Article
Effect of silica fume on the mechanical properties of crushed brick concrete
تأثير مسحوق السيليكا على الخصائص الميكانيكية لخرسانة الطابوق المكسر

Author: Ghanim Mohammed Kamil
Journal: University of Thi-Qar Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية ISSN: 26645564/26645572 Year: 2014 Volume: 5 Issue: 2 Pages: 38-50
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

This paper presents an experimental investigation on the effect of silica fume on the mechanical properties of concrete obtained by replacing 50% of weight of stone aggregate by crushed clay-brick. The only variable considered in this study was the dosage of silica which it is a percent of cement weight, the percent values of replacement silica fume are (0%, 2%, 4%, 6%, and 8%) of cement weight. The comparative study is focus on the effect of the silica fume on this type of concrete not the effect of replacement of crushed brick. The added silica fume has active effect on the strength of crushed brick concrete. The effect of using silica fume on compressive strength is different for the different replacement of silica fume and it is more active for the 2% replacement at 7 days age, while the replacement that yield best enhancement at 28 days is 4%. The compressive strength for 28 days age is about 27.5 MPa,29.5 MPa, 38.5 MPa,31.4MPa, and 10MPa,for (0%, 2%,4%,6%, and8%) of replacement silica percent.Furthermorethe bestincreasing in tensile strength is at 2%while there is a smallgradually increasing in gain in modulus of rupture with using silica fumeuntil 6%, which beyond the least value it starts to drop.The highlevel which is observed in this study beyond 6% reducesthe gain in strength of compressive at 28 days and it gets a compressive strength less than the control value at 7 days. Furthermore it gets a reduction in tensile strength and modulus of rupturein at 28days.

يقدم هذا البحث دراسة حول تأثير مسحوق السيلكا على الخصائص الميكانيكية للخرسانة الناتجة من استبدال 50% من وزن الركام الصخري بوزن مماثل من ركام الطابوق الطيني المكسر. المتغير الوحيد المعتبر في هذه الدراسة هو كمية مسحوق السيليكا المضاف كنسبة من السمنت، كميات الاستبدال للسيليكا هي (0%،2%,4%,6%, 8%) من وزن السمنت.الدراسة مركزة حول تأثير السليكا على هذا النوع من الخرسانة وليس على نسبة الاستبدال من ركام الطابوق المكسر.الكميات المضافة من مسحوق السيليكا تمتلك تأثيرا على مقاومة خرسانة الطابوق المكسر. التأثير مختلف بأختلاف النسب لمسحوق السيليكا وهذا التأثير ذو فعالية اكثر عند 2% استبدال بعمر 7 ايام، بينما نسبة الاستبدال التي حققت افضل تحسين للمقاومة بعمر 28 يوم كانت 4%.مقاومة الانضغاط للنماذج بعمر 28 يوم هي كالاتي (27.5، 29.5،38.5 ، 31.4 ، 10) ميكا باسكال لنسب الاستبدال (0%،2%،4%،6%،8%) على التوالي، كذلك الزيادة الافضل في مقاومة الشد كانت عند نسبة استبدال 2%، بينما كان هناك ازياد تدريجي في كسب المقاومة في معامل الانثناء الى حد 6% ، و بعد هذه النسبة تبدأ المقاومة بالتناقص. المستوى العالي لنسبة استبدال مسحوق السيليكا الملاحظ بعد ال6% استبدال في هذه الدراسة قلل الكسب في المقاومة لمقاومة الانضغاط بعمر 28 يوم واعطى مقاومة انضغاط اقل مقارنة بالنموذج المرجعي بعمر 7 يوم . كذلك قلل ومقاومة الشد ومعامل الانثناء بعمر 28 يوم.


Article
Effect of silica fume on the mechanical properties of crushed brick concrete
تأثير مسحوق السليكا على الخصائص الميكانيكية لخرسانة الطابق المكسر

Author: Ghanim Mohammed Kamil
Journal: University of Thi-Qar Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية ISSN: 26645564/26645572 Year: 2015 Volume: 6 Issue: 1 Pages: 87-99
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

