Article
Effect of Water Absorption on Some Electrical and Dielectrical Properties of Epoxy Resin Reinforced with Chopped Carbon Fibers

Authors: E.A.Al-Ajaj --- S.I.Husaen --- H.I.Jafar
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2011 Volume: 14 Issue: 4 Pages: 87-94
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this research, we study a.c electrical conductivity (σa.c ( ) and dielectric properties (dielectric constant (έ), and dissipation factor ( tanδ) ), with frequency change (102 -107 Hz) for the epoxy resin and composites reinforced with chopped carbon fiber ,prepared by hand lay –up method (EP +5% CF), (EP +10% CF), (EP +15% CF), (EP +20% CF), Were measured electrical conductivity of epoxy and composites with frequency change and at room temperature the results showed a.c electrical conductivity dependence with frequency relationship σ (ω)=Aωs to the values of the exponential factor (s)of less than one all samples, and adopted the theory of filtration for the interpretation of data conductivity for composites reinforced with carbon fibers was selected epoxy+20% C.F showed a higher electrical conductivity (13.6 * 10-7 (ohm.cm)-1). The composites were immersed in water at room temperature for 6, 10,15,20,27 days.The results showed that the electrical conductivity of (σ (ω)) increasing with increasing weight gain(M%) due to water absorption. Itwas found that dielectric constant increases when the percentage moisture absorption increase, whereas dielectric constant (έ) is dependent on capacity of composite materials.

تـم في هـذا البحث دراسـة التوصيليـة الكهربائيـة المتناوبـة ()(σa.c وخـواص العـزل الكهربائـي (έ,tan (مـع تغيـر التردد (102 -107 Hz) لراتنـج الايبوكسي ومتراكباته المدعمة بالياف الكاربون المقطعة والمحضرة بطريقة التشكيل اليدوية(EP+5%C.F)، (EP+10%C.F)، (EP+15%C.F)، (EP+20%C.F) تم قياس التوصيلية المتناوبة للايبوكسي ومتراكباته في مدى التردد وفي درجة حرارة المختبر اظهرت النتائج اعتماد التوصيلية على التردد وفق العلاقة σ(ω)=Aωs بقيم للعامل الاسي اقل من الواحدلكل العينات, واعتمدت نظرية الترشيح لتفسير بيانات التوصيلية لمتراكبات الايبوكسي المدعم بالالياف الكاربون. كما تم دراسة تأثير التردد في قيمة ثابت العزل الكهربائي وفقد العزل فقد وجد بان السماحية ( ( έتقل في حالة التقوية بالياف الكاربون المقطعة، تم اختيار المتراكب ايبوكسي -20% الياف الكاربون المقطعة الافضل من بين المتراكبات باعتبـاره اظهـر اعلـى توصيليـة كهربائيـة( (ohm.cm )-1 13.6*10-7 ). تم تغطيس المتراكبات في الماء بدرجة حرارة الغرفة لمدة 20,1510,6, 7, 2 يوم، اظهـرت النتائـج العمليـة ان التوصيليـة الكهربائيـة((ω)σ) تزداد بزيادة التردد وزيادة النسبة المئوية لامتصاصية الماء بينما ثابت العزل (έ) يزداد عند زيادة النسبة المئوية لامتصاصية الماء اعتمادا على السعة الكهربائية للمواد المتراكبة.


Article
Effect of Filler Type on some Physical and Mechanical Proparties of Carbon Fibers / Polyester Composites
تأثیر نوع الاضافه على بعض الخواص الفیزیائیه والمیكانیكیه من الیاف كاربون ومتراكبات البولي استر

Authors: Osama Sultan Muhammed --- Abbas Khammas Hussein --- Ruaa Haitham Abdel-Rahim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 15 Part (A) Engineering Pages: 2905-2924
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study, traditional and hybrid composites were prepared by Hand lay-upmolding and investigated. The composites constituents were unsaturated polyester resinas the matrix, 3% and 6% volume fractions of carbon fibers as reinforcement and 3% ofAl2O3, Al, Cement and local Gypsum (calcium sulfate anhydrate CaSO4) as fillerparticles. The investigated physical properties were density, porosity while themechanical properties were tensile properties, bending modulus of elasticity. Theexperimental results showed that increased volume fraction of carbon fibers to (6%) ledto increase in physical properties (density, porosity. As for the mechanical properties,carbon fiber composites and (3% carbon fibers/Al2O3)-contained hybrid composites gavethe higher tensile and fracture strength, carbon fiber then gypsum composites gave thehigher bending modulus.


