Article
Studying the Effect of Ni Electroplating on Corrosion Behavior in Presence Ultra Fine Al2O3 and Sic
دراسة تأثير الطلاء الكهربائي بالنيكل مع مسحوق الالومينا وكاربيد السليكون فائقة النعومة على سلوك التآكل

Loading...
Loading...
Abstract

This work focuses on the effect of electro-deposition of nickel on corrosion behavior of mild steel substrate with ultra fine Al2O3 and SiC using the electroplating technology. The experimental results exhibited the substrate microstructure was sensitive to both current density and temperature. Grain growth were increased with increasing each of current density and temperature and thereafter decreased. Optimal values were 0.2A/cm2 and 45C°, respectively. Concentration of each Al2O3 and SiC were essential to electro-deposition, it was found 4gm/l after traditional weight loss technique was performed, it was found that corrosion rate of Ni and Ni- Al2O3 was deceased with exposure time in 3.5% NaCl solution whereas Ni-SiC exhibited higher corrosion rate. the addition Al2O3 was inhibited corrosion in acid solution.

ركز هذا البحث على تأثير الطلاء الكهربائي بالنيكل على سلوك التأكل لفولاذ متوسط الكاربون مع مسحوق كلا من الالومينا وكاربيد السليكون فائقة النعومة. أظهرت النتائج ان البنية المجهرية للمادة الأساس تتأثر بكل من كثافة التيار ودرجة الحرارة. نمو الحبيبات تزداد بزيادة كلا من التيار ودرجة الحرارة وبعد ذلك تقل. أفضل النتائج كانت هي عند 0.2 امبير سم2 و 45 م° . ان تركيز كلا من الالومينا وكاربيد السليكون أساسي في عملية الطلاء الكهربائي حيث وجد ان افضل تركيز هو 4 غم لتر. بعد انجاز تقنية فقدان الوزن التقليدية, وجد ان معدل التأكل عند الطلاء بالنيكل و نيكل-الومينا يقل مع زمن الغمر بمحلول كلوريد الصوديوم في حين اظهر معدلات عالية عند وجود كاربيد السليكون في المحلول. اما في المحاليل الحامضية فان الالومينا عملت كمانع للتأكل حيث قللت من قيمته مقارنة بالنيكل- كاربيد السليكون.


Article
Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel
الطلاء الكهربائي بالكروم الصلد وتحسين الخواص بالمعاملات الحرارية الكيمياوية (الكربنه الصلبة) لفولاذ منخفض الكاربون

Authors: Ahmed Salloum Abbas أحمد سلوم عباس --- Amin Dway Thamir أمين دواي ثامر --- Muna Khedier Abbas منى خضير عباس
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2009 Volume: 5 Issue: 4 Pages: 99-114
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research the hard chromium electroplating process, which is one of the common methods of overlay coating was used, by using chromium acid as source of chromium and sulphuric acid as catalyst since the ratio between chromic acid and sulphuric acid is (100 : 1) consequently. Plating process was made by applying current of density (40 Amp / dm2) and the range of solution temperature was (50 – 55oC) with different time periods (1-5 hr). A low carbon steel type (Ck15) was used as substrate for hard chromium electroplating. Solid carburization was carried out for hard chromium plating specimen at temperature (925oC) with time duration (2 hr) to be followed with quenching and tempering. The phase analysis was conducted by using X– ray diffraction. The examination results show that the chromium carbides in plating layer were (Cr23C6, Cr7C3). The microhardness of hard chromium plating specimen was measured, and the results show that the high hardness was about (907HV). After solid carburization the hardness values increase and the results show that the higher hardness for chromium plating layer on low carbon steel surface was (1276 HV). Wear apparatus type (Pin on Disc) was used to study dry sliding wear properties of low carbon steel (As received) and hard chromium plating specimens and solid carburized. The effect of applied normal load on wear rate was studied with weighting method using five normal loads (5, 10, 15, 20, 25 N) at constant sliding speed (2.198 m / sec). The results reveal that the wear rate increases with the increasing of applied normal load. A good improvement in wear resistance was noticed for hard chromium plating specimens as compared with substrate specimen. It was also seen that, the improvement in wear resistance was (94%) as compared with substrate metal when carburizing treatment is carried out on hard chromium plating specimens.

