SOME MECHANICAL PROPERTIES OF CONCRETE REINFORCED WITH REED FIBERS
بعض الخواص الميكانيكية للخرسانة المسلحة بألياف القصب

Author: Ali Hasson Nahhab علي حسون نهاب
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2009 Volume: 2 Issue: 1 Pages: 31-37
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This research produces a new results about using of locally available reed fibers in concrete. The main parameter of this study was the volume fraction of fibers. The reed fibers were added to the mix in percentages of 1, 2, 3, 4,and 6%. The test program included: slump, compressive strength, splitting tensile strength and impact resistance. It was found that the presence of reed fibers leads to reduce workability, compressive, splitting tensile and impact strength. It was also found that, generally, this reduction increases as the volume percentage of fibers is increased.

يقدم هذا البحث نتائج جديدة حول استخدام ألياف القصب المتوفرة محليا في الخرسانة . المتغير الرئيسي في هذه الدراسة هو النسبة الحجمية للألياف حيث أضيفت بنسب 1و 2و 3 و4 و6 % . تضمن برنامج العمل فحوصات الهطول و مقاومة الانضغاط ومقاومة الشد الانشطاري ومقاومة الصدم . أظهرت النتائج إن وجود ألياف القصب في الخلطة يؤدي إلى نقصان كل من قابلية التشغيل و مقاومة الانضغاط ومقاومة الشد الانشطاري ومقاومة الصدم وبصورة عامة يزداد هذا النقصان بزيادة النسبة الحجمية للألياف .


Article
Re-Use of Glass Wool Fiber as New Composite Polyester System

Author: Raghad U. Abass
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 1 Part (B) Scientific Pages: 7-11
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Four different ratios of composites were prepared by varying thewool glass, at different additive weight percentages (0, 0.2, 0.4, 0.6 wt. %)in order to study the effect of glass wool reinforcement on mechanical andchemical properties of GW-reinforced polyester composites. The vacuumbagging technique was adopted for the fabrication of hybrid compositematerials. Afterword many mechanical properties as hardness, impactresistance, and compression resistance for these hybrid composites wereevaluated according ASTM Standards. The mechanical properties wereimproved as the fibers reinforcement content increased in the matrixmaterial. The chemical properties were improved as increased the weight ofglass wool. The chemical and mechanical properties have been increased


Article
Impact Strength of ZnO and Sand/(Epoxy-Polyester) Blend Composites

Authors: xRafid Hamad Khalaf --- Faik Hammad Anter --- Abdul Al-Hameed R. Al Sarraf
Journal: Al-Mustansiriyah Journal of Science مجلة علوم المستنصرية ISSN: 1814635X Year: 2018 Volume: 29 Issue: 4 Pages: 128-133
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This work included preparation five groups polymeric composites. From matrix of polymer blend (Epoxy (EP) 80% + unsaturated polyester (UPE) 20%) with( Nano ZnO) with weight fraction (2%,4%,6%,8%) of zinc oxide (ZnO), with weight fraction (5%,10%,15%,20%), also sand material in three different grain size (53,63,74) μm respectively with weight fraction (5%,10%,15%,20% ) and by employing hand lay-up method. First group (G1: nano ZnO): consists of four samples prepared from reinforcing blend (80%EP/20%UPE) with (ZnO powder) in the same above weight fraction. Second group (G2: powder ZnO): consists of four samples prepared from reinforcing Blend (80%EP/20%UPE with (powder ZnO) in the same above weight fraction. Third group (G3: powder Sand) and fourth group (G4: powder Sand) and fifth group (G5: powder Sand) in the same weight fraction. It was found that the reinforcement of the above materials leads to an improvement in mechanical properties and impact resistance of composite materials in normal conditions.

تم في هذا العمل تحضير خمس مجموعات متراكبات بوليمرية مكون خليط بوليمري من رتنج الايبوكسي و البولي استر الغير مشبع بوصفة مادة اساس بنسبة (80%) من الايبوكسي و (20%) من البولي استر الغير مشبع ,وتم تدعيمة بإضافة دقائق مايكروية ونانوية من مادة اوكسيد الخارصين ومادة الرمل لثلاث احجام دقائقية مختلفة هي (74,63,53) مايكرون علي التوالي . باستخدام طريقة القولبة اليدوية. تم التدعيم باوكسيد الخارصين المايكروي بنسب وزنية %(5,10,15,20) و اوكسيد الخارصين النانوي وبنسب وزنية %(2,4,6,8) والرمل 53مايكرون والرمل 63مايكرون والرمل 74مايكرون وبنسب وزنية %(5,10,15,20) على التوالي . وقد وجد ان التدعيم يؤدي الى تحسين في الخصائص الميكانيكية المتمثلة بمقاومة الصدمة للمواد المتراكبة في الظروف الطبيعية.


