Article
The Physical and Mechanical Properties of a Shape Memory Alloy Reinforced with Carbon Nanotubes (CNTs)
الخواص الفيزيائية والميكانيكية لسبيكة ذاكرة للشكل مقواة بأنابيب الكاربون النانوية

Loading...
Loading...
Abstract

The shape Memory Alloy (SMA) (Copper-Aluminum-Nickel) was prepared in the research by Powder metallurgy (PM) in component percentage (Cu-13% Al-4% Ni), pressure of (500 Mpa) in one direction, and sintering in (800°C) with Nitrogen gas for three hours. (CNTs) was added in percentage (0,0.5,1.0,1.5,2.0,2.5) % as a volumetric ratio at the relatively of the copper ratio to obtain advanced composites for Carbon Nanotubes with a distinct effect on properties.The elements of the alloy were analyzed using the (EDS) system attached to the Scanning Electron Microscopy (SEM) and study the X-ray Diffraction (XRD) to definition the elements and compounds formed after the process of sintering while imaging the microscopic structure by both Optical Microscopes and (SEM).The physical characteristics were studied as the results showed that by increasing the content of the Carbon Nanotubes (CNTs), The Bulk Density values of the (Cu-13% Al-4% Ni) decrease by ratio (23.5%) for content of Carbon Nanotubes (0%) to (2.0%) associated with an increase in True Porosity with the increase of the (CNTs) content at the same ratio (27.85%) and the impact is reversed when the content is increased to (2.5%) as it corresponds to the Water Absorption. The decrease in thermal conductivity corresponds to the increase in the True porosity ratio while slightly improving the amount Thermal Conductivity at an add (2.5%) percentage (2.0%) of the (CNTs). Some Mechanical properties, such as Hardness and Compressive Strength, have been reduced by increasing the content of the (CNTs) to (2%) While there has been a slight improvement in these two characteristics at the corresponding ratio.

حُضرت سبيكة الذاكرة للشكل (Cu - Al – Ni) في بحثنا هذا بتقانة ميتالورجيا المساحيق (PM) وبنسبة مكونـــــــات (Cu – 13% Al- 4% Ni) وضغط كبس (500 Mpa) باتجاه واحد والتلبيد بدرجة حرارة (800°C) ولمدة ثلاث ساعات وبوجود غاز النيتروجين (N₂) وكانت إضافة انابيب الكاربون النانوية (CNTs) بالنسب %(0,0.5,1.0,1.5,2.0,2.5) كنسبة حجمية على حساب نسبة النحاس للحصول على متراكبات متقدمة لما لأنابيب الكاربون النانوية من تأثير متميز على الخواص.تم تحليل العناصر للسبيكة ومتراكباتها باستخدام منظومة (EDS) الملحقة بالمجهر الإلكتروني الماسح (SEM) ودراسة حيود الأشعة السينية (XRD) لتحديد العناصر والمركبات المتكونة بعد إجراء عملية التلبيد وتصوير البنية المجهرية بكل من المجهر الضوئي (Optical Microscope) و الـ (SEM) .درست الخصائص الفيزيائية إذ أظهرت النتائج أنَّه بزيادة محتوى أنابيب الكاربون النانوية (CNTs) تنخفض قيم الكثافة الحجمية للسبيكة (Cu-13% Al-4% Ni) ومتراكباتها بنسبة مقدارها (%23.5) لمحتوى أنابيب الكاربون النانوية من (%0) الى (%2.0) وترافقت زيادة المسامية الحقيقية مع زيادة محتوى الـ (CNTs) عند ذات النسب بنسبة مقدارها (%27.85) ويكون الفعلُ معاكسً عند زيادة المحتوى إلى (%2.5) إذ يتطابق السلوك مع قابلية امتصاصية الماء, واما الموصلية الحرارية فان سلوكها يتطابق مع سلوك الكثافة الحجمية والظاهرية ولذات النسب, وانخفضت بعض الخصائص الميكانيكية كالصلادة ومقاومة الانضغاط بزيادة محتوى الـ (CNTs) الى نسبة (%2) بينما حدث تحسن طفيف لتلك الخاصيتين عند النسب المتوافقة.


