Article
Investigation of the Inhibitive Effect of Tobacco Leaves Extract on Corrosion of Alpha Brass in Acidic Solutions

Author: Ali Hubi Haleem
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2009 Volume: 7 Issue: 1 Pages: 80-91
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

This study was a trial to find an organic inhibitor that can to easily be prepared and applied , as well as non- toxic , cheep and available. In the present study an aqueous extract of tobacco leaves as corrosion inhibitor to protect α brass alloy in acid solutions (hydrochloric and nitric acid) at 1 M concentration, the inhibitor efficiency was evaluated using the weight loss method and microscopic test. Results obtained reveal that the extract of tobacco leaves plants at various concentration (0.5, 1.5, and 3) vol. % show significant corrosion inhibition during immersion of brass in acid solutions. The inhibition efficiency increased with increasing concentration of the inhibitor, but decrease with increase in exposure time. Inhibitor efficiency in 1M HCl and 1M HNO3 at ( 3%) concentration of inhibitor reached to 75.64% and 73.17% respectively. Microscopic examination test shows the clearness of the metals surface which is under the corrosion medium and which contains inhibitor, from any kind of corrosion that can be found on those surfaces, which are under mediums completely empty from inhibitor, and also shows the clearness of that protect layer on the surface. The data of corrosion rate show that the way of doing this organic inhibitor is adsorbing and the inhibitor molecules are adsorbed on the metal surface according to Langmuir adsorption isotherm.

تمثل هذه الدراسة محاولة لإيجاد مثبط عضوي سهل التحضير والتطبيق , غير سام , رخيص الثمن ومتوفر بكثرة. تم استخدام مستخلص مائي من أوراق نبات التبغ في تثبيط تآكل سبيكة البراص α في محلول حامضي (محلول حامض الهيدروكلوريك ومحلول حامض النتريك) وبتركيز 1M. تم تقييم كفاءة المثبط باستخدام طريقة فقدان الوزن واختبار الفحص ألمجهري . أظهرت النتائج إن مستخلص أوراق نبات التبغ بتراكيز مختلفة (0.5, 1.5, 3 vol. %) يتمتع بقابلية جيدة على التثبيط لسبيكة البراص المغمورة في أوساط حامضية و تزداد كفاءة التثبيط مع زيادة تركيز المثبط وتقل مع زيادة فترة الغمر. وصلت كفاءة تثبيط تآكل سبيكة البراص α في محلول حامض الهيدروكلوريك و في محلول حامض النتريك إلى ( (75.64%و ( 73.17% ( على التوالي عند تركيز ( 3% ) من المثبط. اظهر اختبار الفحص ألمجهري خلو سطح سبيكة البراص المتعرض للمحلول الأكال الحاوي على المثبط من مظاهر التآكل المتواجدة على سطح النماذج المغمورة في الوسط الأكال الخالي من المثبط ووضوح طبقة الحماية الممتزة على السطح. بيانات معدلات التآكل بينت إن آلية عمل المثبط العضوي هي الامتزازAdsorbing)) وان جزيئات المثبط تمتز على سطح المعدن طبقا إلى علاقة لانكمير للأمتزازLangmuir Adsorption Isotherm) ).


Article
Active Inhibitor as Corrosion Protective of Carbon Steel
مثبط فعّال لحماية الفولاذ الكربوني من التآكل

Author: Ali Hubi Haleem
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2008 Volume: 6 Issue: 1 Pages: 196-207
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The present study is attempted to find new inhibitors that can to easily be prepared and applied, as well as nontoxic, cheap and available. In this study hibiscus leaves extractor was used to protect carbon steel in hydrochloric acid solution (1M, 2M, and 3M).Since the usable inhibitor is considered organic inhibitor, and for evaluating the inhibition performance of this compound, many tests have been conducted which include measuring the corrosion rate through methods known weight loss and microscopic examination test. In losing weight method the inhibitor gives good efficiency in protecting, the carbon steel to be corroded at 1M HCl is 77% while the efficiency is drop to 68% in 3 M HCl at 30 oC. Microscopic examination test shows the clearness of the metals surface which is under the corrosion medium and which contains inhibitor, from any kind of corrosion that can be found on those surface, which are under mediums completely empty from inhibitor, and also shows the clearness of that protect layer on the surface. The data of corrosion rate show that the way of doing this organic inhibitor is adsorbing and the inhibitor molecules are adsorbed on the metal surface according to Langmuir adsorption isotherm.

البحث الحالي يمثل محاولة لإيجاد مثبطات جديدة سهلة التحضير والتطبيق, غير سامة, رخيصة الثمن ومتوفرة بكثرة, ففي هذا البحث تم استخدام مستخلص نبات الخبازhibiscus leaves) ) في حماية الفولاذ الكربوني في محلول ( 1M, 2M, 3M) حامض الهيدركلوريك. المثبط المستخدم يعد من المثبطات العضوية Organic Inhibitors) ) ولغرض تقييم الأداء التثبيطي لهذه المركبات فقد أجريت عدة اختبارات تضمنت قياس معدل التآكل بطريقة فقدان الوزن واختبار الفحص المجهري . في طريقة فقدان الوزن أعطى المثبط كفاءة جيدة في حماية الفولاذ الكربوني من التآكل إذ بلغت كفاءة المثبط حوالي 77% في محلول حامض الهيدروكلوريك بتركيز 1M في حين انخفضت كفاءة المثبط إلى 68% في محلول حامض الهيدروكلوريك بتركيز 3M بدرجة حرارة oC .30 اظهر اختبار الفحص المجهري خلو سطح الفولاذ الكربوني المتعرض لمحلول حامض الهيدروكلوريك الحاوي على المثبط من مظاهر التآكل المتواجدة على سطح النماذج للوسط التاكلي الخالي من المثبط ووضوح طبقة الحماية الممتزه على السطح. بيانات معدلات التآكل بينت إن آلية عمل المثبط العضوي هي الامتزازAdsorbing)) وان جزيئات المثبط تمتز على سطح المعدن طبقا إلى علاقة لانكمير للأمتزازLangmuir Adsorption Isotherm) )