Article
Synthesis and Studying Dielectric Properties of Mixed Nanoferrites
تحضير ودراسة بعض الخواص الميكانيكية المتراكبة

Authors: Zainab I. Dhary --- Mohammed S. Hamza --- Fadhil A. Chyad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 1 Part (A) Engineering Pages: 154-164
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Based on a low temperature route (sol-gel autocombustion) a nano-ferrite CoFe2O4and Li0.5Fe2.5O4 and different percentages of cobalt-ferrite are synthesized. The crystalline structure by XRD and dielectric properties with TEM micrographs are presented. The XRD (crystallite size and lattice parameter) are determined which affected by cobalt content. TEM micrographs show a nano-particles in the range of (8-20) nm which correlate with crystallite size. Dielectric properties (dielectric constant, loss tangent and dielectric loss factor) are decreased with frequency and cobalt content.

استخدمت طريقة السول-جيل (الاحتراق الذاتي) لتحضير فيرايت الكوبلت والليثيوم النانوي وكذلك خلط نسب مختلفة من الكوبلت مع الليثيوم. تم دراسة التركيب البلوري باسنخدام حيود الاشعة السينية والتركيب المجهري باستخدام المجهر الالكتروني النافذ بالاضافة الى قياس الخواص العزلية .تم حساب الحجم البلوري و ثابت الشبكية حيث تاثر كليهما باضافة فيرايت-الكوبلت وان صور المجهر الالكتروني النافذ بينت ان معدل الحجم الحبيبي كان من(8-20)نانومتر والتي تكون متقاربة مع الحجم البلوري. اما الخواص العزلية (ثابت العزل, ظل فقدان الزاوية, معامل الفقدان العزلي) فقد تناقصت مع التردد مع محتوى الكوبلت.


Article
Effect of decomposition temperature on crystallite size and strain for alumina
تأثير التفكك الحراري على المقاس الحبيبي والانفعال للألو مينا Al2O3

Authors: Ghazi K.Saeed غازي كمال سعيد --- Sattar A.Abass ستار عبود عباس
Journal: Univesity of Thi-Qar Journal مجلة جامعة ذي قار العلمية ISSN: 66291818 Year: 2015 Volume: 10 Issue: 1 Pages: 1-8
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

The crystallite size and strain of Al2O3 ceramic powder have been determined from x-ray line-broadening analysis at different decomposition temperatures. The Al2O3 powder have been prepared from decomposition of aluminum hydroxide Al(OH)3 at different temperature which have been characterized by X-Ray diffraction (XRD) and Differential, Thermal Analysis (DTA) methods. Deconvolution of the experimental profiles by Fourier cosine coefficients has resulted in corrected values of crystallite size. The crystallite size has been found to increase with increasing decomposition temperature from 38nm at 1673k to 73nm at 1873k. Strain on the other hand decrease from 3.04×10-3 at 1673k to 1.14×10-3 at 1873k. Estimation of micro hardness on compacts of different crystallite size has shown that crystallite size may influence the bearing load that compact can endure

تم تحديد الحجم الحبيبي والانفعال لمسحوق الالومينا بواسطة تحليل الاتساع في خط حيود الأشعة السينية عند درجات حرارة مختلفة . حضر مسحوق الالومينا من التفكك الحراري لهيدروكسيد الألمنيوم Al(OH)3 عند درجات حرارة مختلفة والذي شخص بواسطة جهازي حيود الأشعة السينية وجهاز التحليل الحراري التفاضلي . درست قيم المقاس البلوري بأخذ جذر متوسط مربع الانفعال بواسطة تحليل الاتساع في خط حيود الأشعة السينية باستخدام طريقة فورير. وجد إن المقاس البلوري يزداد بزيادة التفكك الحراري من 38 نانومتر عند درجة حرارة1673 كلفن إلى 73 نانومتر عند 1873 كلفن . من جانب أخر الانفعال يقل من 3-10x3.04 عند 1673 كلفن إلى 3-10x1.14عند 1873 كلفن. يعطي المسحوق المكبوس للالومينا صلادة مجهريه تزداد كلما قل الحجم الحبيبي .