Article
Effect ofweight percentage chopped carbon fibers on the mechanism of cracks propagation for Epoxy composites
تأثير النسب الوزنية لالياف الكاربون المقطعة على ميكانيكية انتشار الشقوق لمتراكبات الايبوكسي

Authors: S.I.Husaen سيناء أبراهيم حسين --- H.I.Jaffer حارث ابراهيم جعفر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2010 Volume: 8 Issue: 11 Pages: 24-28
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, the mechanism of cracks propagation for epoxy/ chopped carbon fibers composites have been investigated .Carbon fibers (5%, 10%, 15%, and 20%) by weight were used to reinforce epoxy resin. Bending test was carried out to evaluate the flexural strength in order to explain the mechanism of cracks propagation. It was found that, the flexural strength will increase with increasing the percentage weight for carbon fibers. At low stresses, the cracks will state at the lower surface for the specimen. Increasing the stresses will accelerate the speed of cracks until fracture accorded .The path of cracks is changed according to the distributions of carbon fibers

درس في هذا البحث ميكانيكية انتشار الشقوق لمتراكبات الايبوكسي بعد اضافة نسب وزنية من الياف الكاربون المقطعة (5%و10%و15%و20%) لراتنج الايبوكسي وفحصت العينات بفحص الانثناء ثلاثي النقاط وحسب من خلاله متانة الانثناء وميكانيكية انتشار الشقوق لقد وجد ان متانة الانثناء تزداد بزيادة النسب الوزنية للالياف وبتقليل الاجهاد الشقوق تستقر في السطح السفلي للعينة وبزيادة الاجهاد تتعجل سرعة الشقوق وتصل الى الكسر ان مسار الشقوق يتغير تبعا لتوزيع الالياف في المادة المتراكبة .


Article
Mechanical Properties of High Performance Carbon Fiber Concrete
الخواص الميكانيكية لخرسانة ألياف الكاربون العالية الأداء

Authors: Wasan I. Khalil --- Akar Abdulrazaq
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 5 Pages: 906-924
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research mechanical properties of high performance carbon fiber concreteare studied. The experimental work includes, producing high performance concreteusing superplasticizer and condensed silica fume reinforced with different volumefractions (0%, 0.2%, 0.3%, 0.4% and 0.5%) of carbon fibers. The effect of choppedcarbon fibers on the mechanical properties (compressive strength, splitting tensile andflexural strengths, and modulus of elasticity) of high performance concrete was alsostudied. Generally, the results show that the addition of carbon fibers improves themechanical properties of high performance concrete. Also the results show that Usingcondensed silica fume as addition by weight of cement increases the compressivestrength more than that as replacement by weight of cement. The percentages increasein compressive strength of concrete containing 15% silica fume as replacement and asaddition by weight of cement are about 14% and 26% respectively. The addition ofcarbon fibers causes a slight increase in compressive strength and modulus ofelasticity of high performance concrete when the fiber volume fraction increases,while the splitting tensile and flexural strengths shows a significant increase relativeto the reference high performance concrete (without fiber). The percentage increase insplitting tensile and flexural strengths for high performance concrete with fibervolume fraction 0.5% at 28 days is about 45% and 46% respectively.