This paper presents an experimental investigation on the effect of silica fume on the mechanical properties of concrete obtained by replacing 50% of weight of stone aggregate by crushed clay-brick. The only variable considered in this study was the dosage of silica which it is a percent of cement weight, the percent values of replacement silica fume are (0%, 2%, 4%, 6%, and 8%) of cement weight. The comparative study is focus on the effect of the silica fume on this type of concrete not the effect of replacement of crushed brick. The added silica fume has active effect on the strength of crushed brick concrete. The effect of using silica fume on compressive strength is different for the different replacement of silica fume and it is more active for the 2% replacement at 7 days age, while the replacement that yield best enhancement at 28 days is 4%. The compressive strength for 28 days age is about 27.5 MPa,29.5 MPa, 38.5 MPa,31.4MPa, and 10MPa,for (0%, 2%,4%,6%, and8%) of replacement silica percent.Furthermorethe bestincreasing in tensile strength is at 2%while there is a smallgradually increasing in gain in modulus of rupture with using silica fumeuntil 6%, which beyond the least value it starts to drop.The highlevel which is observed in this study beyond 6% reducesthe gain in strength of compressive at 28 days and it gets a compressive strength less than the control value at 7 days. Furthermore it gets a reduction in tensile strength and modulus of rupturein at 28days.


Article
Effect of Polypropylene Fibers on Properties of Mortar Containing Crushed Brick as Aggregate
تاثير الياف البولي بروبلين على خواص المونه الحاوية على ركام الطابوق المكسر

Authors: Shakir A. Salih --- Maha E. AL-Azaawee
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 12 Pages: 1508-1523
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

More recently there has been a great attention towards converting wastematerials by- products into useful materials as aggregate in concrete industry.It is thus aimed in this study to investigate the possibility of using waste brickas suitable materials and alternative to the natural aggregate in the productionof lightweight mortar.The essential objective of this work is to study the mechanical properties oflightweight mortar containing different percentages of polypropylene fiberwith high range water reducing agent. The effective synergy of this admixtureon the properties of mortars is also investigated. Compressive strength,splitting tensile strength, thermal conductivity and drying shrinkage tests wereconducted on reference and polypropylene fiber reinforced mortar specimensat various ages of curing (7, 14, 28, 60 and 90 days) respectively.The results show a significant increasing in splitting tensile strength withthe increment of fibers content. Although, a considerable reduction inworkability is recorded as increasing the fiber content. Which is controlled byusing high range water reducing admixture. All mixes show acceptable valuesfor thermal insulation with regards to ACI 213-87 thermal insulationrecommendations.

وجود أهتمام كبيرنحو تحويل مخلفات المواد الى مواد مفيدة كركام في الصناعة  لوحظ مؤخراالخرسانية. لهذا تهدف هذه الدراسة الى البحث عن أمكانية أستخدام الطابوق المكسر كمواد مناسبة و بديلةللركام الطبيعي في أنتاج الملاط الخفيف الوزن.أن الغرض الرئيسي من هذا البحث هو التعرف على الخصائص الميكانيكية للملاط المسلح بنسبمختلفة من ألياف البولي بروبيلين مع المضاف المقلل للماء بدرجة عالية’ أضافة الى دراسة تأثير هذاالمضاف على جميع الخواص. تم اجراء فحوصات مقاومة الانضغاط ’ مقاومة الشد (غير المباشر)’الموصلية الحرارية و انكماش الجفاف لخلطات (الملاط) المرجعية والحاوية على ألياف البولي بروبيلين60 , و 90 يوم). ,28 , خلال فترات مختلفة من معالجة الخرسانة ( 14,7بينت النتائج زيادة ملحوظة في مقاومة شد الانفلاق مع زيادة محتوى الالياف على الرغم من تسجيلانخفاض مناظر فبي قابلية التشغيل كلما زاد محتوى الالياف. وقد تمت السيطرة على هذا الانخفاض بقابليةالتشغيل من خلال استخدام المضاف المقلل للماء بدرجة متفوقة. بينت جميع الخلطات قيم مقبولة للعزل. ACI 213- الحراري بالمقارنة مع توصيات العزل الحراري الخاصة بمعهد الخرسانة الامريكي 87


Article
PROPERTIES OF SUSTAINABLE HIGH PERFORMANCE LIGHTWEIGHT AGGREGATE CONCRETE REINFORCED WITH FIBERS
خواص خرسانة الركام الخفيف الوزن عالية الاداء والمستدامة المسلحة بالالياف

