The effect of annealing temperatures on the optical parameters of NiO0.99Cu0.01thin films
تأثير درجة حرارة التلدين على المعلمات البصرية لأغشية NiO0.99Cu0.01 الرقيقه

Author: Ramiz A.Mohammed Al-Ansari رامز احمد محمد الانصاري
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2016 Volume: 14 Issue: 29 Pages: 73-81
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

NiO0.99Cu0.01 films have been depositedusing thermal evaporation technique on glass substrates under vacuum 10-5mbar.The thickness of the films was 220nm. The as -deposited films were annealed to different annealing temperatures (373, 423, and 473) K under vacuum 10-3mbar for 1 h.The structural properties of the films were examined using X-ray diffraction (XRD).The results show that no clear diffraction peaks in the range 2θ= (20-50)o for the as deposited films. On the other hand, by annealing the films to 423K in vacuum for 1 h, a weak reflection peak attributable to cubic NiO was detected. On heating the films at 473K for 1 h, this peak was observed to be stronger. The most intense peak is at 2θ = 37.12o with the preferential orientation of the films being (111) plane. The optical properties of the films have been studied. The effect of annealing temperature on the optical parameters of NiO0.99Cu0.01 such as transmittance, reflectance, absorption coefficient, refractive index, extinction coefficient, and real and imaginary parts of dielectric constant has been reported.

تم ترسيب أغشيه رقيقه من أوكسيدالنيكل المشوب بالنحاس NiO0.99:Cu0.01 على قواعد زجاجية باستخدام تقنية التبخير الحراري. تم دراسة الخواص البصرية للاغشية المحضرةكداله لدرجة حرارة التلدين. تم تلدين الاغشية المحضرة لثلاث درجات حرارة تلدين (373, 423, و 473) كلفن.تم فحص خصائص تركيب الاغشية المحضرة باستخدام حيود الاشعة السينية(XRD).لقد اظهر فحص تركيب هذه الاغشية بانه لاتوجد اي قمم ضمن المدى 2θ (20-50)o للغشاء المحضر في درجة حرارة الغرفة, بينما عند تلدين الاغشية لدرجة حرارة 423K ولمدة ساعة واحدة ظهرت قمة ضعيفة, وبزيادة درجة حرارة التلدين الى 473K ظهر بان القمة اصبحت اكثر شدة وان الأتجاهات الشبيكية المفضلة لبلورات الغشاء هي .(111)تم دراسة تأثير التلدين على المعلمات البصرية لأغشية NiO0.99:Cu0.01الرقيقة مثل: النفاذية، الانعكاسية، معامل الامتصاص, معامل الأنكسار، معامل الخمود، ثابت العزل الحقيقي وثابت العزل الخيالي.


Article
تأثير التشويب بالنحاس على الخصائص التركيبية وفجوة الطاقة البصرية لأغشية اوكسيد النيكل النانوية المحضرة بطريقة المحلول الغروي

Authors: فؤاد شاكر هاشم --- نور علي سامي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 6 Pages: 1572-1584
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research deals with the study of the structural and optical energy gap of NiO nano films in thickness 100nm were deposited on a glass substrate using sol-gel spin coating technique . XRD results indicated that the films are polycrystalline and have cubic structure with a preferred orientation along (111) . The average grain sizes of the crystallites estimated form XRD data was found to lie in the range of 19.11-23.05 nm. Data of AFM indicate that the surface of films is smooth . The optical transmittance value of nano NiO film reaches to 94% in the VIS and NIR regions, while it is value of films deposited with 0.1mol%Cu reaches to (92)% which is important for its applications as window layers in solar cells .The values of optical energy gap of NiO and Cu doping by 0.01,0.05, 0.1mol% were equal to 3.73 and (3.61,3.49,3.42eV) respectively.

في هذا البحث دُرست الخصائص التركيبية وفجوة الطاقة البصرية لأغشية NiO النقية والمشوبة بالنحاس بتراكيز مختلفة 0,0.01,0.05,0.1mol%)) نانوية بالسمك 100nmرسبت على قواعد زجاجية بتقنية الطلاء الدوار Spin Coating)) . بينت نتائج فحوصات XRD أن جميع الأغشية متعددة البلورات من النوع ألمكعبي مع قمة حادة سائدة باتجاهية 111)) .وقد تم حساب الحجم الحبيبي من بيانات XRD ووجد انه يَزداد حجم الحبيبات بزيادة نسبة التشويب في المدى 19.11 nm-23.05. بيانات AFM أشارت إلى نعومة سطوح الأغشية النفاذية البصرية لغشاء NiO النانوي ذات مقدار كبير تصل إلى94%) ) ضمن المنطقة المرئية وتستمر إلى المنطقة تحت الحمراء القريبة, تناقصت لتصل إلى 92%)) مع التشويب عند نسبة Cu 0.1mol% وهذا يؤكد أمكانية استخدامها كطبقات نافذة في الخلايا الشمسية . قيم فجوة الطاقة البصرية لغشاء NiO والأغشية المشوبة بالنحاس بالنسب 0.01,0.05,0.1 mol% 0,هيeV (3.73,3.61, 3.49, 3.42) على التوالي .