Effect of Grain and Calcinations Kaolin Additives on Some Mechanical and Physical properties on Low DensityPolyethylene Composites
تأثير اضافات (الحبيبات والكلسنة) الكاؤولين على بعض الخصائصالميكانيكية والفيزياوية على متراكبات البولي اثلين الواطئ الكثاف

Author: Zanaib Y. Shnean زينب يوسف شنين
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2008 Volume: 4 Issue: 4 Pages: 37-44
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this work, a composite material was prepared from Low-density polyethylene (LDPE) with different weight percent of grain and calcinations kaolin at temperature of (850oC) using single screw extruder and a mixing machine operated at a temperature between (190-200oC). Some of mechanical and physical properties such as tensile strength, tensile strength at break, Young modulus, and elongation at break, shore hardness and water absorption were determined at different weight fraction of filler (0, 2, 7, 10 and 15%). It was found that the addition of filler increases the modulus of elasticity, elongation at break, shore hardness and impact strength; on other hand, it decreases the tensile strength and tensile strength at a break. Absorption test was carried out in water at different immersion times and different composite .The results of absorption show that it obeys Fick’s law and after the addition of kaolin the amount of absorption decrease. Calcinations kaolin filler produces better mechanical properties , than grain kaolin fillers.

في البحث الحالي تم تحضير مواد مركبة والتي هي عبارة عن مخلوط بوليمري ، يتكون من مزج بولي اثلين الواطئ الكثافة مع الكاؤولين المحروق بدرجه حرارية (850 °م) والغير محروق. وذلك باستخدام جهاز الباثقة الأحادية حيث تم تشغيلها عند درجات حرارة تتراوح بين (150-200 °م). تم استخدام ماكنة البثق أحادية اللولب في تحضير المواد المتراكبة.وبعد ذلك جرت دراسة بعض الخصائص الميكانيكية مثل الشد وإجهاد الشد عند الكسر والاستطالة,قوة الصدمة وصلادة شور، ولجميع المتراكبات المحضرة وقورنت النتائج المستحصلة مع تلك التي تعود لمادة الأساس بمفرده وجرت الفحوصات بكسور وزنيه مختلفة. من النتائج التي تم الحصول عليها لوحظ ازدياد كل من: معامل المرونة,الاستطالة عند الكسر ,صلادة شور وقوة الصدمة ونقصان مقاومة الشد بزيادة نسبة الخلط ألوزني. تم إجراء فحص الامدصاصية لكل نموذج قبل وبعد التدعيم بمسحوق الكاؤؤلين وأظهرت النتائج نقصان في الامدصاصية بعد التدعيم .من النتائج التي تم الحصول عليها تبين أن الكاؤولين المحروق أعطى نتائج أفضل من الكاؤولين الغير محروق.


Article
The Effect of Photo-Initiated Oxidation on Mechanical Properties ofHigh Density Polyethylene / Linear Low Density Polyethylene Blends

Authors: Nabeela A. Mohammed --- Najat J. Saleh
Journal: Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط ISSN: 19974884/E26180707 Year: 2007 Volume: 8 Issue: 4 Pages: 53-58
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The long – term behaviour of polyethylene products used out doors is affected by weathering. In the present work,weathering test was carried out to find the effect of the environment conditions on the mechanical properties of HDPE/LLDPE blends with different weight percents (0, 15, 30, and 45 %) relative to the LLDPE by increasing the exposure times to (100, 150, 200, 250, 300) hr.A series of tests (destructive), tensile, impact and hardness were carried out on the prepared samples, the results obtained declare the changes on the material behaviour from ductile to brittle and the polymer shows a decline in the mechanical properties with increasing the exposure times.In the present work empirical equations were reached which could be used to calculate one of the mechanical properties in terms of exposure time, weight percent of LLDPE content and to other mechanical properties.


