Article
EFFECT OF ADDITIVES ON PROPERTIES OF SAND MOULDS USED IN CASTING OF GRAY CAST IRON
.تأثير المضافات على خواص القوالب الرملية المستخدمة لصب حديد الزهر الرمادي

Loading...
Loading...
Abstract

This research is devoted to study the effect of some additives such as glycerol, oat flour, rye flour, glue, PVC and Na2CO3 on properties of sand moulds then their effects on cast iron castings resulted from casting in these moulds. To prepare sand mixture with suitable properties for casting the required metal, various percentages of additives were added (after selecting the optimum percentage of bentonite and water) to the mixture to show their effects on the properties of the sand mould. Several tests were performed on the castings showed that those obtained from pouring in a mould composed of a mixture containing 0.5% glue, have better surface and mechanical properties, where the mould hardness was (75 Brinell scale) and its green strength was (0.046 MPa) in comparison to other additives, which gave less surface and mechanical properti

تناول هذا البحث دراسة تأثير بعض المضافات مثل الكليسيرول ومسحوق الشوفان ومسحوق الشليم والغراء وبولي فينل كلورايد وكربونات الصوديوم على خواص القوالب الرملية وبالتالي تأثيرها على خواص مسبوكات حديد الزهر الناتجة من الصب في هذه القوالب . لتحضير مزيج رملي ذو خواص ملائمة لصب المعدن المطلوب تم تحديد النسب المفضلة للبنتونايت والماء في المزيج الرملي بعدها تم اضافة نسب وزنية مختلفة من كل مادة مضافة لبيان تأثيرها على خواص القالب الرملي وقد وجد ان المسبوكات التي تميزت بافضل خواص سطحية وميكانيكية كانت تلك التي احتوى مزيج قالبها الرملي على مادة الغراء بنسبة (0.5%) من وزن مزيجها الرملي حيث كانت صلادة القالب (75) بمقياس برينل ومقاومته الرطبة (0.046MPa) اما المسبوكات الناتجة من الصب بقوالب رملية محتوية على الاضافات الاخرى فكانت بخشونة سطحية وخواص ميكانيكية اقل مما في حالة الغراء .الكلمات الدالة: المضافات,القوالب الرملية,حديد الزهر الرمادي


Article
Study on Bond Strength of Bonded Gray Cast Iron

Authors: Awfa Abdul-Rassol Abdullah --- Rasha Rahman Rawhdan
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2014 Volume: 17 Issue: 2 Pages: 94-100
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In the present study, two gray cast iron specimens were diffusion bonded at the temperatures of 700, 750, 800, 850, and 900 °C, the furnace used atmosphericexperiment under a pressing load of 1 and 2 ton for 15, 30 and 60min. After diffusion bonding, shear test measurements of interface region were made. As a result, from the microstructural observations, a good bonding along the interface of the bonded couples were detected since the interface is free from voids and microcracks. To evaluate the bond strength, the shear test investigation was used. The actual bonded area was calculated by using a computer package called (Auto Cad 2006). The results shows that the bond strength increases with increasing the temperature and holding time. Fracturography of the interface was carried out by using optical microscope before and after the experiments. The microstructure results shows the formation of carbide. Its precipitation increases with increasing the bonding temperature and time.

يتضمن البحث دراسة الربط الانتشاري لحديد الزهر الرمادي بالظروف الجوية باستخدام طرق تسخن مختلفة 900,850,800,750,700°م، وباستخـدام قـوة كبـس2,1 طن بأزمان مختلفة 60,30,15 دقيقة لإيجاد الظروف العملية المناسبه التي تؤثر على متانة الربط. قيمت متانة الربط باستخدام فحص القص وأظهرت النتائج إن متانة الربط تزداد مع ازدياد درجات الحرارة وكذلك متانةالربـط تـزداد مع ازدياد الوقـت. استخدم برنامج(Auto Cad 2006) لحساب مساحه التماس. لوحظ عند استخدام غاز الاركون انه لم تتكون وصله ربط بسبب الاكسده. بعد استبيان النتائج التي تم الحصول عليها من الدراسة ألمختبريه تبين إن الوصلات المربوطة وجدت مقاومة قص قصوى تساوي 155.7 ميكاباسكال عند ربطها في درجه حرارة 900°م تحت قوة كبس 1 طن ولفترة تسخين 30 دقيقة. وتبين من اختبارات الفحص المجهري تكون أطواركاربيدية (Carbides) وترسيبها على سطح العينة وداخل السطح البيني.


