Effect of Metakaolin on Properties of Lightweight Porcelinate Aggregate Concrete

Authors: Nada M. Fawzi --- Kalil I. Aziz --- Sheelan M. Hama
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2013 Volume: 19 Issue: 4 Pages: 439-452
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Research in Iraq has expanded in the field of material technology involving the properties of the lightweight concrete using natural aggregate. The use of the porcelinate aggregate in the production of structural light concrete has a wide objective and requires a lot of research to become suitable for practical application. In this work metakaolin was used to improve compressive strength of lightweight porcelinate concrete which usually have a low compressive strength about 17 MPa . The effect of metakaolin on compressive, splitting tensile, flexure strengths and modulus of elasticity of lightweight porcelinate concrete have been investigated. Many experiments were carried out by replacing cement with different percentages of metakaolin. The metakaolin was replaced by 5%, 10%, 15% and 20%. A control reference mix without metakaolin was made for comparison purpose. For all mixes, compressive, splitting tensile, flexure strengths and modulus of elasticity were determined at 28-day. The results showed that the using of metakaolin improve the compressive, splitting tensile, flexure strengths and modulus of elasticity of lightweight porcelinate concrete. The higher compressive, splitting tensile, flexure strengths and modulus of elasticity were found for 15% metakaolin.

توسعت البحوث في العراق في حقل تكلنوجيا المواد من ضمنها دراسة خواص الخرسانة خفيفة الوزن باستخدام ركام طبيعي. استخدام البورسلينايت كركام خفيف الوزن في انتاج خرسانة انشائية يتطلب العديد من الدراسات لفهم وتحسين خواصها لتصبح مناسبة للتطبيقات العملية. في هذه الدراسة استخدمت مادة ميتاكاؤلين كنسبة مئوية مِنْ وزنِ سمنت، لتحسين خواص خرسانة البورسلينايت الخفيفة الوزن التي تمتاز عادة بمقاومة انضغاط واطئة حوالي 17 ميكاباسكال. تم دراسة تاثير اضافة ميتاكاؤلين على كل من مقاومة الانضغاط, مقاومة الانفلاق, معامل التصدع, و معامل المرونة للخرسانة البورسلينايت الخفيفة الوزن. وقد استبدل جزء من السمنت بالنسب التالية من ميتاكاؤلين: 5%, 10%, 15%, و 20% من وزن السمنت, بالاضافة الى الخلطة المرجعية بدون اضافات لغرض المقارنة. لكل الخلطات تم قياس كل من مقاومة الانضغاط, مقاومة الانفلاق, معامل التصدع, و معامل المرونة بعمر 28 يوم. وقد وجد بان اسبتدال نسبة 15% من سمنت بميتاكاؤلين تحسن مقاومة الانضغاط, مقاومة الانفلاق, معامل التصدع, و معامل المرونة.


Article
Some Properties of Concrete Containing High Fraction Volume of Metakaolin
بعض خواص الخرسانة المحتویة على نسبة عالیة من المیتاكاؤولین

Authors: Kais J. Frieh --- Waleed A.Abbas --- Marawan Mohammed Hamid
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 1 Part (A) Engineering Pages: 230-248
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research, a study has been made on the effect of high fractional volume of replacement Metakaolin that results from grinding and burning the local kaolin from (Doeakhla zone / west of Baghdad / Iraq) with fineness of 18000 cm2/gm., and with temperature 700°C for one hour, on some properties of concrete (compressive strength, splitting tensile strength, flexural strength, modulus of elasticity, density,absorption and drying shrinkage). Also, non-destructive tests have been made (Schmidt rebound hummer and Ultrasonic pulse velocity). In this study, ten concrete mixes have been used in two Groups to get a compressive strength 40 N/mm2 at 28 days. In Group A, the percentage replace of Metakaolin have been changed from (0-70) % by weight of cement with percent increment equal to 10% for each mix, andchange the maximum size of aggregates to determine the effect of changing the surface area of aggregate as variable on the properties of concrete-containing Metakaolin, The tests for all mixes were made at ages ranged from 1 day to 90 days after mixing and replacement a dosage of superplasticizer by water content of the mix to make a constant workability with slump 50±5mm. The aim of this research is tofind a type of concrete that can be used in dams as one of the types of mass concrete, concluded from this research that replacing 70% Metakaolin instead of cement mixing the compressive strength aged 90 days less than the 63%, splitting strength at 28 days less than 27%, flexural strength at 28 days less than about 27%, the modulusof elasticity at 28 days less than 54%, density of less than about 8% at 28 days, the absorption rate increases about 27% and drying shrinkage 1.65 * 10-4 at 60 days when compared all these tests with the reference concrete.


