Effect of Metakaolin on Properties of Lightweight Porcelinate Aggregate Concrete

Authors: Nada M. Fawzi --- Kalil I. Aziz --- Sheelan M. Hama
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2013 Volume: 19 Issue: 4 Pages: 439-452
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Research in Iraq has expanded in the field of material technology involving the properties of the lightweight concrete using natural aggregate. The use of the porcelinate aggregate in the production of structural light concrete has a wide objective and requires a lot of research to become suitable for practical application. In this work metakaolin was used to improve compressive strength of lightweight porcelinate concrete which usually have a low compressive strength about 17 MPa . The effect of metakaolin on compressive, splitting tensile, flexure strengths and modulus of elasticity of lightweight porcelinate concrete have been investigated. Many experiments were carried out by replacing cement with different percentages of metakaolin. The metakaolin was replaced by 5%, 10%, 15% and 20%. A control reference mix without metakaolin was made for comparison purpose. For all mixes, compressive, splitting tensile, flexure strengths and modulus of elasticity were determined at 28-day. The results showed that the using of metakaolin improve the compressive, splitting tensile, flexure strengths and modulus of elasticity of lightweight porcelinate concrete. The higher compressive, splitting tensile, flexure strengths and modulus of elasticity were found for 15% metakaolin.

توسعت البحوث في العراق في حقل تكلنوجيا المواد من ضمنها دراسة خواص الخرسانة خفيفة الوزن باستخدام ركام طبيعي. استخدام البورسلينايت كركام خفيف الوزن في انتاج خرسانة انشائية يتطلب العديد من الدراسات لفهم وتحسين خواصها لتصبح مناسبة للتطبيقات العملية. في هذه الدراسة استخدمت مادة ميتاكاؤلين كنسبة مئوية مِنْ وزنِ سمنت، لتحسين خواص خرسانة البورسلينايت الخفيفة الوزن التي تمتاز عادة بمقاومة انضغاط واطئة حوالي 17 ميكاباسكال. تم دراسة تاثير اضافة ميتاكاؤلين على كل من مقاومة الانضغاط, مقاومة الانفلاق, معامل التصدع, و معامل المرونة للخرسانة البورسلينايت الخفيفة الوزن. وقد استبدل جزء من السمنت بالنسب التالية من ميتاكاؤلين: 5%, 10%, 15%, و 20% من وزن السمنت, بالاضافة الى الخلطة المرجعية بدون اضافات لغرض المقارنة. لكل الخلطات تم قياس كل من مقاومة الانضغاط, مقاومة الانفلاق, معامل التصدع, و معامل المرونة بعمر 28 يوم. وقد وجد بان اسبتدال نسبة 15% من سمنت بميتاكاؤلين تحسن مقاومة الانضغاط, مقاومة الانفلاق, معامل التصدع, و معامل المرونة.


Article
A Comparative Study of Thermal Insulations and Physical Properties of Lightweight Concrete Using Some Raw Materials

Authors: Sanaa A. Hafid --- Amenah E. Mohammed Ridha
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 4 Part (B) Scientific Pages: 470-478
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, no-fine lightweight concrete was produced by using crushed bricks, thermostone as coarse aggregates to produce lightweight concrete. For both, superplasticizers were added to the mixture, the specimens were then cured in water for (7, 28, 60) days respectively.Compressive strength determine the mechanical properties, Physical properties of these concrete types were examined through thermal conductivity and fresh density. The compressive strength test showed that the compressive strength of the concrete was about (8-15.7) N/mm2 byusing natural gravel aggregate, (4.8-8.1) N/mm2 by using crushed bricks, and (3.14-5.4) N/mm2 by using thermostone aggregate. After 28 days, the thermal conductivity were (0.58),(0.41),(0.26) W/m.k, for the natural gravel ,crushed bricks and thermostone concrete.Besides; these concrete types are characterized by their low cost, environmentally friendly,high production rate, fire resistance, thermal insulation and light weight.