Article
WEAR RESISTANCE OF DIFFERENT TYPES OF CAST IRON USED IN GLASS BLOW MOULD
مقاومة البلى لأنواع مختلفة من حديد الصب المستخدم في صناعة قوالب الزجاج

Author: Kadhim Mijbel Mashloosh كاظم مجبل مشلوش
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2015 Volume: 8 Issue: 3 Pages: 1-21
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The aim of this work is to study the wear characteristics of different cast iron types which might be used as mould materials in glass blow molding. Wear testing rig was designed and developed to carry out the wear tests. Three types of gray cast iron with different chemical compositions were cast and heat treated, as well as samples taken (for comparison) from another two existing mould already being in use.Samples for wear testing were taken from the prepared materials and abraded against an automobile friction brake pads. Sliding velocity, friction pressure and contact time were taken as test variables. Weight loss of the tested samples was measured after conducting the wear tests at 600 & 800 0C. Cast iron with (2.98% C, 5.117% Si, and 1.39% Cu) showed the highest hardness in its as cast condition compared to the other types. It showed the best wear resistance after heat treatment (stress relief annealing).Results also showed that some of the tested materials gave a good wear resistance at low temperature (up to 600 0C) but they lost their resistance at high temperature (up to 800 0C). It was concluded that hardness is not the only parameter that controls the wear resistance at high temperature.

ان الغاية من هذا البحث هي دراسة خواص البلى لانواع مختلفة من حديد الصب (حديد الزهر) التي يمكن استخدامها في صناعة قوالب النفخ للعبوات الزجاجية.تم تصميم وتطوير منظومة خاصة لاجراء اختبارات البلى. تم سباكة ثلاثة انواع من حديد الصب ذات التركيب الكيماوي المختلف واجراء التعامل الحراري عليها بعد السباكة, اضافة الى اخذ عينات من قوالب حقيقية تم استخدامها سابقاً في صناعة العبوات الزجاجية.تم اجراء تجارب البلى باخذ نماذج من المعادن المعده للاختبار عن طريق الاحتكاك بعينة من المادة الاحتكاكية المستخدمة في موقفات السيارة, تحت ظروف تجربة مختلفة من سرعة الانزلاق, ضغط الاحتكاك, وزمن التلامس اثناء الاحتكاك.تم حساب الوزن المفقود للعينة بعد التجربة عند درجتي حرارة 600 و 800 م0.اظهر حديد الصب الذي يحتوي على (2.98% كاربون, 5.177% سليكون, 1.39 % نحاس) اعلى صلادة بعد السباكة مباشرة وبعد التعامل الحراري كذلك مقارنة بالمعادن الاخرى, اضافة الى امتلاكه اعلى مقاومة بلى بعد التعامل الحراري (تلدين ازالة الاجهاد).اظهرت النتائج كذلك ان بعض السبائك ابدت مقاومة بلى عالية عند درجات الحرارة (لحد 600 م0) ولكنها انخفضت عند درات حرارة (800 م0). كما بينت تلك النتائج ان الصلادة هي ليست العامل الوحيد الذي يسيطر على مقاومة البلى عند درجات الحرارة العالية.


Article
Experimental Study for the Effects of Crystalline Agents on Properties of Glass-Ceramic Coating

Authors: Ibtihal.A. Mahmood --- Ahmed.A.Zainulabdeen --- Jabbar.H. Mohmmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 2 Part (A) Engineering Pages: 179-184
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, four series of glass-ceramic coatings were developed and applied by using the dipping technique to cast iron sheets. The influence of different types of crystallization agents (Li2O, TiO2, ZrSiO4, and CaO.Al2O3.2SiO2) was investigated in relation to the mechanical features of the coatings. The resultant coating is characterized using X-ray diffraction analysis. The properties of micro-hardness and adhesion strength are evaluated using suitable standard tests. The X-ray analysis of resultant coatings showed the existence of some of crystalline phases formed depending on the type of the crystallization agent. The results also indicated that the coating properties were strongly dependent on composition and concentration of crystallization agent. Coating with feldspar gives the highest value of hardness and adhesion index. In general, properties of the resultant coatings were improved in all cases; this is related to the formation of a complicated network from crystalline phases.


