Flexural Behavior of High Strength Concrete Incorporated Super Absorbent Polymer (SAP)

Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2018 Volume: 11 Issue: 3 Pages: 34-38
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This research include the study of flexural behavior of reinforced concrete beams with and without addition of super absorbent polymer (SAP) to concrete, two groups of concrete mixture were used; each one have five concrete mixture (Reactive Powder Concrete RPC, Modified Reactive Powder Concrete, Self Compact Concrete SCC, High Strength Concrete HSC and Normal Strength Concrete NSC) four of them with high compressive strength and the last one with normal compressive strength. Group A casting concrete without addition of SAP, group B casting concrete with addition of SAP. Ten beams are molded of (200*300*1700) mm dimension with same steel reinforcement. Flexural tested for all beams was doing and load-deflection relationships of beams with and without SAP were established. Test results had shown that beams casting with addition of SAP (group B) proved to have larger load carrying capacity and llower deflection compared with group A.


Article
COMPRESSIVE STRENGTH OF CONCRETE CONTAINING WATER ABSORPTION POLYMER BALLS (WAPB)
مقاومة انضغاط الخرسانة الحاوية على الكرات البوليمرية الممتصة للماء

Author: Ikram Faraoun Ahmed اكرام فرعون احم
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2017 Volume: 8 Issue: 2 Pages: 42-52
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Water absorbent polymers (WAP) are new component in producing building materials. They provide internal curing which reduces autogenous cracking, eliminates autogenous shrinkage, mortar strength increased, enhance early age strength to withstand strain, improve the durability, introduce higher early age compressive strength, have higher performance and reduce the effect of insufficient external curing. This research used different percent of polymer balls to choose the percent that provides good development in compressive strength with time for both water and air curing. The water absorption polymer balls in this research have the ability to absorb water and after usage in concrete they spill out the water (internal curing) and shrink leaving voids of their own diameter before shrinking, thus leads to have internal curing with air voids to reduce the samples weight .The required quantity of water for the mixes reduced due to the addition of water from the absorption polymers.

البوليمرات الممتصة للماء هي اسلوب جديد في انتاج المواد البنائية التي تحتفظ بالماء اذ تقدم معالجة داخلية والتي تقلل التشققات الذاتية وتقلل الا نكماش الذاتي وتزيد قوة المونة والخرسانة وتزيد الانفعال المبكر وتزيد مقاومة الانضغاط المبكرة وبالتالي تحسن الاداء العام وتقلل من تاثير المعالجة الخارجية. هذا البحث يستخدم نسب مختلفة من الكرات البوليمرية لاختيار النسبة المثلى التي تعطي تطور جيد لمقاومة الانضغاط مع الزمن للنماذج المعرضة للمعالجة بالماء وبالهواء .ان ) المستخدمة في هذا البحث لها القابلية على امتصاص الماء وبعد وضعها في الخلطات WAPBالكرات البوليمرية ( الكونكريتية تطرح هذا الماء (تعطي معالجة داخلية) وتنكمش تاركة فراغات داخل الخلطة الخرسانية بقدر قطر هذه الكرات قبل انكماشها مما يقلل من وزن النموذج ان كمية الماء المستخدمة لاجراء الخلطات الخرسانية تم تقليلها بما يتناسب واضافة الكرات البوليمرية الماصة للماء وحسب كمية الماء الذي ستطرحه هذه الكرات البوليمرية.


Article
The Effect of Using Lightweight Aggregate on Some Properties of Cement Mortar
تأثير استخدام الركام الخفيف الوزن على بعض خصائص مونة السمنت

Author: Ziyad Majeed Abed زياد مجيد عبد
Journal: Iraqi Journal of Civil Engineering المجلة العراقية للهندسة المدنية ISSN: 19927428 Year: 2018 Volume: 12 Issue: 1 Pages: 1-9
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

The aim of this research is to produce lightweight cement mortar with properties better than reference ordinary cement mortar. Porcelanite stone were utilized as lightweight aggregate with a volumetric partial substitution of fine aggregate. The process includes using different percentages (5, 10, 15 and 20 %) of pre-wetted (24hr.) porcelanite to produce lightweight mortar with internal curing. Water curing was used for reference mortar mixture and air curing for the other mixtures of porcelanite substitution. Compressive strength, flexural strength, density and ultrasonic pulse velocity for different ages (7, 14 and 28 days) have been tested. The results show an improvement in the properties of cement mortar especially in replacement percentage of 10 %.