في هذا البحث استخدمت طريقة الطلاء الكهربائي بالكروم الصلد، وهي إحدى طرائق الطلاء بتكوين غطاء على السطح، باستخدام حامض الكروميك كمصدر الكروم وكذلك حامض الكبريتيك كعامل محفز اذ أن نسبة حامض الكروميك إلى حامض الكبريتيك كانت (1:100) على التوالي. تمت عملية الطلاء بتسليط كثافة تيار مقدارها (40 Amp / dm2) ودرجة حرارة محلول الطلاء 55 – 50)ºC) ولفترات زمنية مختلفة (1 – 5 hr). استخدم الفولاذ منخفض الكاربون نوع ((CK15 كسبيكة أساس (Substrate) لغرض طلاءها بالكروم الصلد. تم أجراء المعاملة الحرارية الكيمياوية ( الكربنة الصلبة) للعينات المطلية بالكروم الصلد عند درجة حرارة (925ºC) ولفترة زمنية (2hr) للحصول على طبقة من كاربيدات الكروم. إذ تم تحديد الأطوار البلورية المكونة لطبقة الطلاء بعد أجراء الكربنة الصلبة والمتبوعة بالتقسية والمراجعة بجهاز حيود الأشعة السينية فقد تم الحصول على كاربيدات الكروم من نوع (Cr23C6, Cr7C3). وتم قياس الصلادة الدقيقة للعينات المطلية بالكروم اذ تم الحصول عل صلادة عالية تقدر (907HV). أما بعد أجراء الكربنة الصلبة لعينات الطلاء فقد ارتفعت قيم الصلادة وبشكل ملحوظ حيث أظهرت النتائج أن أعلى صلادة كانت لطبقة طلاء الكروم على سطح الفولاذ منخفض الكاربون كانت (1276HV) ويعزى سبب ارتفاع قيم الصلادة إلى وجود كاربيدات الكروم ضمن طبقة الطلاء.استخدم جهازالبلى نوع المسمار – القرص (Pin on Disc) لدراسة خواص البلى الانزلاقي الجاف لعينات الفولاذ منخفض الكاربون (كما استلمت) والعينات المطلية بالكروم الصلد والمكربنة كربنة صلبة. ولقد تم دراسة تأثير الحمل المسلط على معدل البلى بطريقة الفقدان بالوزن باستخدام أحمال عمودية مختلفة هي 25 , 20 , 15 , 10 , 5) N) وسرعة انزلاقية (Sliding speed) (2.198 m / sec). وقد أظهرت النتائج ان معدل البلى يزداد مع زيادة الحمل المسلط للعينات المطلية بالكروم, وأن أعلى مقاومة للبلى تم الحصول عليها بعد أجراء الكربنة الصلبة للعينات المطلية بالكروم حيث لوحظ التحسن الكبير في مقاومة البلى وبما يعادل (%94 ) مقارنة بالفولاذ منخفض الكاربون بحالته المستلمه.


Article
Study The Effect of Co Concentration In Nico Thin Films on Some Structure And Mechanical Properties

Author: Alaa A. Abdul-Hamead
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 12 Pages: 2486-2496
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Electroplating process has been used to prepare Magnetic NiCo alloys thinfilm with thickness of 1μm on brass alloy substrate using different Coconcentrations .Surface morphology, XRD, atomic absorption, apparent density,open porosity, stresses and microhardness of pure and alloys thin film has beeninvestigated. Results indicated that the pure and alloy of thin films waspolycrstaline with (111) domain orientation changed to (101) with increment Codeposited percentage, which is spontaneously increase with Co molarity increasedin the deposition solution.Microstructure for thin films change from nodularstructure to pyramidal and dendritic structure with changing Co content in film.Apparent density for prepared thin films was less than theoretical density about(8g/cm3), and varying with actual Co deposited content. Open porosity alsoreduced in general with increment of Co content. Mechanical properties showsalteration in internal stress behavior of deposited thin films from compressivestress to tensile stress at (0.05M) of Co. Microhadness also increased withincreasing in the Co percentage in deposited thin films,to about(467Kg/mm2).

