A Study of the mechanical properties of aluminum composite materials prepared by atomization process
دراسة الخواص الميكانيكية لمتراكبات الألمنيوم المحضرة بطريقة التذرية

Loading...
Loading...
Abstract

Steel fiber aluminum matrix composites were prepared by atomization technique. Different air atomization conditions were considered; which were atomization pressure and distance between sample and nozzle. Tensile stress properties were studied. XRF and XRD techniques were used to study the primary compositions and the structure of the raw materials and the atomized products. The tensile results showed that the best reported tensile strength observed for an atomization pressure equal to 4 mbar and sample to nozzle distance equal to 12 cm. Young modulus results showed that the best result occurred with an air atomization pressure equal to 8 mbar and sample to nozzle distance equal to 16cm.

تم تحضير متراكبات أساس الألمنيوم المدعمة بألياف الفولاذ بطريقة التذرية. تم أخذ ظروف مختلفة لعملية التذرية بنظر الأعتبار وهي ضغط التذرية و المسافة بين العينة والمرذاذ. درس التأثير على خواص اجهاد الشد. تقنيات فلورة الأشعة السينية و حيود الأشعة السينية أستخدمت لدراسة التركيب الأولي و الخواص التركيبية للمواد الأولية والمواد الناتجة من الترذيذ. أظهرت نتائج الشد ان أفضل نتيجة موثقة لحد المرونة لوحظت عند ضغط تذرية يساوي mbar4 و عند بعد للعينة من المرذاذ يساوي cm12 . أما لمعامل يونك فكانت عند ضغط تذرية باستخدام الهواء يساوي mbar8 و عند بعد للعينة من المرذاذ يساوي cm16.

Keywords

MMCs --- Atomization --- Tensile.


Article
Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles

Authors: Ali Hubi Haleem --- Newfal Zuheir --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 30-38
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this work is preparing and studying some of mechanical properties [Brinell hardness (BHN) and compression strength] of aluminum matrix composite material that reinforced by (3, 6 , 9 , and 12 wt.% ) Al2O3 particles. Powder technology technique is used in samples preparing. Samples were compacted by using single action pressing then followed directly by sintering process at 500°C under the effect of inert gas conditionsResults were showed an advancing in the Brinell hardness (BHN) and compression strength especially at 12 wt.% α- Al2O3. The development in the Brinell hardness (BHN) and compression strength were found to reach 89% and 54% respectively from the initial properties of unreinforced aluminum samples.

يهدف البحث الحالي إلى تحضير ودراسة بعض الخواص الميكانيكية ( صلادة برينل ومقاومة الانضغاط) لمادة مركبة ذات أساس من الألمنيوم مقوى بدقائق الألومينا وبنسب وزنيه .(3, 6, 9, 12wt.%) استخدمت تكنولوجيا المساحيق في تحضير النماذج حيث تم كبس النماذج بأسلوب أحادي الاتجاه و تلى ذلك تلبيدها بدرجة حرارة 500°Cفي جو خامل. أظهرت النتائج إن تقوية الألمنيوم بدقائق الألومينا يظهر تحسنا في صلادة برينل ومقاومة الانضغاط وخاصة عند نسبة تقوية .12 wt.% حيث بلغ مقدار التحسن في صلادة برينل ومقاومة الانضغاط للمادة المركبة 89% و 54% على التوالي بالمقارنة مع الألمنيوم غير المقوى.


Article
Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles

Authors: Ali Hubi Haleem --- Newfal Zuheir --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 30-38
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this work is preparing and studying some of mechanical properties [Brinell hardness (BHN) and compression strength] of aluminum matrix composite material that reinforced by (3, 6 , 9 , and 12 wt.% ) Al2O3 particles. Powder technology technique is used in samples preparing. Samples were compacted by using single action pressing then followed directly by sintering process at 500°C under the effect of inert gas conditionsResults were showed an advancing in the Brinell hardness (BHN) and compression strength especially at 12 wt.% α- Al2O3. The development in the Brinell hardness (BHN) and compression strength were found to reach 89% and 54% respectively from the initial properties of unreinforced aluminum samples.

يهدف البحث الحالي إلى تحضير ودراسة بعض الخواص الميكانيكية ( صلادة برينل ومقاومة الانضغاط) لمادة مركبة ذات أساس من الألمنيوم مقوى بدقائق الألومينا وبنسب وزنيه .(3, 6, 9, 12wt.%) استخدمت تكنولوجيا المساحيق في تحضير النماذج حيث تم كبس النماذج بأسلوب أحادي الاتجاه و تلى ذلك تلبيدها بدرجة حرارة 500°Cفي جو خامل. أظهرت النتائج إن تقوية الألمنيوم بدقائق الألومينا يظهر تحسنا في صلادة برينل ومقاومة الانضغاط وخاصة عند نسبة تقوية .12 wt.% حيث بلغ مقدار التحسن في صلادة برينل ومقاومة الانضغاط للمادة المركبة 89% و 54% على التوالي بالمقارنة مع الألمنيوم غير المقوى.


