Study the Microbiologically Influenced Corrosion of Carbon Steel

Author: Zuheir T.Khulief.Al-Tai
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 15 Pages: 3141-3157
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The main objective of this study was to evaluate the microbiologicallyinfluenced corrosion of carbon steel in water, samples of water taken from Al-Hilla rivers and distill water (control medium ). Corrosion analyses by using (Liner polarization tafel test; weight loss method ; microstructure examination , surface roughness test and X-Ray diffraction analysis) and microbiological analyses by using(Isolation and identification by using appearance factors microscopic ,culturing factors and biochemical tests for biofilm of corrosion product) are used in this study. The result of corrosion analyses shows the corrosion rates of carbon steel in rivers water are more than that in control water, the microstructure examination and surface roughness tests show increase in roughness of met.al. surfaces which areunder the corrosion medium (rivers water) compared with control medium. The result of microbiological analyses shows the slides that made from the biofilm (product of corrosion) under microscopic appear small bacilli negative gram strain (G-ve) bacteria, where as culturing test shows small colonies with 2.5ìm in diameter of bacteria have mucin appearance and green pigments as well as the result frombiochemical tests; these facts indicate that Pseudomonas aeruginosa bacteria are correlated with the type of corrosion occurring in the carbon steel in the rivers water.


Article
Microbiologically Influenced corrosion of Aluminum Alloy by Pseudomnas Aeruginosa Bacteria
التآكل المتأثر بالفعل الحيوي لسبيكة الألمنيوم باستخدام بكتريا

Author: Zuheir Talib Khulief Al-Tai. زهير طالب خليف الطائي
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2012 Volume: 3 Issue: 2 Pages: 69-85
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

The aim of this paper was to study microbiologically influenced corrosion of aluminum alloy in the presence Pseudomnas aeruginosa bacteria. Control medium tap water (absence of Pseudomnas aeruginosa bacteria ) and medium with presence Pseudomnas aeruginosa bacteria used in this study. Tafel extrapolation ,weight loss method ,microstructure examination and surface roughness test were carried out to determine the microbiologically influenced corrosion behavior of aluminum alloy. Microbiological analyses, isolation and identification by using appearance factors and biochemical test for biofilm of corrosion product used in this study. Tafel extrapolation and weight loss method of aluminum alloy showed that the presence Pseudomnas aeruginosa bacteria caused corrosion and increasing corrosion current and rate of corrosion. Microstructure examination and surface roughness test showed that the presence Pseudomnas aeruginosa bacteria caused pitting corrosion. Microbiological analyses showed that biofilm are formed as micro colonies, which subsequently caused corrosion and shows the role of Pseudomnas aeruginosa bacteria in acceleration corrosion on aluminum alloy.

الهدف من هذا البحث هو دراسة التاكل المتاثر بالفعل الحيوي لسبيكة الالمنيوم بوجود بكتريا Pseudomnas aeruginosa . وسط للتحكم ماء حنفية ( عدم وجود بكتريا Pseudomnas aeruginosa ) ووسط مع وجود بكتريا Pseudomnas aeruginosa تم استخدامها في هذه الدراسة . اختبار تافل , طريقة فقدان الوزن , فحص طوبغرافية السطح و اختبار خشونة السطح نفذت لتقرير سلوك التاكل المتاثر بالفعل الحيوي لسبيكة الالمنيوم , تحليل مايكرو بايولوجي باستخدام العزل والتشخيص باستخدام العوامل المظهرية وكذلك الفحوصات البايو كيمائية للغشاء الحيوي ناتج التكل تم استخدامها في هذه الدراسة. اختبار تافل وطريقة فقدان الوزن بينت ان وجود بكتريا Pseudomnas aeruginosa سببت التاكل مع زيادة تيار التاكل ومعدل التاكل. فحص طوبغرافية السطح و اختبار خشونة بينت ان وجود بكتريا Pseudomnas aeruginosa سبب حصول التاكل النقري. تحليل مايكرو بايولوجي بينت تكوين غشاء حيوي كمستعمرات دقيقة والتي بعد ذلك تسبب التاكل, وبينت دور بكتريا Pseudomnas aeruginosa في تعجيل التآكل على سبيكة الألمنيوم.