مغناطيسية و NiCo استخدمت طريقة الترسيب الكهربائي لتحضير اغشية سبائكية منعلى قواعد لسبيكة من البراص .تم فحص التصوير Co 1 وبنسب مختلفة من μm بسمكالمجهري و حيود الاشعة السينية و التحليل الكيمياوي و الكثافة الظاهرية والمسامية المفتوحة والاجهادات الداخلية و الصلادة الدقيقة للاغشية المرسبة النقية و السبائكية .بينت النتائج ب أنالاغشية المترسبة النقية و السبائكية متعددة التبلور و بالاتجاهية ( 111 ) ويتحول الى ( 101 ) معزيادة نسبة الكوبلت المترسبة و التي تزداد تلقائيا مع زيادة المولارية المضافة الى محلولالترسيب. وتغيرشكل البنية الدقيقة لسطح الغشاء الرقيق من عقدية ناعمة الى شجيرية وهرميةتقريبا مع تغير نسبة الكوبلت بالغش اء .وكان ت الكثاف ة العملی ة للاغش یة المحض رة اق ل م ن الكثاف ة8) وتغی رت م ع تغی ر نس بة الكوبل ت المترس بة فعلی ا .ایض ا انخفض ت g/cm النظری ة ح والي ( 3المسامیة المفتوحة على العموم مع زیادة نسبة الكوبلت.الخواص المیكانیكیة للاغشة بینت تغیر في سلوك الاجهادات الداخلية في الاغشية الرقيقة المترسبة من ضغطية الى شدية عند (0.05M of Co) كذلك ازدادت قيمة الصلادة الدقيقة لهذه الاغشية مع زيادة نسبة الكوبلت بالاغشية الرقيقة.(467Kg/mm المرسبة,وصلت الى حوالي( 2


Article
MODELING and SIMULATION of ELECTROPATING PROCESS
نمذجة ومحاكاة عمليات الطلاء الكهروكيمياوي

Loading...
Loading...
Abstract

In this study, it is acquainted with the kinetics of the chemical andelectrochemical reactions by modeling and understanding of the essential andsecondary (conjugate) chemical and electrochemical reactions during plating process .In addition , the effects of various conditions on the speed and kinetic of thosereactions is also considered . In order to apply this manner , the mean-field kineticequations and Poisson equation for charged lattice model are adopted using two typesof one-dimensional cells for theoretical part of this study , namely (half and full cell) e/2) . Provided that the cell shouldcontain two identical electrodes of thickness (of size (100) with an applied potential of (10) .A computer program in visualbasic is specially constructed to show the results of this study as it should be .Through this program the concentrations are determined including (metallic atoms,cations, anions, solvents, vacancies and electrons) , the charges distribution andelectrical potential across the sites. the results , during the three periods (10)5,3,1( t) , showed that under potential application across the cell , thedeposition continues for long time then it is suppressed when the anode reaches 5failure limit , and it is observed that the deposition increases with the extension ofspace charges at the cathode , from the other hand , the ionic evolution (cation) willtake a peak shape at the cathode , then it has a certain gradient between anode andcathode. A reversed situation occurs for the anions evolution . At the same time, electric potential distribution across the sites becomes higher resulting in depositionincreasing .


Article
Study the (Wear, Roughness, Micro hardness) of the Electroplated Layers on Low Carbon Steel Improved by Shoot Penning
دراسة (البلیان،الخشونة،الصلادة الدقیقة) لطبقات الطلاء الكیمیائي الكھربائي ىلع سبیكة الصلب منخفض الكربون المطورة بالقصف بالكریات الفولاذیة

