Studying the Corrosion of Graphite Containing pearlitic Cast Irons in Sandy Soil
دراسة تآكل حديد الصب الكرافيتي البيرلايتي في التربة الرملية

Loading...
Loading...
Abstract

Abstract Wide range of industrial and engineering applications for graphite containing cast irons and the harmful effects of corrosion environments on these important engineering materials, make it necessary for continuous Scientific research in this field . In the current study, performed corrosion tests on Pearlitic cast irons using the sandy soil as the corrosion environment . The results obtained show a clear relationship between corrosion rate of graphite containing cast iron with shape of graphite. The graphite flakes in cast iron appeared to cause high corrosion rates compared with spheroidal or rosette graphites . The results also show that corrosion rates of spheroidal cast iron are slightly higher than malleable cast iron. The corrosion rates of grey cast iron represent the highest when compared with those of spheroidal and malleable cast iron.Keywords: Corrosion, Cast Iron, Sandy Soil

الخلاصةإن تعدد الاستخدامات الصناعية والهندسية لأنواع حديد الصب الكرافيتي ، وتأثرها بأوساط التآكل المختلفة من المبررات التي تدعو لدراسات وبحوث علمية لمعرفة مدى تأثير أوساط التآكل ، وخاصة المحلية منها في هذه الأنواع مما يجعل اختيار النوع المناسب من حديد الصب معتمدا على نتائج بحوث ذات طابع علمي معتمد . وقد أجريﹼ في هذا البحث اختبارات مكثفة لأكثر أنواع حديد الصب الكرافيتي أهميةً واستخداماً في التطبيقات المختلفة باستخدام التربة الرملية كوسطاﹰ للتآكل . لقد أظهرت النتائج وجود علاقة بين معدل تآكل حديد الصب الكرافيتي مع شكل ونوع الكرافيت المتواجد فيه . وتبين أن الشكل الشرائحي يسبب معدلات تآكل أعلى مما يسببه شكل الكرافيت الكروي أو الكرافيت الزهري . وأظهرت النتائج أن حديد الصب الكروي الكرافيت يتآكل بمعدلات مقاربة أو أعلى بقليل من معدلات تآكل حديد الصب الزهري الكرافيت ، في حين أن حديد الصب الرمادي تميز بأعلى معدلات التآكل .الكلمات الدالة: التآكل، حديد الصب، التربة الرملية.


Article
Effects of H2SO4 and HCL Concentration on the Corrosion Resistance of Protected Low Carbon Steel
تأثير تركيز حامض الكبريتيك وحامض الهيدروكلوريك على مقاومة التآكل للصلب منخفض الكاربون المحمي

Loading...
Loading...
Abstract

AstractInvestigations were carried out to study the corrosion behavior of unprotected and protected low carbon steel using carburizing and hard chrome plating in different concentrations of H2SO4 and HCL solutions. Weight loss method was used for estimation the corrosion rate in the current study.Theresults show that protected low carbon steels samples by hard chrome platinghad better corrosion resistant (less corrosion rate) than unprotected and carburized low carbon steel samples. Also, the corrosion rate increaseswith increasing acid concentration from (1 to 5)M. for both types of acid used. The corrosion rate of low carbon steel in acid environments indicate that the hydrochloric acidsolution was more corrosive media thanthat of sulphuric acid solutionunderthe same conditions.Keywords:Corrosion rate;Acid environments;Low Carbon Steel;weight loss method.

الخلاصةتم في هذا البحث دراسة سلوك تآكل الصلب منخفض الكاربونغير المحمي من التآكل والمحمي من التآكل باستخدام الكربنة والطلاء بالكروم في تراكيز مختلفةلمحلول حامض الكبريتيك ومحلول حامضالهيدروكلوريك.طريقة فقدان الوزن استخدمت لتقدير معدل التآكل في هذه الدراسة.من النتائج التي تم الحصول عليها ، تبين ان نماذج الصلب منخفض الكاربون المحمي من التآكل بطلاء الكروم أعطتأفضل مقاومة للتآكل(اقل معدل تآكل)من نماذج الصلب غير المحمي ونماذج الصلب المحمي بالكربنة. كما ان معدل التآكل يزداد مع زيادة نسبة تركيز الحامض من( 1 الى 5 ) مولالي لنوعي المحاليل الحامضية المستخدمة . وان نتائج معدل التآكل للصلب منخفض الكاربون في الأوساط الحامضية تبين بانمحلول حامض الهيدروكلوريك كان وسطاً تآكلياًأكثرتأثيرا من محلول حامض الكبريتيك تحت نفس ظروفالاختبار.