This study included the use of poly acryl amide as corrosion inhibitor of the C-Steel in50ml of 15% HCl were used five different weights (0.5, 1, 1.5, 2, 2.5) gm of polymer toobtain different concentrations of the inhibitor and from weight lost in differenttemperature and times were obtained the inhibitor efficiency and covered surface area withpolymer and then calculated the thermodynamic constants. It was noted that in increase oftime and temperatures increases corrosion. The highest efficiency of the inhibitor has beenrecorded at the time of 3 hours and a temperature of 40 ℃.

تم استخدام البولي اكريل امايد كمثبط لتآكل ال C-Steel L80 في 50ml من 15% HCl حيث استخدمت خمسة أوزان مختلفة من مثبط التاكل (0.5, 1, 1.5, 2, 2.5)gm وتم اذابته في 50ml من HCl للحصول على خمسة تراكيز مختلفة من المثبط (1, 2, 3, 4, 5)% بعدها تم غمر السبائك بالمحلول المحضر وتم حساب الأوزان المفقودة لدرجات حرارية مختلفة)℃ (40, 60, 80, 90 وأزمنة مختلفة (3, 4, 5, 6) ساعة ومن الأوزان المفقودة تم حساب الكفاءة ومساحة السطح المغطى (Ɵ) وبعدها حسبت الثوابت الثرموديناميكية ولوحض ان بزيادة الزمن ودرجات الحرارة يزداد تاكل ال C-Steel L80 وان اعلى نسبة كفاءة للمثبط تكون عند زمن 3 ساعة ودرجة حرارة 40 ℃.

Poly acryl amide --- P.A.M --- Corrosion --- C-Steel L80 --- inhibitors --- P.A.M ، المثبطات ، بولي اكريل امايد = C-Steel L80 بولي اكريل امايد ، التآكل ، ال