Article
Studying the Compatibility between Metakaolin Repair Materials And Concrete Substrate
دراسة التوافق بین مواد الاصلاح الحاویة على المیتاكاؤلین والجسم الخرساني

Authors: Maan S. Hassan --- Zainab T. Hadad --- Shaymaa T.Kadhim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 19 Pages: 5857-5868
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study, the compatibility of Metakaolin repair mortar and substrate concrete was investigated in three stages. First: individual properties of Metakaolin as a pozzolanic material and conventional repair materials(cement mortar), and two types of concrete, such as compressive strength, split tensile strength, and flexural strength, were determined using standard ASTM test procedure. Second: the bondstrength of composite cylinder for different combinations of repair materials and substrate concrete were evaluated. Third: the compatibility was investigated using a composite beam of repair material and substrate concrete under third point loading.The experimental results indicated that repairing weak substrate concrete by Metakaolin modified repair material is not preferable du to disparity in mechanical properties and create high level of mismatch between them. Furthermore, bond strength is considered as great influence factor on the success range of repair system.

في هذه الدراسة تم التحري عن التوافق بين مواد الاصلاح الحاوية على الميتاكاؤلين والجسم الخرساني وعلى ثلاث مراحل. الاولى: التحري عن الخواص الذاتية لكل من مواد الاصلاح الحاوية على الميتاكاؤلين والتقليدية ( مونة السمنت ) ولنوعين مختلفين من الجسم الخرساني، مثل مقاومة الانضغاط والثانية: تقييم مقاومة .(ASTM) مقاومة انفلاق الشد ومقاومة الانثناء. واعتمادا على المواصفة الامريكية الربط للاسطوانة المركبة والمصنوعة من انواع مختلفة من مواد الاصلاح والخرسانة. ثالثا: التحري عن التوافق باستخدام عتبة مركبة مصنوعة من الخرسانة ومواد الاصلاح وفحصها بطريقة التحميل بنقطتين.بينت نتائج الجزء العملي انه من غير المفضل اصلاح الجسم الخرساني الضعيف بمواد اصلاح مطوره بمادة الميتاكاؤلين وذلك بسبب تباعد الصفات الميكانيكيه بينهما ويقود ذلك الى عدم التطابق. كما تعد مقاومة الربط عاملا مؤثرا قويا عن مدى نجاح نظام الاصلاح


Article
FFECT OF POZOOLANIC MATERIALS ON COMPRESSIVE STRENGTH OF GEOPOLYMER CONCRETE

Authors: Mohammed H. Shamsa --- Basil S. Al-Shathr --- Tareq S. Al-Attar
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2018 Volume: 9 Issue: 3 Pages: 26-36
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

The development that has occurred in industries and technologies after the Industrial Renaissance and beyond has led to consume a large amount of raw materials. The huge consumption of these materials is hard to be compensated. Therefore, it is necessary to find materials that can be recycled and environmentally friendly materials. Hence, the idea of sustainability, which states, the ability to meet our current needs without compromising the ability of future generation to meet theirs. It has become an urgent to produce materials that called environmentally friendly or sustainable materials. In the field of civil engineering, an important role has been played in producing of environmentally friendly concrete by using pozollanic materials. Using environmentally friendly concrete instead of traditional concrete can participate in reducing the effect of global warming. In this research, local materials like metakaolin and pozollanic materials such as, fly ash and grand granulated blast furnace slag GGBFS were used in the production of an environmentally friendly concrete which they are called Geopolymer concrete. The effect of pozzolanic material type and mixing ratios on compressive strength at 7, 28 and 60 days were studied.

Keywords

Sustainable --- Geopolymer --- Fly ash --- Metakaolin --- GGBFS.


