Article
Preparation of a Reinforced Polymeric Coating with Inorganic Nano Additives as UV-Stabilizers and Protect Oil Pipelines from Corrosion

Authors: I.A.Esmael --- F.M.Ahmed --- N.F.Ibraheem --- H.M.Yas --- et al.
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 10 Part (A) Engineering Pages: 1003-1010
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research a nano polymeric coating has been prepared to be used for the protection of the external surface of oil pipelines (medium carbon steel (CK50)) from corrosion in salt water (3.6% NaCl) . This coating is reinforced by inorganic (nano and micro) additives to apply a high resistance against chemicals and salts. These oxides protect the epoxy resin from degradation by preventing the epoxy molecules and active functional groups from absorbing ultraviolet light in the range (290-315) nm strongly.This coating is also resistant to the high and low temperatures, humidity, scratch and water. This coating was prepared from the reaction of 2-[[4-[2-[4-(Oxiran-2-ylmethoxy) phenyl] propan-2-yl] phenoxy] methyl] oxirane (Diglycidyl Ether of Bisphenol A) and the hardener (EDA). The mixing ratio of the two parts was (4:1). Reinforced with inorganic (nano and micro) additives such as titanium dioxide (TiO2) and zinc oxide (ZnO) which have been used as an anticorrosion. These additives are non-toxic, thermally stable and have a high degree of the miscibility with epoxy. The weight percentages of the mixing are (0 and 10 % wt). The corrosion rate results show that using (nano and micro) coating give good results in increasing the corrosion resistance compared with the (non additives) epoxy.This coating was characterized using different spectroscopic methods (FT-IR, UV/Vis). Several tests were conducted ,including differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) , mechanical tests and evaluation of corrosion resistance was made by using static potential test.


Article
EFFECT OF CATHODIC PROTECTION ON COATING STEEL PIPELINE IN SALINE ENVIRONMENT
تأثير الحماية الكاثودية على الأنابيب الفولاذية المطلية في البيئة الساكنة

Author: Naser Korde Zedin ناصر كردي زيدان
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2015 Volume: 8 Issue: 3 Pages: 88-99
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

There are two main types of cathodic protection systems: galvanic and impressed current. In this research, the effect of coatings on impressed current cathodic protection was studied. The selection of coating process for a specific application depends on several factors including the corrosion resistance that are required, the anticipated lifetime of the coated material and environmental considerations. When using cathodic protection on coated pipelines, the problems that exist if the coating disbands (loses adhesion) must be considered. Many in the oil steel pipeline industry assume cathodic protection will solve their external corrosion problems without truly understanding the relationship between the epoxy-coating and cathodic protection. Most external corrosion on oil steel pipelines is caused by disbanded epoxy-coating that shield cathodic protection. This paper will discuss the differences in cathodic protection of oil steel pipeline that coating and not coating and how cathodic protection works with these coatings (wear used epoxy (G-5470), (G-5471) and (G-5472), three types component epoxy system resistance to acid and chemical from modern paints industrials Company (in Iraq)). The aqueous corrosion properties of the coated samples in 3.5 wt % NaCl solution were studied by Tafel extrapolation measurements.

يوجد نوعين رئيسيين من أنظمة الحماية الكاثودية : الحماية الكاثودية بالعنصر المضحي والثانية هي الحماية الكاثودية بالتيار المسلط . في هذا البحث يتم دراسة تأثير الطلاء على الحماية الكاثودية باستخدام التيار المسلط على الأنابيب الفولاذية الناقلة للنفط . أن اختيار عملية طلاء في اغلب التطبيقات يعتمد على عدة عوامل ، بما في ذلك مقاومة المعدن للتآكل، ومقدار عمر الطلاء للمعدن المراد حمايته والظروف البيئية المحيطة بالمعدن المراد حمايته .ان استخدام الحماية الكاثودية على خطوط الأنابيب الفولاذية المطلية ، يجب أن يؤخذ بنظر الاعتبار المشاكل القائمة فيما إذا كان الطلاء متمزق او غير متلاصق ,ومعظم التآكل الخارجي لخطوط الأنابيب الفولاذية المطلية والناقلة للنفط هو يحدث بسبب فشل في الطلاء الخارجي للأنابيب الفولاذية المطلية ويودي في النهاية إلى حدوث فشل كإرثي للأنابيب.وأكثر البحوث المستخدمة في الصناعة تفترض بأن الحماية الكاثودية على خطوط الأنابيب الفولاذية تحل مشاكل التآكل الخارجي للأنابيب الفولاذية بدون محاولة لفهم العلاقة بين الطلاء والحماية الكاثودية نفسها.وسيناقش هذه البحث دراسة الاختلافات في حماية الأنابيب الفولاذية الناقلة للنفط والتي تكون مطلية وأخرى عارية ودراسة هذه الطلاءات (الطلاءات المستخدمة (G-5470) و (G-5471) و(G-5472) من النوع المركب والمقاوم للتفاعلات الكيميائية والحوامض, حيث أخذت من شركة الأصباغ الحديثة العراقية) وتأثيرها على الحماية الكاثودية , وتم العمل بمحلول(3.5 wt % NaCl) ودراسة سلوك التآكل باستخدام طريقة استكمال منحني تافل.