Article
Numerical and Experimental Analysis of the Bending Deflection of the Composite Beam
التحليل العملي والعددي لتشوه انحناء عمود مركب

Author: Mena Faisal Khdeer
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 3 Part (A) Engineering Pages: 563-572
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work studies the numerical and experimental bending deflection of 3-point test of the composite beam made of epoxy reinforced by glass fibers and carbon fibers at different volume fractions .The results show that the deflection decrease in nonlinear relationship with increase volume fraction for both glass fibers and carbon fibers .The maximum difference between the experimental results and the finite element results difference was (11 %) at load (=20 N) and fibers volume fraction (Vf= 10 %) for glass fibers reinforcement. Also the results indicated that the maximum deflection was (1.65mm) when reinforced by glass fibers at (Vf =10 %) and at load (= 20 N) experimentally, while the maximum value of deflection was (0.55mm) when reinforced at the same load and fibers volume fraction.

تم في هذا البحث دراسة تشوه الانحناء العملي والتحليلي لفحص ثلاثي النقطة لعمود مركب مصنوع من راتنج الايبوكسي والمقوى بالياف الزجاج والياف الكاربون بكسور حجمية مختلفة.بينت النتائج بان التشوه يقل بعلاقات لاخطية مع زيادة الكسر الحجمي لالياف الزجاج والكربون.اقصى فرق بين النتائج العملية والتحليلية كان (11 %) عند حمل (20 N) وكسر حجمي للالياف (10 %) عند التقوية بالياف الزجاج.وكذلك بينت النتائج بان اقصى تشوه كان (1.65 mm) عند التقوية بالياف الزجاج عند كسر حجمي (Vf= 10 %) وحمل (20 N) عمليا. بينما اقصى قيمة للتشوه كانت (0.55 mm) عند التقوية بالياف الكاربون وعند نفس الحمل والكسر الحجمي للالياف.


Article
Coating of Carbon Fibers With Calcium Phosphate by Sol- Gel Method
تغطية الياف الكاربون بفوسفات الكالسيوم بطريقة المحلول الجيلاتيني

Authors: Sewench N. Rafeeq --- Wafaa A. Husaien --- Russel Rushdi Ghanim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 5 Part (A) Engineering Pages: 1117-1128
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Sol-gel technique has been used to coat carbon fibers with calcium phosphate to improve the esthetic of black carbon fibers as it's biocompatible. To improve bonding between carbon fibers and prepared calcium phosphate powders, the surface of carbon fibers has been treated with para-aminobenzoic acid. The structural tests include: (SEM, XRD, AFM and FTIR). The morphology of the coating layers has been examined by scanning electron microscope (SEM). The crystallized phase composition of coatings has been identified by x-ray diffractometry (XRD). The grain size of dried and heat treated calcium phosphate coat has been estimated by atomic force microscope (AFM) and fourier transform ــ infrared spectroscopy (FTIR) analysis which support and verify the x-ray diffraction findings.

أستخدمت تقنية المحلول الجيلاتيني لتغطية الياف الكاربون بفوسفات الكالسيوم, لتحسين جمالية الياف الكاربون الاسود ولكونها مادة متوافقة حيويا. لتحسين الترابط بين الياف الكاربون و مسحوق فوسفات الكالسيوم المحضر, تم معالجة سطح الياف الكاربون بحامض البارا أمينوبينزويك (para-aminobenzoic acid). تتضمن الاختبارات التركيبية (المجهر الماسح الالكتروني (SEM) و حيود الاشعة السينية (XRD) و مجهر القوة الذرية (AFM) ومطيافية الاشعة تحت الحمراء (FTIR)). مورفولوجية طبقات التغطية فحصت بأستخدام (SEM). تركيب الطور المتبلور للتغطية تم تمييزه بأستخدام (XRD). الحجم الحبيبي لطبقة فوسفات الكالسيوم المجففة والمعاملة حراريا تم تقديره بأستخدام (AFM). ونتائج ال (XRD) دعمت بالتحاليل الطيفية للاشعة تحت الحمراء (FTIR).


