Article
Study on Bond Strength of Bonded Gray Cast Iron

Authors: Awfa Abdul-Rassol Abdullah --- Rasha Rahman Rawhdan
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2014 Volume: 17 Issue: 2 Pages: 94-100
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In the present study, two gray cast iron specimens were diffusion bonded at the temperatures of 700, 750, 800, 850, and 900 °C, the furnace used atmosphericexperiment under a pressing load of 1 and 2 ton for 15, 30 and 60min. After diffusion bonding, shear test measurements of interface region were made. As a result, from the microstructural observations, a good bonding along the interface of the bonded couples were detected since the interface is free from voids and microcracks. To evaluate the bond strength, the shear test investigation was used. The actual bonded area was calculated by using a computer package called (Auto Cad 2006). The results shows that the bond strength increases with increasing the temperature and holding time. Fracturography of the interface was carried out by using optical microscope before and after the experiments. The microstructure results shows the formation of carbide. Its precipitation increases with increasing the bonding temperature and time.

يتضمن البحث دراسة الربط الانتشاري لحديد الزهر الرمادي بالظروف الجوية باستخدام طرق تسخن مختلفة 900,850,800,750,700°م، وباستخـدام قـوة كبـس2,1 طن بأزمان مختلفة 60,30,15 دقيقة لإيجاد الظروف العملية المناسبه التي تؤثر على متانة الربط. قيمت متانة الربط باستخدام فحص القص وأظهرت النتائج إن متانة الربط تزداد مع ازدياد درجات الحرارة وكذلك متانةالربـط تـزداد مع ازدياد الوقـت. استخدم برنامج(Auto Cad 2006) لحساب مساحه التماس. لوحظ عند استخدام غاز الاركون انه لم تتكون وصله ربط بسبب الاكسده. بعد استبيان النتائج التي تم الحصول عليها من الدراسة ألمختبريه تبين إن الوصلات المربوطة وجدت مقاومة قص قصوى تساوي 155.7 ميكاباسكال عند ربطها في درجه حرارة 900°م تحت قوة كبس 1 طن ولفترة تسخين 30 دقيقة. وتبين من اختبارات الفحص المجهري تكون أطواركاربيدية (Carbides) وترسيبها على سطح العينة وداخل السطح البيني.


Article
Optimization of Diffusion Bonding of Pure Copper (OFHC) with Stainless Steel 304L
امثلية وصلات الربط الانتشاري للنحاس خالي الأوكسجين عالي الموصلية مع الفولاذ المقاوم للصدأ 304L

Loading...
Loading...
Abstract

This work deals with determination of optimum conditions of direct diffusion bonding welding of austenitic stainlesssteel type AISI 304L with Oxygen Free High Conductivity (OFHC) pure copper grade (C10200) in vacuum atmosphere of (1.5 *10-5 mbr.). Mini tab (response surface) was applied for optimizing the influence of diffusion bonding parameters (temperature, time and applied load) on the bonding joints characteristics and the empirical relationship was evaluated which represents the effect of each parameter of the process. The yield strength of diffusion bonded joint was equal to 153 MPa and the efficiency of joint was equal to 66.5% as compared with hard drawn copper. The diffusion zone reveals high microhardness than copper side due to solid solution phase formation of (CuNi). The failure of bonded joints always occurred on the copper side and fracture surface morphologies are characterized by ductile failure mode with dimple structure. Optimum bonding conditions were observed at temperature of 650 ◦C, duration time of 45 min. and the applied stress of 30 MPa. The maximum depth of diffuse copper in stainless steel side was equal 11.80 µm.

يتضمن البحث تحديد الظروف المثالية للحام الانتشاري المباشر للنحاس خالي الأوكسجين_ عالي الموصلية مع الصلب المقاوم للصدأ الاوستنايتي نوع (304L) مختبريا. وقد تم ربط المعدنين في جو مفرغ من الهواء يصل الى (1*10-5 mbr) وقد تم استخدام برنامج (Minitab16) لمعرفة الظروف المثلى لربط المعدنين. ومن خلال استخدام البرنامج تم دراسة التاثير المشترك لعوامل الربط على قوة الربط. وقد اجريت فحوصات البنية المجهريه لمنطقة الربط الأنتشاري باستخدام المجهر الالكتروني الماسح (SEM-EDS) لمعرفة التركيب المجهري وعمق الانتشار في منطقة الربط والصلاده المايكروية والتحليل الطيفي (XRD) لمعرفة الأطوار التي تكونت في منطقة الربط ومن خلال الفحوصات تبين تكوّن محلول جامد بين النحاس والنيكل (CuNi) بوصفه طورا احاديا يعطي صفات جيده. تم ايجاد الظروف المثلى للربط هي عند درجة حرارة C◦650 وزمن ربط 45 دقيقه والجهد المسلط كان 30 ميكاباسكال. ولمعرفة قوة الربط تم اجراء فحص الشد لمنطقة الربط حيث كانت متانة الربط عند ظروف الربط المثلى تساوي 153 ميكاباسكال وذات كفاءة ربط 66.5% مقارنة بالنحاس وان عمق الأنتشار الذي تم الحصول عليه في منطقة الربط كان 11.80 µm.