Article
Effect of Aluminium Content on Some Physical and Mechanical Properties of The compounds With Base of Ceramic
تأثير تغير محتوى الألمنيوم على بعض الخواص الفيزياوية والميكانيكية لمتراكبات ذات اساس سيراميكي

Loading...
Loading...
Abstract

This research includes the study of the effect of the Aluminium (Al) addition as reinforcement material at a different weight percentages (4,8,12,16,20) % to ceramic matrix material formed from ( Silicon Dioxide , Oxide Chromium (III) , Titanium Dioxide ) with fixed ratios of elements (Co , Ni) for each of them , by using powder metallurgy technique with pressure of (5) tons were used for forming. We have studied the effect of the Aluminium addition on some physical and mechanical properties of prepared sample after sintered it at (1000 Cº) for (2hr) .The results shown that the Aluminium addition have been enhanced the physical and mechanical properties of the Composites samples , When increasing the proportion of aluminum from (% 4) to (% 20) we note that Apparent density , specific gravity and hardness of the composite (C): [ Cr2O3 + Al + Co + Ni ] for example, had improved by (% 3.2) , (% 4.8) and (% 13) respectively, as for Composites (B): [ TiO2+ Al+ Co+ Ni ] and (A): [SiO2 + Al + Co + Ni ] are similar behavior with composite (C) but at low rates according to form of the composite .It is also found that relation between the Aluminium addition with the porosity and water absorption for all compound is an inverse relation , while their relations with the apparent density , specific gravity and other mechanical is a direct relation exact . And the Composite (C) which is containing (Cr2O3) showed the best properties with for all additional rates as a comparing with the other Composites.

يتضمن هذا البحث دراسة تأثير إضافة الألمنيوم ( Al ) كمادة تدعيم وبنسب وزنية مختلفة (4,8,12,16,20)% الى مواد ذات أساس سيراميكي متكونة من ( ثاني اوكسيد السليكون , ثاني اوكسيد التيتانيوم , اوكسيد الكروم الثلاثي ) مع نسبة ثابتة من عنصري ( Ni ,Co ) لكل منهم. باستخدام تقانة ميتالورجيا المساحيق وبضغط كبس (5 ton) لغرض التشكيل .تم دراسة تأثير نسب الإضافة على الخواص الفيزياوية والميكانيكية بعد تلبيدها بدرجة حرارة (1000°C) لمدة ( 2 hr) . وقد تم التوصل إلى أن زيادة نسبة الألمنيوم تعمل على تحسين الخواص الفيزيائية والميكانيكية للنماذج فعند زيادة نسبة الألمنيوم من (%4) إلى (%20) نلاحظ إن الكثافة الظاهرية والوزن النوعي والصلادة للمتراكب (C):[ Cr2O3+Al+Co+Ni]على سبيل المثال قد تحسنت بالنسب (%3.2) و (%4.8) و (%13) على التوالي أما المتراكبان (B):[TiO2+Al+Co+Ni] و SiO2+Al+Co+Ni] [:(A) فيتشابهان بالسلوك مع المتراكب C ولكن بنسب خواص أقل تبعاً لنوع المتراكب . وان علاقة نسبة إضافة الألمنيوم بالمسامية الظاهرية وقابلية امتصاص الماء للمتراكبات كافة هي علاقة عكسية , بينما تكون علاقتها طردية بالكثافة الظاهرية والوزن النوعي والخواص الميكانيكية الأخرى وان المتراكب (C)الذي يحتوي على اوكسيد الكروم الثلاثي (Cr2O3) أظهر أفضل الخواص ولجميع نسب الألمنيوم مقارنة بالمتراكبات الأخرى .