Article
Modeling Time to Corrosion Initiation in High-Performance Ferrocement Exposed to Chlorides Environments
نمذجة الزمن اللازم لبدأ التآكل في الفيروسمنت عالي الاداء المعرض لبيئة الكلور

Authors: J. Forth --- Maan S. Hassan --- S. A. Salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 1 Pages: 18-31
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The applications of a mineral admixture, or a zinc coating to steel surface, or acombination of both are methods used for the corrosion prevention of ferrocementelement in this study. Results of a study to evaluate many corrosion protection systemswith metakaolin and/or galvanized steel mesh are presented in six U-shaped specimens.Specimens were built to simulate exposure conditions typical for marine environment.Laboratory data collected along duration of 40 weeks of exposure were used inmodeling the cover depth as a function of time to corrosion initiation of the investigatedcorrosion prevention methods. Methods used to assess the condition of specimensincluded chloride concentration measurements, and corrosion rates. Model predictionsshow that the ferrocement specimen of high-performance mortar with metakaolinprovides much better level of protection against moisture and chlorides than theconventional specimen, by delay rate of chloride ingress. Application of a galvanizedsteel mesh causes an elevation of the chloride threshold resulting in an additionalincrease in the predicted time to corrosion initiation.

تم تطبيق نظم مختلفة للحماية ضد تاكل مشبك حديد التسليح المستخدم في السمنت الحديدي(الفيروسمنت). منها المعتمد على المضافات المعدنية , ومنها المعتمد على تغطية سطح المشبك الحد يديبمعدن الزنك (الحديد المكلفن ), ومنها المعتمد على كلا الاثنين . تم تقييم نظم الحماية هذه من خلالتصميم عدد من النماذج المختبرية حيث تم تصميمها لتحاكي الظروف التعرضية المحتملة الحدوث فيالبيئه البحرية.استخدمت البيانات المختبرية التي تم جمعها من النماذج ع لى مدى اربعين اسبوع من التعرضالى السائل الملحي , في بناء نموذج (موديل) يحكم الزمن اللازم لبدأ التاكل لنظم الحماية المختلفة التيتم التحري عنه ا. تشمل الطرق التي تم استخدامها في تقييم نماذج الفحص : قياسات تراكيز ايون الكلوروقياسات معدل تيار التاكل (تقنية مق اومة الاستقطاب الخطي . ويتضح من النموذج المذكور ان نماذجالفيروسمنت عالية الاداء التي تم استعمال المضاف المعدني (الميتاكاؤلين ) معها يوفر مستوى افضلمن الحماية ضد التاكل من النماذج المرجعية التقليدية وذلك من خلال ابطاء اختراق المحاليل الملحيةعبر المونة الى المشبك المعدني . كما ان تغطية المشبك الحديدي بمعدن الزنك يؤدي الى رفع قيمة عتبةالكلور المطلوبة لكسر طبقة اوكسيد الحديد الواقية وبالتالي يؤدي الى اطالة الزمن اللازم لبدأ التاكل.


Article
Fusion Face and Palmprint for Human Recognition via Spectral Eigenvector
دمج الوجه مع راحة اليد لتميز الاشخاص بأستعمال المتجهات الطيفية

Author: Hana'a M. Salman
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 4 Pages: 787-798
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The Biometrics recognition systems act as an efficient method with broadapplications in the area of: security access control, personal identification to humancomputercommunication. From other hand, some biometrics have only little variationover the population, have large intra-variability over time, or/and are not present in allthe population. To fill these gaps, a use of multimodal biometrics is a first choicesolution [1].This paper describes a multibiometrics method for human recognition based onnew teacher vector identified as spectrum eigenface, and spectrum eigenpalm. Theproposed combination scheme exploits parallel mode capabilities of the fusion featurevectors in matching level and invokes certain normalization techniques that increase itsrobustness to variations in geometry and illumination for face and palmprint. Thecorrelation distance is used as a similarity measure. A threshold value is used toprevent the imposter for being recognized. Experimental results demonstrate theeffectiveness of the new method compared to the unimodal biometrics for spectrumeigenface/eigenpalm.