Article
A Study the Effect of UV Light on Pigmented and Unpigmented LDPE
دراسة تاثير اشعة فوق البنفسجية (على البولي الاثلين الواطئ الكثافةعند اضافة الاصباغ وبدونها)

Authors: ZanaibY.shnean --- Najat J.saleh
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 4 Pages: 706-716
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present work, specimens of polymeric composites were prepared from LDPEwith different wt% of TiO2 and Fe2O3 using a single screw extruder which operated at atemperature of (150-170) Co. Results obtained reveal that after the addition of 7% of TiO2 toLDPE, some of mechanical properties improved for example tensile strength increased from(18.50 )MPa to (28.12) MPa tensile at break increased from (14.96) MPa to (26.02) MPa,modulus of elasticity increased from (63) MPa to (193.98) MPa, hardness increased from(48 ) to(75),while impact strength decreased from (0.18 ) to (0.02). After the exposure toUV light all mechanical properties declined but pigment LDPE still has higher mechanicalproperties unpigmented LDPE. Empirical equations were reached which could be used tocalculate one of the mechanical properties in terms of exposure time, weight percent ofpigment content and other mechanical properties.

تم في البحث الحالي تم تحضير مو اد متراكبة ذات أساس بوليمري من البولي اثلين الواطئ الكثافةوأضيفت إلية نسب مختلفة من اوكسيد الحديد وثنائي اوكسيد التيتانييوم وتم التحضير باستخدام الباثقة150 ).اطهرت النتائج التي تم - الأحادية والتي تم تشغيله ا عند الدرجة الحرارية التي تتراوح مابين ( 170الحصول عليها بعداضافة نسبة مثلا % 7 من اوكسيد التيتانييوم تحسن العديد من الخواص الميكانيكية كقوة( الشد حيث ازدادت من ( 18.50 ) إلى ( 28.12 ) ميكاباسكال وقوة الشد عند القطع حيث ازدادت من ( 26.0214.96 )ميكاباسكال ومعامل المرونة من ( 63 ) إلى ( 193.98 ) وكذلك الحال بالنسبة للصلادة حيث )ازدادت من ( 48 إلى ( 75 ) في حين لوحظ انخفاض قوة الصدمة من ( 0.18 ) إلى ( 0.02 ) ولأجلالتعرف على تأثير ظرو ف التجوية على النماذج المحضر ة.وقد تم تعريض النماذج للأشعة فوق البنفسجية250 ) ساعة.لوحظ انخفاض الصفات الميكانيكية اعلاة مع ملاحظة ان - ولازمان مختلفة تتراوح بين ( 0النماذج المعالجة بالصبغات تمتلك صفات أعلى من تلك الغير المعالجة بالصبغات . وفي البحث الحالي أيضاتم إيجاد معادلات تجريبية يمكن استعمالها لإيجاد قيمة احد الصفات الميكانيكية بدلالة زمن التعرض ,النسبةالمئوية لمحتوى البولي اثلين الواطئ الكثافة وبدلالة الخواص الميكانيكية.


Article
Mechanical behaviour of Low Density Polyethylene / Shrimp Shells Composite.
دراسة السلوك الميكانيكي لمتراكب البولي اثيلين واطئ الكثافة/ قشور الروبيان .

Author: Abdullah A. Hussein, Abdulwahab A.Sultan and Qusay A. Matoq
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2011 Volume: 37 Issue: 3A Pages: 5-11
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

In the present work, the mechanical behaviour of (LDPE-463) reinforced with Shrimp Shells (Metapenaeusaffinis) composite, as a function filler contact (5, 10, 15, 20, 25, wt %). Filler concentration has an obvious effect on improving several mechanical parameters. The parameters studied are young’s modules, stress at break, and stress at yield which were increased with increasing filler concentration. Elongation as indirect results of stress at break was decreased with increasing filler concentration. It was found that the addition of Shrimp Shells to the LDPE leads to decreases impact strength. Results were analyzed in the frame of drawing model.