Article
Behaviour of Waste Plastic Fiber Concrete Slabs Under Low Velocity Impact
سلوك البلاطات الحاوية على ألياف الفضلات البلاستيكية تحت أحمال الصدم

Loading...
Loading...
Abstract

This research investigates the impact resistance of concrete slabs with different volume perecentage replacement ratios of waste plastic fibers (originaly made from soft drink bottles) as follows : 0.5%, 1% and 1.5%. Reference mix produced in order to compare the result. For the selected mixes, cubes with (100×100×100mm) were made to test compressive strength at age of (90) days. Flexural strength (Modulus of Rupture) test was also conducted using prisms sample of (500*100*100 mm) dimensions. The low-velocity impact test was conducted by the method of repeated falling mass where 1400gm steel ball was used. The ball falling freely from height of 2400mm on concrete panels of (500×500×50 mm) having a mesh of waste plastic fiber.The number of blows that caused first crack and final crack (failure) were determined, according to the former obtained results , the total energy was calculated. Results showed an improvement in mechanical properties for mixes containing plastic fibers compared with reference mix. For compressive strength the maximum increase in compressive strength was equal to (3.2%) at age of (90) days. Flexural strengths for mixes containing plastic fiber at ages 28, and 90 days are higher than that of these of reference mix. The maximum value of increaseing was (18%) for 28 days age of test and it was equal to (26%) for 90 days age of test for the mixture with plastic fiber content by volume equal to (1%) .Results showed a significant improvement in low-velocity impact resistance of all mixes contining waste plastic fibers when comparing with reference mix. Results illustrated that mix with (1.5%) waste plastic fibers by volume give the higher impact resistance at failure than the others. The magnitude of an increase over reference mix was equal to (340%).

يتضمن هذا البحث دراسة مقاومة الحمل الصدمي واطئ السرعة للبلاطات الخرسانية المحتوية على الفضلات البلاستيكية على شكل ألياف وبنسب حجمية هي (0.5%،1%،1.5%) ومقارنتها مع خلطات مرجعية (لا تحتوي على ألياف البلاستك) استخدمت مكعبات بأبعاد (100*100*100)ملم لفحص مقاومة الانضغاط ومواشير بأبعاد (500*100*100)ملم لفحص مقاومة الانثناء (معايير الكسر) وبلاطات بأبعاد (500*500*50)ملم لفحص حمل الصدم واطئ السرعة.إن فحص حمل الصدم واطئ السرعة تم بطريقة الإسقاط المتكرر لكتلة كروية بوزن (1400)غم تسقط من بعد (2400)ملم سقوط حر وتحسب عدد الضربات التي تسبب التشقق الأولي والتشقق النهائي (الذي يسبب الفشل) ومن ثم تحسب الطاقة، حيث بينت النتائج تطور في الخواص الميكانيكية للخلطات المحتوية على ألياف البلاستك مقارنة مع الخلطة المرجعية حيث كانت الزيادة في مقاومة الانضغاط هي (3.2%)عند عمر 90 يوم بنسبة 1% ألياف بلاستك بينما كانت الزيادة في مقاومة الانثناء هي (18%و26%) بعمر (28 و 90)يوم على التوالي للخلطة الحاوية على 1% ألياف بلاستك،كما بينت النتائج تطور واضح في حمل الصدم واطئ السرعة لكل الخلطات الحاوية على ألياف البلاستك وكانت النسبة المثلى هي (1.5%) حيث كانت الزيادة هي (340%).


Article
Using Propylene–Ethylene Grid to Improve the Production of Precast Concret Slabs
استخدام مشبكات البروبلين اثيلين في تطوير صناعة الألواح الخرسانية الجاهزة الصب ( الشتايكر )

