Evaluation of macrohardness of recast-ed Cobalt–chromium alloy

Author: Ahmed A Al–Ali
Journal: Al-Rafidain Dental Journal مجلة الرافدين لطب الأسنان ISSN: 18121217 Year: 2007 Volume: 7 Issue: 1 Pages: 111-117
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

Aims: To study the effect of recasting on the macrohardness of cobalt chromium (Co–Cr)alloy, and to evaluate the effect of finishing and polishing on it. Materials and methods: Two brand of Co–Cr alloys were used, divided into three groups, the specimens of the first group were casted from new materials, the second were casted from previously casted material without the addition of any new material (100% recast), the third were casted by combination 50% new material and 50% used material. Half of the specimens just finished and the other half were finished and polished , hardness for all of them were measured. Results: Showed that recasting, both 100% and 50%, significantly increase the macrohardness of Co–Cr alloys and no significant effect of finishing and polishing on it. Conclusion: Recasting may affect properties of Co–Cr alloy and new material should be used rather than recasted material.


Article
Effect of Laser Surface Treatment on Physical Properties of Composite Material (Al-B4C)
تأثير المعاملة الحرارية السطحية بالليزر على الخواص الفيزياوية لمادة متراكبة (Al-B4C)

Authors: Khansaa D. Selman خنساء داود سلمان --- Sabah N. Mahmood صباح نوري محمودد --- Qamar Q. Mohameed قمر قاسم محم
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2013 Volume: 54 Issue: 4 Pages: 882-887
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work study the effect of laser surface heat treatment on physical properties (green density, density after sintering, theoretical density and porosity)of a composite material of an Al powder as a matrix with different percentage of B4C powder as additive material. This work was done by two stages: First stage: Production the maincomposite material which is contain Al powder with grain size 24μm as a matrix and B4C powder with grain size 50μm as additive with different weight percentage (5%,10%,15%,20%,25%,30%), and the powders Maxined for suitable time 15min, after that the mixture compacted with 2ton and sintered at 550C0. Second stage: Laser surface treatment was done for the productive composite material after sintering by using pulse Nd: YAG laser with 1J energy, wave length 1064nm and pulse duration 100ns.Laser surface heat treatment was carried out with one pulse and two pulses respectively. Macrohardness of the composite material was measured after the sintering process and after the laser surface heat treatment with one pulse and two pulses, also photo-micrographies were taken for the specimens by using ordinary microscopic after each of sintering process and laser surface heat treatment. The results show that improvement of physical properties mentioned above and macrohardness after laser surface treatment with two pulses more than one pulse.

في هذا البحث تمت دراسة تاثير المعاملة الحرارية السطحية بالليزرعلى الخواص الفيزياوية (الكثافة الخضراء ,الكثافة بعد التلبيد, الكثافة النظرية والمسامية) لمادة متراكبة من مسحوق الالمنيوم كمادة اساس مع نسب مختلفة من مسحوق رابع كاربيد البورون (C4B) كمادة مضافة. تم اجراء البحث على مرحلتين: المرحلة الاولى: انتاج المادة المتراكبة المتكونة من مسحوق الالمنيوم بحجم حبيبي كمادة اساس مع مسحوق (C4B) بحجم حبيبي كمادة مضافة وبنسب وزنية (%5,% 10,%15,%20,%25,%30), ومن ثم تمت عملية خلط المساحيق لمدة min15 ,بعد ذلك اجريت عملية التدميج بكبس الخليط بضغط والتلبيد عند درجة حرارية . المرحلة الثانية: اجريت المعاملة الحرارية السطحية بالليزر للمادة المتراكبة المنتجة بعد عملية التلبيد باستخدام ليزر نيديوم – ياك النبضي بطاقة مقدارها , بطول موجة nm1064 وزمن نبضة ns100. وقد اجريت المعاملة السطحية بالليزر بنبضة واحدة وبنبضتين على التوالي. تم حساب الصلادة الماكروية للمادة المتراكبة بعد التلبيد وكذلك بعد المعاملة السطحية بالليزر لنبضة واحدة ونبضتين, كذلك تم تصوير العينات باستخدام المجهر الضوئي الاعتيادي للعينات بعد كل من عملية التلبيد والمعاملة السطحية بالليزر.اظهرت النتائج تحسن في الخواص الفيزياوية المذكورة في اعلاه وكذلك الصلادة الماكروية بعد المعاملة السطحية بالليزر بنبضتين اكثر مما هو عليه للنبضة الواحدة.