Article
Synthesis and characterization of Nanoporous Material via Rice husk
تحضير وتشخيص مادة مسامية نانوية عن طريق قشور الرز

Authors: Hayder Hamied Mihsen --- Thana Jaafar Al-Hasani1 --- Kasim Mohammed hello
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2017 Issue: المؤتمر العلمي الخامس لكلية العلوم Pages: 147-156
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The idea of this research depended on the preparation of nanoporous material via rice husk based on the silica material. The silica material is prepared from the rice husks in appropriate chemical method. Where it is known that the rice husks are produced by the production of rice plants that are too large quantities and cause high pollution in environment. Instead, the husks is embedded or burn in the exposed atmosphere in urban and rural areas could benefit from it by the suitable chemical treatment and burning it in controlled conditions, it produces pure silica labeled as RHA (Rice Husk Ash) can be entered in chemical reactions for the production of Nanoporous Material labeled as RHAC-Pd(DTO)2 .This Nanoporous Material is inorganic-organic hybrid. According to analysis of CHNS and FT-IR spectra can be conclude that the bis- dithiooxamidepalladium(II) chloride [Pd(DTO)2]Cl2 has successful incorporation on RHACCl . X-ray diffraction technique was used to determine the amorphous formula of [Pd(DTO)2]Cl2, while the Transmission electron microscopy (TEM) technique was used to confirm its nanostructure of compounds. The surface area measurements indicated that [Pd(DTO)2]Cl2 had a specific surface area of 70.83 m2g1- and a narrow average pore diameter of 3.25 nm. Thermogravimetric analysis (TGA-DTA) of RHAC-Pd(DTO)2 indication that the physical adsorb water was lost between 30-160 °C which means it is weakly bonded in the silica matrix, while the residual parts of material decomposed up to 300 °C.

تعتمد فكرة البحث على تحضير مادة مسامية نانوية, المادة الاساس في تحضيرها هي السليكا التي يتم استخلاصها من قشور الرز بطريقة كيميائية مناسبة. حيث انه من المعروف ان قشور الرز التي تنتجها معامل انتاج الرز تكون بكميات كبيرة جدا مسببة تلوث عالي للبيئة, فبدلا ان تطمر تلك القشور او تحرق بالأجواء المكشوفة بالمدن والارياف يمكن الاستفادة منها بمعاملة كيميائية مناسبة وحرقها بظروف مسيطر عليها لتنتج سليكا نقية (ناصعة البياض) يرمز لها ب RHA مختصر Rice husk ash يمكن ادخالها في سلسلة تفاعلات كيميائية لتحضير مادة مسامية نانوية يرمز لها RHAC-Pd(DTO)2 وهي هجين من مادة لاعضوية-عضوية. تم الاعتماد على نتائج كل من CHNS ودراسة اطياف الأشعة تحت الحمراء FT-IR باستنتاج الاندماج الناجح للمادة ثنائي- ثنائي ثايو اوكسمايد بلاديوم(II) كلورايد على المادة RHACCl , كما تم التعرف على الطبيعة غير المتبلورة له من خلال تقنية حيود الأشعة السينية X-ray , بينما أثبتت تقنية المجهر الالكتروني النافذ(TEM) أنه يمتلك طبيعة نانوية .في حين ان قياسات المساحة السطحية بينت ان المركب يمتلك مساحة سطحية تقدر ب 70.83 m2g1- وبمعدل قطر مسامي يقدر ب 3.25 nm, كما اوضحت التحاليل الحرارية بتقنية TGA-DTA ان الماء الممتز فيزيائيا يتفكك من المركب بين30-160 م° بينما الاجزاء الاخرى العضوية واللاعضوية تتفكك فوق 300 °C .