Author: Abd Al- khalaq Fawzy Hamood
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 16 Pages: 2910-2922
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study an electroplating method has been employed (with zinc, nickle).Studying of mechanical, surface, metallurgical properties for each coated systemsand made a comparison among them and with shoot penned coated systems. Lowcarbon steel alloy has been selected as a substrate. Studying of specifiedproperties including coating thickness and dry corrosion properties (oxidation athigh temperature) and comparison the results of each treatment with othertreatment results. Coated samples with nickel and zinc by electroplating methodsare used in order to compare among the resulting coating layer properties. Shootpenning method also has been employed to the two coatings in order to determinethe compression residual stresses role in the variation of studied properties.Results showed that nickel coating layer has higher oxidation resistance than zinccoating layer at high temperature, but has lower roughness, micro hardness, wearresistance and density. Microstructure inspection results showed ferrite- pearlitephases in the treated samples for all coated systems, This ensures that thistreatment will not subject to any phases transformation, and formation of coatinglayer with a different thickness as illustrated by micro structure images.

في البحث الحالي تم توظیف طریقة الطلاء الكیمیائي- الكھربائي(بمعدني النیكل والخارصین).وذلك لغرض دراسة الخواص السطحیة والطوریة والمیكانیكیة لكل طلاء ومقارنة جئاتن كل ةلماعمبعد أجراء القصف بالكرات الفولاذیة .وقد تم اختیار سبیكة الصلب منخفض الكربون كم ادة أس اسو تمت دراسة الخ واص المح ددة متض منة س مك الط لاء وخ واص التآك ل الج اف (الأكس دة) عن ددرجات الحرارة العالیة ومقارنة نتائج كل معاملة مع نتائج المعاملات الأخرى. تم استخدام الط لاءبالنیك ل والخارص ین بطریق ة الط لاء الكیمی ائي- الكھرب ائي للمقارن ة ب ین طبق ات الطلاءالمنج زة.


Article
Investigation of Gold Nanostructures on Silicon Using Electrochemical Deposition Method

Authors: Sadek Hani Lafta --- Abdul-Qader Dawood Faisal
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 4 Pages: 134-140
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Nanostructures of gold electrodeposited on silicon (100) substrate with two electrode homemade cell were investigated. In this paper we report our experimental results of gold-electroplating using a sulfite-based electrolyte instead of toxic gold-cyanide. The used electrolyte was safe and friendly environmental. Film thickness as a function of current density and deposition rate were calculated using gravity method. An empirical formula was satisfied the expected deposition thicknesses. Deposition rate of ≈ 5-40nm/ min was achieved. Au (111) structure for gold nanofilm was characterized by XRD. Morphology of gold film deposited was investigated with AFM. Morphology of Au thin films on silicon shows nanosize particles after annealing process at 600°C.

تم دراسة التراكيب النانوية للذهب المرسب بالطريقة الكهربائية على قاعدة السليكون (100) باستعمال خلية مصنعة محليا. ان النتائج العملية لهذا البحث المتعلق بترسيب الذهب أستعملت محلول يستند على الكبريتات بدلا من سيانيد الذهب السام، اي ان المحلول المستعمل امن بيئيا. تم حساب سمك الغشاء كدالة لكثافة التيار ومعدل الترسيب باستعمال الطريقة الوزنية. حققت العلاقة المستنبطة سمك الغشاء المتوقع ترسيبه. تم الوصول الى معدل ترسيب بحدود 40 -5نانومتر بالدقيقة. شخصت البنية البلورية لغشاء الذهب النانوي بواسطة حيود الاشعة السينية (XRD). تم فحص شكل غشاء الذهب المترسب بواسطة مجهر القوى الذرية (AFM). تبين ان شكل الغشاء الرقيق للذهب على السليكون ذو جسيمات بابعاد نانوية وذلك بعد اجراء عملية التلدين عند درجة حرارة600 درجة مئوية.


Article
Electrodeposition of Antimony from Hydrated Ammonium Aluminum Sulfate-Urea Room Temperature Ionic Liquid

Authors: Hadi M. A. Abood --- Azal U. Ahmed
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2017 Volume: 20 Issue: 4 Pages: 7-12
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The electrochemical stability of antimony in a water stable room temperature ionic liquid composed of 1:5 mole ratio of hydrated ammonium aluminum sulfate – urea ionic liquid at 30 °C was investigated at 0.3 M antimony (III) chloride solution. The electroplating of antimony at -0.8 V showed black coating on copper substrate. The stability of this cation in this ionic liquid was studied by cyclovoltammogram. The electrodeposition was followed up by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), Energy Dispersive X-ray analysis (EDAX) and X-ray diffraction (XRD).The nanoparticles size of the metal were in the range of less than 500nm