تم تحضير مزيج من بولي اثلين واطئ الكثافة (463) و قشورالروبيان نوع (ميتابنايص أ فانيص) غير المرغوب ، حيث لا يمتلك أي قيمة غذائية ممكن أن يستفاد منها وبنسب وزنية تتراوح (5, 10, 15, 20, 25, wt%) كداله للمالئ المضاف ، وتمت دراسة السلوك الميكانيكي لهذا الخليط. أظهرت النتائج العملية بان إضافة المالئ يعمل على تحسين الخواص الميكانيكية وذلك بزيادة قوة الإجهاد ومعامل يونك و الإجهاد عند الوهن والإجهاد عند القطع. كما وجد أن مقدار الاستطالة يقل مع زيادة تركيز المضاف. أما بالنسبة إلى فحص الصدم فقد وجد إنه يقل بزيادة نسبة المالئ .لذلك فان البولي اثلين الواطئ الكثافة وبد ون إضافة قد أعطى أعلى قيمة للصدم . تم تحليل البيانات العملية بالاعتماد على موديل السحب.


Article
EFFECT OF KAOLIN ON THE MECHANICAL PROPERTIES OF POLYPROPYLENE/ POLYETHYLENE COMPOSITE MATERIAL
تأثیر الكاؤولین على الخواص المیكانیكیة لمادة مت ا ركبة لمخلوط بولیمیري من البولي بروبیلین والبولي اثیلین

Author: Samir Nassaf Mustafa سمیر نصیف مصطفى
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2012 Volume: 5 Issue: 2 Pages: 162-178
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

In this work, the mechanical and water absorption properties of polymerblend polypropylene (PP) and low density polyethylene (LDPE) at constant ratio (50/50)composites as a function of kaolin powder weight content in the grain size (100,120 μm) wereinvestigated. Polymer composite was fabricated by mixing polymer blend ( PPLDPE) with(0, 1, 3 ,5, 10, 14) wt.% of kaolin powder to obtain desirable properties. The parameters suchas tensile strength, tensile modulus, elongation at break , yield stress, impact strength, shore Dhardness and water absorption test were carried out on the prepared samples. The resultsshowed that the addition of kaolin powder to the polymer leads to increase the tensilestrength, modulus of elasticity, shore-D hardness and impact strength and it decreases the% elongation at break,. Water absorption of the composites behaves as function of time (days)has also been investigated, and it increases by increasing immersion time for the same fillercontent, while the absorbed amount of water increases, by increasing the wt% of kaolin atconstant immersion time.

تم في هذا البحث دراسة الخواص المیكانیكیة وامتصاصیة الماء لمخلوط بولیمیري یتكون من البولي بروبیلین والبولي100,120 ) تم μm) 50 ) كدالة للنسبة الوزنیة لمسحوق الكاؤلین عبد حجم دقائقي اثیلین الواطئ الكثافة وبنسبة خلط ( 500) من مسحوق الكاؤلین , 1, 3 ,5, 10, 14) wt.% تحضیر المتراكبات بمزج المخلوط البولیمري مع نسب وزنیة مختلفةللحصول على افضل الخصائص. تمت دراسة السلوك المیكانیكي من خلال الفحوصات الاتلافیة ( فحص الشد و وفحصالصلادة وفحص الصدمة وقیاس معامل المرونة وقیاس الاستطالة عند الكسر) أظهرت النتائج العملیة أن اضافة مسحوقالكاؤلین یؤدي الى زیادة قوة الشد وقوة الصدمة والصلادة و یقلل اجهاد الخضوع ویقلل نسبة الاستطالة عند الكسر. كما تمدراسة سلوك امتصاصیة الماء كدالة للزمن للمتراكبات المحضرة وتبین بأن كمیة الماء الممتصة تزداد بزیادة زمن الغمربالماء عند ثبوت النسبة الوزنیة للكاؤلین وكذلك فأنها تزداد بزیادة النسبة الوزنیة لمسحوق الكاؤلین مع ثبات الزمن.