Loading...
Loading...
Abstract

يهدف هذا البحث الى انتاج خرسانة الركام خفيف الوزن عالية الاداء والمستدامة تحتوي على مكسر الطابوق الطيني المعاد تدويره من مخلفات البناء كركام خشن خفيف الوزن ومسلحة بالالياف الاحادية والهجينة المزدوجة والثلاثية بانواع ونسب باعية مختلفة. تم تحضير خرسانة عالية الاداء من مكسر الطابوق الطيني الخفيف الوزن بمقاومة انضغاط 41.2 نيوتنمم2 و كثافة جافة 1930 كغمم3 بعمر 28 يوم. الالياف المستخدمة تتضمن, الياف فولاذية معقوفة النهاية بنسبة باعية 60 (نوع S1 ), الياف بلاستك بنسبة باعية63, الياف فولاذية دقيقة معقوفة النهاية بنسبة باعية65 (نوع S ), والياف البولي بروبلين الدقيقة بنسبة باعية667. تم اعداد ست خلطات خرسانية تتضمن على, الخلطة المرجعية بدون الياف , خلطتان مسلحة بنوع واحد من الالياف (الالياف الفولاذية نوع S1 أو الياف البلاستك وبنسبة حجمية (0.75%, اثنان من الخلطات المسلحة بالالياف الهجينة المزدوجة ( الالياف الفولاذية نوع S 0.5%+ الياف بولي بروبلين0.25% وخلطة الياف البلاستك 0.5% + الالياف الفولاذية نوع S 0.25 %) والخلطة الخرسانية الهجينة ثلاثية الالياف (0.25 % ( الياف فولاذية نوع S1 +الياف البولي بروبلين + الياف فولاذية نوع S). تم دراسة الخواص الطرية للخرسانة (قابلية التشغيل والكثافة الطرية ) وخواص الخرسانة المتصلبة (الكثافة الجافة, مقاومة الانضغاط, مقاومة شد الانثناء, مقاومة الشد الانشطاري و الامتصاص للماء ). بصورة فان نماذج الخرسانة العالية الاداء الخفيفة الوزن والمسلحة بالالياف الاحادية والهجينة (الثنائية والثلاثية ) أظهرت زيادة مهمة في مقاومة الشد الانشطاري مقاومة شد الانثناء مقارنة بالنماذج الخرسانية المرجعية (بدون الالياف). ان نسب الزيادة في مقاومة الشد الانشطاري للنماذج المسلحة بالالياف الفولاذية الاحادية هي 55.8%, 65.9,%, 82% و 91.9%, بينما نسب الزيادة للنماذج المسلحة بالالياف البلاستكية الاحادية هي 34%, 45.5%, 61.5% و71.2% للاعمار 7, 28, 60 و 90 يوماً على التوالي بالمقارنة مع النماذج غيرالمسلحة بالالياف. ان اعلى مقاومة شد انشطاري و ومقاومة شد انثناء سُجلت للنماذج المسلحة بالالياف الهجينة ثلاثية الالياف. ان نسب الزيادة لمقاومة الشد الانشطاري للنماذج المسلحة بالالياف الهجينة ثلاثية الالياف هي 57.2%, 68.6 %, 87.5%, 101.8%, بينما نسب الزيادة لمقاومة شد انثناء هي 48 %, 59.6 %, 66.9%, 70.7%, للاعمار 7, 28, 60 و 90 يوماً على التوالي بالمقارنة مع النماذج غيرالمسلحة بالالياف.

In this investigation, sustainable High Performance Lightweight Aggregate Concrete (HPLWAC) containing recycled crushed clay brick from construction and demolition waste as coarse lightweight aggregate (LWA) and reinforced with mono fiber, double and triple hybrid fibers in different types and aspect ratios were produced. High Performance crushed brick lightweight aggregate concrete mix with compressive strength of 41.2MPa, oven dry density of 1930 kg/m3 at 28 days were prepared. The Fibers used including, macro hooked steel fiber with aspect ratio 60 (type S1), macro crimped plastic fiber (P) with aspect ratio 63, micro steel fiber with aspect ratio 65 (type S), and micro polypropylene fiber (PP) with aspect ratio 667. Six HPLWAC mixes were prepared including, one plain concrete mix (without fiber), two mono fiber reinforced concrete mixes ( reinforced with either steel fiber type S or plastic fiber with 0.75% volume fraction), two double hybrid fiber reinforced concrete mixes (0.5% steel fiber type S +0.25% polypropylene fiber and 0.5% plastic fiber + 0.25% steel fiber type S), and one mix with triple hybrid fiber (0.25% steel fiber type S1+0.25% polypropylene fiber +0.25% steel fiber type S). Fresh (workability and fresh density) and hardened concrete properties (oven dry density, compressive strength, splitting tensile strength, flexural strength and absorption) were studied. In general mono and hybrid (double and triple) fiber reinforced HPLWAC specimens give significant increases in splitting tensile strength and flexural strength compared with plain HPLWAC specimens. The percentages increase in splitting tensile strength for specimens with mono steel fiber are 55.8%, 65.9%, 82% and 91.9%, while for specimens with mono plastic fiber the percentages increase are 34%, 45.5%, 61.5% and 71.2% at 7, 28, 60, 90 days age respectively relative to the plain concrete. The maximum splitting tensile and flexure strengths were recorded for triple hybrid fiber reinforced HPLWAC specimens. The percentages increase in splitting tensile strength for triple hybrid fiber reinforced specimens are 57.2%, 68.6%, 87.5% and 101.8%, while the percentages increase in flexure strength are 48%, 59.6%, 66.9% and 70.7% at 7, 28, 60 and 90 days age respectively relative to the plain concrete specimens.


