Synthesis of New Modified PVC and their Photostability Study
تحضير ودراسة الاستقرارية الضوئية لبعض بوليمرات البولي كلوريد الفاينيل المحوره

Author: Olfa A. Naif الفه عبد نايف
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2011 Volume: 16 Issue: 4 Pages: 101-117
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

Reaction of PVC with carbothioimide, thiadiazole and traizole derivative in THF solution give a new polymers which were soluble in THF, DMF, DMSO, Three modified PVC polymer were synthesized through reaction of compounds (1-4) with PVC in THF solvent. The Photo stability of the prepared modified polymer was investigated. The modified polymers differ in their susceptibility to photo oxidation degradation from that unmodified PVC. The photostability effects of these heterocyclic moieties were monitored on the basis of carbonyl, polyene and hydroxyl indexes. The obtained results demonstrate that all modified polymers are more photosstabilized, rather than unmodified PVC. All the structure of these compounds [1-4] and P1,P2,P3 were confirmed by FT-IR, UV/Vis spectroscopy ,mass spectrum for compound [2] and 1H-NMR for compound [4].

الملخصان تفاعل PVC مَع الكاربوثايوايمايد ، الثاياديازول ومشتق ترايازول في محلول THF يعطي بوليمرات جديدة قابلة للذوبان في مذيب THF,DMSO,DMF . ثلاثة بوليمرات محورة للـ PVC قد حضرت من خلال تفاعل المركبات (1،4) مع PVC ذائبة في مذيب THF. الثباتية الضوئية للبوليمرات المحورة قد تحقق. تختلف البوليمرات المحورة في تأثرها بالاكسدة الضوئية مقارنة بـالـ PVC لوحده. تأثيرات الثباتية الضوئية هذه ترجع الى تأثير وجود حلقتي الثايادايازول والتريازول وقد تم تقييمه من خلال قياس المحتوى الهيدروكسيلي، للكاربونيل، والبوليئين. تبين النتائج المكتسبة بأنَّ كُلّ البوليمرات المحورة اعطت صورا اكثر استقرارا بدلاً مِنْ الـ PVC غير المحور. جميع المركبات المحضرة قد شخصت بأطياف الـ UV وFT-IR ودرجات الإنصهار و قد شخص المركب [4] بطيف 1H-NMR في حين شخص المركب [2] بطيف الكتلة.

Keywords

PVC --- Photostability.


Article
Synthesis and Optical Properties Study of Some Metal Complexes of Poly (Vinyl Chloride)-Pyridine-4-Carbohydrazide

Author: Mustafa S. Abdallh
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 2 Pages: 24-29
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Poly (vinyl chloride) (PVC) react with pyridine-4-carbohydrazide (L) in THF to form the PVC-L compound, which have been characterize by spectroscopic methods. PVC-L has further been reacted with different metals ions to form PVC-L-MII complexes. The structures of these complexes have been characterized by FTIR and UV-VIS. Spectrophotometry. The optical properties in the region from (200-900 nm) were studied using UV-VIS spectrophotometer. The optical data analyzed and interpreted in term of the theory of phonon assisted direct electronic transitions. According to energy gap data the conductivity of PVC and the complexes.

تم مفاعلة البولي فنيل كلورايد مع البيريدين-4-كاربوهيدرازايد لتكوين PVC-L والذي تم مفاعلته مع عدد من العناصر الانتقالية لغرض تكوين المعقد PVC-L-MII. تم تشخيص المعقدات باستخدام تقنية الـFTIR وUV-VIS الخصائص البصرية تم دراستها في المنطقة (200-900 nm). تم حساب التوصيلية الكهربائية من خلال حساب فجوة الطاقة.