Author: Zainab Abdulrdha Thweny
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 4 Part (A) Engineering Pages: 741-751
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The precast concrete roofing slab produced from the local factory were below the Iraqi standard requirement (NO 1107-1988). This study has been made to improve the production of precast concrete slabs by using(propylene – ethylene copolymer grid )which is a waste material produced from the base of polymer boxes . The depended mix of the precast concrete slab in the local factory did not use the correct proportion ,tested mixes were redesigned and prepared to achieve the limited requirements . Propylene – ethylene copolymer grid was used to have better results, less costs, with protection of the environment from pollution ,where there is difficulty to remove it even when it is fully exposed to severe weather conditions .the manufactured slabs had dimensions of (800×800×40)mm and testing program extended to 60 days of age and comprised ,breaking loads, water absorption ,and impact resistance of concrete. The total number of manufactured samples was (55 slabs). The test results indicated that the weigh ted mix proportions ((1:1.5:2.45) cement :sand : gravel ) with w/c=0.41 , superplasticizer(0.75 liter/100 kg of cement )and propylene –ethylene copolymer grid with a dimension (600×600)mm enhances the mechanical properties of concrete . It increased the breaking load by 81 % compared to ordinary production. while the impact resistance increased to 26 blows compared to 3 blows for the ordinary production. However, the polymer grid decreased the width and depth of cracks and maintained the integrity of the slabs after failure .

عند اخذ عينات من الألواح الخرسانية الجاهزة الصب المنتجة في المعامل المحلية تبين بأنها لا تحقق النسب المطلوبة ضمن المواصفات القياسية العراقية (رقم 1107 لسنة 1988) وقد تمت دراسة أمكانيه تحسين وتطوير صناعه قطع الصب الجاهز (الشتايكر) باستخدام مواد متوفرة محليا وهي عبارة عن مشبكات الأقفاص البلاستيكية المتكونة من مادة البروبلين اثيلين كوبوليمر . إن الطريقة المتبعة من قبل المنتج المحلي لا تستخدم النسب الصحيحة للخلط وبذلك تم إعادة تصميم الخلطة الخرسانية للوصول إلى الحدود المطلوبة ضمن المواصفة القياسية العراقية ، كما تم إضافة مشبك بلاستيكي لتعزيز الحصول على نتائج أفضل وبكلفة قليلة مع الحفاظ على البيئة حيث إن المواد البوليميرية يصعب التخلص منها حتى في الظروف الجوية القاسية وقد تم أعداد قطع كونكريتية بإبعاد (800*800*40 ) ملم .وأمتد البرنامج العملي لغاية 60 يوم ، وتم دراسة خواص القطع المنتجة من خلال فحوصات قوة الكسر ، امتصاص الماء ومقاومة الصدم , بلغ العدد الكلي للنماذج المصنعة (55 عينه).وبعد إجراء محاولات عديدة تم التوصل إلى خلطة بنسب وزنيه ( 1 :1.5 :2.45 ) ( الاسمنت : رمل : حصى ) مع مضاف مقلل للماء بنسبة 0.75 لتر لكل 100 كيلو غرام من الاسمنت لتصبح نسبة الماء إلى الاسمنت بما يعادل 0.41 ، واستخدام مشبك بلاستيكي بأبعاد (600* 600 ) ملم قد أعطت لهذه الخلطة زيادة في قوة الكسر بما يعادل 81% عن قطع الخلطة المعتمدة في المعامل المحلية ، بينما ازداد عدد الضربات اللازمة لتحقيق الفشل إلى 26 ضربة بدلا من 3 ضربة بالنسبة للخلطة المحلية .كما تبين إن استخدم المشبك البلاستيكي يقلل من عرض ومن عمق الشقوق المتكونة في القطع الكونكريتية ويقلل من تشظي وتكسر الخرسانة ويساعد على بقاء القطعة ككتلة واحدة .


Article
Performance of Powdered Polymerized Concrete at Elevated Temperatures
تصرف خرسانة المسحوق البوليمرية عند درجات الحرارة العالية

Author: Dina Mukheef Hamza
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 5 Part (A) Engineering Pages: 932-950
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the domain of concrete modification by using polymers, the present study, focused on the use of Carboxy-Methyl Cellulose (CMC) as a water-soluble polymer and investigate its effects on the behavior of concrete. The study include two issues, the first one is the effect of polymer adding method on mechanical properties of concrete such as compressive strength, tensile strength and modulus of elasticity in additional to impact resistance and the second is the effect of graded temperature on these properties. The polymer/cement ratio used herein is 3%, this ratio never used before in the previous researches on many types of water soluble powder polymers. Three concrete batches were prepared, the first is the reference one as a normal concrete (NOR), the second is a polymerized concrete (POL1) where the polymer added as a latex, and the last also as a polymerized concrete (POL2) but the polymer added as a powder.Each batch contains twelve cubic specimens (100x100x100)mm for compressive strength test, three cubes for each level of temperature, eight cylindrical specimens (150x300)mm for splitting tensile strength test, two cylinders for each level of temperature, and four paneled specimens (450x450x50)mm for impact resistance test, one panel for each level of temperature. It can be considered from the results that when the polymer CMC used herein added as a latex will give better strength behavior in polymerized concrete than the one which added as a powder by about 28.86% in compressive strength, 19% in splitting tensile strength, very high percent in modulus of elasticity and 16.66% in impact resistance. On the other hand, it is found that the temperature level of 200°C will affect the behavior of polymerized concrete and that contrast with the behavior of normal concrete while in temperature levels 400°C and 600°C the effects on polymerized concrete will be more slightly and more clearly on normal concrete.

