Clathrate hydrates are complex molecules formed by the contact between water and gas at high pressure and low temperatures. One of the important aims of gas hydrate technology is to enhance the formation of hydrate and reduction the induction time for clathrate formation. Effect of the different promoters (nonionic surfactant Tween80) on R-134a gas hydrate formation has been investigated in the isochoric system experiment. It is noted that the surfactants have a significant effect of increasing the speed of nucleation as well as improving the growth of hydrate. In the experiment, the effect of Tween80 surfactant was studied to determine its effect on the composition and cooling capacity of 134 hydrates. From kinetic models, many objective functions such as the amount of gas consumed (Δn), the growth rate (r (t)), the apparent rate constant (Kapp) and conversion of the water to hydrate were obtined. The improvement of hydrate growth is marked by the addition of surfactants, which in turn increase the solubility of hydrate gas and reduce the contact angle. In addition, surfactants positively the contact with the gas through the increase of the gas diffusion in the water and this increases the rate of formation of hydrate. Best value achieved at a surfactant concentration of 100 ppm with maximum gas consumed amount (0.16 mol) and less indction time 32 min.

Clathrate --- gas hydrate --- surfactant --- refrigerant --- thermodynamics model

One of the important aimsof gas hydrate technology is to enhance the formation of hydrate or reduction the induction time for clathrate formation. The effect of the different promoter silica gel powder on R-134a gas hydrate formation has been investigated in the isochoric system experiment.It is noted that the purse media have a significant effect in increasing the speed of nucleation as well as improving the growth of hydrate. In the experiment, the effect of silica gel powder was studied to determine their effect on the composition and cooling capacity of 134 hydrates.From kinetic models were obtained many objective functions such as the amount of gas consumed (∆n), the growth rate (r (t)), and conversion of the water to hydrate. The gas consumed (∆n) of binary system increased with increase initial pressure of hydrate formation, also the hydrate growth rate (r (t)) and increase conversion of water to hydrate increase when this the first time that the effect of silica gel pweder on these functions with average active size (900) nm, BET surface area (0.65) m2/g, pore volume 210.85 cm3/g and average pore size (900) nm that studied for use in industrial applications and water treatment. The improvement of hydrate growth is marked by the addition of silica gel powder, which in turn increase the solubility of hydrate gas and reduce the contact angle. In addition, silica gel powder positively the contact with the gas through the increase of the interaction surface between gas and water and this increases the rate of formation of hydrate.

الكلاثريت هيدراتعبارة عن جزيئات معقدة تتكون من الاتصال بين الماء والغاز عند الضغط العالي ودرجات الحرارة المنخفضة. أحد الأهداف الهامة لتكنولوجيا هيدرات الغاز هو تعزيز تكوين الهيدرات أو تقليل وقت التنوي لتشكيلالكلاثريت . تم دراسة تأثير مسحوق هلام السيليكا كمحفز على تركيبة هيدرات الغاز R-134a في تجربة نظام ايزوكوريك (حجم ثابت).من الملاحظ أن للوسط المسامي تأثير كبير في زيادة سرعة التنوي وكذلك تحسين نمو الهيدرات. في التجربة ، تمت دراسة تأثير مسحوق هلام السيليكا لتحديد تأثيرها على تكوين وتبريد 134 هيدرات و تم الحصول على العديد من الوظائف الموضوعية من النماذج الحركية مثل كمية الغاز المستهلكة (∆n) ومعدل النمو (r (t)) وثابت المعدل الظاهري (Kapp) وتحويل الماء إلى هيدرات. ازدادت كمية الغاز المستهلكة (∆n) في النظام الثنائي مع زيادة الضغط الأولي لتكوين الهيدرات ، وأيضا معدل نمو الهيدرات (r (t)) وزيادة تحويل الماء لزيادة الهيدرات عندما تكون هذه هي المرة الأولى التي يؤثر فيها مسحوق هلام السيليكا. على هذه الوظائف بمتوسط حجم نشط (900) نانومتر ، مساحة سطح (0.65) م 2 / جم ، حجم المسام 210.85 سم 3 / جم ومتوسط حجمالمسام (900) نانومتر الذي درس للاستخدام في التطبيقات الصناعية ومعالجة المياه. بإضافة مسحوق هلام السيليكا يتحسين نمو الهيدرات وذلك لانه يزيد من ذوبان غاز الهيدرات ويقلل من زاوية التلامس. بالإضافة إلى ذلك ، مسحوق هلام السيليكا يؤثر بشكل إيجابي على الاتصال الماء مع الغاز من خلال زيادة سطح التفاعل بين الغاز والماء وهذا يزيد من معدل تكوين الهيدرات.

Clathrate --- Gas hydrate --- Silica gel powder --- Refrigerant --- Thermodynamics model --- كلاثريت --- هيدرات الغاز --- مسحوق هلام السيليكا --- التبريد --- نموذج الديناميكا الحراري.