الهدف من هذا البحث هو إنتاج مونة سمنت خفيفة الوزن مع خصائص أفضل من مونة السمنت العادي المرجعية. تم استخدام حجر البورسلانيت كركام خفيف الوزن مع استبدال جزئي حجمي من الركام الناعم. تشمل العملية استخدام نسب مختلفة (5 ، 10 ، 15 ، 20) ٪ من البورسلانيت المسبق الترطيب (24 ساعة) لإنتاج مونة خفيف الوزن ذات انضاج داخلي. تم استخدام الانضاج بالماء لخلطة المونة المرجعية واستخدام الانضاج بالهواء للخلطات الأخرى ذات الاستبدال بالبورسلانيت. تم اجراء فحوص مقاومة الانضغاط، ومقاومة الانثناء، والكثافة وسرعة الموجات فوق الصوتية لمختلف الأعمار (7 ، 14 ، 28) يوم. اظهرت النتائج تحسنا في خصائص مونة السمنت وخاصة في نسبة استبدال 10٪.


Article
Eliminating the Shrinkage of High Strength Concrete by using Super Absorbent Polymer (SAP)

Authors: Suhad M Abd --- Baidaa Khdheer Ahmed
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2018 Volume: 11 Issue: 4 Pages: 8-13
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

High Strength Concrete (HSC) is one of the most popular types of concrete used in the world. This type of concrete has a low rapid hydration of cementation materials with low w/cm and the external surrounding environment condition exposed the HSC to high autogenous shrinkage. If this shrinkage is not treated well that well led to cracking, in this case HSC need to convenient curing necessary at the earliest time. This study presents the use of Super Absorbent Polymer (SAP) as internal curing agent to eliminate shrinkage. Two types of shrinkage are tested in this study (Autogenous shrinkage and drying shrinkage). Two groups of concrete mixes(A and B) are studied in this study each group have five types of concrete mixes, four mixes with high and ultra-high compressive strength (RPC, MRPC, HSC and SCC) and the last one with normal compressive strength (NSC). Group A represent concrete mixes without SAP addition and group B for concrete mixes with SAP. SAP was added for all mixes at 0.3% by weight of cement and adding 20ml water for each gram of SAP, specimens with dimensions (40*40*160) mm were used for testing shrinkage for each mix with and without SAP, average values for two specimens was taken as a results. It was found that concrete mixes of group B have lower shrinkage than the shrinkage of concrete mixes in group A at 28 days age with reduction of autogenous shrinkage(AS) of (57%, 35%, 37%, 44.5% and 37.5%) respectively and for drying shrinkage the percentage of reduction was (89.5%, 72%, 82%, 70% and 71%) respectively, addition of SAP to concrete mixes proves to have active effect in reducing the shrinkage of concrete.


Article
Enhancing Performance of Self–Compacting Concrete with Internal Curing Using Thermostone Chips
تحسين اداء الخرسانه ذاتية الرص بواسطة الانضاج الداخلي باستعمال فتات الكتل الخرسانية الخلوية

