, 4, 5 and 6)hrs. the covered surface area (θ)and the efficiency were calculated from the lose weights; then the thermodynamic constants were calculated. It was observed that the less corrosion was obtained by increasing the inhibitor concentration.

في هذا البحث استخدمت خمسة اوزان ثابتة (0.5)غم من البولي اكريل امايد ومزجها مع خمسة احجام مختلفة من ثايوفين-2-كاربوكسيل ديهايد (0.5,1,1.5, 2, 2.5)مل للحصول على خمسة تراكيز من المثبط في 50 مل من15% HCl وبعدها تم غمر سبائك (C-SteelL80)بالمحلول المحضر وتم حساب الاوزان المفقودة لدرجات حرارية مختلفة (40, “60, “80, “90)مل وازمنة مختلفة (3, 4,5, 6) ساعة ، ومن الاوزان المفقودة تم حساب الكفاءة ومساحة السطح المغطى (θ) وبعدها حسبت الثوابت الثرموديناميكية ولوحظ ان بزيادة تركيز المثبط يقل التآكل.


Article
Use of poly acryl amide Corrosion inhibitors for the C-Steel L80 in acid medium
في وسط حامضي (C-Steel L80استخدام البولي اكريل امايد كمثبط تآكل لل (

Author: Muthar Jawad K.1 Abdullah Saleem K.2 Ghassan B. Yaqoob مظر جواد كاظم
Journal: kirkuk university journal for scientific studies مجلة جامعة كركوك - الدراسات العلمية ISSN: 19920849 / 26166801 Year: 2016 Volume: 11 Issue: 4 Pages: 198-214
Publisher: Kirkuk University جامعة كركوك

Loading...
Loading...
Abstract

This study included the use of poly acryl amide as corrosion inhibitor of the C-Steel in50ml of 15% HCl were used five different weights (0.5, 1, 1.5, 2, 2.5) gm of polymer toobtain different concentrations of the inhibitor and from weight lost in differenttemperature and times were obtained the inhibitor efficiency and covered surface area withpolymer and then calculated the thermodynamic constants. It was noted that in increase oftime and temperatures increases corrosion. The highest efficiency of the inhibitor has beenrecorded at the time of 3 hours and a temperature of 40 ℃.

تم استخدام البولي اكريل امايد كمثبط لتآكل ال C-Steel L80 في 50ml من 15% HCl حيث استخدمت خمسة أوزان مختلفة من مثبط التاكل (0.5, 1, 1.5, 2, 2.5)gm وتم اذابته في 50ml من HCl للحصول على خمسة تراكيز مختلفة من المثبط (1, 2, 3, 4, 5)% بعدها تم غمر السبائك بالمحلول المحضر وتم حساب الأوزان المفقودة لدرجات حرارية مختلفة)℃ (40, 60, 80, 90 وأزمنة مختلفة (3, 4, 5, 6) ساعة ومن الأوزان المفقودة تم حساب الكفاءة ومساحة السطح المغطى (Ɵ) وبعدها حسبت الثوابت الثرموديناميكية ولوحض ان بزيادة الزمن ودرجات الحرارة يزداد تاكل ال C-Steel L80 وان اعلى نسبة كفاءة للمثبط تكون عند زمن 3 ساعة ودرجة حرارة 40 ℃.