Article
EFFECT THE COATED LAYER OF HARD CHROMIUM ON FATIGUE BEHAVIOR FOR AISI 1039 MEDIUM CARBON STEEL

Authors: Zeyad Dushan Kadhim --- Mohammed Abdulraoof Abdulrazzaq --- Zahraa Naseef Jassim
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2018 Volume: 22 Issue: 2 (Part-3) Pages: 72-85
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this paper, study the effect of fatigue behavior on AISI 1039 medium carbon steel electroplated with hard chromium in which the electro deposition method was carried out within a period of 10, 15, 20, 25, 30 minutes plating time, As shot peening were used in this work as a type of surface treatment in which peening was carried out with steel balls for a period of 10 minutes. It was found that the highest fatigue limit was 300 MPa in case of 10 minutes chromium plated shot peened steel , also it was observed there is reduction in fatigue limit with increasing in time of electroplating. Coating thickness increases as coating time increasing and this leading to lower the fatigue limit, where the highest coating thickness value was 33µm with 30 minutes coating time and fatigue limit is reduced till 250 MPa. Also it was found that the coating thickness causes an increase in surface hardness of the alloy. While as coating thickness increased the surface roughness decreased.


Article
Comparison between Electroplating and Electroless on Plastic Surface

Loading...
Loading...
Abstract

We report a method of converting non-conductive plastic surfaces into conductive by plating either copper electroless or copper electroplating -carbon black containing bending Agent onto Perspex plastics . Various approaches have been studied in order to comparing properties of the plated copper for two methods such as scanning electron microscopy (SEM),thickness, roughness, porosity, tensile Strength and elongation. The results show that the surface of electroplating was uniform, compact, and continuous and it had an obvious metallic sheen, while the surface of plated copper for electroless for it had many pores. Also observed that the coating was composed of small cells. These cells have been deposited together closely.Thick copper layer was deposited a(38μm ) electroplating while (5μm) for electroless plating tensile strength and elongation of copper electroplating became greater compared with copper electroless, whereas the roughness and Porosity became smaller.The electroplating copper deposition process developed in this study may open up a new route of plating on plastics (POP) for printed circuit boards, electromagnetic interference shielding, and many other applications


Article
Comparative Study between Nanofiltration and Reverse Osmosis Membranes for the Removal of Heavy Metals from Electroplating Wastewater
دراسة مقارنة بين اغشية النانو والتناضح العكسي لإزالة المعادن الثقيلة من مياه الصرف الصحي الناتجة من الطلاء الكهربائي

Authors: Ahmed Faiq Al-Alawy أحمد فائق العلوي --- Miqat Hasan Salih ميقات حسن صالح
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 4 Pages: 1-21
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The present work aimed to study the efficiency of nanofiltration (NF) and reverse osmosis (RO) process for water recovery from electroplating wastewater and study the factors affecting the performance of two membrane processes. Nanofiltration and reverse osmosis membranes are made from polyamide as spiral wound module. The inorganic materials ZnCl2, CuCl2.2H2O, NiCl2.6H2O and CrCl3.6H2O were used as feed solutions. The operating parameters studied were: operating time, feed concentrations for heavy metal ions, operating pressure, feed flow rate, feed temperature and feed pH. The experimental results showed, the permeate concentration increased and water flux decreased with increase in time from 0 to 70 min. The permeate concentrations increased and flux decreased with increase in feed concentrations from 10 to 300 mg/l. Raising of pressure from 1 to 4 bar, permeate concentration decreased for RO, for NF decreased and then increased at high pressure and increase the flux. The rises of flow rate from 20 to 50 l/h decreased permeate concentration and the flux increase. The rises of temperature from 26 to 40 °C, increased permeate concentration and increased the flux. The rise in pH from 4 to 7, decreased the flux as the pH goes from acidic side towards alkaline. The polyamide nanofiltration membrane had allowed permeation of chromium and copper ions to lower than permissible limits. Nanofiltration membrane had allowed permeation of nickel and zinc ions at low concentration of these ions. The polyamide RO membrane gave a high efficiency for removal of chromium, copper, nickel and zinc and it had allowed permeation of these ions to the lower than permissible limits. The rejection at first three minutes when the feed concentration approximately was constant for chromium in NF and RO, was 99.7% and 99.93%, for copper was 98.43% and 99.33%, for zinc was 97.96% and 99.49%, and for nickel was 97.18% and 99.49% respectively. The maximum recovery for chromium in NF and RO was 71.75% and 48.5%, for copper was 75.62% and 50.68%, for zinc was 80.87% and 54.56%, for nickel was 60.06% and 46.18% respectively. For a mixture of synthetic electroplating wastewater, nanofiltration and reverse osmosis membranes have a high rejection percentage for heavy metal ions. It was obtained pure water and concentrations of less than allowable limits for heavy metals in the case of the mixture.