Article
Effect of Crushed Brick on Some Load-Bearing Hollow Concrete Block Properties
تأثير اضافة الطابوق المكسر على بعض خواص الكتل الخرسانية المجوفة المحملة

Author: Mushtaq Sadiq Radhi مشتاق صادق راضي
Journal: Albahir journal مجلة الباهر ISSN: 23125721 Year: 2016 Volume: 4 Issue: 7+8 Pages: 115-131
Publisher: AL-Abbas Holy Shrine العتبة العباسية المقدسة

Loading...
Loading...
Abstract

In this research, the effect of using crushed brick as an alternative to the coarse aggregate onsome load-bearing hollow concrete block properties were investigated.The hollow concrete blocks with standard dimension (150 ×150×300) mm, were produced. Themix proportions were (1) cement to (6) total aggregate. The course aggregate was replaced bythe crushed brick in volumetric percent at rate of (25 %, 50%, 100%), then the effect of thereplacement was investigated on some concrete block properties such as compressive strength ,density, absorption and thermal and sound insulation in different ages (7, 14, 28) days. According tothe results, crushed brick can be used as course aggregate to produce load-bearing hollow concreteblocks class B with medium concrete density that can be used in interior wall or exterior wall thatprotected from moisture and weather conditions. The optimum percent of replacement of crushedbrick was (50%). Some properties like density, thermal insulation was improved, while, the otherproperties like compressive strength, absorption, sound insulation was kept at acceptable range. Itcan be concluded that the effect of the crushed brick as aggregate on concrete blocks properties,compared to normal aggregate, resulting from the combined effect low density, low crushing value,surface roughness, and its contribution to the process of internal curing for the concrete. Also, theuse of crushed brick has an environmental effect in terms of its contribution to the recycling processfor this waste materials and save the environment from it, as well as to reduce the pressing onsources of natural aggregates, which considered a national resources and must be preserved and beused in optimal utilization.

في هذا البحث تم دراسة تاثير استخدام الطابوق المكسر كبديل عن الركام الخشن على بعض خواص الكتل الخرسانية المجوفة المحملة حيثتم انتاج كتل خرسانية مجوفة بابعاد قياسية ) 300 × 150× 150 ( ملم وبنسب خلط اسمنت الى ركام اعتيادي 1 : 6 ومن ثم تم استبدال الركامالخشن الاعتيادي بالطابوق المكسر وبنسب حجمية )% 25 و% 50 و% 100 ( ومن ثم دراسة تاثير الاستبدال على بعض خواص الكتل الخرسانيةاالمنتجة مثل تحمل الضغط والكثافة والامتصاص والعزل الحراري والعزل الصوتي وباعمار ) 7 و 14 و 28 ( يوم. وفقا للنتائج بالامكان استخدامالطابوق المكسر كركام خشن في انتاج كتل خرسانية مجوفة ذات كثافة خرسانة متوسطة ومن الصنف ب المستخدم في الجدران الحاملة للاثقالالداخلية او الجدران الحاملة للاثقال الخارجية المحمية من الظروف الجوية والرطوبة حيث كانت افضل نسبة استبدال للطابوق المكسر كبديل عنالركام الاعتيادي فى انتاج الكتل هي )% 50 ( حيث تم تحسين الكثافة والعزل الحراري مع المحافظة على الخواص الاخرى مثل مقاومة الانضغاطوامتصاص وعزل صوتي ضمن الحدود المقبولة . ان تأثير ركام الطابوق المكسر على خواص الكتل الخرسانية ناتج من التاثير المشترك لقلة الكثافةوالتحمل وخشونة السطح ومساهمته في عملية الانضاج الداخلي للخرسانة مقارنة مع الركام الاعتيادي. ان استخدام الطابوق المكسر، اضافة الىتأثيره الايجابي على الخواص المذكورة سابقا، له اثر بيئي مزدوج حيث يساهم في عملية اعادة التدوير لهذة المخلفات ويخلص البيئة منها وكذلكيساهم في تقليل الضغط على مصادر الركام الطبيعية والتي تعتبر ثروة وطنية يجب المحافظة عليها واستخدامها الاستخدام الامثل .