Article
Nonlinear Finite Element Analysis of High Strength Lightweight Concrete Beams
التحليل اللاخطي للعتبات الخرسانية الخفيفة الوزن ذات المقاومة العالية باستخدام طريقة العناصر المحددة

Author: Farked Kais Ibrahim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 10 Pages: 1910-1923
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research work presents a nonlinear finite element investigation on thebehavior of lightweight reinforced concrete beams. This investigation is carriedout in order to get a better understanding of their behavior throughout the entireloading history.The three-dimensional 20-node brick elements are used to model theconcrete, while the reinforcing bars are modeled as axial members embeddedwithin the concrete brick elements. The compressive behavior of concrete issimulated by an elastic-plastic work-hardening model followed by a perfectlyplastic response, which terminated at the onset of crushing. In tension, a fixedsmeared crack model has been used .The effect of some important parameters(ƒ'c , rw ,a/d) have been investigated to study their influence on the predicted loaddeflectioncurves

تم في هذا البحث اختبار سلوك العتبات الخرسانيةالخفيفة الوزن المسلحة ذات المقاومةالعالية والمعرضة لاحمال القص باستخدام انموذج التحليل غير الخطي بطريقة العناصرالمحددة. هذا الانموذج استخدم للحصول على تفهم افضل لتصرف هذه الاعضاء من خلالتاريخ التحميل الكامل.تم استخدام العنصر الطابوقي ذو العشرين عقدة لتمثيل الخرسانة ، اماقضبان التسليح فقد مثلت كعناصر احادية البعد مطمورة في العنصر الخرساني ثلاثي الابعاد ،تمتمثيل تصرف الخرسانة تحت تاثير اجهادات الضغط بالانموذج المرن -اللدن ذو التقويةالانفعالية حيث يتضمن هذا الانموذج افتراض سلوكاً مرناً للخرسانة في مستهل التحميل يعقبهسلوك مرن – لدن عند حدوث التشقق في الخرسانة ،ويستمر تحمل الاجهادات بمعدل انفعالمتزايد لحين وصول مرحلة اللدونة التامة، وتنتهي هذه المرحلة بحدوث تهشم في الخرسانة .اماسلوك الخرسانة تحت تاثير اجهادات الشد فقد تم تبني انموذج التشقق المنتشر لتمثيله.تم دراسةعلى منحنيات الحمل-هطول المتوقع. (ƒ'c , rw ,a/d) تاثير المعاملات المهم

Keywords

Nonlinear --- Finite Element --- Lightweight --- Beams


Article
Effect of Polypropylene Fibers on Properties of Mortar Containing Crushed Brick as Aggregate
تاثير الياف البولي بروبلين على خواص المونه الحاوية على ركام الطابوق المكسر

Authors: Shakir A. Salih --- Maha E. AL-Azaawee
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 12 Pages: 1508-1523
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

More recently there has been a great attention towards converting wastematerials by- products into useful materials as aggregate in concrete industry.It is thus aimed in this study to investigate the possibility of using waste brickas suitable materials and alternative to the natural aggregate in the productionof lightweight mortar.The essential objective of this work is to study the mechanical properties oflightweight mortar containing different percentages of polypropylene fiberwith high range water reducing agent. The effective synergy of this admixtureon the properties of mortars is also investigated. Compressive strength,splitting tensile strength, thermal conductivity and drying shrinkage tests wereconducted on reference and polypropylene fiber reinforced mortar specimensat various ages of curing (7, 14, 28, 60 and 90 days) respectively.The results show a significant increasing in splitting tensile strength withthe increment of fibers content. Although, a considerable reduction inworkability is recorded as increasing the fiber content. Which is controlled byusing high range water reducing admixture. All mixes show acceptable valuesfor thermal insulation with regards to ACI 213-87 thermal insulationrecommendations.