Keywords

PVC --- phonon


Article
Optimizing the Conditions for the PVC Playing- Balls Fabrication

Authors: Suhair Mohammad Yaseen --- Ali Najem Abdullah
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 11 Pages: 2274-2281
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Although PVC polymer is one of the cheapest plastics that are widely used in industry. The conditions of PVC processing industries are still industrially and commercially confidential and uncovering it is still industrially and commercially confidential and uncovering it is not easy. This work aims to make processing conditions available to whom interest. This has been achieved by studying the parameters associated with production process and determine the optimum conditions which are necessary to get best quality and more economical product. These parameters are included:1- Mixing equal quantities of both rigid and flexible PVC will giverequiredhardness for product with degree of polymerization 600-700.2- Addition of 3% stabilizer (tribasic lead sulfate) works on raising temp. Of process to 250 centigrade without polymer burning or dissociation.3- Addition of 55% plasticizer (dioctyl phthalate) to polymer (melting point of polymer Tm = 90-100 centigrade and glass transition temp. Tg = 170 Co) decreases Tg below room temp. 20-25Co .As a result of this work, product has enough strength and good flexibility to charge with required volume of air.4- Coloring of product by 2% Titanium oxide to give bright white color.Oven temp. Is 150-180 Co.


Article
Synthesis of New Polymers Derived from Poly (Vinyl Chloride) and Study Their Optical Properties

Authors: Yasmeen Al-Daeif --- Emad Yousif --- Mohammed Abdul Nabi
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2012 Volume: 15 Issue: 2 Pages: 79-83
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Poly (vinyl chloride) (PVC) react with different amines in THF to form new polymers (PVC-L), which been characterize by spectroscopic methods. The structures of these complexes have been characterized by IR and Uv-Vis. Spectrophotometry. The optical properties of PVC in the region from (200-600 nm) were studied by preparing the composites PVC-L. The optical data analyzed and interpreted in term of the theory of phonon assisted direct electronic transition; it is observed that the energy is affected by doping type polymers used.

تم تحضير بوليمرات جديده من تفاعل متعدد كلوريد الفانيل مع امينات مختلفه وقد شخصت البوليمرات المحضره بالاجهزه الطيفيه (جهاز الاشعه فوق البنفسجيه وجهاز اطياف تحت الحمراء).القياسات البصريه للبوليمرات تم قياسها في المنطقه المحدده بين 200 الى 600 نانوميتر ومن خلال حساب فجوه الطاقه استتنجنا توصيليه البوليمرات الجديده.


Article
Synthesis, Characterization and Optical Properties of New Pvc- Amines Polymers

Author: Ahmed A. Ahmed
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2014 Volume: 17 Issue: 1 Pages: 7-13
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Poly (vinyl chloride) (PVC) react with different amines in THF to form new polymers (PVC-L). The structures of these polymers have been characterized by IR and Uv-Vis. spectrophotometry. The optical properties of pure and modified PVC were studied in the region (200-400 nm). The optical data analyzed and interpreted in term of the theory of phonon assisted direct electronic transition; it is observed that the energy is affected by doping type polymers used.

تم مفاعلة بولي فنيل كلورايد مع امينات مختلفة بوجود التتراهيدرو فيوران كمذيب. تم تشخيص البوليمرات الجديدة باستخدام الطرق الطيفيةUv-Vis وIR .تم دراسة الخصائص البصرية للبوليمرات في المنطقة 200-400 nm ومن خلال حساب فجوه الطاقه استتنجنا توصيليه البوليمرات الجديدة.

Keywords

PVC --- optical properties --- Energy gap


Article
Some Factors Effecting on the Dielectric Strength for (PVC- Kaolin) Composites
تأثير بعض العوامل في متانة العزل الكهربائي لمتراكبات (PVC- كاولين )

Authors: شهاب أحمد زيدان الجبوري --- فرح جميل أبراهيم الزبيدي
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 3 Pages: 103-116
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research includes the effect of kaolin additions to the polymer matrix (PVC)and study some factors affecting to dielectric strength.The kaolin powder was added as percentage by weight (1,2,3 and 4%) to PVC,and the specimens formed by hot pressing method, with different thickness (0.8-2mm). Some of the results was showed decrease in the electrical strength with kaolinadditives, especially for large thickness due to presence of lattice water, which hashigh dielectric constant but in the same time has high dielectric loss factor, where theelectrical strength decrease when dielectric loss factor increases. Thus the influence ofleakage currents is evident in the large thickness as a result of the electro-thermaleffects.Electrical strength was decreased when the time rate of raising voltage increases.The effect of the cycles number of breakdown for composite specimens was studded.Also the dielectric strength decreased with temperature increases.Optical microscopy images for breakdown region was shown thecarbonization in the breakdown points as a result of crashing polymers chains.Also, micro cracks occurring for specimens that has large amount of kaolin andthis cracks extend directly from the breakdown region.