Article
Evaluation of the Surface Temperature and Study of Its Effects on the Dry Sliding Wear Characteristics of a Bainitic Ductile Cast-Iron
تقييم درجة الحرارة السطحية ودراسة تاثيرھا على خصائص البلى الأنزلاقي الجاف لحديد الزھر اللدن الباينايتي

Author: Adel K. Mahmoud عادل خليل محمود
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 2 Part (A) Engineering Pages: 68-79
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work shows the evaluation process of the surface temperature by using heat sink (thermocouple) technique from type Alumel-Chromel (Ni-Al/ Ni-Cr) and to study its effect on the dry sliding wear characteristics of a bainitic ductile cast – iron. These characteristics represented with wear rates and coefficient of friction, which evaluated by using Pin on Disc machine under different laboratories conditions involved four applied normal loads (10, 20, 30, 40)N and three linear sliding speeds (1.4, 2.2, 3.0)mm/sec at room temperature. The present work shows the dry sliding wear characteristics and variables depend on the surface temperature generated during wear test. So, it can’t ignore these effects during the service. In addition to, it must be avoided using loads range (30-40)N and temperature range (310-360)Cͦ during practical applications it may be used this alloy within these ranges, because of both the two ranges may be led to occur severe wear of the bainitic ductile cast – iron surfaces with other counter surfaces of its working conditions.

تضمنت الدراسة تقييم درجة الحرارة السطحية باستخدام تقنية الغاطس الحراري (المزدوج الحراري) من نوع الالوميل – الكروميل وتاثيرها على خصائص البلى الانزلاقي الجاف لحديد الزهر اللدن الباينايتي والتي تمثلت بمعدلات البلى ومعامل الاحتكاك فقد تم تقييمها بأستخدام جهاز قياس البلى الانزلاقي الجاف ذي ترتيبة المسمار على القرص وتحت ظروف مختبرية مختلفة تمثلت باستخدام اربعة احمال عمودية (10,20,30,40) نيوتن وثلاثة سرع انزلاقية خطية (1.4, 2.2, 3.0) متر/ثانية وعند درجة حرارة الغرفة. تبين بأن متغيرات عملية البلى الانزلاقي الجاف والمتمثلة بالاحمال والسرع الانزلاقية المستخدمة في هذه الدراسة البحثية تعتمد بصورة رئيسية وكبيرة جدا على درجات الحرارة السطحية الناتجة عنهما بالرغم من ان تأثيرهما على البلى لايمكن ان يهمل عملياً. بالاضافة الى ذلك يجب تجنب استخدام مدى الاحمال (30-40) نيوتن ومدى درجات الحرارة من (310-360) مº عند التطبيقات العملية التي تستخدم فيها هذه السبيكة اثناء عملية انزلاقها واحتكاكها مع المواد الاخرى في العديد من التصاميم والتطبيقات العملية التي تسستخدم فيها , وذلك لكون هذه المديات من الاحمال ودرجات الحرارة تودي الى حصول بليان شديد (severe wear) لسطوح سبيكة حديد الزهر اللدن الباينايتي وبمعدلات كبيرة وذلك نتيجة لحدوث انتقال مادة هذه السبيكة الصناعية الى سطح المادة المحتكة معها والمرافقة لها اثناء عمليات الاحتكاك والانزلاق الجاف التي تحدث اثناء العمل والخدمة.