في نطاق تطوير الخرسانة باستخدام البوليمرات تم في هذا البحث التركيز على استخدام مادة الكاربوكسي مثيل سيليلوز المعروف برمز CMC وهو من بوليمرات المساحيق القابلة للذوبان بالماء حيث تم التحري عن تاثير هذا البوليمر على تصرف الخرسانة. الدراسة تضمنت محورين اساسيين المحور الاول هو تاثير طريقة اضافة البوليمر على الخواص الميكانيكية للخرسانة مثل مقاومة الانضغاط ومقاومة الشد الانشطاري ومعامل المرونة اضافة الى مقاومة الصدمة اما المحور الثاني هو تاثير الحرارة المتدرجة على هذه الخواص. ان نسبة البوليمر/الاسمنت المستخدمة في هذا البحث هي 3% وهنا تجدر الاشارة الى ان هذه النسبة لم يتم استخدامها نهائيا في البحوث السابقة على العديد من انواع بوليمرات المساحيق القابلة للذوبان بالماء. تم اعداد ثلاث خلطات خرسانية الاولى هي خلطة خرسانة اعتيادية NOR اما الثانية فهي خلطة خرسانة بوليمرية POL1 يكون فيها البوليمر المضاف على شكل صمغ اما الخلطة الاخيرة فهي ايضا خرسانة بوليمرية POL2 لكن البوليمر المضاف لها يكون على شكل مسحوق. كل خلطة تتضمن اثنى عشر مكعب (100x100x100) مم من اجل فحص مقاومة الانضغاط, ثلاث مكعبات لكل مستوى حرارة معين, ثمانية اسطوانات (300x150) مم من اجل فحص مقاومة الشد الانشطاري, اسطوانتين لكل مستوى حرارة واربع بلاطات 50x450x450) مم من اجل فحص مقاومة الصدمة, بلاطة واحدة لكل مستوى حرارة. لقد بينت نتائج الفحوصات المختبرية ان بوليمر CMC المستخدم في هذا البحث سوف يعطي نتائج افضل للخرسانة البوليمرية بالمقارنة مع الخرسانة المضاف اليها البوليمر على شكل مسحوق بمقدار 28,86 % لمقاومة الانضغاط, 19% لمقاومة الشد الانشطاري, نسبة عالية جدا لمعامل المرونة و 16,66 % لمقاومة الصدمة. من ناحية اخرى وبعد فحص النماذج المحروقة تبين ان درجة الحرارة 200°م لها تاثير واضح جدا على تصرف الخرسانة البوليمرية بعكس الخرسانة الاعتيادية حيث ان هذه الحرارة توثر تاثير طفيف على الخرسانة الاعتيادية, بينما عند درجة حرارة 400°م و600°م يكون التاثير قليل على الخرسانة البوليمرية وواضح على الخرسانة الاعتيادية.


Article
Experimental Investigation on the Efficacy of Polyethylene Aggregate on Impact Resistance of Concrete Slab

Authors: Noor A. Rajab --- Mohammed T. Nawar --- Sheelan M. Hamah
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2019 Volume: 8 Issue: 1 Pages: 9-15
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

The impact resistances of concrete slabs have a different volume fraction replacement of waste plastic aggregate has been examined in this study as a fine aggregate as: 0% (reference), 10%, 20% and 30%. These tests include the splitting tensile, density, compressive strength. Also, the (ultrasonic pulse velocity tests) was carried out. Repeated falling mass was used in order to carry out the low-velocity impact test in which a 1300 gm steel ball was utilized. From a height of 2400mm, the ball falls freely on concrete panels of (500×500×50 mm) with a network of waste plastic aggregate. As per the results, a prominent development was seen in the mechanical properties for mixes involving polyethylene aggregate up to 20% as compared to the reference mix. A significant development was seen in low-velocity impact resistance of all mixes involving waste plastic fine aggregate as compared to reference mix. As per the results, the greater impact resistance at failure is offered by the mix with (20%) waste plastic aggregate by volume of sand than others. The reference mix increased by (712.5%).