Article
Study of preparation for co-polymer nanocomposites using PLA/LDPE/CTAB modified clay
دراسة تحضير كوبوليمر ( PLA/LDPE/CTAB ) المعدل بالطين بطريقة النانوكومبوزت

Loading...
Loading...
Abstract

Abstract Study of preparation involve the examination of the effects of operating variables on mechanical properties of polylactic acid /low density polyethylene (PLA/LDPE)/clay nanocomposites including tensile strength, modulus, and elongation at break. Thermal stability of these nanocomposites that’s investigated. Montmorillonite clay with alkyl ammonium ion of hexadecyl trimethylammonium bromide (CTAB) was examined. Among the parameters studied, PLA/ LDPE nanocomposites showed larger improvements in mechanical properties compared to PLA/ LDPE blend due to higher shear forces exerted by polymer blend matrix on clay aggregates during polymer-clay mixing. The original MMT with Na+ cation results in weak improvements in mechanical properties compared to organoclays. It was observed that the tensile strength, modulus, and elongation at break of the nanocomposite samples can be optimized with 4% of clay loading. The morphology and chemical structure of the optimum sample were examined by X-ray diffraction and FT-IR spectroscopy, respectively.

الخلاصةتتناول هذا البحث تحضير ودراسة تاثير المتغيرات على الخواص الميكانيكية للكوبوليمرالمتكون من حامض البولي لاكتيك / البولي اثيلين منخفض الكثافة (PLA / LDPE) مع الطين المعدل (organoclay) بطريقة النانوكومبوزت وتشمل هذه الخواص قوة الشد والمرونه واستطالة عند الكسر.ايضا تم دراسة الثباتية الحرارية للكومبوليمر بعد انتاجه بطريقة النانو . تم مفاعلة وفحص الطين من نوع مونتمورينوليت مع أيون هكساديسايل ثلاثي مثيل الامونيوم trimethylammonium hexadecyl (CTAB)لانتاج الايون (organoclay) الذي يعمل بطريقة النانو. اضهرت النتائج على دراسة PLA/LDPE نانوكومبوزت ان هنالك تحسن كبير في الخواص الميكانيكية والحرارية كما ظهر في فحص TGA والتنسايل والمرونه مقارنة بمزيج PLA/LDPE لوحده حيث ان الطين المعدل(organoclay) المضاف حسن من قوة تحمل البوليمرللحرارة والشد . كما تمت ملاحظة ان قوة الشد التنسايل والاستطارة قد ازدادت بوجود الطين المعدل المضاف بمعدل 4% فيما قلت هذه الخواص عند زيادة النسبة عن 4% . ايضا تم فحص التركيب الكيميائي والمورفولوجي للناتج للعينة الامثل المضاف لها 4% من الطين المعدل بواسطة FTIR و XRD ايضا تم اخذ صور للناتج لاضهار النانو بواسطة SEM و TEM .


Article
A modeling comparison studies for thermo-mechanical and other Properties of RHDPE and RLDPE Wastes
نمذجة دراسات مقارنة للخصائص الثرمو- ميكانيكية وخصائص اخرى للبولي اثليين عالي وواطيء الكثافة المعاد

Authors: Falak O. Abas --- Raghad U.Abass --- Mohammed O.Abass
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (A) Engineering Pages: 681-701
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

A recycled waste plastic (recycled high density poly ethylene RHDPE and recycled low density poly ethylene RLDPE) are exposed to environmental conditions during the usage for many years ago. Also the chemical contaminants in the internal composition had effects on the thermo-mechanical and other properties for these wastes.Then weathering effect data are examine for both locally and international wastes on their thermo-mechanical and chemical properties such as (Tensile strength, modulus, elongation, impact and permeability) respectively.Afterward different mathematical software models are applied to analysis these weathering – properties data in order to estimate the more effective properties that changed by these weathering conditions such as (concentration of contaminant, time, temperature, thickness of specimen, length of spectra, basic property).The results shows that a multi-polynomial model has a best fit for most or several of properties to active weathering variables, also gave a vary residual and deviation than experimental analyzed data for both sources of wastes local and international RHDPE and RLDPE. Also results of thermo-mechanical and chemical properties prove that both tensile strength and modulus of elasticity thermo-mechanical properties and permeability / length of spectra chemical property were given a high quality of correction and fitting factor from 93-99 %, with less deviation and residual function was produced. And analyzed weathering properties of RHDPE gave a best fit than RLDPE; all of them fitted the mathematical software model below: …(1) Where:a, b, c …J = coefficient of the best fit model.x1 = concentration of contaminants.x2 = time of aging.