وجود أهتمام كبيرنحو تحويل مخلفات المواد الى مواد مفيدة كركام في الصناعة  لوحظ مؤخراالخرسانية. لهذا تهدف هذه الدراسة الى البحث عن أمكانية أستخدام الطابوق المكسر كمواد مناسبة و بديلةللركام الطبيعي في أنتاج الملاط الخفيف الوزن.أن الغرض الرئيسي من هذا البحث هو التعرف على الخصائص الميكانيكية للملاط المسلح بنسبمختلفة من ألياف البولي بروبيلين مع المضاف المقلل للماء بدرجة عالية’ أضافة الى دراسة تأثير هذاالمضاف على جميع الخواص. تم اجراء فحوصات مقاومة الانضغاط ’ مقاومة الشد (غير المباشر)’الموصلية الحرارية و انكماش الجفاف لخلطات (الملاط) المرجعية والحاوية على ألياف البولي بروبيلين60 , و 90 يوم). ,28 , خلال فترات مختلفة من معالجة الخرسانة ( 14,7بينت النتائج زيادة ملحوظة في مقاومة شد الانفلاق مع زيادة محتوى الالياف على الرغم من تسجيلانخفاض مناظر فبي قابلية التشغيل كلما زاد محتوى الالياف. وقد تمت السيطرة على هذا الانخفاض بقابليةالتشغيل من خلال استخدام المضاف المقلل للماء بدرجة متفوقة. بينت جميع الخلطات قيم مقبولة للعزل. ACI 213- الحراري بالمقارنة مع توصيات العزل الحراري الخاصة بمعهد الخرسانة الامريكي 87


Article
Preparing Lightweight Aggregate for Production Lightweight Insulating Concrete
تحضير ركام خفيف لانتاج خرسانة خفيفة عازلة

Author: Mahmood. F. Abed محمود فاضل عبد
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2009 Volume: 14 Issue: 3 Pages: 194-200
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This research dealt with preparing of lightweight aggregate by using local materials for manufacturing lightweight insulating concrete. Two materials were used, the first material was the Clay (Montmorillonite), and the other had ability to makes or leaves cavities or pores when subjects to heating which is Sodium Silicate. The mix of 40 % Montmorillonite and 60 % Sodium silicate burnt between 750- 800 centigrade showed good results in manufacturing lightweight clayey aggregate, the density of lightweight aggregate obtained was approximately (0.38 ) gm/cm3 comparison with density of normal aggregate between ( 2.55 – 2.65 ) gm/cm3 . The lightweight insulating concrete produced by using lightweight clayey aggregate had density about (700) kg/m3 and thermal conductivity about (0.296) watt/m.k .

تناول هذا البحث تصنيع ركام طيني خفيف الوزن لانتاج خرسانة خفيفة الوزن وعازلة للحرارة تلبية لحاجة القطر الملحة لمثل هذا النوع من المواد الانشائية.استخدمت مادتين في تصنيع الركام الطيني خفيف الوزن , المادة الاولى هي الطين (Clay ) حيث اختيرت أطيان المونتموريلونايت (Montmorillonite) لتمثل مادة الركام الصناعي الاساسية , اما المادة الثانية فهي مادة لها القابلية على ترك فجوات او فراغات في محلها عند تعرضها الى درجات حرارة معينة وهي سيليكات الصوديوم (Sodium Silicate ) .أظهر خليط اطيان المونتموريلونايت وسيليكات الصوديوم وبنسبة % 40 و % 60 على التوالي والمحروق بدرجة حرارة 750 – 800 درجة مئوية نتائج جيدة في مجال تصنيع الركام الخفيف حيث تراوحت كثافة الركام المحضر حوالي (0.38) غم/سم 3 مقارنة مع كثافة الركام الاعتيادي الذي تتراوح بين ( 2.55-2.65 ) غم /سم3 . تم استخدام الركام الطيني الخفيف المحضر بهذه الطريقة في انتاج خرسانة خفيفة الوزن وعازلة للحرارة بلغت كثافتها بحدود (700 ) كغم/م3 وموصولية حرارية بحدود (0.296) واط/م.ك .