هذا العمل يهدف إلى دراسة كفاءة غشاء النانو وعملية التناضح العكسي لاسترجاع المياه من مياه الصرف الصحي الناتجة من الطلاء الكهربائي، ودراسة العوامل التي تؤثر في أداء الغشائين. اغشية النانو والتناضح العكسي مصنوعة من مادة البولي أميد على شكل ((spiral wound module. المواد غير العضوية كانت كلوريد الزنك، كلوريد النحاس المائي، كلوريد النيكل المائي، و كلوريد الكروم المائي استخدمت ك محلول اللقيم. العوامل التشغيلية التي تم دراستها هي: الزمن, تركيز الداخل, الضغط, التدفق, درجة الحرارة, درجة الحموضة. وأظهرت النتائج التجريبية، تركيز الناتج يزداد و تدفق المياه يقل مع زيادة الوقت (0-70 دقيقة). تركيز الناتج يزداد و تدفق المياه يقل مع زيادة تركيز الداخل (10-300) ملغ/لتر. رفع الضغط (1-4 بار)، تركيز الناتج يقل للتناضح العكسي ويقل ثم يزداد عند الضغط العالي لغشاء النانو ويزداد تدفق المياه. رفع التدفق (20-50 لتر/ساعة)، يقل تركيز الناتج ويزداد الجريان. رفع درجة الحرارة (26-40 درجة مئوية)، يزداد تركيز الناتج ويزداد الجريان. رفع درجة الحموضة (4-7)، يقل الجريان كلما يذهب الرقم الهيدروجيني من الجانب الحمضية نحو القلوية. غشاء بولي أميد NF أتاح تخلل ايونات الكروم والنحاس إلى أقل من الحدود المسموح بها. NF أتاح تخلل أيونات النيكل والزنك إلى أقل من الحدود المسموح بها عندما تتواجد بتراكيز منخفضة. غشاء بولي أميد RO يعطي كفاءة عالية لإزالة الكروم والنحاس والنيكل والزنك، وقد أتاح تخلل هذه الأيونات إلى أقل من الحدود المسموح بها. كان الرفض في ثلاث دقائق الأولى عندما كان تركيز التغذية ثابتا تقريبا للكروم في NF و RO 99.7% و 99.93%، للنحاس هو 98.43% و 99.33%، للزنك هو 97.96% و 99.49%، للنيكل 97.18% و 99.49% على التوالي. وكان الحد الأقصى لاسترداد الماء في حالة الكروم في NF و RO % و 48.5%، النحاس 75.62% و 50.68%، الزنك 80.87% و 54.56%، النيكل 60.06% و 46.18% على التوالي. لخليط من مياه الطلاء الكهربائي الاصطناعية، أغشية النانو والتناضح العكسي لديها نسبة الرفض عالية لأيونات المعادن الثقيلة. تم الحصول على مياه نقية وبتراكيز أقل من الحدود المسموح بها للمعادن الثقيلة في حالة الخليط.

Listing 1 - 10 of 11 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (11)


Language

English (9)

Arabic and English (2)


Year
From To Submit

2018 (1)

2017 (2)

2014 (2)

2013 (1)

2012 (2)

More...