HOT CORROSION OF CERIA-YTTRIA STABILIZED ZIRCONIA PLASMA SPRAYED THERMAL BARRIER COATING BY EUTECTIC VANDIUMPENTAOXIDE-SODIUM SULFATE
التاكل الساخن لطبقات الرش بالبلازما للحواجز الحرارية للسيريا-ياتريا المثبتة للزركونيا بالاويتكتيك لخماسي اوكسيد-الفناديوم- كبريتات الصوديوم

Loading...
Loading...
Abstract

The high temperature corrosion behavior of thermal barrier coating (TBC) system consisting of IN-738 LC superalloy substrate, air plasma sprayed Ni24.5Cr6Al0.4Y (wt%) bond coat and air plasma sprayed ZrO2-20 wt% ceria-3.6 wt% yttria (CYSZ) ceramic coat were characterized. The upper surfaces of CYSZ covered with 30 mg/cm2 , mixed 45 wt% Na2SO4-55 wt% V2O5 salt were exposed at different temperatures from 800 to 1000 oC and interaction times from 1 up to 8 h. The upper surface plan view of the coatings were identified for topography, roughness, chemical composition, phases and reaction products using scanning electron microscopy, energy dispersive spectroscopy, talysurf, and X-ray diffraction. XRD analyses of the plasma sprayed coatings after hot corrosion confirmed the phase transformation of nontransformable tetragonal (t') into monoclinic phase, presence of YVO4 and CeVO4 products. Analysis of the hot corrosion CYSZ coating confirmed the formation of high volume fraction of YVO4, with low volume fractions of CeOV4 and CeO2. The formation of these compounds were combined with formation of monoclinic phase (m) from transformation of nontransformable tetragonal phase (t').

تم تقييم التاكل الكيميائي بدرجة الحرارة العالية لطلاءات الحواجز الحراية المنتجة بالرش بالبلازما للزركونيا الحاوية على 20 wt% سيريا و 3.6 wt% ياتريا والمطلية على طبقة طلاء وسطية من Ni24.5Cr6Al0.4Y (wt%). ان طبقات الطلاء السيراميكية والوسطية المنتجة بالرش بالبلازما تم طلائها على سبيكة فائقة من .IN-738 LC طبقات الرش بالبلاما السيراميكية التي تم تغطيتها بمزيج ملحي من 45 wt% Na2SO4-55 wt% V2O5 وبمعدل تغطية 30 mg/cm2 تم اختبارها بدرجة حرارة من 800 الى oC 1000 ولفترات زمنية 1 و 8 ساعات. طوبوغرافية الاسطح والخشونة والتركيب الكيمائي والاطوار ونواتج التاكل للاسطح العلوية لطبقات الرش تم تحديدها باستخدام المجهر الالكتروني الماسح ومطياف مفرق الطاقة و جهاز قياس الخشونة وحيود الاشعة السينية. اثبتت نتائج حيود الاشعة السينية لطبقات الرش بعد التاكل الكيميائي تحول الطور السداسي الغير متحول t') ) الى الطور احادي الميل m)) و الاطوار YVO4 و CeVO4. اوضح تحليل طبقات الرش بالبلازما بعد التاكل بان الطور السائد بكسر حجمي كبير هو YVO4 وكمية قليلة من الاطوار CeOV4 و .CeO2 أن تكزن هذه الاطوارمصاحب لتكوين الطور الاحادي الميل m)) الناتج من تحول الطور السداسي الغير متحول (t') .


Article
Ionic Strength Estimation and Development Of Equation For Estimation Of Ion Atmosphere Thickness In Aqueous Solutions By Electrical Conductivity For Some Electrolytes
تقدير القوة الأيونية وتطوير معادلة تقدير سمك الجو الايوني في المحاليل المائية بطريقة التوصيل الكهربائي لبعض الالكتروليتات

Author: Amir –F-Dawood عامر فاضل داودالنعيمي
Journal: Journal of Research Diyala humanity مجلة ديالى للبحوث الانسانية ISSN: 1998104x Year: 2009 Issue: 39 Pages: 11-25
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The relation between electrical conductivity (cond) and ionic strength (I) in aqueous solutions for some electrolytes (NaCI,NaNO3,Na2CO3,NaSO4,K2SO4,CuSO4,MgSO4.7H2O), has been studied at 25 ◦C, at various concentrations (0.1- 10 molar). The ionic strength was calculated from the measurements of the electrical conductivity. The Factors (F) of these electrolytes have been obtained to certain limits of the concentration from equation (I = F . Cond) .By this method ,we can calculate the ionic strength directly by measuring the conductivity for any unknown sample. This relationship gives more accurate results with a simple and easy method. The ionic strength values obtained from the suggested mathematical relationship was substituted in Debye-Huckle equation to determine activity coefficient(γ±). The results were similar if compared with the calculated values from the general law I=½∑Zi2Ci. The electrical conductivity is increased with increasing of Ionic strength as in the following order :Na2SO4 > K2SO4 > MgSO 4 > CuSO4 And Na2SO4 > Na2CO3 > NaCI > NaNO3

درست العلاقة بين التوصيلية الكهربائية (cond) والشدة الأيونية (I) في المحاليل المائية للالكتروليتاتNaCI,Na2CO3, NaNO3, Na2SO4, K2SO4, CuSO4, MgSO4 . 7H2O بتراكيز تتراوح بين (0.1 - 1) مولاري عند درجة حرارة 25◦C وتم حساب الشدة الأيونية من قياسات التوصيلة الكهربائية.تم إيجاد المعاملات (F) للمعادلة المقترحة (I =F .Cond) في حدود معينة لتراكيز هذه الالكتروليتات .وبهذه الطريقة يمكن تقدير الشدة الأيونية مباشرة عن طريق قياس التوصيلية لأي نموذج مجهول وتمتاز هذه الطريقة بأنها تعطي نتائج دقيقة وبشكل بسيط وجهد أقل . وتم تعويض قيم القوة الأيونية المحسوبة من العلاقة الرياضية المقترحة في قانون ديباي –هيوكل لتعيين معامل الفعالية كانت النتائج متقاربة جدا" مع تلك المحسوبة عند تعويض قيم القوة الأيونية المحسوبة عن طريق القانون العام I=½∑Ci Zi2 حيث كانت الايصالية الكهربائية تزداد بزيادة القوة الايونية بحسب الترتيب الاتي :Na2SO4 > K2SO4 > MgSO 4 > CuSO4 And Na2SO4 > Na2CO3 > NaCI > NaNO3طورت علاقة رياضية لحساب سمك الجو الايوني (d) عن طريق قياس التوصيلية الكهربائية لمحاليل الالكتروليتات والمبينة في أدناه.