Article
EVALUATION OF TELLOL AL-KIEND CLAY IN MOSUL CITY FOR THE PRODUCTION OF LIGHT WEIGHT AGGREGATES

Authors: Doaa M. Hammed --- Mayada S. Joodi --- Abdul Wahab AR. Al-Ajeel
Journal: Iraqi Bulletin of Geology and Mining مجلة الجيولوجيا والتعدين العراقية ISSN: 18114539 Year: 2013 Volume: 9 Issue: 2 Pages: 151-160
Publisher: Ministry of Industry and Minerals وزارة الصناعة والمعادن

Loading...
Loading...
Abstract

In this research a representative sample from Tellol Al-Kiend clay deposit (Injana Formation), Naenava Governorate, Iraq, was evaluated for lightweight aggregates preparation. Two methods of heat treatment were carried out. Iso-thermal treatment conducted at (1180 – 1200) °C range, for aggregates made from clay only, using different socking time. Whiles, rapid (or flush) firing, were carried out at 1200 °C, for aggregates made from clay with different types and amounts of additives (dolomite, waste engine oil, and straw). The iso-thermal tests reveal that bloating can occurs at 1180 °C only for 45 minutes holding time. The aggregates obtained, have a specific gravity of about 1.38 and 0.8% water absorption. In rapid firing, it was found that, the bloating of the clay can be significantly improved by the addition of dolomite. The results obtained indicated that aggregates having 1.35 specific gravity with about 1% water absorption value could be produced from aggregates made of clay and 5 wt.% dolomite. The firing time has been about 5 minutes. Thereupon, it can be suggested that, Tellol Al-Kiend clay can be used for the production of lightweight aggregates by rapid firing. Concrete made from these lightweight aggregates shows a compressive strength (28 days) of about 173 kg/cm2, which can be designated as structural and insulating concrete.

جرى في هذا البحث تقييم نموذج ممثل لترسبات أطيان تلول الكند (تكوين إنجانة) في محافظة نينوى لإنتاج الركام الخفيف، وجربت طريقتان للمعالجة الحرارية. جرى في الطريقة ألأولى معالجة الركام المحضر من الطين فقط في درجات حرارة تتراوح مابين (1180 ـ 1200) °م وزمن استبقاء مختلف. أما الركام المحضر من الطين مع كميات وأنواع مختلفة من المواد المضافة (دولومايت، مخلفات زيت المحركات والقش) فقد تم معالجتها بالحرق السريع (أو المفاجئ) عند درجة حرارة 1200 °م مع زمن استبقاء 2 أو 3 دقائق. بينت نتائج حرق الركام المحضر من الأطيان فقط بأن الانتفاخ يمكن أن يحصل فقط عند حرارة 1180 °م وبزمن استبقاء 45 دقيقة، وإن الركام الناتج من هذه العملية أعطى كثافة نوعية بحدود 1.38 ونسبة امتصاص للماء 0.8%. ولكن وجد أنه باستخدام الحرق المفاجئ فإن انتفاخ ركام الطين يتحسن بشكل ملحوظ عند إضافة الدولومايت وبينت النتائج المستحصلة من هذه العملية إمكانية إنتاج ركام يمتلك كثافة نوعية بحدود 1.35 ونسبة امتصاص للماء 1% عند إضافة 5% وزناً من الدولومايت للطين وإن الزمن اللازم للحرق هو بحدود 5 دقائق. وعليه يمكن استخدام أطيان تلول الكند في إنتاج الركام الخفيف بإتباع الحرق السريع. كما بينت نتائج فحص الكونكريت المحضر من الركام الخفيف بأن مقاومة الانضغاط بعد 28 يوم بحدود 173 كغم/ سم2 والذي يمكن أن يستخدم في تحضير الخرسانة الإنشائية العازلة.