Article
Effect of SiC particulates on fracture toughness of an Al-1.5% Mg matrix composite.

Author: Ali Ismail Salih
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467 Year: 2012 Volume: 18 Issue: 73 / ملحق Pages: 63-72
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The fracture toughness of the SiC-Al-1.5%Mg PMMCs has been studies. The MMCs were prepared by conventional method's the stir cast. The SiC preheated particle content was varied from 2, 4, 6 to 8 wt% and their average size was 53µm. we have noticed that the fracture toughness was decreased due to the increase in SiC wt%. Also the hardness has been investigated and show the hardness of the composite material was increased with the increases in the SiC wt%.The X-ray diffraction test was also investigated to the matrix alloy, SiC particle and the reinforcement material in order to study the phases which are produced into the MMCs structure. Its show that there is good contact has been produced between them.

ان متانة الكسر للمادة المركبة SiC-Al-1.5%Mg PMMCs قد درست في هذا البحث. والذي حضرت فية المواد المركبة عن طريق الخلط الميكانيكي بواسط الخلاط للحبيبات السيراميكية في المنصهر المعدني. وكانت نسب الاضافة للحبيبات السيراميكية هي 2، 4، 6، و 8 wt% مع معدل للحجم الحبيبي 53µm ، وقد لوحظ ان متانة الكسر للمادة المركبة قد انخفضت نتيجة لزيادة النسبة المئوية لحبيبات SiC مقارنة مع المادة الاساس . وكذلك لوحظ ان الصلادة قد ارتفعت نتيجة زياد النسبة المئوية لحبيبات SiC. قد تم اجراء فحص حيود الاشعة السينية للمادة الاساس واللحبيبات السيراميكية والمادة المركبة لمعرفة الاطوار الناتجة خلال عملية انتاج المادة المركبة . وقد لوحظ انة قد حصل تفاعل بيني مناسب لتوليد ربط بين المادة الحبيبية والمادة الاساس.


Article
Influence of Nanoreinforced Particles (Al2O3) on Fatigue Life and Strength of Aluminium Based Metal Matrix Composite
تاتير حبيبات المادة النانوية المقواة (Al2O3) على عمر ومقاومة الكلال لمركب ذي الاساس المعدني

Loading...
Loading...
Abstract

In this investigation, Al2O3 nano material of 50nm particles size were added to the 6061 Al aluminium alloy by using the stir casting technique to fabricate the nanocomposite of 10wt% Al2O3. The experimental results observed that the addition of 10wt% Al2O3 improved the fatigue life and strength of constant and cumulative fatigue. Comparison between the S-N curves behaviour of metal matrix (AA6061) and the nanocomposite 10wt% Al2O3 has been made. The comparison revealed that 12.8% enhancement in fatigue strength at 107cycles due to 10wt% nano reinforcement. Also cumulative fatigue life of 10wt% nanocomposite was found to be increased by 33.37% and 39.58% for low-high and high-low loading sequences, respectively, compared to the metal-matrix cumulative life.

في هذا البحث تم اضافة المادة النانوية Al2O3 ذات حجم حبيبات 50 نانوميتر الى سبيكة الالمنيوم AA6061 باستخدام تقنية السباكة بالتحريك لتصنيع المركب النانوي ذو 10wt% من المادة النانوية Al2O3.النتائج المستخرجة عمليا اوضحت ان اضافة 10wt% Al2O3 بوصفه نسبة وزنية حسنت من عمر مقاومة الكلال الثابت والمتراكم .تمت مقارنة بين سلوك منحنيات S-N للمعدن الاساس AA6061 والمركب النانوي 10wt% Al2O3 .واوضحت المقارنة تحسن بمقدار 12.8% في مقاومة الكلال عند 107 دورة نتيجة 10w% للمادة المقواة. كذلك وجد ايضا ان عمر الكلال التراكمي ازداد نسبة 33.37% و% 39.58 للتحميل المتتابع من واطئ-عالٍ ومن عالٍ-واطئ على التوالي مقارنة مع العمر التراكمي للمعدن الاساس.


Article
دراسة بعض الخواص الفيزيائية و الميكانيكية لمادة متراكبة ذات اساس من الالمنيوم6063 مدعم بدقائق الزركونيا و المحضرة بتقانة ميتالورجيا المساحيق

Authors: نجيب سلمان عبطان --- رابحة صالح ياسين --- انمار ضيف مهدي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 3 Pages: 932-941
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this work is studying some physical properties (density , porosity & water absorption) and some mechanical properties (micro hardness Vickers , compression strength & wear resistance) of aluminum 6063 matrix composite material that reinforced by (2.5,5,7.5&10) wt.% of ZrO2 particles. Powder metallurgy technique is used in samples preparing. Samples were compacted by using cold uniaxial pressing then followed sintering process at 600 oC under inert gas.Results were showed improving in (wear resistance , compression strength & micro hardness Vickers) and increasing in (density , porosity & water absorption). Increase micro hardness (44.5 – 101.13), compression strength (36.1998 – 46.7) N/mm2 and decrease wear rate (9.5*exp(-8) – 4.8*exp(-8)) g/cm at time 30 min. with (0 – 10)% ZrO2. While increase apparent density (1.388 – 3.15) g/cm3 , apparent porosity (0.96 – 4.61)% and water absorption (0.699 – 2.09)% at (0 – 10)% ZrO2.

