Article
Preparation and Characterization of γ-Al2O3/Al Composite
تحضير ودراسة خصائص المتراكب –Al2O3/Alγ

Authors: Hanan Jamil Mustafa حنان جميل مصطفى --- Abd AL Hameed Raheem Mahdi عبد الحميد رحيم مهدي
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2016 Volume: 57 Issue: 3B Pages: 1959-1967
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

A cermet (ceramic-metal) composite have been prepared from alumina (γ-Al2O3) reinforced with aluminum (Al) for the concentrations of (0, 10, 20, 30, 40, & 50) wt. %Al. The cermet was formed by single axial pressing, sintered in vacuum atmosphere. Compaction behaviors were studied in solid state sintering at sintering temperatures (400, 450, & 550) °C, sintering times (2, 4, & 6) hrs., and forming pressures (5, 10, 15) MPa, also in liquid phase sintering at (800 °C). The cermet was characterized by x-ray diffraction (XRD) and by scanning electron microscope (SEM), also physical and mechanical properties have been studied. SEM results showed the Al flowing inside the ceramic body due to uniform distribution of Al particles and due to sintering temperature (800 °C) have been used. XRD results showed that there is no new phase formed between Al and Al2O3 after sintering due to there is no chemical reaction but physical reaction between them. The existence of Al enhanced the physical properties as the sintering (time & temperature) and pressure increase. Hardness values increased to 30 wt. % Al then decreased due to Al ductility. The oxide layer on the friction surfaces played important role for increasing wear rate.

تم تحضير المتراكب السيرميتي (سيراميك-معدن) من الالومينا (γ-Al2O3) المدعمة بالألمنيوم (Al) بالتراكيز (0، 10، 20، 30، 40، 50)%Al. شكل السيرمت بفعل الضغط باتجاه واحد، ولبد في جو مفرغ من الهواء. تم دراسة سلوكيات الرص بحالة التلبيد الصلب عند (400، 450، 550) م° و ( 2، 4، 6) ساعات وكذلك (5، 10، 15) ميكاباسكال، وكذلك تم دراستها عند تلبيد الطور السائل عند ( 800 م°). تم تشخيص السيرمت بواسطة حيود الاشعة السينية (XRD)، و المجهر الالكتروني (SEM)، وكذلك تم دراسة الخواص الفيزيائية والميكانيكية. اظهرت نتائج الفحص المجهري (SEM) انسياب الالمنيوم داخل الجسم السيراميكي وذلك تبعا للتوزيع المنتظم لجسيمات الالمنيوم وكذلك درجة حرارة التلبيد المستعملة ( 800 م°)، واظهرت نتائج (XRD) ان ليس هنالك تكون طور جديد بين الالمنيوم و الالومينا بعد التلبيد نسبة الى عدم حدوث تفاعل كيميائي بين المادتين فقط حدوث تفاعل فيزيائي بينهما. وجود الالمنيوم حسن الخواص الفيزيائية بزيادة كل من درجة حرارة التلبيد وزمن التلبيد و الضغط. قيم الصلادة ازدادت حتى التركيز 30%Al وبعدها تبدا القيم بالنقصان و ذلك نسبة الى مطيلية الالمنيوم. الطبقة الاوكسيدية المتكونة عند السطوح المحتكة لعبت دور مهم في زيادة معدل البلى.

Keywords

cermet --- composite --- ᵞ-alumina


Article
The Effect of Pure Aluminum Weight Percent on Different Properties of a New Cermet Material Made of Al-Machinable Glass Ceramic

Author: Bayda,a Abdul-Hassan Khalaf
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 4 Pages: 805-813
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research high pure aluminum metal with the following weight percent(1,2,3,4,5) has been added to machinable glass-ceramic, after the preparation of thesamples by pressing then firing the effect of this addition on the density, hardness,young modulus, and polishing and grinding time of the machinable glass-ceramichave been studied. It has been found that the increasing in aluminum percent lead toslightly increase in density while the hardness, young modulus, and polishing andgrinding time decreased.


Article
الخصائص الفيزيائية لنظام(بازلت-نيكل) بتقنية الرش الحراري باللهب

Authors: باسل صباح احمد* --- اسماعيل خليل جاسم
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2019 Volume: 27 Issue: 4 Pages: 98-108
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Many surfaces suffer cracks and external corasion such as turbo blades and oil pipes. In order to solve these problems are used coatings of high durability and low cost. In the current research, the powder of the basalt with multiple oxides supported by metal (Ni) 50% was sprayed models with thermal spraying by flame and at multiple spraying distances of (10,12,14,16,18,20) cm after the preparation of the models coated on a base of alloy steel, the process of sintering of the samples at (700, 900, 1100)℃ and within two hours have been done. The mechanical tests were (strength adhesion, porosity, hardness, wear and tear) (SEM) for prepared samples before and after sintering. The results showed that the best spraying distance was 16 cm and the best heat treatment is ( (1100 ℃), depending on the results of the adhesion strength tests at (24.43 MPa) and (8.653%) porosity, (1140 Hv) and the hardness of the Vickers and at a constant sliding speed (12000 cm / min). The results of the scanning electron microscopy showed clear surface consistency after thermal conductivity with a few pores and treatments the best (1100.).

تعاني العديد من السطوح تشققات وتأكل خارجي مثل الريش التوربينية وانابيب النفط ولأجل حل تلك المشاكل يتم استخدام طلاءات ذات متانة عالية وكلفة واطئة. ففي البحث الحالي تم استخدام مسحوق صخور البازلت((Basalt ذات الاكاسيد المتعددة مدعمة بمادة معدنية (Ni)50% تم رش النماذج المجهزة بتقنية الرش الحراري بواسطة اللهب وعند مسافات رش متعددة هيcm (10,12,14,16,18,20) وبعد اكمال تحضير النماذج المطلية على قاعدة من الفولاذ السبائكي تم اجراء عملية التلبيد للعينات وعند معاملة ((700℃, 900℃,1100℃ وبزمن ساعتين. اما الفحوص الميكانيكية تمثلت ب( قوة التلاصق, المسامية, الصلادة, البلى) وكما تم اجراء فحص بالمجهر الالكتروني الماسح(SEM) للعينات المحضرة قبل وبعد عملية التلبيد. اظهرت نتائج الفحص ان احسن مسافة رش كانت cm 16 وافضل معاملة حرارية هي ( (1100℃ وذلك بالاعتماد على كل من نتائج فحوص قوة التلاصق التي بلغتMPa(24.43) و المسامية التي بلغت %((8.653 وصلادة فيكرز هي (HV 1140) وكما ووجد عند سرعة انزلاقية ثابتة هي (cm/min.12000) وعند زمن خمسة دقائق وحمل ( (20Nالحصول على اوطئ معدل بلى(wear)هو (0.397), اما نتائج فحص المجهر الالكتروني الماسح اوضحت تناسق سطحي واضح بعد اجراء المعاملات الحرارية مع وجود قليل للمسامات