Article
Effect of Plastic Fibers on Properties of Foamed Concrete
تأثير الألياف البلاستيكية على خواص الخرسانة الرغوية و الخفيفة الوزن

Authors: Hisham K. Ahmed --- Waleed A. Abbas --- DohaM. Abdul-Razzaq
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 7 Part (A) Engineering Pages: 1313-1330
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The main objective of this work is to study the effect of adding plastic fibers on Lightweight Aggregate Foamed Concrete (LWAFC) using mix proportion of 1:2.6:0.4 by volume (cement: fine Porcelanite: coarse Porcelanite) with 2% foaming agent by weight of water, and using sand as a partial and total replacement of local Porcelanite aggregate in that mix. The properties of lightweight aggregate foamed concrete reinforced with different percentages of plastic fiber (0.5, 0.75, and 1% by volume) were studied. Compressive strength, splitting tensile strength, flexural strength, dry density, initial surface absorption, water absorption, ultrasonic pulse velocity, acoustic impedance, and impact resistance tests were conducted on mixes at ages of 7, 28, and 60 days. The results showed a significant increasing in impact resistance, splitting tensile strength, and water absorption 34.55%, 4.2%, 326%, and 27.3% respectively. While the results indicated that the compressive strength, ultrasonic pulse velocity, dry density and acoustic impedance of the composites were reduced when the crimped plastic fiber volume fraction increases. The percentage of reduction of these properties was 15%, 11.1%, 6.23%, and 12.55% respectively.

إن الهدف الرئيسي لهذا البحث هو دراسة تأثير إضافة الالياف البلاستيكية على الخرسانة الرغوية الخفيفة الوزن باستعمال نسب خلط حجمية 1 ، 2.6 ، 0.4 (سمنت : بورسيلانايت ناعم : بورسيلانايت خشن) وباضافة 2% من المادة الرغوية كنسبة وزنية من الماء وباحلال الرمل كبديل جزئي أو كلي من ركام البورسيلانايت المحلي في الخلطة. تمت دراسة استعمال الالياف البلاستيكية بنسب حجمية مختلفة ( 0.5 ، 0.75 ، 1.0% ) لتسليح الخرسانة الرغوية الخفيفة الوزن. تم إجراءفحوصات مقاومة الانضغاط و مقاومة الشد و فحص الانثناء و مقاومة الصدم والكثافة الجافة و الامتصاص السطحي الاولي و الامتصاص الكلي وسرعة الذبذبات الفوق الصوتية والمعاوقة الصوتية للخلطات بأعمار 60،28،7 يوماً. بينت النتائج زيادة ملحوظة في مقاومة الصدم و مقاومة شد الانفلاق و امتصاص الماء و التي بلغت 34.55% , 4.2%, 27.3% على التوالي مع زيادة محتوى الالياف على الرغم من تسجيل انخفاض في مقاومة الانضغاط و الذبذبات فوق الصوتية و الكثافة الجافة و المعاوقة الصوتية مع زيادة محتوى الالياف. وقد بلغ مقدار الأنخفاض في هذه الخصائص 15%, 11.1%, 6.23%, 12.55% على التوالي.


Article
Experimental study of lightweight concrete used for the production of canoe
دراسة تجريبية للخرسانة الخفيفة الوزن المستخدمة في صناعة القوارب الخرسانية

Author: Dr.Eethar Thanon Dawood* د. ايثار ذنون داؤد
Journal: AL-Rafdain Engineering Journal (AREJ) مجلة هندسة الرافدين ISSN: 18130526 Year: 2015 Volume: 23 Issue: 2 Pages: 187-197
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

AbstractThis study was conducted to investigate the properties of lightweight concrete produced by the inclusions of polystyrene beads and perlite that can be used for production of Canoe.Different percentages of polystyrene (20, 35, 50 and 65%) were used.Besides, the 50% of polystyrene beds with different percentages of perlite (10, 20, 30, 40, 50 and 60%) as partial replacement of sandwere used. The fresh density, compressive strength, flexural strength and absorption capacity of the mixes were tested. The results show that the uses of 50% of polystyrene with 50% of perlite as partial replacementof sand exhibit suitable ranges of density, compressive and flexural strengths of lightweight concrete used for canoe production. Thus, the Canoe produced from these inclusions of polystyrene and perlite show a clear success in terms of floating.