يهدف البحث الى دراسة بعض الخواص الفيزيائية (الكثافة و المسامية و قابلية إمتصاص الماء) و بعض الخواص الميكانيكية (صلادة فيكرز المايكروية و مقاومة الإنضغاط القطرية و مقاومة البلى) لمادة متراكبة ذات اساس من الالمنيوم 6063 مدعمة بنسب وزنية مختلفة (2.5,5,7.5&10) wt.% من دقائق الزركونيا. وقد تم إتباع تقانة ميتالورجيا المساحيق في تحضير العينات حيث تم كبس العينات على البارد بطريقة الكبس احادي الإتجاه بضغط 5 طن تلى ذلك تلبيد العينات بدرجة حرارة 600 مo في جو خامل.وقد اظهرت النتائج ان تدعيم الالمنيوم 6063 بدقائق الزركونيا تحسن من مقاومة البلى و مقاومة الإنضغاط و صلادة فيكرز المايكروية وكذلك زيادة في قيم الكثافة و المسامية و قابلية إمتصاص الماء . إذ تزداد الصلادة من (101.13 – 44.5) و مقاومة الإنضغاط القطرية من (46.7 – 36.1998) N/mm2و يقل معدل البلى من (4.8*exp(-8) – 9.5*exp(-8)) غم/سم عند زمن 30 دقيقة ومحتوى (0 – 10)% من الزركونيا. بينما تزداد الكثافة الظاهرية (3.15 – 1.388) غم/سم3 و المسامية الظاهرية (4.61 – 0.96)% و قابلية إمتصاص الماء (2.09 – 0.699)% عند محتوى (10 – 0)% من الزركونيا.


Article
Studying the dry sliding wear behavior of Al-4%Cu/ SiC Metal Matrix Composite with heat treatment
دراسة سلوك الانزلاق الجاف للمادة المركبة Al-4%Cu/ SiC والمعاملة حراريا

Loading...
Loading...
Abstract

In This study metal matrix composite (MMCs) was produced by using aluminum as base metal matrix reinforced with the SiC particulates using conventional casting technique, macro structural studies showed that uniform distribution of SiC particulates. The density of MMCs decreased with the increase in SiC wt%. The Hardness of MMCs increased with the increase in SiC wt%, composites exhibit a significant acceleration in kinetics of preciptation in compare with the unreinforced matrix alloy. A pin on disc wear testing machine was used to evaluated the wear loss of composites. The results showed that wear rates of composites are lower than of the matrix alloy and further decrease with increase in SiC particulate content.

في هذه الدراسة تم أستعمال معدن الالمنيوم كمادة أساس وحبيبات كاربيد السلكون كمادة تقوية وذلك بأستخدام تقنياتَ الصب التقليديةِ في انتاج المادة الاساس والمادة المدعمة، أظهرت نتائج الفحص العياني للتركيب بأنّ التوزيعِ الحبيبي لمادة التقوية وهي حبيبات كاربيد السلكون كانت منتظة أما كثافة المادة المدعمة فقد أنخفضت بزيادةِ نسبة حبيبات كاربيد السلكون المضافة. وبالنسبة للصلادة فهي زادت للمادة المركبة بزيادةِ نسبة حبيبات كاربيد السلكون ألمضافة، وحصل زيادة في سرعة الترسيب للمادة المدعمة بحبيبات كاربيد السلكون بالمقارنةِ مع سبيكةِ المادة الاساس غير المدعمةِ. أستخدمت تقنية الدبّوس على ماكنةِ أختبار البلى والتي تستعمل القرصِ الدوار لمعرفة خسارةِ البلى للمادة الاساس والمادة المدعمة. أظهرت النَتائِجَ بأنّ نِسَبِة خسارة البلى للمادة المدعمة أوطأ مِنْها بالنسبة لسبيكةِ المادة المتراكبة الاساس ويزداد النقصانَ بزيادةِ المحتوى من حبيبات كاربيد السلكون.


Article
Effect of Nano BN Addition on the Properties of an Aluminum Metal Matrix Composite

Authors: Fadhal A. Hashim --- Niveen J. Abdulkader --- Nibras S. Jasim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 6 Part (A) Engineering Pages: 691-695
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present work, the wear rate and hardness of recycled Aluminum alloy based metal matrix composite that reinforced with nano Boron Nitride with (2%, 4%, 6%, and 8%) weight percentage with 33 nm particle size were evaluated. A stir casting process was applied to fabricate composite the mechanical and metallurgical characteristics of the fabricated composite were evaluated through the hardness and wear test. The results indicate that the value of hardness increased and wear rate decreased with increasing the BN percentage due to high surface area to weight ratio for nanoparticles.

Listing 1 - 8 of 8
Sort by
Narrow your search

Resource type

article (8)


Language

English (5)

Arabic (2)

Arabic and English (1)