Annealing temperature effect on the Structure, Morphology and Optical properties of Copper Oxide CuO thin Films
تأثير درجة حرارة التلدين على الخصائص التركيبية والطبوغرافيه والبصرية للاغشية الرقيقة لأوكسيد النحاس (CuO)

Author: Najat A.Dahham نجاة احمد دحام
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2017 Volume: 22 Issue: 6 Pages: 115-124
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

Copper oxide (CuO) thin films were deposited on glass substrates by (sol-gel ) method using a spin -Coating technique and the speed of the spin coater was fixed at 3000 rpm for 30 sec and the samples were are annealed at temperatures (250,350,450 and 550) ° C for 1 hrs. The structural, Morphology, and optical properties of the film are determined by using X-ray diffraction (XRD), Atomic force microscopy (AFM) and UV-visible spectroscopy respectively. The XRD patterns showed that copper oxide (CuO) thin films prepared has polycrystalline structure and when increase the annealing temperature of the thin film over than 300° C the thin film turns from phase Cu2O to CuO phase and through examination (AFM) showed that the average grain size increases with the annealing temperature either Optical examinations showed decrease in transmission and increase in absorption coefficient with increase annealing temperature. The prepared thin films have direct energy gap and the value of the optical energy gap decreased with increasing annealing temperature from 3.99 eV to 3.94 eV

في هذه الدراسة تم ترسيب الاغشية الرقيقة لأوكسيد النحاس(CuO) على قواعد زجاجية بطريقة (sol-gel) باستخدام تقنية الطلاء الدوراني (spin –Coating) وبسرعة دوران ثابتة (3000) rpm وبزمن ترسيب (30 sec) ولدنت العينات تحت درجات حرارة (250,350,450,550) ° C ولمدة ساعة واحدة. حيث تم تحديد الخصائص التركيبية والطبوغرافية والبصرية بواسطة حيود الاشعة السينية (XRD) ومجهر القوة الذرية AFM)) ومطياف الاشعة الفوق البنفسجية والمرئية على التوالي . أظهرت أنماط حيود الأشعة السينية ان الاغشية الرقيقة المحضرة لاوكسيد النحاس (CuO) ذات تركيب متعدد التبلور وعند زيادة درجة حرارة الغشاء إلى درجة حرارة اكثر من ° C 300 يتحول الغشاء من الطور Cu2O إلى الطورCuO ، وتبين من خلال فحص(AFM) أن معدل الحجم الحبيبي يزداد مع زيادة درجة حرارة التلدين إما الفحوصات البصرية فقد أظهرت انخفاضا في النفاذية وزيادة في معامل الامتصاص مع زيادة درجة حرارة التلدين, وان الاغشية المحضرة تمتلك فجوة طاقة مباشرة وان قيمة فجوة الطاقة تتناقص مع زيادة درجة حرارة التلدين من 3.99 eV الى 3.94 eV.


Article
Optical Properties,Structure,and Morphology of CuO Grown by Thermal Oxidation of Cu thin film on Glass Substrate
الخواص البصريت والطبوغرافيت لأوكسيذ النحاس المحضر بطريقت الأكسذة الحراريت على الزجاج

Author: Amar hadee Jareeze عمار هادي جابر
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2014 Volume: 6 Issue: 1 English and Arabic Pages: 36-41
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Oxidation method was used to prepare nanostructure of cupric oxide (CuO) film. Thin film of Copper metal were deposited on substrate (quartz) in a thermal vacuum evaporator. The thickness of the film was measured to about 20 μm. The thermal oxidation of this evaporated film was done in a horizontally heated quartz furnace at temperature (400°C) in air for 4 hour. The product was tested by X-ray diffraction pattern (XRD), Fourier transfer infrared (FTIR) spectrometer, The surface properties was characterized using scanning electron microscopy(SEM),UV–vis spectrometer ,the average crystal diameter derived from the XRD data analysis is found to be 27nm and completely converts this Cu film to tenorite structure with composition of CuO with peak appeared at 2θ equal to 35.5˚, 38.7˚.The conversion was also confirmed by the FTIR spectrometer measurement. The UV–vis spectrum of the material shows significant amount of blue-shift in the band gap energy(Eg) and is found to be 3.82eV due to the quantum confinement effect exerted by the nanocrystals.

حم ححض رٍ غشاء مه اوكس ذٍ انىحاش را حراك بٍ واوى تٌ بطر قٌت الاكسذة , حم حرس بٍ معذن انىحاش عهى قاعذة مه زجاجانكىارحس بطر قٌت انخبخ رٍ انحراري بانفراغ .سمك انغشاء كان حىان 02 م كٍرومخر . حم الاكسذة انحرار تٌ نهغشاء بىاسطتحسخ هٍ زجاج كىارحس ف فرن افق اٍ بذرجت حرارة 022 س هٍ سٍ تٌ ف انهىاء نمذة اربعت ساعاث . حم دراست انخىاص انخرك بٍتبىاسطت ح ىٍد الاشعت انس ىٍ تٍ , ومط اٍف تٍ الاشعت ححج انحمراء , وانخىاص انسطح تٍ بىاسطت انمجهر الانكخروو انماسح ,وانخىاص انبصر تٌ بىاسطت مط اٍف تٍ الاشعت انمرئ تٍ وفىق انبىفسج تٍ , معذل ق اٍش حجم انبهىرة 02 واوىمخر مع ححىل كاممنغشاء انىحاش انى لاوكس ذٍ انىحاش بقمت ظهرث بسوا اٌ 35.5˚, 38.7