Article
Experimental Study on Effect of Changing Dr. Maha Abdul Ameer Kadhum Dr. Entidhar Mhawes Zghair Hayder Mohammed Hasan Welding Current on Mechanical and Metallurgical Properties of Seam Welding Joint for Low Carbon Steel AISI 1005 (0.8 mm)

Author: Ammar Azeez Mahdi AL-Yasari
Journal: Thi-Qar University Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية ISSN: 20759746 Year: 2013 Volume: 4 Issue: 1 Pages: 92-99
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

The aim of this work is to study the effect of changing welding current on the mechanical and metallurgical properties and choose the best welding current depend on result of study. The present work is an experimental study on effect of changing welding current on properties of seam welding joint for low carbon steel AISI 1005. Experiments results shows with increase welding current, hardness number will increase, also differentness in hardness number between weld nugget and HAZ (Heat Affected Zone) will increase and border of HAZ become bigger. Best mechanical results was achieved when welding current increased this doesn't mean that the highest current will become the suitable one, because the higher current will cause burin through in metal sheets and will cause leakage in products (liquid or gas storage tank), also will effect on grain size and microstructure due to changes in cooling rate, also the final shape of joints its important because most application of this type of weld is weight-goods industries (for civil using), so when use high welding current the final shape of joint will deform. Depended on above the best welding current rang is between 17 ≤ I < 19 K Amp.

يهدف البحث الى دراسة تاثير تغير تيار اللحام على الخواص الميكانيكية والميتالورجية لوصلات اللحام النقطي المستمر للحديد واطىء الكاربون, واختيار افضل تيار معتمداً على النتائج, حيث اظهرت النتائج العملية انه كلما زاد تيار اللحام زاد رقم الصلادة للملحومة وزادة مقاومة الشد اي تحسنت الخواص الميكانيكية ولاكن هذا لايعني ان افضل تيار يستخدم هو الأعلى قيمة لانه قد يؤدي الى انصهار بعض مناطق اللحام مما يؤدي العيب في المنتج لأن اغلب استخدامات هذا النوع من اللحام يكون في الخزانات, كما ان تطبيقات هذا اللحام تكون ظاهرة للعيان في اغلب التطبيقات المدنية لذلك يكون الشكل النهائي للمنتج ضروري وبناءاً على معطيات الخواص المجهرية والميكانيكية كما اوصت الجمعية الأمريكية للحام كانت افضل نتائج هي باستخدام تيار لحام يتراوح بين17 و19 كيلو امبير.


Article
Study The Effect Of Rienforcement & cintering particals On Some Metallurgical And Mechanical Properties For Composite ( Cu – SiC ) Prepared By Powder Metallurgy Technique .
دراسة تأثير جسيمات التقوية والتلبيد على بعض الخواص الميتالورجية والميكانيكية لمتراكب (نحاس – كاربيد سليكون) المحضر بتقانة ميتالورجيا المساحيق

Author: Najeeb S. Abtan1 , Kamal M. Hussein2 نجيب سلمان عبطان1 , كمال مصطفى حسين2
Journal: kirkuk university journal for scientific studies مجلة جامعة كركوك - الدراسات العلمية ISSN: 19920849 / 26166801 Year: 2016 Volume: 11 Issue: 2 Pages: 168-196
Publisher: Kirkuk University جامعة كركوك

Loading...
Loading...
Abstract

commercially pure copper matrix composite reinforced with ( 0,2,4,6,8,10 and 12vol % ) of ( SiC ) prepared by powder metallurgy technique. , then The mixture was mixed mechanically by using rotating mixer for two hour and frequently mixer for five minute for each sample . The mixture was cold pressed uniaxially at (350 MPa) using die of (12)mm diameter and height (100)mm and sintered at (900 oC) for two hours and studying the effect of reinforcement content on mechanical and metallurgical properties were studied . The results showed decrease in values of Green & Bulk Density and increasing the percentage of true porosity and increase in values of Vickers hardness and yield compressive resistance and decrease in wear rate with increase reinforcement content with improvement of properties after centering .

تم تحضير متراكب ذي اساس من معدن النحاس النقي تجارياً والمدعم بنسب حجمية (%12,10,8,6,4,2,) من جسيمات كاربيد السليكون باتباع تقانة ميتالورجيا المساحيق .ثم تم خلط المزيج في خلاط دوراني لمدة ساعتين ثم في خلاط إهتزازي ترددي لمدة 5 دقائق لكل نموذج وتم كبس المزيج على البارد من اتجاه واحد بضغط (350 MPa) في قالب فولاذي بقطر (12 mm) وإرتفاع (100 mm ). وأجري التلبيد عند درجة حرارة (900 oC ) لمدة ساعتين . وتم ودراسة بعض الخصائص الميكانيكية والميتالورجية وبيان تأثير جسيمات التقوية على هذه الخصائص . وتبين إنخفاض في قيم الكثافة الخضراء والحجمية وإرتفاع النسبة المئوية للمسامية الحقيقية وزيادة صلادة فيكرز ومقاومة الخضوع الإنضغاطي وإنخفاض في معدل البلى مع زيادة محتوى جسيمات التقوية مع تحسن لبعض الخواص ( مثل زيادة الكثافة ونقصان المسامية وانخفاض معدل البلى وزيادة مقاومة الانضغاط ) بعد عملية التلبيد .