Article
Mechanism of Hybrid Reinforcement and its Effect on some Properties of Binary Polymer Blend
ألية التسليح الهجين وتأثيرها على بعض الخواص لخليط بوليمري ثنائي

Authors: Awham M. Hameed --- Entihaa G. Daway
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 2 Part (B) Scientific Pages: 287-301
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of current study is carrying out some modifying in properties of resin material (Unsaturated polyester, UPE) by adding thermoplastic material (polystyrene, PS) with different weight ratios included (0%, 5%, 10%, 15% and 20%) of (PS) to prepare binary polymer blend. The optimum ratio was selected in terms of the homogeneity case between the two polymers and studying the nature of the surfaces of the prepared materials using the optical microscope. Some mechanical tests were performed to determine the values of impact strength (I.S), ultimate tensile strength (UTS) for all prepared specimens. The ratio (80/20, weight/weight)% of (UPE/PS) blend was selected and reinforced with fibers volume fraction Фf = 10% using three types of fibers included(glass fibers (G.F), Carbon fibers (C.F) and hybrid from the two types (5% G.F and 5% C.F). All the above tests were repeated after the reinforcement for comparing the results and studying the behavior of materials under work. The results exhibited that the values of (I.S) increase with increasing of the blending ratio of (PS) while the values of (UTS) decrease at blending ratios (10, 15) % of (PS) and return to increase at the ratio 20% . After the reinforcement, it was found that the composite reinforced with carbon fibers records the highest values of impact strength for un notch specimens while the hybrid composite has the highest value of the ultimate tensile strength comparing with E-glass and carbon fibers composites.

الهدف من الدراسة الحالية هو اجراء بعض التحوير في خواص مادة راتنجية ( البولي استر غير المشبع , UPE) بأضافة مادة ثرموبلاستيكية (البولي ستايرين ,PS) وبنسب وزنية مختلفة شملت0,5 10, 15, 20) )% من البولي ستايرين لتحضيرخليط بوليمري ثنائي.وقد تم اختيارالنسبة المثلى بدلالة حالة التجانس بين البوليمرين ودراسة طبيعة السطوح للموادالمحضرة بأ ستخدام المجهر الضوئي. أجريت بعض الاختبارات الميكانيكية لتحديد قيم مقاومة الصدمة (I.S) , مقاومة الشد القصوى (UTS) لجميع النماذج المحضرة. تم اختيارالنسبة الوزنية (80/20)% من خليط البولي استر غير المشبع/ البولي ستايرين وسلحت بالالياف وبكسرحجمي (Фf = 10%) باستخدام ثلاثة انواع من الالياف شملت (الياف الزجاج (G.F), الياف الكاربون ((C.F وهجين من نوعي الالياف (5% G.F) و(5% C.F). تم تكرار جميع الاختبارات اعلاه بعد التسليح لغرض مقارنة النتائج ودراسة سلوك المواد قيد البحث. أظهرت النتائج بأن قيم (I.S) تزداد مع زيادة نسبة الخلط للبولي ستايرين في حين قيم (UTS) تنخفض عند نسبتي الخلط (10, 15)% من البولي ستايرين وتعود لتزداد عند النسبة 20%. وبعد التسليح اظهرت النتائج بأن المتراكب المسلح بألياف الكاربون يسجل القيم الاعلى لمقاومة الصدمة لنماذج غير محزوزة في حين المتراكب الهجين يمتلك القيمة الاعلى لمقاومة الشد القصوى مقارنة مع متراكبات الياف الزجاج والكاربون.


Article
Proportioning of Foamed Concrete Reinforced with Carbon Fibers

Authors: Eethar Tihanon Dawood --- Waleed Abdulrazzaq Abbas --- Yahya Ziad Mohammad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 15 Part (A) Engineering Pages: 2864-2876
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This paper shows the production of foamed concrete reinforced with carbon fibers. Firstly, different mortar mixes were prepared by varying ratio of sand/cement. Continuously, the selected mortar mix was used for the foamed concrete produced due to the results of density, compressive strength, splitting tensile strength and flexural strength test. Secondly, different foam agent amounts (0.8, 1, 1.2 and 1.4 kg/m3) with 10% of silica fume were included in the selected mortar mix to produce the optimum foamed concrete mix depending on the same set of tests mentioned above. Lastly, various volumetric fractions of carbon fibers (0.5, 1 and 1.5%) were incorporated with the optimum foamed concrete mix and the same set of tests was done to examine such foamed concrete reinforced with carbon fibers. The results give acceptable ranges of strength for mortar mix using 1.9 sand/cement ratios. Besides, the foamed concrete produced by the inclusions of foaming agent 1 kg/m3 shows acceptable ranges of density and strength to be suitable for the reinforcing by carbon fibers. The carbon fiber included in the foamed concrete exhibit significant increases for the strengths. Such increases are varied from about 35% using 1% carbon fibers to 44% and 116% using 1.5% carbon fibers for compressive, splitting tensile and flexural strength, respectively