Article
CORROSION BEHAVIOR OF GRAY CAST IRON IN SEA WATER AT DIFFERENT PARAMETERS
سلوك التآكل لحديد الزهر الرمادي في ماء البحر عند متغيرات مختلفة

Authors: Nisreen Sabti Mohammed نسرين سبتي محمد علي --- Wisam Ismail Tayh وسام أسماعيل تايه
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2017 Volume: 30 Issue: 6 Pages: E31-E40
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

The corrosion behavior of gray cast iron in sea water at diverse temperatures (25, 50 and 75) °C and diverse velocity (1, 2 and 3) m/min was actualized. Many specimens were prepared in dimensions of (1.5* 1.5 * 0.3) cm according to ASTM G7-1-31then electrochemical potential state cell was used for corrosion tests, the positive electrode (anode) was signifies the test specimen while the cathode was made from tungsten metals, the voltage was determined by open circuit and associate with the positional of metal in the electrochemical series then voltage was increased + 100 mV, at each 10-mV increasing in the current and determine the corrosion current Sea water (3.5% NaCl in 1 litter distill water) temperature altered after each test then varying the velocity after each test (1, 2 and 3) m/min at stable temperature sea water 25 oC, calculating corrosion rate by using Tafel equation. Another test implemented such as microstructure examination using optical microscope. The results show that the corrosion rate increased with increasing solution temperature this is because of the prevention of oxygen from dissolving in water while the corrosion rate decreases by increasing velocity of sea water. Since the movement of the liquid avoids the formation of sums and ions gathering on cathode electrode where corrosion can simply improve.

هدف البحث دراسة سلوك التآكل لحديد الزهر الرمادي في ماء البحر عند ظروف متغيرة من درجة حرارة وسرعة وسط، أذ تم تصنيع عينات أختبار التآكل من المعدن بأبعاد (1.5 x 1.5 x 0.3) وفق مواصفات القياسيةASTM G7-1-31 لأجراء أختبار تآكل كهروكيميائي بطريقة المجاهد الساكن أذ تم أمرار تيار كهربائي في خلية تتألف من قطبين أحدهما قطعة العمل والثاني قطب من تنكستن عند جهد حدد من دائرة مفتوحة حسب موقع المعدن في السلسلة الكهروكيميائية ،وبعدها تم زيادة الجهد بــ (100 + ) ملي فولت عند كل 10 ملي فولت يزداد التيار، وأن التيار الذي يؤدي الى زيادة في الجهد يمثل تيار التآكل، وتم حساب تيار التآكل أعتماداً على معادلة تافل. في كل أختبار يتم تغيير درجة حرارة الوسط (25، 50 و 75) درجة مئوية وبعدها تم تثبيت درجةالحرارةعند 25 درجة مئوية وتغير سرعة الوسط (1، 2 و 3) م / دقيقة لتحقيق هدف البحث. تم أجراء فحص البنية المجهرية بأستخدام مجهر ضوئي ذو كاميرا للتعرف على التركيب الداخلي للمعدن وتأثيره على معدل التآكل. ومن النتائج التي تم الحصول عليها تبين أن بزيادة درجة الحرارة يزداد معدل التآكل بسبب منع الحرارة لذوبان الأوكسجين في الوسط بين ما يقل معدل التآكل بزيادة السرعة لدورها في منع تجمع الأيونات عند القطب الموجب الممثل للحديد.


Article
INVESTIGATION CORROSION BEHAVIOUR OF DUCTILE CAST IRON WELD JOINT IN SEA WATER
التحقيق من سلوك التاكل لملحومات سبائك الحديد الطرية في ماء البحر

Loading...
Loading...
Abstract

Manual metal-arc welding was carried out for ductile cast iron under welding conditions of (90) A DC current (DCEN) and 20 volts. Welding wire type E- Ni -Fe- CI in diameter of 3.2mm was used and travel speed of 7 inch /min and welded through two passes. The weld joined are examined using X-ray radiography, broken down joint are excepted. Corrosion specimens prepared from free defects joints having measurements of (15*15*3) mm agreeing to ASTM G71-31. Then Optical microscopy was employed to detect the welded joint microstructure and base metal. Micro hardness was implemented using Vickers test. Corrosion examinations are conducted using electrochemical potential state chamber in equipped (sea water 3.5% NaCl),Corrosion examination is achieved using potentiostatic polarization dimensions in saltwater 3.5%NaCl at potential scan rate (+100-100 mv/sec) to estimate corrosion parameters by extrapolating. The corrosion rate was calculated by Tafel equation. The results of corrosion rate can be predicted using a mathematical model using data achieved from practical method and compare these results with the theoretical one, results show that corrosion rate for welded joint is more than the base metal because of the change in metal microstructure during welding process.

