Reducing of Flammability for Polymeric Composite Material by Using Flame Retardants Coating

Author: Ali Ibrhim Al-Mosawi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 11 Pages: 2210-2215
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The low thermal resistance of polymeric materials to high temperatures consideredthe main limitation to used these materials in such applications required high thermalresistance ,so ,the present research aimed to study the possibility to increasing flameretardancy of advanced polymeric composite materials reinforced by fibers bycoating by a flame retardant layer represent antimony tetroxide (Sb2O4) as a coatinglayer (4mm) thickness to react and prevent spread of flame on surface of compositematerial consist of araldite resin(AY103) reinforced by woven roving carbon - Kevlarfibers (0°-45°) and exposed this coating layer to direct flame generated fromoxyacetylene flame with different exposure distances (10mm,15mm,20mm) andstudy the range of resistance of flame retardant material layer to the flames andthermal resistance and flame retardancy after coating by antimony tetroxide as wellas rising flame resistance increased exposure distances to flame .


Article
IMPROVEMENT OF FLAME RETARDANCY FOR HYBRID COMPOSITE MATERIAL BY USING ZINC BORATE
تحسين إعاقة اللّهب لمادة متراكبة هجينة بإستعمال بورات الزنك

Loading...
Loading...
Abstract

Zinc borate was added as a surface layer of (4mm) thickness on the surface of araldite resin reinforced by woven roving carbon-kevlar fibers .This system was exposed under different exposure intervals (10,15, and 20mm) to a direct flame which generated from oxyacetylene and gas flame (3000ºC,2000ºC) respectively, and study the range of resistance of flame retardant material layer to the flames and protected the substrate . Surface temperature opposite to the flame method was used to measuring the temperature transferred through this system. The experimental results show that a great increment in thermal resistance and flame retardancy after coating by zinc borate and the best percentage was (20%) from zinc borate, as well as rising flame resistance increased exposure intervals to flame

تم إضافة بورات الزنك بشكل طبقة سطحية بسمك (4mm) على سطح راتنج الإرلدايت المقوى بألياف كاربون -كيفلار المحاكة. تم تعريض هذا النظام وبمسافات تعرض مختلفة (20mm,15,10) إلى لّهب مباشر متولد من شُعلة أُوكسي أستلينية وشُعلة غازية بدرجة حرارة 3000ºC) (2000ºC, على التوالي ، ودراسة مدى مقاومة طبقة المادة المعيقة للّهب لحرارة الشُعلتين ومدى حمايتها للمادة المتراكبة الواقعة تحتها . تم إعتماد طريقة قياس درجة حرارة السطح المقابل للشعلة في قياس درجة الحرارة المنتقلة خلال هذا النظام . أظهرت نتائج الإختبارات العملية زيادة كبيرة في المقاومة الحرارية وإعاقة اللّهب للمادة المتراكبة بعد طلائها ببورات الزنك وأفضل زيادة كانت عند نسبة (%20) من بورات الزنك ، إضافة إلى إرتفاع مقاومة اللّهب مع زيادة مسافة التعرض للشُعلة الحرارية .