أن المواد البلاستيكية المعادة تتعرض للتغيرات الجوية المحيطة بها نتيجة الاستخدام لعدة سنوات. بالأضافة الى تأثير الشوائب الكيمياوية نتيجة معاملتها إثناء عمليات التصنيع والصب وخصوصاً على الخصائص الثرمو-ميكانيكية والخصائص الأخرى.لذلك تم تفحص العديد من البيانات حول تأثير ظروف التجويه لنماذج محلية وعالمية لمواد معادة على خصائصئها الثرموميكانيكة والكيمياوية مثل (قوة الشد، معامل المرونة، الأستطالة، قوة الصدمة،والنفاذية)على التوالي.فيما بعد تم تطبيق مختلف الموديلات الرياضية الالكترونية لتحليل تلك البيانات (ظروف التجوية) لتحديد اكثر هذه الخصائص تاثرا اي تغيرا مع تلك الظروف (ظروف التجوية مثل تركيز الشوائب، زمن التعرض للظروف البيئية القاسية، درجة الحرارة، سمك العينة او الشريحة، الطول الموجي للأشعة المطبقة، الخاصية الاساسية).وأثبتت النتائج الرياضية التحليلية بواسطة الحاسوب انطباق الموديل المتعدد الدوال على اغلب الخصائص المقاسة / متغيرات ظروف التجوية المطبقة حيث اعطى هذا الموديل النتائج اقل انحرافاً للقيم العملية عن النظرية وانطباقاً اكثر بين النوعين من البلاستيك المعاد المحلي والعالمي الواطئ والعالي الكثافة.واكدت نتائج كل من الخصائص الثرمو-ميكانيكية والكيمياوية انطباقاً اكثر لخاصتي الشد والمرونة والخاصية الكيمياوية وهي علاقة النفاذية / الطول الموجي للاشعة الجوية حيث اعطت معامل تصحيح عالي النوعية واقل انحرافاً من 93-99 %.اضافة الى ذلك علاقة الخصائص الثرمو-ميكانيكية والكيمياوية للبولي اثيلين عالي الكثافة (PETH) كانت اكثر انطباقاً من النوع الأخر من المعاد البولي اثيلين الواطئ الكثافة(PETL) واعطى الكل انطباقاً للموديل الرياضي التالي: ..(1)


Article
Study of the Tensile strength properties of Low density polyethylene composites with Cannabis (Hemp fibers)
دراسة خواص قوة الشد للبولي ايثيلين واطئ الكثافة مع الياف القنب كمالئات بوليمرية

Author: Einas A. Al-Nasir ايناس عبد العزيز الناصر
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2013 Volume: 39 Issue: 3A Pages: 15-22
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

The mechanical properties of hemp fibers (cellulosic fibers) composites were studied. The range of added Hemp fibers has the values (0%, 3%, 5%, 7%, 10%, 15%, and 20%) of polyethylene weight and, the best fibers ratio was 5%.The properties (LDPE / Cannabis) composites were analyzed as a function of the fibers amount. All prepared composites showed improved fibers dispersion in the low density polyethylene matrix. All composites displayed lower elongation of break compared to pure LDPE.

تمت دراسة الخواص الميكانيكية للألياف القنب (ألياف السليولوز) كمواد مالئة للبوليمر. وقد تم تحضير نماذج بنسب وزنية (0٪، 3٪، 5٪، 7٪، 10٪، 15٪، و 20٪) من وزن البولي اثيلين و، كانت أفضل نسبة الألياف 5٪، وقد تم تحليل الحشوات كدالة لكمية من كمية الألياف. وأظهرت جميع النماذج المحضرة تحسن في انتشار الالياف بشكل متجانس في البولي ايثيلين واطئ الكثافة ،ومن الملاحظ ان جميع النسب المضافة للبوليمر عملت على تقليل نسبة الاستطالة مقارنة مع البوليمر النقي