Article
Preparation and Characterization of Nanoporous Zeolitic Membranes for Catalytic Applications
تحضیر وفحص خصائص الغشاء الزیولایتي النانوي المسامي لتطبیقات التحفی

Author: Talib M. Naieff Al-Bayati
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 17 Part (A) Engineering Pages: 3343-3357
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The Hydroisomerization and Hydrocracking of n-Heptane was carried out in apacked bed plug-flow zeolitic catalytic membrane reactor at a constant pressureof (100 kpa).Material was encapsulated by trimetallic 1% (Pt-Ni-Co). Thestructural and textural features for encapsulated nanoporous MCM-48 werestudied by X-ray diffraction, scanning electron microscopy (SEM), EDAX,nitrogen adsorption-desorption (BET) and FTIR. The characterizations werecarried out before and after loading.The results show that the catalytic activity evaluation in a membrane reactorrevealed that trimetallic 1 % (Pt-Ni-Co)/MCM-48 catalyst possess a high activityfor conversion of n-heptane around (83%) at 400 ºC with a maximum selectivityaround (65%) at 325 ºC.


Article
Hydroisomerization and Hydrocracking of n-Heptane over Nanoporous Trimetallic (Pt-Ni-Co/SBA-15 Catalyst)
عملية ألأزمرة والتكسيرالحراري للهبتان الاعتيادي فوق العامل المساعد النانوي المسامي ثلاثي المعادن Pt-Ni-Co/SBA-15))

Authors: Talib M.Albayati --- Aidan M. Doyle
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 18 Part (A) Engineering Pages: 36-52
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The heterogeneous hydroisomerization and hydrocracking of n-heptane was carried out within the pores of the mesoporous SBA-15 silicas, within which was encapsulated trimetallic nanoparticles of Pt-Ni-Co. The structural and textural features of the nanoporoussilicas, both with and without encapsulated nanoparticles, were characterised using small angle X-ray diffraction, scanning electron microscopy (SEM), EDAX, nitrogen adsorption-desorptionporosimetry/BET surface area analysis,Fourier-transform infrared (FTIR) spectroscopyand transmission electron microscopy (TEM).Catalytic testing was conducted using a plug-flow reactor in a catalyst testing rig under tightly controlled conditions of temperature, reactant flow rate and pressure.Species were leaving the reactor andanalysed by Gas Chromatography. The results show thatPt-Ni-Co/SBA-15 had a high activity for conversion of n-heptane (around 85%). The catalyst was found to be stable to heating and did not undergo any significant deactivation during reaction at temperatures up to 400 °C.

ان عملية الازمرة والتكسير الحراري للهبتان الاعتيادي في تفاعلات غير متجانسة (متباينة) الاطوار وبوجود العامل المساعد قد حدثت ضمن مسامات المادة النانوية المسامية SBA-15 التي تم حشوتها بجسيمات او جزيئات المعادن النانوية الثلاثية 1% (البلاتين-النيكل-الكوبلت). ان تركيب المادة النانوية المسامية SBA-15 ومميزات السطح الخارجي لها تم دراستها بواسطة الاشعة السينية XRD بالاضافة الى دراسة المسح الالكتروني المجهريSEM وتحليل نسبة العناصرEDAX. وكما تم قياس المساحة السطحية وقطر المسامات بواسطة غاز النيتروجين بعملية الامدصاص وازالة الامدصاصBET . بالاضافة الى قياس المجاميع الفعالةFT-IR وكذلك تم استخدام المجهر الالكتروني الناقل (TEM). ان جميع هذه الخصائص تم دراستها قبل وبعد عملية التحميل بالمعادن.ان عملية اختبار العامل المساعد قد اجريت في المفاعل الانبوبي وفي ظروف مسيطرة عليها مثل الضغط ، درجة الحرارة، ومعدل التدفق. النتائج اظهرت ان فعالية تقييم العامل المساعد في المفاعل الانبوبي توحي بان المعادن الثلاثية المحملة 1% (Pt-Ni-Co)/SBA-15 لها فعالية عالية اثناء تحويل الهبتان الاعتيادي بحدود 85% في المفاعل الانبوبي.اوجدت النتائج استقرارية العامل المساعد للتسخين ولم يخضع لاي عملية تعطيل مؤثرة في درجة حرارة التفاعل لحد 400 درجة مئوية.