أنظمة تميز المقاييس البايولوجية تعمل كوسائل فعالة مع العديد من التطبيقات في مجالات :سرية سيطرة الوصول، تميز الأشخاص عند الاتصال بين الحاسوب مع الإنسان . من ناحية أخرى بعض المقاييس البايو لوجية قد لا تكون متنوعة جدا إذا ما أخذت لحشد من الناس، أو ممكن تتغير مع مرور الزمن، و /أو غير متوفرة للعديد من الأشخاص . وللتغلب على هذه المشاكل تم استعمال المقاييس البايولوجية المتعددة. في هذا البحث نستعرض طريقة المقاييس البايولوجية المتعدد لتمييز الأشخ اص و المبنية على استخدام متجهات جديدة تدعى محدد الوجه الطيفية ومحدد راحة اليد الطيفية . المخطط المدموج يستثمر قابليات النموذج المتوازي للدمج في مستوى التطابق ويدخل طريقة تسوية والتي تزيد من فعاليتها اتجاه التغير بالإضاءة وهندسة الوجه مع راحة اليد . مسافة الا رتباط استخدمت كمقياس للتشابه. تم استعمال حد لمنع المتطفل من أن يميز داخل النظام . نتائج الاختبارات عبرت عن مدى فعالية الطريقة الجديدة المطبقة اتجاه استعمال النموذج البايولوجي الواحد للمحدد الوجه الطيفي أو محدد راحة اليد الطيفي.


Article
Effect of Using Metakaolin on Chloride Ion Penetration in High Performance Steel Fiber Reinforced Concrete

Author: Adnan Mohammed Shihab
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 1 Pages: 191-202
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This paper attempts to reduce the penetrability of high performance steel fiber reinforced concrete to chloride ions originating from external sources, by using High Reactivity Metakaolin (HRM) as a highly active pozzolanic material, in order to prolong the time to initiation of the steel fibers corrosion and to minimize concrete damage that may occur due to the exposure to chloride ion penetration.According to pozzolanic activity index (P.A.I.), 8% content of HRM was used as a partial replacement by weight of cement with 2% steel fibers by volume of concrete. During the exposure period of 300 days in 4.5% of NaCl solution, the total and free chloride contents (Cltotal, Clfree) with the chloride profiles at the ages of 28 and 300 days were investigated. Also the rapid chloride penetrability test (RCPT), compressive and flexural strengths tests were conducted at the ages of 28, 90, 180 and 300 days.Results showed that the incorporation of 8% HRM caused a reduction in the (Clfree/Cltota) ratio, the chloride penetration depth and the electrical conductivity with percentages of 21%, 40% and 43% respectively after 300 days exposure to chloride solution in comparing with the mix of 0% HRM. Results also indicated that the losses in compressive and flexural strengths after exposure of 300 days to chloride solution for the mix incorporating 8% HRM were by 5% and 5.8% respectively while they reached 9.5% and 11% respectively for the mix without HRM in relation to the correspondent test specimens cured in tap water.