يتضمن البحث دراسة سلوك التاكل لوصلات لحام انابيب من حديد الزهر المطيلي في ماء البحر تم اللحام بواسطة لحام القوس الكهربائي المحمي بالصهيرة عند ظروف لحام من تيار90 امبير و فولتية 20 فولت وسرعة 7 انج/ دقيقة باستخدام سلك لحام نوع Fe- CI ENi وقطر 3.2 ملم و بعدد اثنان من التمريرات باستخدام تيار (DCEN) للحصول على وصلة لحام تناكبية ,وبعد عملية اللحام والتاكد من خلوها من العيوب من خلال فحصها بواسطة جهاز X-ray radiography تم تحضير عينات اختبار التاكل بابعاد 15×15×3ملم وفق المواصفة القياسية ASTM G71-31 اتبعتها عمليات تحضير من تنعيم وصقل لاجراء فحص البنية المجهرية باستخدام المجهر الضوئي ذو كاميرا للملحومات والمعدن الاساس واختبار الصلادة الماكروية.اجري اختبار تاكل كهروكيمياوي بطريقة المجهاد الساكن عند جهد محدد وفق موقع المعدن في السلسلة الكهوكيمياوية وبعدها تم زيادة الجهد ب ( ±100) ملي فولت عند كل 10 ملي فولت يزداد التيار ، وأن التيار الذي يؤدي الى زيادة في الجهد يمثل تيار التآكل ، وتم حساب معدل التآكل اعتمادا على معادلة تافل .وقد تم التنبأ بمعدل التآكل عن طريق بناء نموذج رياضي اعتمادا على البيانات المحصلة عمليا ومقارنة تلك النتائج مع النتائج النظرية ومن النتائج التي تم الحصول عليها وجد ان معدل التآكل للملحومات اكثر من معدل التآكل للمعدن الاساس بسبب التغيرات التي تحدث بالبنيه المجهريه خلال عملية اللحام .


Article
Studying the Corrosion of Graphite Containing pearlitic Cast Irons in Sandy Soil
دراسة تآكل حديد الصب الكرافيتي البيرلايتي في التربة الرملية

Loading...
Loading...
Abstract

Abstract Wide range of industrial and engineering applications for graphite containing cast irons and the harmful effects of corrosion environments on these important engineering materials, make it necessary for continuous Scientific research in this field . In the current study, performed corrosion tests on Pearlitic cast irons using the sandy soil as the corrosion environment . The results obtained show a clear relationship between corrosion rate of graphite containing cast iron with shape of graphite. The graphite flakes in cast iron appeared to cause high corrosion rates compared with spheroidal or rosette graphites . The results also show that corrosion rates of spheroidal cast iron are slightly higher than malleable cast iron. The corrosion rates of grey cast iron represent the highest when compared with those of spheroidal and malleable cast iron.Keywords: Corrosion, Cast Iron, Sandy Soil

الخلاصةإن تعدد الاستخدامات الصناعية والهندسية لأنواع حديد الصب الكرافيتي ، وتأثرها بأوساط التآكل المختلفة من المبررات التي تدعو لدراسات وبحوث علمية لمعرفة مدى تأثير أوساط التآكل ، وخاصة المحلية منها في هذه الأنواع مما يجعل اختيار النوع المناسب من حديد الصب معتمدا على نتائج بحوث ذات طابع علمي معتمد . وقد أجريﹼ في هذا البحث اختبارات مكثفة لأكثر أنواع حديد الصب الكرافيتي أهميةً واستخداماً في التطبيقات المختلفة باستخدام التربة الرملية كوسطاﹰ للتآكل . لقد أظهرت النتائج وجود علاقة بين معدل تآكل حديد الصب الكرافيتي مع شكل ونوع الكرافيت المتواجد فيه . وتبين أن الشكل الشرائحي يسبب معدلات تآكل أعلى مما يسببه شكل الكرافيت الكروي أو الكرافيت الزهري . وأظهرت النتائج أن حديد الصب الكروي الكرافيت يتآكل بمعدلات مقاربة أو أعلى بقليل من معدلات تآكل حديد الصب الزهري الكرافيت ، في حين أن حديد الصب الرمادي تميز بأعلى معدلات التآكل .الكلمات الدالة: التآكل، حديد الصب، التربة الرملية.