Article
Preparation of PVC composite using reinforced Iraqi Bentoniet clay as a filler & study their mechanical and thermal properties
تحضير متراكب بولي فاينيل كلورايد (PVC ) باستعمال طين البنتونايت العراقي المعالج مادة ملء ودراسة خصائصه الميكانيكية والحرارية

Author: Foaad SH. Hashim* فؤاد شاكر هاشم*
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2012 Volume: 9 Issue: 3 Pages: 450-458
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study , Iraqi Bentonite clay was used as a filler for polyvinyl chloride polymer. Bentonite clay was prepared as a powder for some certain particle size ,followed by calcinations process at (300,700,900) OC ,then milled and sieved. The selected sizes were D ~75 µm and D ~150. After that polyvinyl Al-Cohool solution prepared and used as a coated layer covered the Bentonite powder before applied as a filler ,followed by drying , milling and sieving for limited recommend sizes. polyvinyl chloride solutions were prepared and adding of modified Bentonite power at certain quantities were followed .Sheet of these variables on the mechanical and thermal properties of the prepared reinforced particular polyvinyl chloride composite Experimentally, it was found that the composite prepared by adding modified Iraqi Bentonite powder , that calcined at 700 oC as a filler have an advantage in heating insulator properties by 30 from that found for PVC as it is ,and the value of stress strength exceed by three times as that for original value.

استعمل طين البنتونايت العراقي مادة ملء لبوليمر بولي فاينيل كلورايد (PVC) حيث حضر مسحوق البنتونايت لمقاس حبيبي µm (75,150) وأجريت عليه عمليات تحميص بدرجات حرارية مختلفة (900,700,300) OC ،ثم عولج بمادة البولي فاينيل الكحول (PVA) بوصفها طبقة رابطة لمادة الملء مع البوليمر.تم تحضير محلول بولي فاينيل كلورايد وذلك بإذابته بالسايكلوهكسانون تحت التسخين غير المباشر.بعد ذلك تمت إضافة البنتونايت المعالج مع المزج المستمر, ثم أضيفت ستيارات الكالسيوم بوصفه مثبتا حراريا وبنسبة محددة. درس تأثير هذه المتغيرات في خاصية التوصيل الحراري وخاصية المتانة ومعامل المرونة للمتراكب المحضر اذ حضرت عينات لهذا الغرض. عمليا وجد أن استخدام البنتونايت العراقي المعالج بمادة PVA والمحمص لدرجة 700oC بوصفه مادة ملء لبوليمر PVC أعطى توصيلية حرارية بحدود 0.25 W/m.k مقارنة بالقيمة لمادة PVC والتي تقع ضمن مدى 0.36 W/m.K وهذا يعني تحسن العزلية الحرارية للمنتج بنسبة ٪30 أفضل منه لمادة PVC وحدها، وأعطى خاصية متانة إجهاد بمقدار ثلاثة أضعاف أعلى من القيمة القياسية


Article
The Influence of Operation Conditions on the Permeative Flux of (PVC/PS) Hollow Fiber Membrane
تاثیر ظروف الغشاء على الجریان التنافذي للغشاء اللیفي المجوف ( PVC/PS)

