Effect of Nanocomposites TiO2 addition on the Dielectric Properties of Epoxy resin
تأثير متراكبات النانو بإضافة TiO2¬ على خواص العزل لراتنج الأيبوكسي

Loading...
Loading...
Abstract

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

في هذا البحث تم تحضير صفائح راتنج الايبوكسي Ep باضافة ثنائي اوكسيد التيتانيوم TiO2 بمقاس حبيبي ((1.5μm, 50nm وبنسب وزنية مئوية مختلفة (1%, 3%, 5%). تم قطع اقراص بقطر 20mm وسمك 3mm من المادة المحضرة ولذلك لغرض القياسات العزلية. الخواص العزلية (ثابت العزل وعامل الفقد والتوصيلية الكهربائية) اجرت القياسات لمدى من الترددات بين 102 -106 Hz.تم كذلك مقارنة تأثير الجسيمات TiO2 من ابعاد النانومتر والمايكرمتر على الخصائص العزلية من متراكبات الايبوكسي وبنسب وزنية مختلفة. وتبين من النتائج ان الجسيمات TiO2 بابعاد المايكرو متر ذات خصائص عزلية افضل

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2009 (1)