Article
تأثير التشويب بالنحاس على الخصائص التركيبية وفجوة الطاقة البصرية لأغشية اوكسيد النيكل النانوية المحضرة بطريقة المحلول الغروي

Authors: فؤاد شاكر هاشم --- نور علي سامي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 6 Pages: 1572-1584
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research deals with the study of the structural and optical energy gap of NiO nano films in thickness 100nm were deposited on a glass substrate using sol-gel spin coating technique . XRD results indicated that the films are polycrystalline and have cubic structure with a preferred orientation along (111) . The average grain sizes of the crystallites estimated form XRD data was found to lie in the range of 19.11-23.05 nm. Data of AFM indicate that the surface of films is smooth . The optical transmittance value of nano NiO film reaches to 94% in the VIS and NIR regions, while it is value of films deposited with 0.1mol%Cu reaches to (92)% which is important for its applications as window layers in solar cells .The values of optical energy gap of NiO and Cu doping by 0.01,0.05, 0.1mol% were equal to 3.73 and (3.61,3.49,3.42eV) respectively.

في هذا البحث دُرست الخصائص التركيبية وفجوة الطاقة البصرية لأغشية NiO النقية والمشوبة بالنحاس بتراكيز مختلفة 0,0.01,0.05,0.1mol%)) نانوية بالسمك 100nmرسبت على قواعد زجاجية بتقنية الطلاء الدوار Spin Coating)) . بينت نتائج فحوصات XRD أن جميع الأغشية متعددة البلورات من النوع ألمكعبي مع قمة حادة سائدة باتجاهية 111)) .وقد تم حساب الحجم الحبيبي من بيانات XRD ووجد انه يَزداد حجم الحبيبات بزيادة نسبة التشويب في المدى 19.11 nm-23.05. بيانات AFM أشارت إلى نعومة سطوح الأغشية النفاذية البصرية لغشاء NiO النانوي ذات مقدار كبير تصل إلى94%) ) ضمن المنطقة المرئية وتستمر إلى المنطقة تحت الحمراء القريبة, تناقصت لتصل إلى 92%)) مع التشويب عند نسبة Cu 0.1mol% وهذا يؤكد أمكانية استخدامها كطبقات نافذة في الخلايا الشمسية . قيم فجوة الطاقة البصرية لغشاء NiO والأغشية المشوبة بالنحاس بالنسب 0.01,0.05,0.1 mol% 0,هيeV (3.73,3.61, 3.49, 3.42) على التوالي .


Article
Noble Metals/NiO Core- Shell Based Gas Sensors
المعادن النبيلة / اوكسيد النيكل لب- قشرة كمتحسسات غازية

Author: Iftikhar M. Ali افتخار محمود علي
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2016 Volume: 57 Issue: 3A Pages: 1732-1741
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The application of novel core-shell nanostructure composed of Cu, Ag, Au/NiO to improve the sensitivity of pure NiO to H2S gas sensors is demonstrated in this study. The growth of Cu, Ag, Au/NiO core-shell nanostructure is performed by chemical reaction of NiO on metal nanoparticle (Cu, Ag and Au) that prepared by pulsed laser ablation (PLA( technique. This is to form the homogeneous structure of the sensors investigated in this report to assess their sensitivity in terms of H2S detection. These novel H2S gas sensors were evaluated at operating temperatures of 25 °C, 100 °C and at 150 °C. The result reveals the Cu, Ag, Au/NiO core-shell nanostructure present a good sensitivity at low working temperatures compared by pure NiO nanoparticles. These core-shell nanostructure sensors also possess the highest response (<32 s) and recovery (<28 s) values with greater repeatability seen for H2S sensors at low temperatures, unlike traditional sensors that only work effectively at much higher temperatures. The data in this study indicates the newly-developed Cu, Ag, Au/NiO core-shell nanostructure based sensors are highly promising for industrial applications.

التطبيق المبتكر للتركيب النانوي لب-قشرة المتكون من نحاس، فضة، ذهب / اوكسيد النيكل لتحسين تحسسية اوكسيد النيكل النقي قد تم إظهاره في هذه الدراسة. ان انماء التركيب النانوي لب-قشرة من نحاس، فضة، ذهب / اوكسيد النيكل يرسب بالتفاعل الكيميائي لأوكسيد النيكل مع جسيمات معدن النحاس، الفضة، الذهب النانوية المحضرة بتقنية الاجتثاث بالليزر النبضي لتكوين تركيب متجانس للمتحسسات لتقييم تحسسيتها في الكشف عن غاز كبريتيد الهيدروجين عند درجات حرارة 25، 100، 150 oم. وضحت النتائج بان التركيب النانوي لب-قشرة من نحاس، فضة، ذهب / اوكسيد النيكل له تحسسية جيدة عند درجات تشغيل واطئة مقارنة بأوكسيد النيكل النقي. ان المتحسسات ذات التركيب النانوي لب-قشرة تمتلك قيم استجابة سريعة بزمن استجابة سريع اقل من 32 ثانية وبزمن نزول اقل من 28 ثانية وبتكرارية جيدة لمتحسسات كبريتيد الهيدروجين عند درجات حرارية منخفضة مقارنة بالمتحسسات التقليدية التي تعمل بفعالية عالية فقط عند درجات حرارية عالية جداً. في هذه الدراسة تشير القيم الى امكانية تصنيع متحسسات جديدة ومطورة مبنية من التركيب النانوي لب-قشرة من نحاس، فضة، ذهب / اوكسيد النيكل لتطبيقات صناعية واعدة.

Keywords

NiO --- Cu/NiO --- Ag/NiO --- Au/NiO --- core shell --- nanostructure --- H2S --- gas sensor --- sensitivity.