Authors: Qusy F.Alsalhy --- Jamal M.Ali --- Khitam S.Shaker
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 16 Pages: 2767-2777
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Membranes have gained an important place in chemical technology and are usedin a wide range of applications. This investigation has studied the effect of operatingconditions such as temperature, trans-membrane pressure and solute concentrationon the separation performance of (PVC/ PS) hollow fiber membrane, which wasprepared in the laboratory from 15% (PVC) and 2% (PS) using phase inversionmethod. An attempt was done to investigate the ability of PVC/PS hollow fibermembrane for ultrafiltration application. A (PVP) solute was used to measure (PVP)rejection of prepared membrane.The predicted flux was found to increase from (18.88 l/m2.hr) to 33.05 l/m2.hr)when the operation temperature was increased from (10Ž) to (30Ž).While itincreased from (28.57 l/m2.hr) to (263.36 l/m2.hr) when the operation pressure wasincreased from (1bar) to (3bar). It was also found to decrease from(17.97 l/m2.hr) to(12.20 l/m2.hr) with increase solute concentration from (1000ppm) to (2500ppm).The rejection efficiency was equal to (99.93%) when using (2500ppm) solute. Thisis considered within UF range.

الاغشیة تكسب مكانة مھمة في تقنیة الكیمیاویة وتستعمل في مدى واس ع م ن التطبیق ات . یتض منھذا البحث درسة تاثیر الظروف التشغیلیة مثل درجة الحرارة والضغط وتركیز المحل ول عل ى اداة% وبنسبة 15 (PVC) اللیفي المجوف والذي تم تحضیرة في المختبر من (PVC /PS) عمل اشغءةبسنب 2% باستخدام طریقة الطور الانعكاسي .وایضا في ھذا العمل تم دراسة قابلیةاستعمال (PS) وكم ادة مذاب ة لغ رض قی اس كف اءة PVP ت م اس تخدام . (UF ) الغشاء اللیفي المجوف في تطبیقات الاللیفي المجوف . لقد وجد ان نفاذی ة الت دفق ازداد (PVC /PS) من قبل غشاء (PVP) الارجاع لل 75 ) بزی ادة درج ة الح رارة م ن (℃ 10 ) ال ى (℃ L/m2.hr) 18.88 ) ال ى L/m2.hr) م ن263 ) م ع زی ادة . 36 L/m2.hr ) 28.57 ) ال ى L/m2.hr) 30 ) وك ذلك ازداد نفاذی ة الت دفق م ن17.54 ) ال ى L/m2.hr) 3 ) ولك ن نفاذی ة الت دفق یق ل م ن bar) 1 )ال ى bar) الض غط م ن25000 ( ) كفاءة الفصل ppm الى (ppm مع زیادة تركیز المذاب من )( 1000 (L/m2.hr) 12.20.(UF) 2500 ) وھذا یعتبر ضمن المدى التطبیقي لل ppm) تساوي (% 99.93 ) باستخدام


Article
Study of the Effect of the Variation Effect of Water Temperatures on Shore (D) Hardness for Some Polymers

Author: Zaynab Naif Rasheed
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 3 Pages: 110-118
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The current investigation was carried to study and determine the value of shore [D] hardness for different kinds of polymers [Epoxy [Ep], unsaturated polyester [UPE] and unplasticised PVC. After the preparation our samples Shore [D] hardness values were measured for the samples at 25 ºC. Then the samples were immersed in water bath of two types of water [distilled and tap water] at different temperatures [40,50 & 60] ºC for different times [1,2,3 & 4] hour. Other samples immersed in cooled water at 10 ºC for the same previous periods for comparing the obtained results from samples under test, it was found that the shore hardness value decreases after the immersion of samples in both types of water at 25 ºC for [1,2,3 & 4] hours, the hardness value decreased after immersing these samples in water bath at higher temperature as, while increases when the samples immersed in two types of water at 10 ºC at the same period. The obtained results showed that the rate of decreasing or increasing of hardness value depends on the period of the immersion and the type of the solution used as well as the nature of water and it's temperature.

