Using of Some Inorganic Additives as Flame Retardants for Some Polymers; a Comparison Study

Author: Jalil R. Ugal
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 2 Pages: 8-17
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Five additives were used as flame retardants for epoxy and unsaturated polyester resins which are: Tetraethyl ammonium bromodichloro phenyl phosphonate, (C2H5)4N[PhPCl2Br] (I), Ammonium phosphate (II), Borax (III), Chlorinated paraffine (IV) and a mixture of additives (I+IV) in the mole ratio (1:1) (V) to study their synergetic effect. The compounds, tetraethyl ammonium bromodichloro phenyl antimonate (C2H5)4N[PhSbCl2Br] and tetraethyl ammonium chlorodibromo phenylantimonate(C2H5)4N[PhSbBr2Cl] were used as flame retardantsfor polyethylene (Low density and high density ) and polypropylene. These additives were used in different percentages(0-10%) and the samples of polymers were prepared in the dimensions of (3×130×130)mm. Three standard test methods (ASTM) were used to measure the limiting oxygen index (LOI), rate of burning (RB) and maximum height of flame (H). the results showed that all of these additives exhibit sufficient flame retardants and some percentage caused non burning of the polymers under study.

استخدمت خمسة مضافات لتثبيط لهوبية راتنجي الايبوكسي والبولي استر غير المشبع وهي : رباعي اثيل امونيوم برومو ثنائي كلورو فنيل فوسفونيت (I) (C2H5)4N [PhPCl2Br] فوسفات الامونيوم (II)، البوراكس (III)، البارافين المكلور (IV) ومزيج من المضافين (IV+I) بنسبة مولية (1:1)(V) لدراسة فعلهما التازري. استخدم المركبان رباعي اثيل امونيوم برومو ثنائي كلوروفنيل انتيمونيت] (C2H5)4N [PhSbCl2Brورباعي اثيل امونيوم كلورو ثنائي بروموفنيل انتمونيت(C2H5)4N[PhSbBr2Cl] لتثبيط لهوبية البولي اثلين (واطئ الكثافة وعالي الكثافة) والبولي بروبلين. استخدمت هذه المضافات بنسب وزنية مختلفة (0-10 %) وزناً وتم تحضير النماذج البوليمرية بابعاد (3* 130 * 130) ملم. استخدمت ثلاث طرائق قياسية للفحص (ASTM) لقياس معامل الاوكسجين المحدد (LOI)، معدل الاحتراق (RB) واقصى ارتفاع للهب (H) بينت النتائج بان جميع هذه المضافات اظهرت كفاءة في تثبيط اللهوبية وقسم من النسب تسببت في عدم اشتعال البوليمرات قيد الدراسة.


Article
Study the Synergetic Activity of Aluminium Tri Hydroxide with Zinc Oxide as Flame Retardants for Unsaturated Polyester Resin
دراسة الفعل التازري لهيدروكسيد الالمنيوم مع اوكسيد الخارصين كمثبطات للهوبية البولي استر غير المشبع

Authors: Jalil R. Ugal --- Rawnaq B. Jimaa
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 1 Issue: المؤتمر العلمي الاول للتربية للعلوم الصرفة Pages: 43-50
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this work, aluminum tri hydroxide (I), zinc oxide (II) and their mixture (1:1) (III) were used as flame retardants for unsaturated polyester resin in the weight ratios of (0, 2, 4, 7, 10, and 12) %, by preparing films of (130*130*3) mm in dimensions.Three standard test methods used to measure the flame retardation which are: ASTM: D-2863 to measure the limiting oxygen index (LOI), ASTM: D-635 to measure the rate of burning (R.B) & ASTM: D-3014 to measure the maximum height of flame (H). Results obtained from these tests indicated that; ATH, ZnO and their mixture have a good effect as flame retardants for unaturated polyester resin. The synergetic effect was the best.

في هذا البحث تم استخدام هيدروكسيد الالمنيوم (مضاف I), اوكسيد الخارصين(مضاف II) ومزيجهما بنسبة (1:1) مضاف (III) كمثبطات للهوبية البولي استر غير المشبع. بنسب مئوية وزنية (10, 7, 4, 2, 0و 12) % بواسطة تحضير شرائح بابعاد (130*130*3) ملم.استخدمت ثلاث طرق قياسية لاختبار تثبيط اللهوبية وهي: الطريقة القياسية (( LOI ASTM: D-2863 لقياس معامل الاوكسجين المحدد, الطريقة القياسية ASTM: D-635 لقياس سرعة الاحتراقوالطريقة القياسية ASTM: D-3014 لقياس اقصى ارتفاع يصل اليه اللهب(H) اظهرت النتائج المستحصل عليها ان المضافات المستعملة في هذه الدراسة تمتلك تاثير جيدا كمثبطات لهب للبولي استر غير المشبع. وان افضلها كانت عندما كان التاثيرتازريا


Article
STUDY OF FLAME RESISTANCE FOR ADDITIVES – CONTAINING EPOXY AND POLYESTER
دراسة مقاومة احتراق بوليمرات الايبوكسي والبولي استر التي تحتوي على المضافات

Author: Mohammed Hallol Mokhilif م. محمد هلول مخيلف
Journal: Univesity of Thi-Qar Journal مجلة جامعة ذي قار العلمية ISSN: 66291818 Year: 2015 Volume: 10 Issue: 4 Pages: 1-9
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

In this paper, additives dechlorane plus which used synergistically with sodium-orthophosphate and with alumina, sodium-orthophosphate , and alumina have been used as a flame retardants for unsaturated polyester and epoxy resin .The additives were used at low and high levels with unsaturated polyester and they were used at high levels with epoxy resin .At low levels ,the additives were used in weight percentages of (1,3,5,7and 10)%,At high levels ,They were used in weight percentages of (15,20,25,30 and 35 )%.Hand –lay up was used to prepare the specimens .The paper showed that the additives have good effectiveness in reducing the burning at high weight percentages and they appeared high effectiveness in resisting the flame when they were used as a synergistic flame retardants.

في هذا البحث تم دراسة تأثير بعض المضافات مثل اورثو- فوسفات الصوديوم وديكلوران بلس والالومينا على احتراق بوليمرات الايبوكسي والبولي استر المشبع كما تم دراسة تأثير هذه المضافات تهجينيا مع بعضها على احتراق البوليمرات . لقد اضيفت هذه المضافات بنسب مئوية معينة الى البوليمرات و استخدمت طريقة الصب اليدوي في تحضير عينات الفحص . اظهرت نتائج الفحص ان تأثيرهذه المضافات على مقاومة احتراق البوليمرات كان ضعيفا جدا عند النسب المئوية الواطئة لكنها اظهرت تأثيرا كبيرا عند النسب المئوية العالية وخاصة عند استخدامها تهجينيا

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

English (3)


Year
From To Submit

2015 (1)

2013 (1)

2012 (1)