Authors: Amar Yahia Ebrahem AL-Awadi عمار يحيى إبراهيم العوادي --- Nada Mahdi Fawzi ندى مهدي فوزي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 7 Pages: 1-13
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This paper is devoted to investigate the effect of internal curing technique on the properties of self-compacting concrete (SCC). In this study, SCC is produced by using silica fume (SF) as partial replacement by weight of cement with percentage of (5%), sand is partially replaced by volume with saturated fine lightweight aggregate (LWA) which is thermostone chips as internal curing material in three percentages of (5%, 10% and 15%) for SCC, two external curing conditions water and air. The experimental work was divided into three parts: in the first part, the workability tests of fresh SCC were conducted. The second part included conducting compressive strength test and modulus of rupture test at ages of (7, 28 and 90). The third part included the shrinkage test, at ages (7, 14, 21, 28) days. The results show that internally cured SCC has the best workability, and the best properties of hardened concrete which include (compressive strength and modulus of rupture) then the externally cured SCC with both water and air as compared with reference concretes. Also, the hardened properties of internally cured SCC with replacement percentage of (10%) by thermostone chips is the best as compared with that of percentages (5% and 15%) for both external curing conditions. In general, the results of shrinkage test, showed reduction in shrinkage of internally cured SCC as compared with reference concrete.

ان الغرض من هذا البحث هو التحري عن تأثير تقنية المعالجه الداخليه على خصائص الخرسانه ذاتية الرص. في هذه الدراسه تم انتاج الخرسانة ذاتية الرص باستعمال غبار السليكا كإستبدال جزئي من وزن السمنت بنسبة 5 % ، وتم استبدال الرمل جزئيا بركام ناعم خفيف الوزن ومشبع وجاف السطح هو فتات الكتل الخرسانية الخلوية كمادة معالجة داخلية وبثلاث نسب حجمية هي (5%,10%,15%) كاستبدال حجمي، ظرفين للمعالجة الخارجية هما الماء والهواء. قسم العمل المختبري في هذه الدراسه الى ثلاثة اجزاء اساسية : في الجزء الاول تم اجراء الفحوص المختبرية للخرسانه ذاتية الرص الطريه لايجاد قابلية التشغيل. أما القسم الثاني فيتضمن اجراء فحوص مقاومة الانضغاط و مقاومة الانثناء للخرسانه ذاتية الرص المتصلبه بأعمار (7، 28 ، 90 ) يوم. والجزء الثالث يتضمن اجراء فحص الانكماش باعمار (7، 14، 21، 28) يوم . لوحظ من استعراض نتائج فحوص الخصائص الطريه والمتصلبه للخرسانة ذاتية الرص المعالجه داخليا بفتات الكتل الخرسانيه الخلوية حصول تحسن واضح في قابلية التشغيل وكذلك حصول تحسن ملحوظ في الخصائص المتصلبه والتي تشمل (مقاومة الانضغاط و مقاومة الانثناء) في كلا ظرفي المعالجه الخارجيه مقارنة بالخرسانه المرجعية. كما ان الخصائص المتصلبه للخرسانه ذاتية الرص باستعمال فتات الكتل الخرسانيه الخلوية بنسبة استبدال (10%) هي الافضل قياسا بنسب الاستبدال الاخرى. وبشكل عام بينت النتائج حصول نقصان واضح في انكماش الخرسانه ذاتية الرص المعالجه داخليا.


Article
Assessing Saturated Porcelinite As Internal Curing Agent In Self Compacted Concrete
تقييم البورسيلنايت المشبع كعامل إنضاج داخلي في الخرسانة ذاتية الرص

Author: Abeer Abdulqadir Salih عبير عبد القادر صالح
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 6 Pages: 134-145
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Self compacted concrete (SCC) describes concrete with the ability to compact itself only by means of its own weight without the requirement of vibration. It fills all recesses reinforcement spaces and voids even it highly reinforced concrete members and flow free of segregation nearly to a level balance. This research aims to assess the fresh and hardened properties of SCC using saturated porcelinite as curing agents for internal curing of SCC.Five mixes with different percentage of replacement of saturated porcelinite range from (0, 12, 16, 20, 24) % of fine aggregate volume of the same grading , were prepared ,each mix tested in fresh state with slump test .Then 120 concrete cubes of (100*100*100(mm for different mixes were tested for ,density and compressive strength, at (7,28,60 and 90) days of water and air curing. Results show that the slump decreases as saturated porcelinite content increase ,density and compressive strength increase with increasing saturated porcelinite for all age’s .the rate of increasing is (10.1-30.0) % and (8.2-25.7) % for compressive strength of cubes cured in water and air respectively. The optimum percentage of saturated porcelinite which gave higher density and compressive strength was 20%.