Article
Fresh, Mechanical Properties and Impact Resistance Behavior of Eco-Friend Self-Compacted Concrete

Authors: Mohammed T. Nawar --- Alhareth M. Abdulghafor --- Sheelan M. Hama
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2019 Volume: 22 Issue: 3 Pages: 208-212
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this work, waste glass powder from broken windows and plastic fibers from waste polyethylene terephthalate bottles are utilized to produce an economical self-compact concrete. Fresh properties (slump flow diameter, slump Flow T50, V. Funnel, L–Box), mechanical properties (Compressive strength and Flexural strength) and impact resistance of self-compact concrete are investigated. 15% waste glass powder as a partial replacement of cement with five percentages of polyethylene terephthalate plastic waste were adopted: 0% (reference), 0.5%, 0.75%, 1%, 1.25% and 1.5% by volume. It seems that the flow ability of self-compact concrete decreases with the increasing of the amount of plastic fibers. The compressive strength was increased slightly with plastic fiber content up to (0.75%), about 4.6% For more than (0.75%) plastic fiber. The compressive strength began to decrease about 15.2%. The results showed an improvement in flexural strength and an impact on the resistance in all tested specimens’ content of the plastic fibers, especially at (1.5%) fibers.


Article
Effect of Crumb Tyres Rubber on Some Properties of Foamed Concrete
تأثير فتات مطاط الإطارات على بعض خصائص الخرسانة الرغوية

Author: Ameer Abdulrahman Hilal أمير عبد الرحمن هلال
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2011 Volume: 4 Issue: 2 Pages: 1-17
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

During the last years, several researches have been studying the final disposal of tyres wastes, due to the great volume generated worldwide, as well as the difficulty for discarding the disposal sites which become a serious environmental problem. In spite of this, recycling appears as the best solution for disposing tyres residues, due to its economical and ecological advantages. This research carried out to assess the feasibility of using crumb rubber (the product of shredding used rubber tyres) as a partial sand replacement in foamed concrete, and investigates the effect of it on some properties of foamed concrete such as, density, water absorption, compressive strength, tensile strength, flexural strength and impact resistance.Crumb rubber of tyres ranging from (0.7 to 5mm) in size was used in this research. Three proportioned mixes were designed in this research, have the same cement content, water-cement ratio, and foam content. The first mix represents a typical reference formulation of foamed concrete without crumb rubber (FC). In the others mixes (FCR-1 and FCR-2), respectively, 20 and 30% of volume of sand were replaced by crumb tyres rubber waste. Tests carried out to assess the behaviour of final product. The results obtained were demonstrated decreasing in foamed concrete strength (compressive, tensile, flexural, and impact) with the increasing of crumb tyres rubber content in the mixture and rubberized foamed concrete specimens (FCR-1 and FCR-2) show a cohesive behaviour than the specimens of reference mix (FC), especially in tensile strength. Comparing with the reference mix (FC), at an age of (28 days), the decreasing of compressive strength was (20.85%) for (FCR-1) and it for (FCR-2) was (37.76%).

الميكانيكية, مقاومة الصدم خلال السنوات السابقة, درست العديد من البحوث فضلات الإطارات القابلة للطرح, وبسبب الكميات الكبيرة لتلك الفضلات وصعوبة التخلص من مواقعها, أصبحت هنالك مشكلة بيئية جدية. على الرغم من ذلك ظهرت عملية إعادة أستخدام تلك الفضلات كحل امثل للتخلص منها بالإضافة إلى تحقيق فوائد اقتصادية وبيئية اجري البحث لغرضت تقييم عملية استخدام فتات المطاط (ناتج تقطيع الإطارات المطاطية) كبديل عن جزء من الرمل في الخرسانة الرغوية والتحري عن تأثير إضافته على بعض خواص الخرسانة الرغوية مثل الكثافة, امتصاص الماء, مقاومة الانضغاط, مقاومة الشد, مقاومة الانثناء ومقاومة الصدم. تضمن الجزء العملي استخدام فتات مطاط الإطارات بحجم من (0.7 ملم) إلى _5 ملم). في هذا البحث تم تصميم ثلاث خلطات تمتلك نفس محتوى الاسمنت, نسبة الماء إلى الاسمنت و محتوى الرغاوي. الخلطة الأولى(FC) تمثل الخلطة المرجعية وكانت مكوناتها لا تحتوي على فتات الإطارات بينما تم في الخلطات (FCR- 1وFCR-2) استبدال 20 و 30 % من حجم الرمل بفتات فضلات الإطارات المطاطية. أجريت عدد من الفحوصات على الناتج النهائي وقد أظهرت النتائج المستحصلة من العمل المختبري بان مقاومة الخرسانة الرغوية سواء كانت مقاومة ( انضغاط, شد, انثناء, صدم) تقل مع زيادة محتوى فتات مطاط الإطارات وان عينات الخلطات الحاوية على الفتات قد أظهرت تماسكا عند الفشل بخلاف عينات الخلطة المرجعية خصوصا في فحص الشد. كان مقدار النقصان في مقاومة الانضغاط بعمر (28 يوم) للخلطة (FCR-1) عن الخلطة المرجعية (FC) (20.85%) بينما كان مقدار النقصان بمقاومة الانضغاط لنفس العمر للخلطة (FCR-2) عن الخلطة المرجعية (37.76%).


