Article
FABRICATION AND CHARACTERIZATION OF HIGH EFFICIENTCd O/SI PHOTOVOLTAIC SOLAR CELLS

Author: Khalid Z. Yahiya
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2008 Volume: 11 Issue: 1 Pages: 56-58
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In the present work, CdO/Si heterojunction solar cell has been made by vacuum evaporation of CdO thin film onto monocrystalline silicon substrate. XRD was investigated, the transmission was determined in range (400-1000)nm and the direct band gap energy is 2.5 eV, I-V characterization of the cell under illumination was investigated , the cell shows an open circuit voltage (VOC) of 0.4 V, a short circuit current density (JSC) of 40 mA/cm2, a fill factor (FF) of 0.34, and a conversion efficiency (η) of 5.5%.

في هذا البحث ، تم تصنيع خلايا شمسية هجينة نوع CdO/Si وذلك بتبخير أغشية CdO الرقيقة على قواعد سليكونية أحادية البلورة . تم دراسة البناء البلوري للغشاء بواسطة حيود الأشعة السينية وتم دراسة النفاذية للمدى (400-1000)nm تم حساب فجوة الطاقة المباشرة وتساوي (2.5)eV وتم دراسة القياسات تيار-جهد في حالة الإضاءة أبدت الخلية أداء فولطائي جيد حيث أن تيار دائرة القصر (40)mA/cm2 وان فولتية الدائرة المفتوحة (0.4)V وبكفاءة تحويل 5.5% وعامل ملئ 0.34 .


Article
FABRICATION AND STUDY OF SnO2/INP HETEROJUNCTION SOLARCELL BY SPRAY PYROLYSIS

Author: Jehan E. Simon
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2008 Volume: 11 Issue: 1 Pages: 64-67
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

SnO2/InP heterojunction solar cells have been prepared by spray pyrolysis low-cost technique with an open circuit voltage of 500 mV, a short circuit current density of 28 mA/cm2, fill factor of 0.28, and conversion efficiency of 4%. Halogen lamp was used as a simulated AM 1 condition. Electrical properties of this heterojunction have been examined.

تم تحضير الخلايا الشمسية ذات المفرق الهجين SnO2/InP بطريقة الرش الكيميائي الحراري ذات الكلفة المنخفضة من دراسة الخصائص الكهروبصرية وجد ان فولتية الدائرة المفتوحة 500 mV وكثافة تيار دائرة القصر 28mA/cm2 وبعامل ملئ 0.28 وكفاءة تحويل 4% باستخدام مصباح هالوجين عند حالة AM1 وتم دراسة الخصائص الكهربائية للمفرق.


Article
Fabrication and Characterization of High Efficient CdS/Si Heterojunction Solar Cells
تصنيع ودراسة خلايا Cds/Si الشمسية الهجينة عالية الكفاءة

Author: Khalid Z. Al-Ta'ai
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2005 Volume: 24 Issue: 7 Pages: 869-876
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract


Article
Enhancing Photoelectric Conversion Efficiency of Photovoltaic Panel Using Cooled Water by Evaporation

Authors: A.J. Kadem --- S. R. Fafraj --- I A. Hasan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 5 Part (A) Engineering Pages: 525-531
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

It has been found a linear progression between the panel temperature and its efficiency. A novel cellulose pad arrangement, which is saturated with water, at back surface of photovoltaic panel for cooling has achieved better results. The experimental results showed a reduction in maximum PV panel temperature at using the proposed water cooling system. The average temperature of the PV panel dropped 10.1°C and an increase in average solar panel efficiency about 20.8% during operating time. Then, a comparison between the PV panel results cooling by natural convection and using the proposed water cooling system will reveal the most efficient.


Article
Fabrication and Study Nanostructure Deposited Thin Films Heterojunction Solar Cell
تصنیع ودراسة خلیة شمسیة ھجینة بترسیب اغشیة رقیقة ذات تراكیب نانویة

Authors: Khaled Z.Yahya --- Muhanad Adel Ahmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 1 Pages: 43-50
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present paper, nanostructure tin oxide (SnO2) thin films on Si P-typesubstrates heterojunction solar cell has been made by using a pulsed 532 nm Nd:YAGlaser. Deposition of films is achieved at 400 °C substrate temperatures. The X-raydiffraction (XRD) results show that the deposited films are crystalline with tetragonalrutile SnO2 structure. The morphology of deposited films were characterized byscanning electron microscope (SEM) and atomic force microscope (AFM), the grainsize value (30–50) nm and rms roughness values are (2.8 nm) for thin filmsdeposited at 400ºC. Photoluminescence PL spectrum showed good light emission inthe visible field. The photovoltaic characteristics included short circuit current (Jsc),open circuit voltage (Voc), where the maximum (Jsc) and (Voc)obtained at AM1were 14.3 (mA cm-2) and 630(mV), respectively. The fill factor (FF) was (0.68). Thefabricated cell exhibits good performance with 7 % conversion efficiency.

