Article
Synthesis Of Nano Ni-Mo/γ-Al2O3 Catalyst

Loading...
Loading...
Abstract

Nano γ-Al2O3 support was prepared by co-precipitation method by using different calcination temperatures (550, 600, and 750) oC. Then nano NiMo/γ-Al2O3 catalyst was prepared by impregnation method were nickel carbonate (source of Ni) and ammonium paramolybdate (source of Mo) on the best prepared nano γ-Al2O3 support at calcination temperature 550 oC. Make the characterizations for prepared nano γ-Al2O3 support at different temperatures and for nano NiMo/γ-Al2O3 catalyst like X-ray diffraction, X-ray fluorescent, AFM, SEM, BET surface area, and pore volume.The Ni and Mo percentages in the prepared nano NiMo/γ-Al2O3 catalyst determined by X-ray fluorescence were 2.924 wt % and 12.9 wt %, respectively. SEM of prepared nano γ-Al2O3 support at calcination temperature 550 oC. The average particles diameter of prepared γ-Al2O3 support determined by AFM at calcination temperatures 550, 600, and 750 oC and for prepared nano NiMo/γ-Al2O3 catalyst at calcination temperature 550 oC.


Article
Novel Co-Precipitation Method for Synthesis of Nanostructured Nickel Oxide in Accordance to PH: Structural and Optical Properties as an Active Optical Filter

Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: P16094042/ E25213407 Year: 2019 Volume: 32 Issue: 1 Pages: 1-6
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Low cost Co-Precipitation method was used for Preparation of novel nickel oxide (NiO)nano particle thin films with Simple, with two different PH values 6, 12 and its effect onstructural and optical properties as an active optical filter. Experimental results of structuralproperties X-ray diffraction (XRD) showed that both Nickel oxide nanoparticles with (PH=6and 12) have polycrystalline structure smaller average particle size about 8.5 nm for PH = 6 incomparison with PH = 12. Morphological studies using Scanning electron microscopy (SEM)and atomic force microscope (AFM) show uniform nano rod distribution for PH=6 withsmaller average diameter, average roughness as compared with NiO with PH=12 that showedlarger diameter, grain size, spherical shape with scope of excellent sensing applications due tohigh roughness. Optical properties results show blue shift for PH = 6 as compared withPH=12m leading to potential of optoelectronic applications and as active optical


Article
Variation of lattice parameter, average grain size, dielectric constant and saturation magnetization with different temperature for 0.30Ni0.7Zn0.3Fe2O4+ 0.70 PLZT composite by Co-precipitation method
تغایر معاملات الشبیكة ، معدل الحجم الحبیبي ، ثابت العزل الكھربائي والإشباع 0.30 درجات الحرارة للمركب باختلاف المغناطیسي Ni0.7Zn0.3Fe2O4+ 0.70 PLZT بطریقة الترسیب الكیمیائي

Author: Abdul Samee Flaws AbdulAziz عبد السمیع فوزي عبد العزیز
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2012 Volume: 8 Issue: 3 - part 1 Pages: 228-244
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Magnetoelectric composites containing Ni0.7Zn0.3Fe2O4 and Pb0.93La0.07(Zr0.60Ti0.40)O3 phases have been prepared by chemical co-precipitation method. The structure and morphology of the composites were examined by means of X-ray diffraction (XRD) and scanning electronmicroscopic (SEM) The XRD result showed that the composites consisted of spinel Ni0.7Zn0.3Fe2O4 and perovskite PLZT annealing at temperature higher than 700 oC. The average grain size for the piezoelectric phase of the composite was found to increase the overall dielectric and ferroelectric properties of the composite increased with increasing insintering temperature. Variation of dielectric constant (ε) and dielectric loss (tanδ) with frequency for 0.30NZFO + 0.70PLZT composite with annealed at different temperature showed dispersion in the low frequency range. The variation of dielectric constant with temperature reflects DPT type behaviour. The dielectric properties are strongly influenced by interface phenomena (Maxwell-Wagner) due to the local electrical inhomgeneity. At low frequency range, the composite showed the dielectric dispersion is associated with very high polarization. The peak value of dielectric constant for composite decreased with increasing its sintering temperature. coercivity, saturation magnetization and squareeness have been found to vary with concentration of ferrite phase and annealing temperature due to the increase in crystallite size. The maximum value of the magnetoelectric conversion factor (dE/dH)max equal to 5.2 mV/cm.Oe is observed for 30%NZFO – 70% PLZT composites when sintered at 1100 oC.

