Article
Study of the Tensile strength properties of Low density polyethylene composites with Cannabis (Hemp fibers)
دراسة خواص قوة الشد للبولي ايثيلين واطئ الكثافة مع الياف القنب كمالئات بوليمرية

Author: Einas A. Al-Nasir ايناس عبد العزيز الناصر
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2013 Volume: 39 Issue: 3A Pages: 15-22
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

The mechanical properties of hemp fibers (cellulosic fibers) composites were studied. The range of added Hemp fibers has the values (0%, 3%, 5%, 7%, 10%, 15%, and 20%) of polyethylene weight and, the best fibers ratio was 5%.The properties (LDPE / Cannabis) composites were analyzed as a function of the fibers amount. All prepared composites showed improved fibers dispersion in the low density polyethylene matrix. All composites displayed lower elongation of break compared to pure LDPE.

تمت دراسة الخواص الميكانيكية للألياف القنب (ألياف السليولوز) كمواد مالئة للبوليمر. وقد تم تحضير نماذج بنسب وزنية (0٪، 3٪، 5٪، 7٪، 10٪، 15٪، و 20٪) من وزن البولي اثيلين و، كانت أفضل نسبة الألياف 5٪، وقد تم تحليل الحشوات كدالة لكمية من كمية الألياف. وأظهرت جميع النماذج المحضرة تحسن في انتشار الالياف بشكل متجانس في البولي ايثيلين واطئ الكثافة ،ومن الملاحظ ان جميع النسب المضافة للبوليمر عملت على تقليل نسبة الاستطالة مقارنة مع البوليمر النقي


Article
Effect of Addition of A Marble Dust on Drying Shrinkage Cracks of Cement Mortar Reinforced with Various Fibers

Author: Basim Thabit Al-Khafaji
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 2 Pages: 652-669
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This investigation is conducted to study the effect of addition of marble powder (marble dust) and different fibers on drying shrinkage cracks and some properties of fibers reinforcment cement mortar. Steel molds having a trapezoidal section, and the end restrained at square shape with( 2.7 meter) at length are used to study restrained drying shrinkage of cement mortar. Specimens of ( compressive .flextural. splitting strength) were cast. The admixture (marble dust) was used to replacie weight of cement with three levels of (4%, 8% and 16%) and the fiber hemp and sisal fiber were added for all mixes with proportion by volum of cement . All specimens were cured for (14 days). Average of three results was taken for any test of compressive, tensil and flextural strength. The experimental results showed that the adding of this admixture(marble dust) cause adelay in a formation of cracks predicted from a drying shrinkage ,decreases of its width , and hence increases of (compressive, splitting tensil and flextural strength) at levels of (4%, and 8%). Thus there is a the positive effect when fiberes added for all mixes of cement mortar with addition of (marble dust). All The admixtures (marble dust and fibers) have the obvious visible effect in the delay of the information of shrinkage cracks and the decrease of its width as Compared to the cement mortar mixes when marble dust added a alone.

هذه الدراسة تهدف الى دراسة تأثير اضافة (غبار المرمر) مع الياف مختلفة على انكماش الجفاف وبعض الخواص لمونة السمنت المسلحة بالالياف، في هذه الدراسة تم استخدام قوالب حديدية بمقطع على شكل شبه منحرف بطول (2.7 متر) ومن نهايتيه قالب بشكل مربع لغرض تقييد النموذج لضمان حدوث (تشققات انكماش الجفاف) لمونه السمنت وأيضاً تم صب نماذج لغرض تعيين مقاومة الانضغاط ومقاومة الانشطارو الانثناء. استخدمت ثلاث نسب مئوية من) مسحوق المرمر( وهي (4% مر و 8% و 16%) كاستبدال من وزن السمنت , واستخدمت الياف ( السيسال واالقنب ). بنسب حجمية من السمنت .تم انضاج النماذج جميعاً بفترة إنضاج) 14 يوم(. تم اخذ معدل ثلاثة نتائج لكل فحص من مقاومة الانضغاط والشد و الانثناء. أوضحت النتائج العملية أن إضافة ا المضاف(MD ( يؤخر حدوث التشققات الناتجة من (انكماش الجفاف ( لمونة السمنت ويقلل من عرضها ويزيد من مقاومة الانضغاط والشد و الانثناء عند النسب (4% و 8%) ونفس التاثير عند اضافة الالياف لمونة السمنت جميعا و كل على حدة مع (غبار المرمر) ولكل نسب الاضافة لها . وعند اضافةالالياف مع غبار المرمر سوية نلاحظ تأثير ملموس في تأخير حدوث (تشققات الانكماش(في مونة السمنت و تقليل في عرض تلك التشققات مقارنة مع خلطات مونة السمنت المضاف لها غبار المرمر لوحده .