Article
STUDY THE EFFECT OF ADDING DIFFERENT RATIOS OF IRON AND ALUMINUM OXIDES ON THE COMPRESSIVE STRENGTH AND THE SOFTENING TEMPERATURE OF A LOW-DENSITY POLYETHYLENE
دراسة تاثير اضافة نسب مختلفة من اكاسيد الحديد و الالمنيوم على مقاومة الانضغاط ودرجة حرارة الليونة للبولي اثيلين واطئ الكثافة

Loading...
Loading...
Abstract

This research aims to study the effect of adding Iron Oxide Fe2O3 and Aluminum Oxide Al2O3 on mechanical properties of Low Density Polyethylene (LDPE), where various weight percentages of the oxides of (1%, 3%, 5%, 7%, and 10%) were used.To investigate the effect of adding oxides on the mechanical properties of (LDPE), Compression test was performed and the ultimate compression test was determined, then the softening point was measured. From the results reached it was concluded that the best compression strength was recorded at 7% addition of Iron Oxide, while for the Aluminum Oxide the highest compression strength was recorded at 5%. Also it was found that the relationship was directly proportional between softening point and oxide percentage. It was noticed that the adding of the oxides up to 10% results in decreasing of the formability during compression.

يهدف هذا البحث الى دراسة تاثير اضافة اوكسيد الحديد واوكسيد الالمنيوم على الخواص الميكانيكية للبولي اثيلين، حيث استخدمت نسب وزنية مختلفة من الاكاسيد وهي(1%,3%,5%,7%,10%).لتقييم مدى تاثير الاكاسيد المظافة على الخواص الميكانيكية تم اجراء اختبار الانضغاط وتحديد اجهاد الانضغاط الاقصى ومن ثم قياس نقطة الليونة. ومن خلال النتائج التي تم التوصل اليها تبين ان افضل مقاومة انضغاط كانت عند اضافة اوكسيد الحديد بنسبة 7% ، اما بالنسبة لاوكسيد الالمنيوم فكانت افضل قيمة مقاومة انضغاط عند اضافة 5%. كذلك تبين ان العلاقة كانت طردية مابين زيادة النسب المضافة ونقطة الليونة. وقد لوحظ ان اضافة اوكسيد الحديد واوكسيد الالمنيوم لغاية 10% ادت الى انخفاض في قابلية التشكيل اثناء الانضغاط.


Article
Effect of temperature on some rheological properties of low-density polyethylene
تأثير درجة الحرارة في بعض الخصائص الانسيابية لبولي إثيلين واطئ الكثافة

Author: Saleh H. Abud صالح حسون عبود
Journal: journal of al-qadisiyah for pure science(quarterly) مجلة القادسية للعلوم الصرفة (فصلية). ISSN: 19972490 Year: 2016 Volume: 3 Issue: 21 Pages: 78-82
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This paper presents some of rheological properties of low-density polyethylene (LDPE) that Soluteinto benzene with different concentrations and at a range of temperatures of 20 - 40oC. Density, flowtime and viscosity measurements showed that these properties increase with increasing theconcentration while all of them decrease with increasing the temperature.

يتضمن البحث دراسة بعض الخصائص الفيزيائية لمادة بولي اثلين واطى الكثافة المذاب في البنزين20,30,40 ) وهذه الخصائص هي الكثافة، )oC 0.005 ) وبمدى من درجات الحرارة , 0.01, 0.015, 0.02, 0.025) gm/ml بتركيزاتزمن الانسياب، اللزوجة القصية، اللزوجة النسبية، اللزوجة النوعية، اللزوجة المختزلة واللزوجة الذاتية للبوليمر. بينت الدراسة بأن جميعالخصائص في اعلاه تزداد مع زيادة التركيز وتتناقص مع زيادة درجة الحرارة.

Listing 1 - 10 of 19 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (19)


Language

English (12)

Arabic (4)

Arabic and English (2)


Year
From To Submit

2018 (1)

2017 (3)

2016 (1)

2015 (3)

2014 (4)

More...