أجري البحث الحالي لدراسة وتحديد قيم صلادة شور (D) لمواد بوليميرية مختلفة (ايبوكسي 〖 E〗_pوالبولي استر غير المشبع UPE والبولي فاينيل كلورايد PVC غير المشبع. بعد تحضير نماذج البحث وتحديد قيم صلادة شور لجميع النماذج عند درجة حرارة الغرفة (25 درجة مئوية) و يتم غمر النماذج في نوعين من المياه (ماء الحنفية و الماء المقطر) وباستعمال حمام مائي يسخن بدرجات حرارية (40 50 و 60) مئوية ولفترات زمنية (1,2,3,4) ساعة. تغمر نماذج اخرى بعد خفض درجة الحرارة الى (10) درجة مئوية باستخدام انواع المياة المستخدمة سابقا ولنفس الفترة الزمنية لغرض المقارنة بين جميع النتائج المستحصلة. لقد وجد ان قيم صلادة شور تقل بعد غمر النماذج الثلاثة في جميع انواع المياة المستعملة عند درجة حرارة الغرفة للفترات الزمنية التي اجري فيها الاختبار وهذه القيم تستمر بالنقصان عند غمر النماذج بحوض مائي وبزيادة درجة حرارة الماء لكلا نوعي المياة المستعمل، بينما نجد ان قيم صلادة شور تزداد لجميع العينات عند الغمر بدرجات حرارية منخفضة تصل الى (10) مئوية لنفس الفترات الزمنية. وقد لوحظ من خلال النتائج المستحصلة ان معدل الانخفاض او الزيادة لقيم الصلادة للعينات المستخدمة تعتمد على فترة الغمر ونوع المحلول او طبيعة الماء المستخدم للغمر ودرجة حرارته.


Article
Potentiometric Study of Phenytoin – PVC Membrane Electrodes for Determination of Phenytoin in pharmaceutical preparations

Authors: Yehya K. Al-Bayati --- Raad R. Karabat
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2015 Volume: 18 Issue: 1 Pages: 79-87
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Ion selective electrodes for phenytoin were prepared using sodium tetraphenyl borate (NaTPB) ionophore and various plasticizers: di-n-butylphthalate (DBPH), tri-n-butylphosphate(TBP), o-nitrophenyloctyl ether (ONPOE) and di-octylphenylphosphonate (DOPH). The response characteristics of these electrodes, including slope of the calibration plot, the corresponding concentration range, detection limit, response time, life time, pH effect, and selectivity were studied. The experimental results showed that the best electrode was based on DOPH and DBPH as plasticizers, displaying a linear range from1.00×10−1 M to 1.00 × 10−5 M and 1.00×10−1 M to 2.00×10−5 with a Nernstian slope of 26.6 mV/decade and 26.2 mV/decade, correlation coefficient of 0.9993 and 0.9989, The detection limit was 6.00×10−6 M and 9.00×10−6, the lifetime was around 30 and 28 days respectively. The proposed electrodes were successfully applied to the determination of phenytoin in a pharmaceutical preparation.

الاقطاب الانتقائية لدواء الفينتون تم تحضيرها في هذا البحث من خلال استخدام الليكاند صوديوم تترا فنيل بوريت وتكوين معقد المزدوج الايوني (فينتون-تترافنيل بوريت) ومن ثم تحضير الاغشية البولميرية بوجود بولي فانيل كلورايد وبأستخدام الملدنات الاتية الاتيةdi-n-butylphthalate (DBPH-(1tri-n- butylphosphate(TBP)-2o- nitrophenyloctyl ether (ONPOE)-3di-octylphenylphosphonate (DOPH)-4على التواليوتم دراسة زمن الاستجابة وعمر القطب والدالة الحامضية ووجد ان الاقطاب المحضرة الحاوية على الملدنdi-n-butylphthalate (DBPH-( di-octylphenylphosphonate (DOPH)-تمتلك مى الخطيةfrom1.00×10−1 M to 1.00 × 10−5 M and 1.00×10−1 M to2.00×10−5على التوالي والميل 26.2 and 26.6 ملي فولت/حقبة وعمر القطب 30,28 يوم وعلى التوالي وتم تقدير الأدوية الصيدلانية باستخدام الاغشية المحضرة.

Listing 1 - 10 of 53 << page
of 6
>>
Sort by
Narrow your search

Resource type

article (53)


Language

English (45)

Arabic and English (4)

Arabic (3)


Year
From To Submit

2019 (1)

2018 (8)

2017 (8)

2016 (4)

2015 (13)

More...