المركبات الكهرومغناطيسية والتي تحتوي على الاطوار Ni0.7Zn0.3Fe2O4 وPb0.93La0.07 (Zr0.60Ti0.40) O3 والمحضرة بطريقة الترسيب الكيميائي المشترك. تم فحص بنية ومورفولوجية والمواد المركبات عن طريق حيود الأشعة السينية (XRD) والمسح الضوئي الإلكترون وأظهرت المجهرية (SEM) والنتيجة أن XRD المركبة تتألف من Ni0.7Zn0.3Fe2O4 الإسبنيل الصلب وPLZT perovskite في درجة حرارة أعلى من 700 درجة مئوية. تم العثور على متوسط ​​حجم الحبوب للمرحلة كهرضغطية من مركب لزيادة عازلة الشاملة وخصائص متعلق بالعازل الكهربائي الشفاف من مركب زاد مع زيادة في درجة حرارة التلبيد. تباين عازلة أظهرت خسارة ثابت (ε) وعازلة (tanδ) مع تردد ل0.70PLZT 0.30NZFO مركب + مع صلب في درجة حرارة مختلفة التشتت في مدى التردد المنخفض. تباين ثابت العزل الكهربائي مع درجة الحرارة يعكس السلوك DPT نوع. وتتأثر بشدة من خصائص عازلة الظواهر واجهة (ماكسويل-فاغنر) بسبب inhomgeneity الكهربائية المحلية. في نطاق التردد المنخفض، وأظهرت المركب يرتبط تشتت عازلة مع الاستقطاب عالية جدا. انخفضت قيمة ثابت العزل الكهربائي ذروة لمركب مع زيادة درجة الحرارة تلبد. تم العثور على الأكراه والتشبع ومغنطة squareeness أن تختلف مع تركيز المرحلة الفريت ودرجة الحرارة الصلب بسبب الزيادة في حجم الكريستال. الحد الأقصى لقيمة عامل التحويل الكهرومغناطيسية (دي / درهم) كحد أقصى لوحظ على قدم المساواة إلى 5.2 بالسيارات / cm.Oe لNZFO 30٪ - 70٪ PLZT المركبة عندما متكلس الساعة 1100 درجة مئوية.


Article
Humidity and Gas Sensitivity of NI and Co Ferrites pellets with nanoscale grain size at Room Temperature
الرطوبة وحساسية الغاز لعينات ف ا ريت النيكل والكوبمت مع الحجم الحبيبي عند درجة ح ا ررة الغرفة

Loading...
Loading...
Abstract

Ni and Co ferrite pellets were prepared by co-precipitation method at 100 oC as a reaction temperature and then sintered at 400 oC for the phase formation. The identified phase was confirmed by x-ray diffraction analysis in which all intensity peaks of Ni and Co ferrites were observed which clearly indicates that the single phase of inverse spinel ferrite. Surface morphology of pellet was studied by Scanning Electron Microscopy (SEM), which shows high reacting surface area due to small grain size ≈ 32 to 40 nm. The pellets were prepared as gas sensor elements. We have studied humidity sensing with Ni and Co ferrite in pellet form. Also with Ni and Co ferrite, sensing to NH4 and acetone gas has been studied. It has been found that the gas sensing for test gases is found to be in the order of humidity, NH4, acetone and Cl2. Here it is shown that CoFe2O4 acts as a good sensor as compared to NiFe2O4 especially for acetone and ammonia gases

تم تحضير جسيمات ف ا ريت النيكل والكوبمت النانوية بطريقةة الترسةيب بدرجةة حة ا ررة 100oC )درجةة حة ا ررة التعاعةل ب وبعةد لةت تةم تمبيةد اعند درجة ح ا ررة 400OC لغ رتشكيل الطور. وتم التاكد من تشكيل الطور بواسطة تحميل حيود الاشعة السينية والةي ظهرةر ان شةدة جميةع القمةم لكةلمن ف ا ريت النيكل وف ا ريت الكوبمت والتي بينت وبشكل واضح الطور المنعرد لمع ا ريت عكسةي البةرم . تمةت د ا رسةة مورفولوجيةة سةطون العينةات المحضةرةباستخدام المجرر الالكتروني الماسح والتي بينت وجود مساحة تعاعل سطحي عالية نتيجة لصغر الحجةم الحبيبةي تقريبةا مةن 32 nm الة 40 nmنانومتر. وان العينات التي ي عم يئة حبات حضرت لتكون عناصر لمتحسس غاز . د ا رسة حساسةية الرطوبةة باسةتخدام في ا ريةت النيكةل والكوبمةتعم يئة حبات )كرياتب. وتمت د ا رسة حساسيترا لغاز الامونيا والاسةيتون. وجةد ان التحسةس الغةاز لمغةا ا زت المعحوصةة ةو ضةمن حةدود الزطوبةةوغا ا زت الامونيا والاسيتون والكمور. نا وجد ان المركب CoFe2O4 يعمل كمتحسةس جيةد بالمقارنةة مةع المركةب NiFe2O4 ويلاحةه للاسةيتون وغا ا زت الامونيا .


Article
Photocatlytic oxidation of congo red dye by using Co2O3–Cr2O3 as a Photocatalyst

Author: Alaa R. Amrin
Journal: Mesopotamia Environmental Journal بيئة وادي الرافدين ISSN: 24102598 Year: 2016 Volume: 2 Issue: 2 Pages: 66-74
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Homogeneous crystalline chromium and cobalt oxides (Cr2O3- Co2O3) was prepared by co-precipitation method by mixing metals nitrate in the basic medium and the precipitate was calcinated at 700 C for 6 hrs. The crystalline structure of the synthesized products were analyzed by X-ray diffraction (XRD). The obtained XRD patterns of specimens revealed formation of a well-crystallized structure of double oxides after calcination at 700 C. The photocatalytic activity of double prepared oxides was investigated via following removal of congo red dye from the aqueous solution upon irradiation of reaction suspension under irradiation with UV light.