الخرسانة ذاتية الرص هي الخرسانة التي لها القدرة على الرص تحت تأثير وزنها فقط دون الحاجة الى استخدام الهزازات كذلك لها القدرة على الانسياب خلال حديد التسليح الكثيف دون حدوث اي انعزال .يهدف هذا البحث الى تقييم بعض خواص الحالة الطرية والمتصلبة للخرسانة ذاتية الرص عند استخدام بورسيلنايت مشبع بالماء كعامل انضاج للحصول على انضاج داخلي للخرسانة ذاتية الرص. تم تحضير 5 خلطات خرسانية باستخدام نسب استبدال مختلفة من البورسيلنايت المشبع بالماء تراوحت بين (24،20،16،12،0)% من حجم الركام الناعم وبنفس التدرج فحصت بحالتها الطرية بفحص الهطول بعدها تم صب 120 مكعب خرساني باستخدام قوالب حديدية بإبعاد (100×100×100)ملم وتم إجراء فحص الكثافة ومقاومة الانضغاط للخلطات أعلاه بأعمار (7، 28، 60 و90 )يوم تحت ظروف إنضاج خارجي في الماء والهواء.أوضحت النتائج انخفاض الهطول وزيادة الكثافة ومقاومة الانضغاط بزيادة محتوى البورسيلنايت المشبع وفي كل الأعمار وتراوحت نسب الزيادة في مقاومة الانضغاط بين (10.1-30.0) %و (8.2-25.7)% عند الإنضاج بالماء والهواء على التوالي.النسبة المثلى لاستبدال البورسيلنايت المشبع والتي تعطي أعلى كثافة ومقاومة انضغاط كانت 20%.


Article
Assessing the Effect of Using Porcelanite on Compressive Strength of Roller Compacted Concrete
تقييم تأثير اضافة مادة البورسيلنايت على مقاومة الانضغاط للخرسانة المرصوصة بالحدل.

Authors: Abeer Abdulqader Salih Abeer Abdulqader Salih عبـير عبد القادر صالح --- Ziyad Majeed Abed زيــاد مجــيــد عــبــد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2014 Volume: 20 Issue: 10 Pages: 16-28
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Roller-Compacted Concrete (RCC) is a zero-slump concrete, with no forms, no reinforcing steel, no finishing and is wet enough to support compaction by vibratory rollers. Because the effectiveness of curing on properties and durability, the primary scope of this research is to study the effect of various curing methods (air curing, emulsified asphalt(flan coat) curing, 7 days water curing and permanent water curing) and different porcelanite (local material used as an Internal Curing agent) replacement percentages (volumetric replacement) of fine aggregate on some properties of RCC and to explore the possibility of introducing more practical RCC for road pavement with minimum requirement of curing. Cubes specimens were sawed from the slabs of (38*38*10) cm for determination of compressive strength. The results show that using (5) % porcelanite improved the compressive strength of RCC (with air curing) as compared with reference RCC (with permanent curing) by percentage ranging from(-2.9 to 6)%.

