Studying the effect of a new polyamide as adhesive for wood-wood surfaces

Authors: Mohammad N. AL-Baiati --- Laith B. AL-Asady --- Hawraa H. AL-Zubadi --- Saja A. Abd-Alkareem
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 1 Issue: المؤتمر العلمي الاول للتربية للعلوم الصرفة Pages: 15-21
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this research, a new copolyamid was prepared from reaction Aceglutamide with Formaldehyde by esterfication process, and used this copolymer as adhesive between wood – wood surface. Five different weight ( 0.2, 0.4 , 0.6, 0.8 & 1.0 gm ) from the prepared copolymer respectively, were used as adhesive to prepared the specimens of wood / adhesive . Four standard test methods were used to measured the adhesion properties which are; ASTM: D-790, ASTM: D- 695, ISO – 179 &ASTM: D-638 .The results obtained from these tests indicated that, the specimens of wood / adhesive containing 1.0 gm from the prepared copolymer have high values in all standard tests; Impact strength was 45 MPa, Compressive strength was 40 MPa, Flexural strength was 250 MPa and Tensile strength was 8150.41 MPa ; compared with the other specimens which contain on less weight from the prepared copolymer.


Article
Studying the effect of a new polyamide as adhesive for woodwood surfaces which experiment in the Holly Karbala
دراسة تأثير بولي أمايد جديد كلاصق لسطوح خشب – خشب، والتي جربت في كربلاء المقدسة

Author: Ass. Prof. Dr. Mohammad Nadhum Bahjat AL-Baiati أ.م.د محمد ناظم بهجت البياتي
Journal: KARBALĀʾ HERITAGE Quarterly Authorized Journal Specialized in Karbalāʾ Heritage مجلة تراث كربلاء ISSN: 23125489 24103292 Year: 2015 Volume: 2 Issue: ع2 -ج2 Pages: 282-266
Publisher: Shiite Endowment ديوان الوقف الشيعي

Loading...
Loading...
Abstract

AbstractIn this research, a new polyamide was prepared from reactionAceglutamide with Formaldehyde by esterfication process, andused this copolymer as adhesive between wood – wood surface.Five different weights (0.2, 0.4, 0.6, 0.8 & 1.0 gm) from the preparedcopolymer respectively were used as adhesive to preparethe specimens of wood / adhesive. Four standard test methodswere used to measured the adhesion properties which are; ASTM:D-790, ASTM: D- 695, ISO – 179 & ASTM: D-638 .This adhesive has been used of large quantities of this resin appliedin three carpentry workshops in the province of holly Karbalain the area (Ekd carpenters) for a period of six months and hasgiven good results when used in practice in the manufacture ofwooden furniture.The results obtained from these tests indicated that, the specimensof wood / adhesive containing 1.0 gm from the preparedcopolymer have high values in all standard tests; Impact strengthwas 45 MPa, Compressive strength was 40 MPa, Flexural strengthwas 250 MPa and Tensile strength was 8150.41 MPa ; comparedwith the other specimens which contain on less weight from theprepared copolymer

الملخصتم في هذا البحث تحضير بولي أمايد مشترك جديد من تفاعل edimatulgecA معالفورمالديهايد بواسطة عملية الأسترة ، وأستخدام هذا البوليمر المشترك كلاصق بينسطوح خشب – خشب . خمسة أوزان مختلفة ) 6.o، 4.o، 2.0 ، 8.0 و 0.1 غرام(من البوليمر المشترك المحضر على التوالي ، أستخدمت كلاصق لتحضير عينات خشب /لاصق .أربعة طرق قياسية ، أستخدمت لقياس الخواص اللصوقية وهي : 097 -D : MTSA ،971 :OSI ، 956 -D:MTSA و 836 -D:MTSA .تم استخدام كميات من هذا الراتنج تطبيقا في ثلاثة ورش نجارة في محافظة كربلاء المقدسةفي منطقة )عكد النجارين ( ولمدة ستة اشهر واعطت نتائج جيدة عند استخدامها عمليا فيتصنيع الأثاث الخشبي .النتائج التي تم التوصل اليها تشير الى أن عينات خشب / لاصق الحاوية على mg 0.1 منالبوليمر المشترك المحضر يمتلك قيم عالية في جميع الأختبارات القياسية ، قوة الصدمة 54aPM ، قوة الأنضغاط aPM 04 ، قوة الأنحناء aPM 052 و قوة الشد 14.0518aPM ، مقارنة مع العينات الأخرى الحاوية على أوزان أقل من البوليمر المشترك المحضر