STUDYING THE FLEXURAL PROPERTIES AND MAX.SHEAR STRESS OF SELF CURE PMMA RESIN FOR DENTURE APPLICATIONS .
دراسة خصائص الانحناء واجهاد القص الاعظم لراتنج البولي مثيل ميثا اكريليت المبلمر ذاتيا لتطبيقات طقم الاسنان .

Loading...
Loading...
Abstract

Poly Methyl Methacrylate were widely accepted material in dental and medical field due to the excellent biocompatibility and easy fabrication, however exhibit inferior mechanical properties. Therefore, the present study conducted to determine the flexural properties of PMMA based material by reinforcing PMMA with two different natural fibers (bamboo & siwak fibers). Discontinuous random fibers used in three lengths (2, 6 & 12 mm) and three weight percentage (3, 6 & 9 wt. %) of the both types of fibers. Results indicated that Flexural modulus, flexural strength and max.shear stress increase with increasing weight fraction and fiber length of fibers (bamboo & siwak) and reach the maximum amount at addition of weight fraction of (9 wt.%) and (12mm) length of fibers. The highest value of flexural modulus, flexural strength and max.shear stress were (10.09GPa), (112MPa), (6MPa) respectively, for composite specimens with bamboo fibers, while for composite specimen with siwak fibers (9.71GPa),(101MPa),(4.44MPa) at the optimum condition of (9wt.%) and (12mm) length . All composite specimens reinforced with bamboo fibers showed the highest flexural strength and flexural modulus among the composite specimen reinforced by siwak fibers.

ان مادة البولي مثيل ميثا اكريليت مادة مقبولة بشكل واسع في تطبيقات طقم الاسنان والتطبيقات الطبي نظرا للتوافق الطبي وسهولة التصنيع على الرغم من الخواص الميكانيكية الضعيفة. لذلك فان الدراسة الحالية تهدف لحساب خصائص الانحناء لبوليمر البولي مثيل ميثا اكريليت المقوى بنوعين من الالياف الطبيعية (الياف السواك والخيزران) والتي استخدمت بشكل متقطع عشوائي الترتيب بثلاث اطوال (2 و 6 و12 ملم) وثلاث كسور وزنية (3 و6 و9 %) لكلا النوعين من الالياف. ولقد بينت النتائج ان معامل الانحناء ومقاومة الانحناء واجهاد القص الاعظم تزداد مع زيادة الكسر الوزني وطول الليف لالياف الخيزران والسواك وتصل الى اعظم قيمة عند (9%) و (12 ملم).وان اعلى قيم لمعامل الانحناء ومقاومة الانحناء واقصى اجهاد قص للعينات المتراكبة المقواة بالياف الخيزران ( GPa10.09, 112 MPa , (6MPa بينما للعينات المتراكبة المقواة بالياف السواك (4.44 MPa,101MPa,9.71GPa) على التوالي عند افضل ظروف (12 ملم و 9%).كل العينات المتراكبة المقواة بالياف الخيزران تكون لها قيم معامل انحناء ومقاومة انحناء اعلى من المواد المتراكبة المقواة بالياف السواك .


Article
COMPARATIVE STUDY THE FLEXURAL PROPERTIES AND IMPACT STRENGTH FOR PMMA REINFORCED BY PARTICLES AND FIBERS FOR PROSTHETIC COMPLETE DENTURE BASE
دراسة مقارنة حول خصائص الانحناء ومقاومة الصدمة للبولي مثيل ميثا اكريليت المقوى بالدقائق والألياف لمادة قاعدة طقم أسنان أصطناعي كامل