Article
Effect of Deposition Temperature on Optical and Crystallographic Properties of CsI Thick Films Deposited using Spray Pyrolysis

Author: J.H. Khulaef
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 2 Part (B) Scientific Pages: 195-203
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

A deposited layer of CsI has been prepared at different substratetemperatures using spray pyrolysis technique. The X Ray diffraction of CsIfilms reveals special pattern peaks (110), (200), (211), (220), (310) and (321).From transmission spectra we calculated the energy gap of CsI films whichincrease with increasing deposition temperature for direct transition isestimated.


Article
Annealing Temperature Dependent Structural, Optical and Electrical Properties of Thermally Deposited CdSe Thin Films

Author: Mohammad M. Ali
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2018 Volume: 44 Issue: 1A Pages: 33-46
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

CdSe thin films have been deposited on suitably cleaned glass substrates by thermal evaporation method. The pressure during evaporation was maintained at 10-6 to 10-5 Torr. The samples are annealed in vacuum for 2h at various temperatures and characterized by structural, optical and electrical properties. The crystal structure and lattice parameter of these films were determined from X-ray diffractograms. It was observed that the films have a polycrystalline hexagonal (wurtzite) structure with preferred orientation along (002) plane. The crystallite size, dislocation density and micro strain were calculated by considering high intense diffraction peaks of the as-deposited and annealed films. It was found that the average size of the crystallites increases and the average dislocation density decreases with increasing annealing temperature. Absorption and transmittance spectra of these thin films were studied using UV-visible double beam spectrophotometer in the wavelength range of 300 – 1100 nm. The energy band gaps have been determined using absorption spectra. The values of the optical band gap energy, Eg, decreased from 2.37 – 2.08 eV with increasing the annealed temperature. Dependence of optical band gap on crystallite size has also been studied. The electrical resistivity and activation energy of CdSe thin films are calculated by two probe resistivity measurements. The decrease in dc resistivity with increase the grain size was also noted.


Article
Synthesis, Structural and Optical Properties of Nanostructured ZnO Thin Films Prepared by Sol Gel Process

Author: F. A. Kasim
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2010 Volume: 36 Issue: 2A Pages: 16-21
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

Nanostructured ZnO thin films have been synthesized by Sol Gel process. The ZnO precursors were prepared by using zinc acetate dehydrate and a mixed solution of monoethanolamine and ethanol, and were prepared with Zn2+ concentration 0.5mole. The films were deposited on glass substrates by spin coating at 3000 rpm for 30s at room temperature. These films were postheated at 400oC for 1h at air. ZnO thin films have a polycrystalline and wurtzite structure. The crystallite size was determined by X-ray diffraction using Scherrer method. The crystallite size of ZnO thin film was 23.4nm. The transmittance spectra of ZnO films were 85% in the visible region from 600 to 800nm. The energy band gap is found to be 3.24 eV for ZnO film.

حضرت اغشية أوكسيد الزنك النانوتركيبية بواسطة عملية Sol Gel. وتم تحضيرها باستخدام خلات الزنك المائية ومحلول ممتزج من احادي اثانول امين ومذيب الايثانول وقد كان تركيز Zn (0.5 مول). وتم ترسيب المادة المحضرة على الزجاج بواسطة جهاز الطلاء عن طريق التدوير Spin Coating بسرعة قدرها 3000 دورة لمدة 30 ثانية وفي درجة حرارة الغرفة وتم الاحماء النهائي للاغشية بدرجة حرارة 400oC ولمدة ساعة واحدة. تم دراسة الشكل التركيبي للاغشية باستخدام الـ XRD، اذ امتلكت الاغشية الرقيقة لاوكسيد الزنك تركيباً متعدد التبلور وتركيب wurtzite. وتم حساب حجم التبلور باستخدم حيود الاشعة السينية بواسطة معادلة شرر، اذ وجد ان حجم تبلور غشاء أوكسيد الزنك هو 23.4nm . اثبتت دراسة الخصائص البصرية لاغشية اوكسيد الزنك من ملاحظة طيف النفاذية زيادة النفاذية من 85% فما فوق عند الطول الموجي 600nm لاغشية اوكسيد الزنك بتركيز 0.5 مول. كذلك أثبتت دراسة الخصائص البصرية لأغشية اوكسيد الزنك ان فجوة الطاقة كانت (3.24eV).