Article
Studying Some Of Mechanical properties Of (sawdust/Un Saturated Polyester) Composite in salt solution
دراسة بعض الخواص الميكانيكية لمتراكبات (نشارة الخشب /البولي أستر غير المشبع )في المحلول الملحي

Author: Sanaa A. A. Hafad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 16 Pages: 5238-5245
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Commercial sawdust is the most common wood filler used for polysterthermosetting and is produced from graduated particles of different sizes which has in general has a lower aspect ratio than wood and other natural fibers. Wood additives include a mixture of sawdust and short chopped fibers. To study how characteristics of fibers and sawdust influence the mechanical properties of unsaturated polyester composites .Investigations were made by studying the effects of different volumetric fractions from sawdust and fiber fillers (up to limitof 1.4mm), then these results were compared with the properties of sawdust –fiber filled composites immersed for different periods in a salt solution of (2 N) . wood volume fractions {(20, 30, 50) vf %} selected to be added for un saturated polyester were studied which gave improvement in their selected studied mechanical properties for all reinforced composites -(only impact is decreased)- and particularly at higher values of volume fractions ,were hardness showed an improvement by (15% ) , compressive strength gave obvious Improvement by(38% ) ,while impact resistance decreased by (16%) with the reinforcement of (50 vf %) sawdust . The above values were reduced when the items were immersed in asalt solution for (60days).

أن نشارة الخشب التقليدية ،تعد من أكثر الأخشاب التي تستخدم كمالئات للبوليمرات المتصلدة حراريا،يتم أنتاجها بهيئة مزيج متدرج من الحجوم الحبيبية ،وبشكل عام تمتلك نسبة باعية أوطأ من ألياف الخشب والمواد الطبيعية الأخرى ،أن إضافات الخشب تتضمن مزيجا من النشارة والألياف القصيرة المقطعة . ولدراسة تأثير مميزات نشارة وألياف الخشب على الخواص الميكانيكية لمتراكبات البولي أستر ،تم التحقق في تأثير دراسة الكسور الحجمية المختلفة لمالئات من ألياف و نشارة الخشب (ذات حد حبيبي 1,4 ملم) على الخواص الميكانيكية لمتراكبات البولي أستر المدعمة ،وبعدها تم مقارنة تلك النتائج مع نتائج لمتراكبات البولي أستر المدعمة بنفس المالئات بعد غمرها لفترات زمنية مختلفة في أوساط ملحية ذات عياريه ( 2) . تم اختيار كسورا 50 ) % } من البوليستر غير المشبع المختار . ) , (30) , ( حجميه للمالئات تراوحت بين { ( 20 أوضحت النتائج تطورا واضحا في الخواص الميكانيكية - (ماعدا مقاومة الصدمة) - وبالخصوص عند ارتفاع قيم الكسر ألحجمي حيث حققت الصلادة تطورا بنسبة ( 15 % ) , في حين حققت مقاومة الانضغاط تطورا ملحوظا وبنسبة ( 38 % ) ،بینما انخفضت مقاومة الصدمةبنسبة ( 16 %) عند التدعیم بنسبة ( 50 ) % حجما من نشارة الخشب.أن القیم أعلاه أنخفضت عند الغمر في المحلول الملحي لمدة ستون یوما.

Listing 1 - 10 of 13 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (13)


Language

English (9)

Arabic and English (4)


Year
From To Submit

2019 (2)

2018 (2)

2014 (2)

2013 (3)

2012 (1)

More...