Loading...
Loading...
Abstract

In the present search, attempts are made to develop the properties of PMMA resin that used for upper and lower prosthesis complete denture, by addition two different types of particles, which included: nano-hydroxyapatite (nHA) particles and micro-zirconia (ZrO2) particles that added with different volume fractions of (1%, 2% and 3%) to poly methyl methacrylate (PMMA) cold cured resin as new fluid resin matrix. Also woven glass fiber kind (E-glass) and woven Kevlar fiber kind (49), it were added with a fixed volume fraction of (5%) to PMMA composites. In this work the composite prosthetic dentures specimens preparation was done by using (Hand Lay-Up) method as six groups which includes: the first group consists of PMMA resin reinforced by nHA particles, the second group consists of PMMA resin reinforced by ZrO2 particles, the third group consists of (PMMA-nHA) and glass fiber layer as laminated composite , the fourth group consists of (PMMA-ZrO2) and glass fiber layer, the fifth group consists of (PMMA-nHA) and Kevlar fiber layer and the sixth group consists of (PMMA-ZrO2) and Kevlar fiber layer.The experimental part of this study included performing many mechanical tests which, includes (Flexural, Maximum Shear Stress and Impact) tests. The result of this study showed the values of most properties increased with increasing of the volume fraction of (nHA and ZrO2) particles in polymer composite materials. While, the impact strength decreased. The ZrO2 particle and woven mat Kevlar fiber had shown greater values for the most composite materials properties for all groups’ specimens except the flexural strain.Also the results showed the maximum values for hybrid laminated composite properties (flexural modulus and impact strength) were obtained in hybrid laminated composite materials for sixth group specimens. While, the maximum value for properties (flexural strength and max shear stress) were obtained in hybrid laminated composite materials for fourth group specimens.

تم في هذا البحث أجراء عدة محاولات لغرض تطوير مواصفات راتنج البولي مثيل ميثا اكريليت المستخدم كطقم أسنان أصطناعي كامل علوي أو سفلي. وقد حضرت هذه المواد المتراكبة من البولي مثيل ميثا اكريليت على شكل راتنج سائل جديد معالج ذاتياً كمادة أساس وقد تم تقويتها بنوعين مختلفين من الدقائق تضمنت دقائق الهيدروكسي اباتايت النانوية ودقائق الزركونيا الميكروية اضيفت بكسور حجمية مختلفة هي (1%, 2% and 3%)، ونوعين مختلفين من الالياف الحصيرية الثنائية الاتجاه هي الياف الزجاج نوع (E-GLASS) والياف الكفلر نوع (49) وقد اضيفت الى المواد المتراكبة بكسر حجمي ثابت هو (%5). في هذا البحث حضرت عينات من أطقام الاسنان الأصطناعية المتراكبة بطريقة (الصب اليدوي) على شكل ستة مجاميع هي: المجموعة الاولى تضم راتنج البولي مثيل ميثا اكريليت ودقائق الهيدروكسي اباتايت النانوية، المجموعة الثانية تضم راتنج البولي مثيل ميثا اكريليت ودقائق الزركونيا، المجموعة الثالثة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الهيدروكسي اباتايت النانوية، المجموعة الرابعة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الزركونيا، المجموعة الخامسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الهيدروكسي اباتايت النانوية، المجموعة السادسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الزركونيا.يتضمن الجزء العملي من هذا البحث اجراء العديد من الاختبارات الميكانيكية والتي شملت فحوصات (الانحناء، اجهاد القص الأعظم والصدمة(. وقد بينت النتائج بان قيم اغلب الخواص ازدادت مع زيادة الكسر الحجمي لدقائق الهيدروكسي أباتايت النانوية ودقائق الزركونيا، بينما قلت مقاومة الصدمة. وان دقائق الزركونيا والياف الكفلر الحصيرية تعطي قيم أعلى لاغلب خواص المواد المتراكبة ولكافة مجاميع العينات ماعدا الانفعال الأنحنائي. كذلك أظهرت النتائج بان اعلى قيم لخصائص (معامل الانحناء ومقاومة الصدمة) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة السادسة. بينما اعلى قيم لخصائص (مقاومة الانحناء واجهاد القص الأقصى) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة الرابعة.