Article
The Use of Crushed Brick Waste for The Internal Curing In Cement Mortar
استخدام مخلفات الطابوق المحطم في الانضاج الداخلي في مونة السمنت

Author: Alaa Ahmed Shakir
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2017 Volume: 5 Issue: 1 Pages: 16-21
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

Internal curing has become a modern technology holds promises for making a durable mortar and decreasing early-age cracking. Since mortar service life is a crucial factor of providing sustainable structures, internal curing can provide a distinct contribution to increase the sustainability of our nation’s building. This study shows results of an experimental investigation of using crushed brick waste (CBW) in cement mortar mixtures prepared by substituting sand by some percentages (5, 10, 15, 20 and 25%) of (CBW). Three curing regimes were adopted in this study: water curing by immersing specimens in water for 28 days, partially water curing by immersing specimens in water for 3 days and left them in laboratory for 24 days and air curing in laboratory for 28 days without immersing samples in water to recognize an ideal methodology for determining whether a given (CBW) can be used for internal curing in cement mortar. Fresh density, hardened density, compressive strength, water absorption, and modulus of rupture were tested. Results indicated that fresh and hardened density, compressive strength and modulus of rupture were decreased with the addition of (CBW). However, they were higher for mortars cured in air conditions than those cured in water and partially water curing. Water absorption was increased with the increase of (CBW). It was demonstrated that air cured mortar give good results for mechanical properties as compared with water cured mortar, hence (CBW) can be used for internal curing in cement mortar especially in finishing works.

ان العمر الخدمي لقد أصبح الانضاج الداخلي تكنولوجيا حديثة يحمل وعودا لانتاج مونة دائمة وتقليل التشققات في سن مبكرة. حيث للمونة هي العامل الحاسم في بناء المنشآت المستدامة. الإنضاج الداخلي يقدم مساهمة متميزة لزيادة استدامة بناء أمتنا. تبين هذه الدراسة نتائج فحص تجريبي لاستخدام الطابوق المحطم في خليط مونة السمنت عن طريق استبدال الرمل في بعض النسب (5، 10، 15، 20 , 25٪) من مخلفات الطابوق المحطم. تم اعتماد ثلاثة أنظمة انضاج في هذه الدراسة: الانضاج بالماء عن طريق غمر العينات في الماء لمدة 28 يوما، انضاج جزئي بالماء عن طريق غمر العينات في الماء لمدة 3 أيام، وتركهم في المختبر لمدة 24 يوما والانضاج بالهواء هو ترك العينات في المختبر لمدة 28 يوما دون غمر العينات في الماء للحصول على منهجية مثالية لتحديد امكانية استخدام الطابوق المحطم للانضاج الداخلي في مونة الأسمنت. تم اختبار الكثافة الطازجة ,الكثافة الصلبة، قوة الضغط، امتصاص الماء، ومعامل الكسر. أشارت النتائج إلى أن الكثافة الطازجة , الصلبة، قوة الضغط ومعامل الكسر قد انخفضت مع إضافة الطابوق المحطم ، ومع ذلك سجلت النتائج قيم اعلى للمونة التي تم انضاجها في الهواء ممقارنة بالعينات التي تم انضاجها في الماء وجزئيا بالماء. امتصاص الماء قد ارتفع مع زيادة نسبة استبدال الطابوق المحطم بديل عن الرمل المضاف الى المونة .برهنت الدراسة ان المونة التي تم انضاجها في الهواء قد اعطت نتائج جيدة للخواص الميكانيكية بالمقارنة مع المونة التي تم انضاجها بالماء، وبالتالي يمكن استخدام الطابوق المحطم للانضاج الداخلي في مونة الأسمنت خاصة في اعمال النهاء .

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (5)

Arabic (1)


Year
From To Submit

2017 (2)

2016 (1)

2015 (1)

2014 (1)

2008 (1)