Article
The Atmospheric Corrosion of Carbon Steel and Cast Iron in the Environment of South Mosul
التآكل الجوي للصلب الكربوني وحديد الزهر الرمادي في بيئة جنوب الموصل

Author: Nadum Ibrahim Naser ناظم إبراهيم ناصر
Journal: AL Rafdain Engineering Journal مجلة هندسة الرافدين ISSN: 18130526 Year: 2014 Volume: 22 Issue: 3 Pages: 165-175
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

AbstractThe carbon steel and cast iron are widely used metals in engineering and industrial applications. In this study, samples of carbon steel and cast iron chosen and distributed on six selected sites in the southregion of Mosul city in Iraq, Because these sites distinguished by the existence of natural emanations of hydrogen sulfide gas is produced and the existence of materials that cause metal corrosion like sulfates and chlorides. The corrosion measured by weight loss method according to the standard (ISO 9223:1992) and the higher rates registered in the sites that contain high emanations of hydrogen sulfide gas and sulfates and chlorides. In addition, it became obvious that there is a relationship between the corrosion exposure time and the corrosion rates which decreased by increasing of corrosion exposure time and continuous increasing in weight loss. The test continued for a complete year.

الخلاصةيعد الصلب الكربوني وحديد الزهر الرمادي من المعادن الواسعة الاستخدام في التطبيقات الهندسية والصناعية,وفي هذه الدراسة تم اختيار عينات من الصلب الكربوني وحديد الزهر الرمادي ووزعت هذه العينات على ستة مواقع منتخبة في منطقة جنوب الموصل في العراق لما تتميز به هذه المناطق بوجود انبعاثات طبيعية لغاز كبريتيد الهيدروجين بالإضافةإلى وجود المواد التي تسبب تأكل المعادن مثل الكلوريدات والكبريتات . تم قياس التآكل بطريقة نقصان الوزن وحسب معيار (ISO 9223:1992)وقد سجلت أعلى النسب في الأماكن التي توجد فيها انبعاثات عالية لغاز كبريتيد الهيدروجين والكبريتات الكلوريدات.كما تبين أن هنالك علاقة بين زمن التعرض للتآكل ومعدلات التآكل فهي تقل بزيادة زمن التعرض للتآكل مع بقاء استمرار الزيادة في فقدان الوزن حيث استمرت التجربة لمدة عام كامل.الكلمات ألدالة : الصلب ألكربوني , حديد ألزهر الرمادي ، التآكل


Article
DESTABILIZATION HEAT TREATMENT EFFECT ON EROSIVE WEAR CHARACTERISTICS OF HIGH CHROMIUM WHITE CAST IRON

Authors: Ali H. Ataiwi --- Israa F. Yousif
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2018 Volume: 9 Issue: 2 Pages: 45-56
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

In the present investigation, erosive wear property of high chromium white cast irons (HCWI) is reported. HCWI were destabilized at two different temperatures of 955oC and 1100°C, air cooling followed by tempering heat treatment at 400°C and 700°C at each destabilized temperature. Erosion damage was evaluated by the removed material mass at impact angle 45° and time of 10 Hours. The surface metal flow was observed. Surface morphology of each specimen was characterized with scanning electron microscopy (SEM). The effect of heat treatment on differences in wear features of specimens is discussed. Experiment showed that the erosion rate of specimen destabilized at 1100°C, air cooled followed by tempering at 400°C air cooling is the best than other treatments. The hardness of test surface by this treatment increased from the initial 57 to 58 HRC after 10 hour. It showed that austenite in the surface structure has been transformed to martensite , which hardened the surface. Similarly, work- hardening effect also occurred on specimen destabilized at 955°C, air cooled followed by tempering at 400oC, air cooling to make its surface hardness increased to 59 HRC. It was shown that HCWI series heat treated at 955°C and 1100°C and tempered at 400°C have a very good erosive wear resistance and they are expected to find wide application as wear-resistant materials.

Listing 1 - 10 of 11 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (11)


Language

English (6)

Arabic (5)


Year
From To Submit

2019 (1)

2018 (3)

2017 (1)

2016 (1)

2015 (1)

More...