في هذا البحث , تم ترسيب اغشية نانوية لأوكسيد القصدير وترسيبها على قواعد من السليكونالاحادي البلورة من النوع القابل لتصنيع خلايا شمسية هجينة باستخدام ليزر النيودميوم-ياك النبضيذو الطول الموجي 532 نانو متر.تم ترسيب الاغشية عند درجة حرارة قاعدة 400 درجة مئوي.اذ أظهرت النتائج تكون طور الروتيل (XRD) حدد التركيب البلوري باستخدام حيود الأشعة السينيةالرباعي لأغشية اوكسيد القصدير البلورية. حددت خصائص طبوغرافية السطح من خلال قياس(30– المجهر الالكتروني الماسح و مجهر القوى الذرية , حيث تراوحت قيمة الحجم الحبيبي ( 50( نانو متر وقيمة خشونة السطح ( 2.8 )نانومتر للأغشية المحضرة بدرجة حرارة قاعدة ( 400مئوي.اظهر طيف الانبعاثية الضوئية انبعاثا" جيدا" في المنطقة المرئية. درست الخواص الفولطائية(FF) بالاضافة لعامل الملئ (Voc) وفولتية الدائرة المفتوحة (Jsc) المتمثلة بتيار الدائرة القصيرة630(mV), 14.3 و (mA cm- هي ( 2 AM لحالة 1 (Voc) و (Jsc) ووجد ان اعظم قيمة لكل منعلى التوالي وان قيمة عامل الملئ هي ( 0.68 ) .الخلية المصنعة اظهرت قيمة كفاءة جيدة بلغت.7


Article
Performance Analysis of Laser Diode Single-End-Pumped Solid State Laser

Authors: Mohammed. J. Abdul-Razak --- Hisham .M. Ahmed --- Abdulla. K. Abass
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2013 Volume: 21 Issue: 4 Pages: 1359-1363
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In this work, results are presented for a continuous wave diode laser single-end-pumped Nd:YVO4 laser with maximum output power of 240mW in the TEM00 mode at an optical pump power of 850mW. The laser performance under different output couplers has been studied both analytically and experimentally. The theoretical analysis provides a good prediction of the laser performance parameters which are in broad agreement with the experimentally observed results. An optical to optical conversion efficiency of 28% and an average optical slope efficiency of 29% were obtained. The fluctuation of the output power is less than 1.5% in 10 min.

تم في هذا العمل عرض نتائج ليزر Nd:YVO4 مستمر الموجة ومضخ طولياً بواسطة ليزر الدايود. حيث بلغت أعظم قدرة خارجة لهذا الليزر 240mW بنمط كاوسي TEM00 عند قدرة ضخ بصرية قدرها 850mW. تمت دراسة أداء الليزر عملياً وتحليلياً باستخدام مرآيا اقتران خرج ليزري ذات انعكاسيات مختلفة ، لقد أعطى التحليل النظري تكهناً جيداً لمعلمات أداء الليزر وكانت النتائج النظرية في تطابق جيد مع النتائج المقاسة عملياً بكفاءة تحويل بصرية- بصرية بلغت 28% وبمعدل كفاءة ميل بصرية 29%. وقد بينت الحسابات إن التذبذب الحاصل في القدرة الخارجة كان أقل من 1.5% خلال 10 دقائق.


Article
Deposited Nanostructure Cds Thin Film by Using Pulse Laser Deposition Technique for Fabrication of Heterojunction Solar Cell
ترسيب اغشية كادميوم سلفايد الرقيقة النانوية باستخدام تقنية الليزر النبضي لتصنيع خلية شمسية هجينة

Author: Heba Salam Tareq
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 2 Part (B) Scientific Pages: 313-320
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study, nanostructure Cadmium sulfide (CdS) thin films on Si P-type substrates heterojunction solar cell has been made by using a pulsed 532 nm Nd:YAG laser. Deposition of films is achieved at 200 °C substrate temperatures and oxygen pressure 10-1 Torr. X-ray diffraction (XRD), Scanning electron microscopy (SEM), atomic force microscope (AFM) and UV-VIS transmittance analyses were employed to characterize thin films. XRD measurements approved that CdS film is a hexagonal Wurtzite structure. The morphology of deposited films were characterized by scanning electron microscope (SEM) and atomic force microscope (AFM), the grain size value (18) nm and rms roughness values are (12.6 nm) for thin films deposited at 200ºC. UV-VIS transmittance measurements have shown that our films are highly transparent in the visible wavelength region, with an average transmittance of ~90% . The direct optical band gap of the film has been found to be 2.2 eV.The photovoltaic characteristics included short circuit current (Jsc), open circuit voltage (Voc), where the maximum (Jsc) and (Voc)obtained at AM1 were 29.3 (mA cm-2) and 635(mV), respectively. The fill factor (FF) was (0.44). The fabricated cell exhibits good performance with 7.8 % conversion efficiency.