هذا البحث يتناول دراسة خصائص الخرسانة الخفيفة الوزن المصنعة من قطع الفلين مع البرلايت وذلك لتصنيع قارب خرساني. لذلك تم استخدام نسب مختلفة من الفلين وهي 20 و 35 و50 و 65%. بالاضافة الى ذلك فان نسبة 50% من الفلين تم استخدامها مع نسب مختلفة من البرلايت كاستبدال جزئي من الرمل وهذه النسب هي 10و 20و 30و 40 و50و 60%. الكثافة الرطبة ومقاومة الانضغاط ومقاومة الشد والامتصاص تم اختبارها للخلطات الخرسانية الخفيفة المصنعة. النتائج بينت بان استخدام نسبة 50% من الفلين مع 50% من البرلايت كاستبدال جزئي من الرمل اعطت مديات من الكثافة والمقاومة مناسبة لتصنيع القارب الخرساني. ولهذا فان القارب الخرساني المصنع من هذه الخلطة المحتوية على الفلين والبرلايت اظهرت نجاح واضح في فحص الطفو للقارب.


Article
Some Properties of Hybrid Fibers High Strength Lightweight Aggregate Concrete
بعض خواص خرسانة الركامالخفيف الوزن عالية المقاومةوالمسلحة بالالياف الهجينة

Authors: Wasan Ismail Khalil --- Suhad Abd Al-Jabbar Mozan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 4 Part (A) Engineering Pages: 815-829
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This investigation aims to study some properties of high strength lightweight aggregate concrete (HSLWAC) reinforcedwith mono and hybrid fibers in different dimensions and types. High strengthporcelinite lightweight aggregate concretemix with compressive strength 41 MPa at 28 day age was prepared. The fibers used included macro hooked steel fiber with aspect ratio 100 (type S1), macro hooked steel fiber with aspect ratio 60 (type S2), micro polypropylene fiber (pp)and micro carbon fiber (CF). Eight HSLWAC mixes were prepared including, one plain concrete mix (without fibers), three mono (single) fiber reinforced concrete mixes (with 0.5% volume fraction of steel fiber type S1, 1% volume fraction of steel fiber type S1and 0.25% volume fraction of CF) and four double hybrid fiber reinforced concretes mixes [0.5% steel fiber type S1 +0.5% steel fiber S2 mix (HSF1), 0.75% steel fiber S1+ 0.25% steel fiber type S2mix ( HSF2), 0.75% steel fiber type S1+ 0.25% pp mix (HSPPF) and 0.75% steel fiber type S1+ 0.25% CF mix (HSCF)]. Fresh properties (workability and fresh density) and hardened properties (oven dry density, compressive strength, splitting tensile strength, flexural strength and thermal conductivity) of HSLWAC were studied. Generally mono and hybrid fiber reinforced HSLWAC specimens show significant increase in splitting tensile strength and flexural strength in comparison with plain HSLWAC specimen. All hybrid fiber HSLWAC specimens show significant increase in splitting tensile strength and flexural strength compared to concrete specimens reinforced with 1% volume fraction of mono steel fiber type S1. The percentage of increase in splitting tensile strength for hybrid fiber reinforced specimens prepared from HSLWAC mixes HSF1, HSF2, HSPPF and HSCF is 316.6%, 361.1%, 377.7% and 433.3%, while the percentage of increase in flexural strength is 29.43%, 59.89%, 26.56% and 64.58% respectively relative to the plain specimens.