Article
Density and Ultrasonic Pulse Velocity Investigation of Self-Compacting Carbon Fiber- Reinforced Concrete

Author: G.A. Salman
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 1 Part (A) Engineering Pages: 89-99
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

comprehensive research has been carried out to understand the effect of adding carbon fibers to density and ultrasonic pulse velocity of self-compacting concrete. Fifteen SCC mixes were prepared with two types of mineral admixtures and carbon fibers. Metakaoline and silica fume were used as mineral admixtures while carbon fibers were used as fiber inclusions. Two different fiber length (6mm and12mm) and fiber fraction (0.1 % and 0.5 %) was used. Different parameters such as slump flow diameter, T500 time, V-funnel time, blocking ratio and filling height difference were used to evaluate fresh state properties. Air-dry density and Ultrasonic Pulse Velocity values are determined for mixes at age of 7, 28, 90 and 180 days. The experimental results indicate that concrete mixes contained carbon fiber showed higher air dry density than concrete mixes without fiber, the percentage increase were between 0.85% to 3.31% at age (7,28,90 and 180) days respectively. Concrete mixes contained carbon fiber compared with the reference mixes without carbon fiber exhibits an increase in the ultrasonic pulse velocity values of about 0.74% to 5% at age (7,28,90 and 180) days respectively .


Article
Some Properties of High Performance Carbon Fibres Cement Composites
بعض خواص الخرسانة عالية الأداء المسلحة بألياف الكاربون

Author: Nada Al – Jalawi
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2009 Volume: 15 Issue: 4 Pages: 4409 -4416
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The paper presents properties of high performance concrete reinforced with relatively high percentage of choped carbon fibers vol. fraction ranging from (1 to 5) %. The great advantage of such composites is their relatively high flexural strength. A low water to cement ratio of 0.3 with super plasticizer was used in order to keep the cement mix easily workable. To improve the properties, a locally existing pozzolan based on reactive meta- kaolin was used in the mixture together with silica sand. A high modulus carbon fibers (450 KN/mm2) were also used. In addition to the flexural strength, dynamic modulus of elastisity were found using dynamic methods. The results showed that the specimen failed in flexureal by a single crack although the ultimate tensile strength and the stiffness of the composite were increased as the fibers content was increased.

يقدم البحث خواص الخرسانة العالية الأداء المسلحة بألياف الكاربون بنسب حجمية عالية نسبياً تتراوح من (1 – 5) % . إن الفائدة الكبيرة لهذا النوع من الخرسانة هي مقاومتها العالية للشد في الانحناء.تم استخدام نسبة واطئة من الماء/السمنت تساوي (0.3) مع استخدام ملدن متفوق للحصول على قابلية تشغيل مقبولة كما تم استخدام بوزلان محلي متكون من دقيق الكاؤولين النشط واستخدام رمل ذو أساس سيليكي وكانت ألياف الكاربون من نوع ذات معامل المرونة العالية (450 كيلونت/ملم2), بلإضافة إلى الخواص الانحنائية فقد تم بحث الخواص الديناميكية باستخدام طرق ديناميكية, وبينت النتائج بأن نوع فشل النماذج كانت بشق منفرد (single crack) وأن كلاً من مقاومة الانثناء القصوى ومعامل المرونة تزداد بزيادة نسبة الألياف.

Listing 1 - 10 of 19 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (19)


Language

English (15)

Arabic (4)


Year
From To Submit

2019 (1)

2018 (2)

2017 (1)

2016 (2)

2015 (1)

More...