تهدف هذه الدراسة الى محاولة تقليل نفاذية الخرسانة العالية الاداء المسلحة بالألياف الفولاذية للكلوريدات باستخدام الميتاكاؤلين العالي الفعالية باعتباره مادة بوزولانية عالية النشاط وذلك من اجل الحد من الصدأ الحاصل في الالياف الفولاذية والضرر الذي قد يحدث في الخرسانة عند تعرضها لنفوذ المحاليل الحاوية على املاح الكلوريدات . تم استخدام محتوى مقداره 8% من الميتاكاؤلين العالي الفعالية كأستبدال جزئي من وزن السمنت وذلك أستنادا" الى مؤشر الفعالية البوزولانية (P.A.I.)، مع%2 من الالياف الفولاذية نسبة الى الحجم الكلي للخرسانة. تم غمر النماذج الخرسانية في محلول كلوريد الصوديوم وبتركيز 4.5% ولفترة تعرض بلغت 300 يوماً تم خلالها ايجاد محتوى الكلوريدات الحرة والكلية ومنحنى توزيع تراكيزها نسبة الى العمق عن سطح النموذج الخرساني عند الاعمار 28و300 يوماً، كما تم قياس مقاومة الخرسانة لنفوذ أيونات الكلوريدات (RCPT) وكذلك مقاومتيَ الانضغاط والانثناء عند الاعمار 28، 90، 180 و300 يوماً. أظهرت النتائج ان استخدام 8% من الميتاكاؤلين العالي الفعالية أدى الى تقليل نسبة محتوى الكلوريدات الحرة الى محتوى الكلوريدات الكلية(Clfree /Cltota) ، عمق نفوذ تلك الكلوريدات عن سطح النموذج الخرساني وكذلك قابلية الخرسانة لتمريرالشحنة الكهربائية بحدود وصلت الى 21%،40 % و43 % على التوالي بعد فترة تعرض بلغت 300 يوماً لمحلول الكلوريدات بالمقارنة مع الخرسانة الغير الحاوية على الميتاكاؤلين.كما أشارت النتائج أيضاً الى ان مقدار النقصان الحاصل في مقاومتيَ الانضغاط والانثناء للنماذج المعرضة الى محلول الكلوريدات كان بحدود 5% و 5.8% على التوالي للخلطة الحاوية على 8% من الميتاكاؤلين العالي الفعالية بينما كان النقصان للخلطة التي لا تحتوي عليه بحدود وصلت الى 9.5% و11% على التوالي بالمقارنة مع نماذج الفحص المطابقة والمعالجة بالماء.


Article
Effect of Using Metakaolin on Chloride Ion Penetration in High Performance Steel Fiber Reinforced Concrete

Author: Adnan Mohammed Shihab
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 1 Pages: 191-202
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This paper attempts to reduce the penetrability of high performance steel fiber reinforced concrete to chloride ions originating from external sources, by using High Reactivity Metakaolin (HRM) as a highly active pozzolanic material, in order to prolong the time to initiation of the steel fibers corrosion and to minimize concrete damage that may occur due to the exposure to chloride ion penetration.According to pozzolanic activity index (P.A.I.), 8% content of HRM was used as a partial replacement by weight of cement with 2% steel fibers by volume of concrete. During the exposure period of 300 days in 4.5% of NaCl solution, the total and free chloride contents (Cltotal, Clfree) with the chloride profiles at the ages of 28 and 300 days were investigated. Also the rapid chloride penetrability test (RCPT), compressive and flexural strengths tests were conducted at the ages of 28, 90, 180 and 300 days.Results showed that the incorporation of 8% HRM caused a reduction in the (Clfree/Cltota) ratio, the chloride penetration depth and the electrical conductivity with percentages of 21%, 40% and 43% respectively after 300 days exposure to chloride solution in comparing with the mix of 0% HRM. Results also indicated that the losses in compressive and flexural strengths after exposure of 300 days to chloride solution for the mix incorporating 8% HRM were by 5% and 5.8% respectively while they reached 9.5% and 11% respectively for the mix without HRM in relation to the correspondent test specimens cured in tap water

تهدف هذه الدراسة الى محاولة تقليل نفاذية الخرسانة العالية الاداء المسلحة بالألياف الفولاذية للكلوريدات باستخدام الميتاكاؤلين العالي الفعالية باعتباره مادة بوزولانية عالية النشاط وذلك من اجل الحد من الصدأ الحاصل في الالياف الفولاذية والضرر الذي قد يحدث في الخرسانة عند تعرضها لنفوذ المحاليل الحاوية على املاح الكلوريدات . تم استخدام محتوى مقداره 8% من الميتاكاؤلين العالي الفعالية كأستبدال جزئي من وزن السمنت وذلك أستنادا" الى مؤشر الفعالية البوزولانية (P.A.I.)، مع%2 من الالياف الفولاذية نسبة الى الحجم الكلي للخرسانة. تم غمر النماذج الخرسانية في محلول كلوريد الصوديوم وبتركيز 4.5% ولفترة تعرض بلغت 300 يوماً تم خلالها ايجاد محتوى الكلوريدات الحرة والكلية ومنحنى توزيع تراكيزها نسبة الى العمق عن سطح النموذج الخرساني عند الاعمار 28و300 يوماً، كما تم قياس مقاومة الخرسانة لنفوذ أيونات الكلوريدات (RCPT) وكذلك مقاومتيَ الانضغاط والانثناء عند الاعمار 28، 90، 180 و300 يوماً. أظهرت النتائج ان استخدام 8% من الميتاكاؤلين العالي الفعالية أدى الى تقليل نسبة محتوى الكلوريدات الحرة الى محتوى الكلوريدات الكلية(Clfree /Cltota) ، عمق نفوذ تلك الكلوريدات عن سطح النموذج الخرساني وكذلك قابلية الخرسانة لتمريرالشحنة الكهربائية بحدود وصلت الى 21%،40 % و43 % على التوالي بعد فترة تعرض بلغت 300 يوماً لمحلول الكلوريدات بالمقارنة مع الخرسانة الغير الحاوية على الميتاكاؤلين.كما أشارت النتائج أيضاً الى ان مقدار النقصان الحاصل في مقاومتيَ الانضغاط والانثناء للنماذج المعرضة الى محلول الكلوريدات كان بحدود 5% و 5.8% على التوالي للخلطة الحاوية على 8% من الميتاكاؤلين العالي الفعالية بينما كان النقصان للخلطة التي لا تحتوي عليه بحدود وصلت الى 9.5% و11% على التوالي بالمقارنة مع نماذج الفحص المطابقة والمعالجة بالماء.


