Article
Effect of Plastic Fibers on Properties of Foamed Concrete
تأثير الألياف البلاستيكية على خواص الخرسانة الرغوية و الخفيفة الوزن

Authors: Hisham K. Ahmed --- Waleed A. Abbas --- DohaM. Abdul-Razzaq
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 7 Part (A) Engineering Pages: 1313-1330
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The main objective of this work is to study the effect of adding plastic fibers on Lightweight Aggregate Foamed Concrete (LWAFC) using mix proportion of 1:2.6:0.4 by volume (cement: fine Porcelanite: coarse Porcelanite) with 2% foaming agent by weight of water, and using sand as a partial and total replacement of local Porcelanite aggregate in that mix. The properties of lightweight aggregate foamed concrete reinforced with different percentages of plastic fiber (0.5, 0.75, and 1% by volume) were studied. Compressive strength, splitting tensile strength, flexural strength, dry density, initial surface absorption, water absorption, ultrasonic pulse velocity, acoustic impedance, and impact resistance tests were conducted on mixes at ages of 7, 28, and 60 days. The results showed a significant increasing in impact resistance, splitting tensile strength, and water absorption 34.55%, 4.2%, 326%, and 27.3% respectively. While the results indicated that the compressive strength, ultrasonic pulse velocity, dry density and acoustic impedance of the composites were reduced when the crimped plastic fiber volume fraction increases. The percentage of reduction of these properties was 15%, 11.1%, 6.23%, and 12.55% respectively.

إن الهدف الرئيسي لهذا البحث هو دراسة تأثير إضافة الالياف البلاستيكية على الخرسانة الرغوية الخفيفة الوزن باستعمال نسب خلط حجمية 1 ، 2.6 ، 0.4 (سمنت : بورسيلانايت ناعم : بورسيلانايت خشن) وباضافة 2% من المادة الرغوية كنسبة وزنية من الماء وباحلال الرمل كبديل جزئي أو كلي من ركام البورسيلانايت المحلي في الخلطة. تمت دراسة استعمال الالياف البلاستيكية بنسب حجمية مختلفة ( 0.5 ، 0.75 ، 1.0% ) لتسليح الخرسانة الرغوية الخفيفة الوزن. تم إجراءفحوصات مقاومة الانضغاط و مقاومة الشد و فحص الانثناء و مقاومة الصدم والكثافة الجافة و الامتصاص السطحي الاولي و الامتصاص الكلي وسرعة الذبذبات الفوق الصوتية والمعاوقة الصوتية للخلطات بأعمار 60،28،7 يوماً. بينت النتائج زيادة ملحوظة في مقاومة الصدم و مقاومة شد الانفلاق و امتصاص الماء و التي بلغت 34.55% , 4.2%, 27.3% على التوالي مع زيادة محتوى الالياف على الرغم من تسجيل انخفاض في مقاومة الانضغاط و الذبذبات فوق الصوتية و الكثافة الجافة و المعاوقة الصوتية مع زيادة محتوى الالياف. وقد بلغ مقدار الأنخفاض في هذه الخصائص 15%, 11.1%, 6.23%, 12.55% على التوالي.


Article
MECHANICAL PROPERTIES FOR ORDINARY CONCRETE CONTAINING WASTE PLASTIC FIBERS
الخصائص الميكانيكية للخرسانة الاعتيادية التي تحتوي على الفضلات البلاستيكية

Authors: Khalil Ibrahim Aziz خليل ابراهيم عزيز --- Huda Al Moqbel kuhair هدى مقبل قهير
Journal: Iraqi Journal of Civil Engineering المجلة العراقية للهندسة المدنية ISSN: 19927428 Year: 2017 Volume: 11 Issue: 2 Pages: 33-44
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This study program has been conducted to investigate the influence of adding waste plastic fibers (WPF) resulting from manual cutting for bottles used in the conservation gassy beverage on different characteristics of ordinary concrete.Cutting plastic waste by volumetric rates ranging between (0.5%) to (2%) was approved. Reference mix was produced for comparison. Tests were conducted on the models produced from waste plastic fiber concrete like compressive strength, flexural strength and splitting tensile strength. The analysis of the results showed that the use of plastic waste fibers (1%) has led to improve the properties of flexural strength and splitting tensile strength compared with reference concrete .When the( 0.75%)WPF ratio improved the compressive strength as compared with the control specimen . Compressive strength in (28 days) with fiber ratio (0.75%) WPF is higher than equal (5.1%) from compressive strength in (28 days) of reference concrete. Volumetric ratio (1%) WPF can be also observed that each of the flexural strength and splitting tensile strength increases equal (12.5 and 12.5%) respectively, from flexural strength and splitting tensile strength for the reference mix at(28day).

يتضمن هذا البحث دراسة الخصائص الميكانيكية للخرسانة الحاوية على فضلات بلاستيكية الناتجه من التقطيع اليدوي للقناني البلاستيكية المستخدمة في حفظ المشروبات الغازية ولقد تم اعتماد الياف الفضلات البلاستيكيه بنسب حجمية مختلفه تتراوح من(0.5%-2%)حيث ان.0.75% اعطت اعلى مقاومة انضغاط و1% اعطت اعلى مقاومة شد مع انتاج خرسانه اعتياديه مرجعيه لغرض المقارنة. وتم اجراء الفحوصات على النماذج المنتجة من الخرسانة الحاوية على فضلات الالياف البلاستيكية كفحوصات مقاومة الانضغاط ومقاومة الانثناء ومقاومة الشد بلانشطار ولقد اظهر تحليل النتائج ان استخدام الياف الفضلات البلاستيكة بنسبة (0.75%) ادى الى تحسين مقاومة الانضغاط بنسبة (5.1%) مقارنة مع الخلطة المرجعية بعمر 28 يوم.وكذلك يمكن ملاحظة بان كل من مقاومة الانثناء ومقاومة الشد بلانشطار تزداد بمقدار(12.5%)و(12.5%) على التوالي من مقاومة الانثناء والشد بالانشطار للخلطه المرجعية.


Article
Fresh, Mechanical Properties and Impact Resistance Behavior of Eco-Friend Self-Compacted Concrete

Authors: Mohammed T. Nawar --- Alhareth M. Abdulghafor --- Sheelan M. Hama
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2019 Volume: 22 Issue: 3 Pages: 208-212
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this work, waste glass powder from broken windows and plastic fibers from waste polyethylene terephthalate bottles are utilized to produce an economical self-compact concrete. Fresh properties (slump flow diameter, slump Flow T50, V. Funnel, L–Box), mechanical properties (Compressive strength and Flexural strength) and impact resistance of self-compact concrete are investigated. 15% waste glass powder as a partial replacement of cement with five percentages of polyethylene terephthalate plastic waste were adopted: 0% (reference), 0.5%, 0.75%, 1%, 1.25% and 1.5% by volume. It seems that the flow ability of self-compact concrete decreases with the increasing of the amount of plastic fibers. The compressive strength was increased slightly with plastic fiber content up to (0.75%), about 4.6% For more than (0.75%) plastic fiber. The compressive strength began to decrease about 15.2%. The results showed an improvement in flexural strength and an impact on the resistance in all tested specimens’ content of the plastic fibers, especially at (1.5%) fibers.