الخرسانة المرصوصة بالحدل هي الخرسانة العديمة الهطول والتي لا يتم فيها أستعمال القوالب أوحديد التسليح ولا تحتاج الى عمل الانهاءات ،ويجب ان تكون ذات رطوبة كافية لتحمّل الحدل بواسطة الحادلة الهزازة.بسبب تأثير الانضاج على خصائص وديمومة لذا فإن الهدف الرئيسي من هذا البحث هو دراسة تأثير طرق الانضاج المختلفة (الانضاج بالهواء،الانضاج بالمستحلب الاسفلتي (الفلنكوت) ،الانضاج 7 ايام بالماء،الانضاج الدائمي بالماء ) وبأستخدام البورسيلنايت (مادة محلية تستعمل كعامل أنضاج داخلي) وبنسب استبدال مختلفة (استبدال حجمي من الركام الناعم) على بعض خواص الخرسانة المرصوصة بالحدل واستكشاف مدى امكانية انتاج هذه الخرسانة لرصف الطرق لتكون اكثر عملية وبأستعمال الحد الادنى من متطلبات عملية الانضاج.يتم نشر الواح خرسانة بأبعاد (38*38*10) سم لتشكيل مكعبات لفحص مقاومة الانضغاط.تظهر النتائج ان استعمال (5%) بورسيلنايت يقوم بتحسين مقاومة الانضغاط للخرسانة المرصوصة بالحدل (بأستعمال الانضاج بالهواء) مقارنة مع الخرسانة المرصوصة بالحدل المرجعية (بأستعمال الانضاج الدائمي) بنسبة تتراوح بين (6 – 2.9 - )%.


Article
Effect of Using Porcelanite as Partial Replacement of Fine Aggregate on Roller Compacted Concrete with Different Curing Methods
تأثير أستعمال مادة البورسيلنايت كأستبدال جزئي من الركام الناعم على الخرسانة المرصوصة بالحدل وبطرق انضاج مختلفة.

Authors: Abeer Abdulqader Salih عبـير عبد القادر صالح --- Ziyad Majeed Abed زيــاد مجــيــد عــبــد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2016 Volume: 22 Issue: 9 Pages: 21-35
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Roller-Compacted Concrete is a no-slump concrete, with no reinforcing steel, no forms, no finishing and wet enough to support compaction by vibratory rollers. Due to the effect of curing on properties and durability of concrete, the main purpose of this research is to study the effect of various curing methods (air curing, 7 days water curing, and permanent water curing) and porcelanite (local material used as an Internal Curing agent) with different replacement percentages of fine aggregate (volumetric replacement) on some properties of Roller-Compacted Concrete and to explore the possibility of introducing practical Roller-Compacted Concrete for road pavement with minimum requirement of curing. Specimens were sawed from slabs of (380*380*100) mm for determination of Ultrasonic Pulse Velocity (UPV) and Voids volume. Results show that using (5) % porcelanite improved the results of UPV and Voids volume of Roller-Compacted Concrete (with air curing) as compared with reference Roller-Compacted Concrete (with permanent water curing) by percentages ranging from(3.6 to 28.9)% and (-8 to -15.5)% respectively.

الخرسانة المرصوصة بالحدل هي الخرسانة عديمة الهطول والتي لا يتم فيها أستعمال حديد التسليح أو القوالب ولا تحتاج الى عملية الانهاء وكذلك يجب ان تكون ذات رطوبة كافية لتحمّل الحدل بواسطة الحادلات الهزازة.نتيجة لتأثير الانضاج على خصائص وديمومة الخرسانة لذا فإن الهدف الاساسي من البحث هو دراسة تأثير طرق مختلفة من الانضاج (الانضاج بالهواء ،الانضاج 7 ايام بالماء، الانضاج الدائمي بالماء) وبأستخدام البورسيلنايت (مادة محلية تستعمل كعامل أنضاج داخلي) وبنسب استبدال مختلفة من الركام الناعم (استبدال حجمي) على بعض خواص الخرسانة المرصوصة بالحدل وتحري مدى امكانية انتاج هذه الخرسانة لرصف الطرق لتكون اكثر عملية وبأستعمال الحد الادنى من متطلبات عملية الانضاج .يتم نشر الواح خرسانة بأبعاد (380*380*100) مم لعمل نماذج لفحوص الامواج فوق الصوتية والمسامية.تظهر النتائج ان استعمال (5%) بورسيلنايت يقوم بتحسين نتائج فحوص الامواج فوق الصوتية والمسامية للخرسانة المرصوصة بالحدل (بأستعمال الانضاج بالهواء) بالمقارنة مع الخرسانة المرصوصة بالحدل المرجعية (بأستعمال الانضاج الدائمي بالماء) بنسب تتراوح بين (3.6 to 28.9)% و(-8 to -15.5) % على التوالي .