في هذا البحث , تم ترسيب اغشية رقيقة نانوية من الكادميوم سلفايد على قواعد من السليكون الاحادي البلورة من النوع القابل لتصنيع خلايا شمسية هجينة باستخدام ليزر النيودميوم-ياك النبضي ذو الطول الموجي 532 نانو متر.تم ترسيب الاغشية عند درجة حرارة قاعدة 200 درجة مئوي. اظهرت قياسات الاشعة السينية ان الاغشية المحضرة ذات طور الفرتزايت السداسي .حددت خصائص طبوغرافية السطح من خلال قياس المجهر الالكتروني الماسح و مجهر القوى الذرية , حيث بلغت قيمة الحجم الحبيبي18) ) نانو متر وقيمة خشونة السطح (12.6) نانومتر للأغشية المحضرة بدرجة حرارة قاعدة( 200) مئوي.اوضحت نتائج مطياف الاشعة المرئية والفوق البنفسجية امتلاك غشاء الكادميوم سلفايد نفاذية بلغت بحدود 90% و بلغت قيمة فجوة الطاقة المياشرة (2.2 الكترون.فولط) درست الخواص الفولطائية المتمثلة بتيار الدائرة القصيرة (Jsc) وفولتية الدائرة المفتوحة (Voc) بالاضافة لعامل الملئ (FF) ووجد ان اعظم قيمة لكل من (Jsc) و (Voc) لحالة AM1 هي 29.3 (mA cm-2) و 635(mV), على التوالي وان قيمة عامل الملئ هي (0.44) .الخلية المصنعة اظهرت قيمة كفاءة جيدة بلغت 7.8%.


Article
Effect of concentrations ratios of NiO on the efficiency of solar cell for (CdO)1-x(NiO)x thin films
تأثير نسب تراكيز أوكسيد النيكل على كفاءة الخلية الشمسية لاغشية أوكسيد الكادميوم المشوبة بأوكسيد النيكل بدرجة حرارة الغرفة ودرجة 723 كلفن

Authors: Suaad Khafory سعاد غفوري --- Kadhim A. Aadim كاظم عبد الواحد عادم --- Ghasaq Ali غسق علي
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2017 Volume: 15 Issue: 33 Pages: 63-70
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

CdO:NiO/Si solar cell film was fabricated via deposition of CdO:NiO in different concentrations 1%, 3%, and 5% for NiO thin films in R.T and 723K, on n-type silicon substrate with approximately 200 nm thickness using pulse laser deposition. CdO:NiO/n-Si solar cell photovoltaic properties were examined under 60 mW/cm2 intensity illumination. The highest efficiency of the solar cell is 2.4% when the NiO concentration is 0.05 at 723K.

تم ترسيب اغشية أوكسيد الكادميوم المشوبة باوكسيد النيكل على قواعد من السيليكون من النوع السالب بتقنية الليزر النبضي، تم حساب سمك الغشاء لتراكيز معينة هي 1%،3%،5% من أوكسيد النيكل لدرجة حرارة الغرفة ودرجة 723 كلفن، وجد 200 نانومتر وتم قياس أيضا كفاءة الخلية تحت شدة ضوء مقدارها 60 ملي واط/سم2، وتم إيجاد اعلى كفاءة للخلية الشمسية هي 2.4% عند تركيز 0.05لاوكسيد النيكل في درجة 723 كلفن.


Article
Study effect of window and BSF layers on the properties of the CZTS / CZTSe solar cell by SCAPS–1D
دراسة تأثير الطبقة النافذة وطبقة BSF على خصائص الخلية الشمسية eCZTS / CZTS باستخدام SCAPS - 1D

Authors: Alaa H. Najim علاء حسين نجم --- Ayed N. Saleh عايد نجم صالح
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2019 Volume: 24 Issue: 3 Pages: 77-83
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

The solar cell CZTS / CZTSe was studied using SCAPS-〖1D 〗^* computer simulator. It was noted that increasing the thickness of the absorber layer p-CZTSe from 250nm to 5μm leads to increase the IV curve. thus increasing the values of Voc, Jsc, FF,

لقد تم دراسة الخلية الشمسية CZTS/CZTSe باستخدام المحاكي الحاسوبي SCAPS-1D, وقد تبين أن زيادة سمك طبقة الإمتصاص p-CZTSe من 250nm إلى 5µm يعمل على زيادة المنحني I-V وبذلك تزداد كل من قيم Voc، Jsc ، FF ،

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (9)


Year
From To Submit

2019 (1)

2017 (2)

2014 (1)

2013 (1)

2012 (1)

More...