Features of Spot-Matrix Surface Hardening of Low-Carbon Steel Using Pulsed Laser
خصائص التصليد السطحي بنمط المصفوفة النقطية للفولاذ منخفض الكاربون باستخدام الليزر النبضي

Authors: Khawla S. Khashan --- Oday A. Hamadi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2007 Volume: 25 Issue: 2 Pages: 168-175
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, results of spot hardening in low-carbon steel by using a pulsedNd:YAG laser are presented. These results include determination ofhardening depth, diameter of hardened spot, aspect ratio and heat-affectedzone width with varying laser energy density. In order to determine the effectof irradiation profile on the overall achievable hardness, the profiles ofoverlapping, adjacent and separated hardened spots are compared and thepercent coverage of the workpiece as a function of the laser-hardened spotdimensions.

في هذا البحث، جرى تقديم نتائج عملية لتصليد عينات من الفولاذ منخفض الكاربون بالنمطالنقطي باستخدام ليزر النيدميوم -ياك النبضي . تضمنت هذه النتائج تحديد عمق التص ليد وقطرالبقعة المصلدة والنسبة الباعية وعرض المنطقة المتأثرة حرارياً كدالة لتغير كثافة طاقة الليزر.ومن أجل التعرف على تأثير نمط التشعيع على الصلادة الإجمالية للسطح والتي يمكن تحقيقها،جرى مقارنة الأنماط المحتملة لاستخدام الليزر النبضي في التصليد وهي نمط التراكب ونمطالبقع المتجاورة ونمط البقع المنفصلة، كما جرى تحديد النسبة المئوية لتغطية سطح العينةكدالة لأبعاد البقعة المصلدة بالليزر


Article
IMPROVING THE MECHANICAL PROPERTIES OF CK35 STEEL USING ND: YAG LASER SURFACE HARDENING
تحسين الخواص الميكانيكيه للفولاذ CK35 بأستخدام التصليد بالليزر نيديميوم-ياك

Authors: Khansaa Dawood Salman --- Muhannad Zedain Khalifa
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2016 Volume: 20 Issue: 2 Pages: 250-258
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this investigation CK35 steel was treated by using laser surface treatment and make comparison with conventionally heat treatment. Laser hardening was done by using pulse ND: YAG laser with energy of 1000mj, whilst the conventionally heat treatment was carried out by quenching at 840 with cooling in oil and then tempered at 200for 2hr. Mechanical tests were made for all the specimens which were used in this research before and after heat treatments such as: Tensile test and Microhardness test. Also grain size measurement and microstructural evaluation were done by using computerized optical microscopy. The results of this work showed that obviously improvement in mechanical properties for the specimen treated by laser more than the specimen treated conventionally as the following: From tensile test it showed that increasing in yield strength, ultimate tensile strength , elongation percentage and plasticity constant (k). Also decreasing in young modulus (E) and the coefficient of strain hardening (n). Whilst the microhardness results showed that the highest value was obtained by laser hardening at the surface of the specimen and deceased far from the surface with depth of hardening equal to 0.5 mm. Also metallographic examination of the specimens after heat treatments showed that refining in grain size of the specimen treated by laser treatment more than the specimen treated by conventional heat treatment.

في هذا البحث تمت معاملة الفولاذ(CK35) بأستخدام المعاملة السطحية بالليزر ومقارنة ذلك مع المعاملة الحرارية التقليدية. تم التصليد بالليزر بأستخدام الليزر نيديميوم- ياك النبضي وبطاقة mj1000, بينما أجريت المعاملة الحرارية التقليدية بالتقسية عند درجة حرارة والتبريد بالزيت ثم المراجعة عند 200 ولمدة hr2. أجريت أختبارات ميكانيكية لجميع العينات التي استخدمت في هذا البحث قبل وبعد المعاملات الحرارية مثل: أختبار الشد وأختبار الصلادة الدقيقة.كذلك تم قياس الحجم الحبيبي وتحديد البنية المجهرية وذلك بأستخدام المجهر الضوئي المزود بحاسوب. أظهرت نتائج هذا البحث بتحسن واضح في الخواص الميكانيكية للعينة المعاملة بالليزر اكثر من العينة المعاملة بمعاملة حرارية تقليدية وكما يلي:من أختبار الشد نلاحظ زيادة في مقاومة الخضوع, مقاومة الشد القصوى, النسبة المئوية للاستطالة وثابت اللدونةk. كذلك نقصان معامل يونكE ومعامل الاصلاد الانفعاليn. بينما أظهرت نتائج الصلادة الدقيقة بان أعلى قيمة يمكن الحصول عليها بالتصليد بالليزر عند سطح العينة ومن ثم تقل بالأبتعاد عن سطح العينة وبعمق تصليد mm0.5. كذلك أظهر فحص البنية المجهرية للعينات بعد المعاملات الحرارية بتنعيم في الحجم الحبيبي للعينة المعاملة بالليزر اكثر مما هو عليه للعينة المعاملة بمعاملة حرارية تقليدية.