Article
X-band Region Characterization of Neoprene Rubber Reinforced Cd-Zn Ferrite Composite Material
توصيف حزمة (X) لمطاط النيوبرين المدعم بمواد متراكبة من كادميوم- زنك فرايت

Authors: FirasA’aidNajim فراس عائد نجم --- Wissam Adel Hussien وسام عادل حسين
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2019 Volume: 11 Issue: 01 Pages: 120-127
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

The compound was prepared from (ZnFe2O4) and (CdFe2O4)The process of mixing the ferrite compounds was done according to the formula (CdxZn1-xFe2O4),The resulted compound was (Cd0.7Zn0.3 Fe2O4). The compounds (ZnFe2O4) and (CdFe2O4) were prepared by Co-Precipitation method because this method gives a good homogeneity to the powder particles. XRD and FE-SEM were performed, the results showed that ferrites had a phase-shaped cube and an increase in the concentration of cadmium in the (CdxZn1-x Fe2O4)compound .This result showed an increase in the lattice constant, the rate of crystalline size and the distance between the crystalline surfaces,due to the fact that the ionic radius of the cadmium is greater than the ionic diameter of the zinc, which is (0.83 A°).The images of the electron microscope (FE-SEM) showed an increase in particle size with an increase of concentration of cadmium ferrite in relation to the compound (CdxZn1-x Fe2O4),The components of the ferrite structures prepared by EDS technique were verified, where the ferritecompound (Cd0.7Zn0.3Fe2O4) mixed with the Neoprene (Chloroprene Rubber) (CR) according to weight ratio of (3,6g)of ferrite, after the process of forming rubber paste. The VNA was investigated for (8-12 GHz). It was observed that the reflection coefficient was reduced by increasing the fraction of ferrite to (6g) and obtain highly absorbent materials .Where the material behavior varies according to the frequency, as well as the concentration ratio in the ferrite and the quantity of the ferrite with Chloroprene rubber (CR).ThePermeability of (Cd0.7Zn0.3Fe2O4) was calculated as a function of frequency.The real part of the amplitude showed the amount of energy from the external electric field stored in the material.

تم تحضير الفرايت ذو التركيب (Zn Fe2O4) و(Cd Fe2O4) ومن ثم تمت عملية خلط المركبات الفرايت حسب الصيغة (CdxZn1-xFe2O4) والحصول على المركب (Cd0.7Zn0.3Fe2O4) حيث تم تحضير المركبات الفرايتية (Zn Fe2O4)و(Cd Fe2O4) بطريقة ( Co-Precipitation Method ) لأنها تعطي تجانسا لجزيئات المسحوق. تم دراسة الخواص التركيبية للنماذج المحظرة حيث أظهرت النتائج ان الفرايت من نوع (الطري ) وان زيادة تركيز الكادميوم في المركب (CdxZn1-x Fe2O4) أدى الى زيادة كل من ثابت الشبيكة و معدل الحجمالبلوري والمسافة بين السطوح البلورية كلما ازداد فرايت الكادميوم ويرجع سبب ذلك لان نصف القطر الايوني للكادميوم اكبر من نصف القطر الايوني للخارصين الذي يبلغ (A°0.83) واظهرت صور المجهر الالكتروني ( FE-SEM) تزايد حجم الجسيمات مع زيادة تركيز فرايت الكادميوم بلنسبة للمركب (CdxZn1-x Fe2O4) وتم التحقق من العناصر المكونة للتراكيب الفرايتية المحضرة بواسطة تقنية (EDS) تمت عملية مزج المركب (Cd0.7Zn0.3Fe2O4) مع (GRT) (Neoprene Chloroprene Rubber) بإضافة (3,6) غم من الفرايت ,بعد عملية تكوين العجينة المطاط تم اجراء فحص( VNA ) للعينات ضمن حزمة X من الموجات الميكروية (8-12) GHz . لوحظ أن معامل الانعكاس قد انخفض عن طريق زيادة جزء الفريت إلى (g 6) والحصول على مواد شديدة الامتصاص .حيث يختلف سلوك المادة باختلاف التردد ، وكذلك نسبة التركيز في الفريت وكمية الفريت مع المطاط النيوبرين (CR). حيث تم احتساب نفاذية للمركب (Cd0.7Zn0.3Fe2O4) كدالة للتردد. تم حساب الجزء الحقيقي والجزء الخيالي من ثابت العزل كدالة للتردد في النطاق X . أظهر الجزء الحقيقي من السعة مقدار الطاقة من الحقل الكهربائي الخارجي المخزن في المادة.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (5)


Year
From To Submit

2019 (2)

2016 (2)

2013 (1)

2012 (1)