يهدف هذا البحث الى دراسة بعض خواص خرسانة الركام خفيف الوزن عالية المقاومة المسلحة بالالياف الاحادية والالياف الهجينة بأبعاد وأشكال مختلفة . الالياف المستخدمة هي، ألياف فولادية معقوفة النهاية بنسبة باعية 100 نوع S1، ألياف فولادية معقوفة النهاية بنسبة باعية 60 نوع S2 ، الياف دقيقة من البولي بروبلين والياف الكاربون الدقيقة. تم أعداد ثمان خلطات خرسانية متضمنة الخلطة المرجعية (بدون ألياف)، ثلاث خلطات مسلحة بنوع واحد من الالياف (0.5% نوع S1، 1% نوع S1 ، 0.25% ألياف كاربون ) ، اربعة خلطات مسلحة بألياف هجينة مزدوجة]0.5% نوعS1 + 0.5% نوعS2( الخلطة (HSF1, 0.75% نوع S1 + 0.25% نوعS2 (الخلطة HSF2( ,%0.75 نوعS1+ 0.25% الياف البولي بوبلين (الخلطة HSPPF) و 0.75% نوعS1 + 0.25% الياف الكاربون (الخلطة HSCF)[. تم دراسةالخواص الطرية للخرسانة ( قابلية التشغيل والكثافة الطرية ) وخواص الخرسانة في الحالة الصلبة (الكثافة الجافة ، مقاومة الأنضغاط ،مقاومة شد الانثناء ، مقاومة شد الأنشطار والموصلية الحرارية ).بصورة عامة اظهرت نماذج خرسانة الركام خفيف الوزن المسلحة بالالياف الاحادية والالياف الهجينة زيادة ملحوظة بمقاومة الشد الانشطاري وشد الانثناء مقارنة مع نماذج الخرسانة غي المسلحة بالالياف. اظهرت جميع نمادج خرسانة الركام خفيف الوزن عالية المقاومة الحاوية على خليط الالياف الفولاذية نوع S1 مع الالياف الفولاذية نوع S2 زيادة في مقاومة شد الأنثناء والشد الأنشطاري مقارنة مع الخلطة الخرسانية المسلحة بنسبة حجمية 1 % بالألياف الفولاذية المنفردة نوع S1 . كانت نسبة الزيادة في مقاومة الشد الأنشطاري للنماذج المسلحة بالألياف الهجينة والمهيئة من الخلطات HSF1 ، HSF2 ، HSPPFوHSCF هي 316.6٪، 361.1٪، 377.7٪ و 433.3٪ على التوالي بينما كانت نسبة الزيادة في مقاومة الأنثناء 6.88٪، 32.04٪، 4.52٪ و 35.91٪ على التوالي مقارنة مع النماذج غير المسلحة بالألياف .


Article
Fresh and Hardened Properties ofLightweight Self CompactingConcrete Containing Attapulgite

Authors: Waleed A. Abbas --- Qais J.Frayyeh --- Shubbar J. Al Obaidey
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 9 Part (A) Engineering Pages: 1767-1781
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The main objectives of this study were investigating the possibility of producing lightweight self -Compacting concrete (LWSCC) by using artificial coarse lightweight aggregate manufactured by burning locally available Attapulgite clay, estimating the optimum dosage of high reactivity Attapulgite (HRA) and studying its effects on fresh and hardened properties of LWSCC when using it as a partial replacement by weight of cement.Tests results showed that, It is possible to produce (LWSCC) by using Attapulgite as artificial coarse (LWA) and (HRA).The optimum content for (HRA) used in this study was 10 %, the percentages of increment in compressive strength and splitting tensile strength with 10% (HRA) relative to reference mix were (10.0%, 12.1%, 11.1% and 12.4%) and ( 12.0%, 18.2%, 16.6% and 16.2%) for 7, 28, 56 and 90 days respectively.The values of the calculated equilibrium density ranged between (1788 and 1829) kg/m3

Listing 1 - 10 of 73 << page
of 8
>>
Sort by
Narrow your search

Resource type

article (73)


Language

English (60)

Arabic (6)

Arabic and English (6)


Year
From To Submit

2019 (13)

2018 (13)

2017 (8)

2016 (8)

2015 (6)

More...