Article
Effect of Water Proof Admixture on Hardened Concrete
تأثير المضاف المانع للرطوبة على الخرسانة المتصلبة

Authors: Asmaa Mahdi Ali --- Gheed Basil Hameed
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467(print) 27068536(online) Year: 2012 Volume: 18 Issue: 73 Pages: 49-67
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Admixtures improve the compressive strength of concrete. This study shows the using of water proof admixture on hardened concrete (40MPa) when the samples Water curing condition is used and the age at testing are 7, 28 and 90 days to evaluate the mechanical properties such as compressive strength, splitting tensile strength and flexure strength and 28 days and are exposed to temperature (100°C and 500°C) at samples in 28 days. In this study the compressive strength decreases by about (33.03 %) and increases by about (29.95%) at (7 and 90) days respectively. They study shows that the compressive strength decreases by about (0.96% and 19.12 %) at 100°C and 500°C respectively while the tensile strength decreases by about (2.06% and 19.38%) at 100°C and 500°C respectively, and the flexural strength decreases by about (3.01% and 21.07%) at 100°C and 500°C respectively. All the above results are compared with cubes tested at room temperature (25 °C).

تستخدم المضافات لتقليل كمية الماء المضافة و زيادة مقاومة الانضغاط، حيث تم استخدام مضافات "Water reducing" للخرسانة ذات مقاومة انضغاط مقدارها (40 نت/مم2). تم صب50 نماذج مكعبة بأبعاد (150X150)مم لفحص مقاومة الانضغاط بعمر (7، 28و 90) يوم لكل عمر وقد تم تعريض هذه النماذج بعمر 28 يوم الى درجات حرارة (100 م° و 500م°)، ثم مقارنتها مع النماذج التي تم فحصها بدرجة حرارة الغرفة (25 م°) وكذلك صب 50 نماذج اسطوانية بأبعاد (150X300) مم لفحص مقاومة الشد الانشطاري وصب 50 نماذج موشورية بأبعاد (100X100X500) مم لفحص مقاومة الانحناء بعمر 28 يوم و تعريضها إلى درجات حرارة (100م° و 500م°)، ثم مقارنتها مع النماذج التي تم فحصها بدرجة حرارة الغرفة (25 م°) ، لوحظ أن مقاومة الانضغاط تقل بمقدار ( 33,03 % ) بعمر 7 ايام و تزداد بمقدار (29,95 %) بعمر 90يوم عند مقارنتها مع النماذج بعمر 28 يوم. عند تعرض النماذج الى درجة حرارة (100 م° و 400م° ) لوحظ أن مقاومة الانضغاط تقل بمقدار(0,96% و 19,12% ) على التوالي بينما تقل مقاومة الشد الانشطاري بمقدار ( 2,06% و19,38 %) و مقاومة الانحناء تقل بمقدار (3,01 % و 21,07%) عند التعرض الى درجة حرارة (100 م° و 400م° ) على التوالي


Article
Properties Of Hardened Concrete Using Crushed Clay Brick As Aggregates
خصائص الخرسانة المتصلبة باستخدام مكسر الطابوق الطيني

Author: Osama M. Ghazi
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2011 Volume: 17 Issue: 4 Pages: 1022-1038
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This paper provides the result of an investigation to use of crushed clay brick as aggregates in producing concrete. Eight different crushed clay brick aggregate concretes were used in this investigation. Compressive strength, splitting tensile strength and pulse velocity of crushed clay brick aggregates concrete were determined and compare to natural aggregate concrete. The compressive strength of crushed clay brick aggregates concretes were always lower than the compressive strength of natural aggregates concrete regardless the age of concrete, but the crushed clay brick aggregates concrete showed better performance as the age of concrete increases and average reduction in compressive strength were 33.5% at the age of 7 days but it becomes only 20% at the age of 56 days compared to natural aggregates concrete. The splitting tensile strength of crushed clay brick aggregates concrete were always lower than natural aggregate concrete, the reduction in splitting tensile strength of crushed clay brick aggregates concrete is ranging between 11 and 26% with an average reduction of about 18.5% compared to natural aggregates concrete. The pulse velocity of crushed clay brick aggregates concrete were also lower than natural aggregates concrete, the reduction in pulse velocity of crashed clay brick aggregates concrete is ranging between 6 and 22% with an average reduction of about 14% compared to natural aggregates concrete.

يبين هذا البحث نتائج استخدام مكسر الطابوق الطيني كركام في إنتاج الخرسانة ثمانية نسب من مكسر الطابوق الطيني استخدمت في إنتاج الخرسانة . تم فحص مقاومة الانضغاط باعمار (56,28,7) مقاومة الشد غير المباشر بعمر 28 يوم وفحص سرعة الذبذبات فوق الصوتية بعمر 28 يوم ايضاً لخرسانة مكسر الطابوق الطيني ومقارنتها مع خرسانة الركام الاعتيادي ووجد إن مقاومة الانضغاط لخرسانة مكسر الطابوق الطيني كانت دائماً أقل من مقاومة الانضغاط لخرسانة الركام الطبيعي بغض النظر عن عمر الخرسانة لكن وجد ايضاً أن مقاومة الانضغاط لخرسانة مكسر الطابوق الطيني تزداد مع تقدم عمر الخرسانة ، حيث وجد أن معدل انخفاض مقاومة الانضغاط هي 33.5% بعمر 7 أيام ولكنها تصبح 20% بعمر 56 يوم مقارنة بخرسانة الركام الطبيعي . أما مقاومة الشد غير المباشر لخرسانة مكسر الطابوق الطيني كانت هي الاخرى أقل بنسبة تتراوح ما بين 26%) - 11) أي بمعدل % 18.5مقارنة بخرسانة الركام الاعتيادي . في حين كان فحص سرعة الذبذبات فوق الصوتية لخرسانة مكسر الطابوق الطيني أقل من سرعة الذبذبات لخرسانة الركام الطبيعي و كانت نسبة الانخفاض تتراوح ما بين (6-22%)أي بمعدل 14%