Article
Studying The Effect of Nano-Metakaolin Admixture Material On Mechanical Properties of Oil Well Cement (OWC)

Author: A.D. Salman
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 9 Part (A) Engineering Pages: 909-913
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work aimed to study the effects of incorporate Nano-metakaolin (NMK) as pozzolonic material on some mechanical properties (compressive strength) of Oil Well Cement (OWC). Nano-metakaolin (NMK) was prepared from Kaolin rock brought by thermal activation of kaolin clay at different temperatures (700–800 oC) for 2 h then crushing and ball milled for (40-60) hours. The cement used in this study comprise of Oil Well Cement class G and NMK were incorporate as a partial replacement additive by NMK of (3%, 6% & 10%) by weight of cement with two different average particle sizes (75nm,100nm) and a w/c of 0.44. Several techniques were used to prepare and characterize NMK Particle Size Analyzers (PSA), X-ray diffraction (XRD), X-ray fluorescence (XRF), scanning electron microscopy (SEM) and the Brunauer-Emmett-Teller (BET). The results showed and approved that the NMK was not only work as filler, but also as an activator to consolidate hydration process, through NMK particles react and consumes calcium hydroxide CH crystals to produce more C–S–H, fills pores to increase the strengths, decrease the size of the crystals at the interface zone and transmutes the calcium hydroxide feeble crystals to the C–S–H crystals, and upgrade the interface zone and cement paste domain.


Article
Performance of Geopolymer Concrete Exposed to Freezing and Thawing Cycles

Authors: Mohammed H. Shamsa --- Basil S. Al-Shathr --- Tareq S. al-Attar
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2019 Volume: 37 Issue: 3 Part (A) Engineering Pages: 78-84
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study, the effect of rapid freezing and thawing (ASTM C666– procedure A) on three different types of Geopolymer concrete studiedusing three types of pozzolanic material: fly ash, metakaolin and groundgranulated blast furnace slag (GGBFS). The Geopolymer concrete wasprepared using 400 kg of the pozzolanic material with alkaline liquidprepared at 8 molar concentration with normal fine and coarse aggregates.The ratio of alkaline to fly ash and GGBFS was 1.5: 1 and for metakaolinwas 2: 1 for workability and compressive strength requirements. Specimens(100 × 100 × 400) mm were exposed to 100, 200 and 300 cycles of freezingand thawing. The decrease in measured compressive strength was (23, 43,and 26%) for Fly ash, metakaolin and GGBFS respectively. The investigatedtypes of concrete showed good resistance to freezing and thawing. Thedurability factor of these types was (77%, 68%, and 81%) for fly ash,metakaolin, and GGBFS respectively.Keywords- Freezing and thawing,

Listing 1 - 10 of 22 << page
of 3
>>
Sort by
Narrow your search

Resource type

article (22)


Language

English (22)


Year
From To Submit

2019 (1)

2018 (1)

2017 (3)

2016 (7)

2015 (1)

More...