Article
The Use of Crushed Brick Waste for The Internal Curing In Cement Mortar
استخدام مخلفات الطابوق المحطم في الانضاج الداخلي في مونة السمنت

Author: Alaa Ahmed Shakir
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2017 Volume: 5 Issue: 1 Pages: 16-21
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

Internal curing has become a modern technology holds promises for making a durable mortar and decreasing early-age cracking. Since mortar service life is a crucial factor of providing sustainable structures, internal curing can provide a distinct contribution to increase the sustainability of our nation’s building. This study shows results of an experimental investigation of using crushed brick waste (CBW) in cement mortar mixtures prepared by substituting sand by some percentages (5, 10, 15, 20 and 25%) of (CBW). Three curing regimes were adopted in this study: water curing by immersing specimens in water for 28 days, partially water curing by immersing specimens in water for 3 days and left them in laboratory for 24 days and air curing in laboratory for 28 days without immersing samples in water to recognize an ideal methodology for determining whether a given (CBW) can be used for internal curing in cement mortar. Fresh density, hardened density, compressive strength, water absorption, and modulus of rupture were tested. Results indicated that fresh and hardened density, compressive strength and modulus of rupture were decreased with the addition of (CBW). However, they were higher for mortars cured in air conditions than those cured in water and partially water curing. Water absorption was increased with the increase of (CBW). It was demonstrated that air cured mortar give good results for mechanical properties as compared with water cured mortar, hence (CBW) can be used for internal curing in cement mortar especially in finishing works.

ان العمر الخدمي لقد أصبح الانضاج الداخلي تكنولوجيا حديثة يحمل وعودا لانتاج مونة دائمة وتقليل التشققات في سن مبكرة. حيث للمونة هي العامل الحاسم في بناء المنشآت المستدامة. الإنضاج الداخلي يقدم مساهمة متميزة لزيادة استدامة بناء أمتنا. تبين هذه الدراسة نتائج فحص تجريبي لاستخدام الطابوق المحطم في خليط مونة السمنت عن طريق استبدال الرمل في بعض النسب (5، 10، 15، 20 , 25٪) من مخلفات الطابوق المحطم. تم اعتماد ثلاثة أنظمة انضاج في هذه الدراسة: الانضاج بالماء عن طريق غمر العينات في الماء لمدة 28 يوما، انضاج جزئي بالماء عن طريق غمر العينات في الماء لمدة 3 أيام، وتركهم في المختبر لمدة 24 يوما والانضاج بالهواء هو ترك العينات في المختبر لمدة 28 يوما دون غمر العينات في الماء للحصول على منهجية مثالية لتحديد امكانية استخدام الطابوق المحطم للانضاج الداخلي في مونة الأسمنت. تم اختبار الكثافة الطازجة ,الكثافة الصلبة، قوة الضغط، امتصاص الماء، ومعامل الكسر. أشارت النتائج إلى أن الكثافة الطازجة , الصلبة، قوة الضغط ومعامل الكسر قد انخفضت مع إضافة الطابوق المحطم ، ومع ذلك سجلت النتائج قيم اعلى للمونة التي تم انضاجها في الهواء ممقارنة بالعينات التي تم انضاجها في الماء وجزئيا بالماء. امتصاص الماء قد ارتفع مع زيادة نسبة استبدال الطابوق المحطم بديل عن الرمل المضاف الى المونة .برهنت الدراسة ان المونة التي تم انضاجها في الهواء قد اعطت نتائج جيدة للخواص الميكانيكية بالمقارنة مع المونة التي تم انضاجها بالماء، وبالتالي يمكن استخدام الطابوق المحطم للانضاج الداخلي في مونة الأسمنت خاصة في اعمال النهاء .

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (7)

Arabic and English (2)